• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.27 no.1
• /
• pp.9-17
• /
• 2017

$K_2Ti_6O_{13}$ whisker have been synthesized by hydrothermal process at low temperature and pressure condition. The average length of the synthesized $K_2Ti_6O_{13}$ whisker was about in the range of 300 nm to $1.5{\mu}m$. The average diameter of the synthesized $K_2Ti_6O_{13}$ whisker was 15 nm to 60 nm. The aspect ratio of the synthesized $K_2Ti_6O_{13}$ whisker was below 12. The average length and diameter of the synthesized $K_2Ti_6O_{13}$ whisker can be controlled by reaction temperature and time, KOH molar ratio. $K_2Ti_6O_{13}$ whisker was synthesized from more than $210^{\circ}C$ and 4 h at reaction temperature and time. The length of the whisker is increased with increasing reaction temperature. Characterization of the synthesized $K_2Ti_6O_{13}$ whisker was carried out using the XRD and FE-SEM.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.9 no.4
• /
• pp.371-376
• /
• 1999

A large NaX type zeolite crystal of a uniform particle size of 20$\mu\textrm{m}$ are grown with various {{{{{H}_{2}O}}}} content by hydrothermal reaction and added seed crystal (2~3$\mu\textrm{m}$) to reactant solution as a function of different adding seed levels from 3 to 15%. The result that increased purity of NaX zeolite above 95% and homogeneity of crystal size by increasing adding seed levels, also decreased crystallization time. It was explained that adding seed to synthesis solution leaded out increase of surface area for physical contact reaction and directed growth of seed crystal, so more rapid consumption of reaction gel as increase seeding levels.

• Korean Journal of Materials Research
• /
• v.23 no.1
• /
• pp.1-6
• /
• 2013

A simple thermal oxidation of Cu thin films deposited on planar substrates established a growth of vertically aligned copper oxide (CuO) nanorods. DC sputter-deposited Cu thin films with various thicknesses were oxidized in environments of various oxygen partial pressures to control the kinetics of oxidation. This is a method to synthesize vertically aligned CuO nanorods in a relatively shorter time and at a lower cost than those of other methods such as the popular hydrothermal synthesis. Also, this is a method that does not require a catalyst to synthesize CuO nanorods. The grown CuO nanorods had diameters of ~100 nm and lengths of $1{\sim}25{\mu}m$. We examined the morphology of the synthesized CuO nanorods as a function of the thickness of the Cu films, the gas environment, the oxidation time, the oxidation temperature, the oxygen gas flow rate, etc. The parameters all influence the kinetics of the oxidation, and consequently, the volume expansion in the films. Patterned growth was also carried out to confirm the hypothesis of the CuO nanorod protrusion and growth mechanism. It was found that the compressive stress built up in the Cu film while oxygen molecules incorporated into the film drove CuO nanorods out of the film.

• Proceedings of the Materials Research Society of Korea Conference
• /
• 2009.11a
• /
• pp.5.2-5.2
• /
• 2009

From 10 years ago, the development of nano-devices endeavored to achieve reconstruction of information technology (IT) and nano technology (NT) industry. Among the many materials for the IT and NT industry, zinc oxide (ZnO) is a very promising candidate material for the research of nano-device development. Nano-structures of ZnO-based materials were grown easily via various methods and it attracts huge attention because of their superior electrical and optical properties for optoelectronic devices. Recently, among the various growth methods, MOCVD has attracted considerable attention because it is suitable process with benefits such as large area growth, vertical alignment, and accurate doping for nano-device fabrication. However, ZnO based nanowires grown by MOCVD process were had the principal problems of 1st interfacial layers between substrate and nanowire, 2nd a broad diameter (about 100 nm), and 3rd high density, and 4th critical evaporation temperature of Zinc precursors. In particular, the growth of high performance nanowire for high efficiency nano-devices must be formed at high temperature growth, but zinc precursors were evaporated at high temperature.These problems should be repaired for materialization of ultra high performance quantum devices with quantum effect. For this reason, we firstly proposed the growth method of vertical aligned slim MgZnO nanowires (< 10 nm) without interfacial layers using self-phase separation by introduced Mg at critical evaporation temperature of Zinc precursors ($500^{\circ}C$). Here, the self-phase separation was reported that MgO-rich and the ZnO-rich phases were spontaneously formed by additionally introduced Mg precursors. In the growth of nanowires, the nanowires were only grown on the wurzite single crystal seeds as ZnO-rich phases with relatively low Mg composition (~36 at %). In this study, we investigated the microstructural behaviors of self-phase separation with increasing the Mg fluxes in the growth of MZO NWs, in order to secure drastic control engineering of density,diameter, and shape of nanowires.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.4 no.3
• /
• pp.223-229
• /
• 1994

$KTP(KTiOPO_4)$ single crystals have been hydrothermally grown in KOH solutions. Properties and Raman spectra of grown crystal were investigated. The most effective solvents for the crystal growth of KTP were KOH and KF solutions. In this study, the properties of KTP single crystals grown hydrothermally at $500^{\circ}C$ in 9 m KOH solution were measured. The following results were obtained : lattice parameters ; a=1.281 nm and c=1.058 nm, density ; $2.94 g/cm^3$, Vickers hardness ; $562kg/cm^2$, refractive indices ; $n_e=1.740$ and $n_e= 1.747.$ And Raman spectra of hydrothermal growth KTP single crystal have been investigated at room temperature under atmospheric pressure. As a result, the $A_1$ modes agree very well with KTP single crystal of high temperatures solution growth but the behavior of $B_2$ modes were slightly different.

• Korean Journal of Crystallography
• /
• v.8 no.1
• /
• pp.15-19
• /
• 1997

Single crystals of Co-doped quartz (blue quartz) were grown hydrothermally from the $Na_2CO_3$ solution. The size of as-grown crystal was $100{\times}50{\times}35mm^3$ and the growth rate was 0.55 mm/day under the growth condition of $5wt.\%\;Na_2CO_3$ mineralizer, growth temperature of $343^{\circ}C$ and temperature gradient of $22^{\circ}C$. Visible spectrum showed a typical absorption feature of the synthetic blue quartz near 545, 570 and 643 nm. The concentration of color of the as-grown blue quartz related not to the concentration of cobalt in raw material but to the growth temperature.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.18 no.3
• /
• pp.131-135
• /
• 2008

This study is to establish the coating technique for synthetic mica and to prepare synthetic mica with the non-aqueous property. The surface coating of synthetic mica is prepared with stearic acid using the high speed stirrer. The characterizations for mica powders coated the stearic acid are carried out by the deposition test, XRD and SEM. The results of research could be coated the stearic acid on the mica by 1600 rpm/min at $70^{\circ}C$ for 10 min. From the observation of SEM was found that the non-aqueous property mica could obtained by mixture ratios for stearic acid and mica, the inner temperature and rotation speed of the stirrer but treated time be unrelated.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.10 no.2
• /
• pp.171-176
• /
• 2000

The phosphatic calcium compounds such as calcium hydrogen phosphate, bone ash, hydroxyapatite and tricalcium phosphate were prepared using the high purity calcium hydroxide and calcium carbonate obtained from shell resources. Calcium hydrogen phosphate had been prepared using the high purity calcium hydroxide and phosphoric acid solution. Using the calcium hydrogen phosphate as a starting materials, bone ash have been prepared by solid state reaction method and hydroxyapatite could be obtained by hydrothermal treatment method, respectively. The tricalcium phosphate was prepared by the solid state reaction of a stoichiometic mixture of bone ash and high purity calcium carbonate. In this paper, the optimal preparation process and conditions of phosphatic calcium compounds were established.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.28 no.1
• /
• pp.1-8
• /
• 2018

The 23 wt% polyvinylidene fluoride (PVDF)/15 wt% polyurethane (PU) fibers were electrospun using the conjugated nozzle at a flow rate of 1.0 mL/h and an electric field of 1 kV/cm. The formation of ${\beta}$ crystal phase in the PVDF and the PVDF/PU fibers was confirmed by Fourier transform infrared spectroscopy. After electrospinning, the asspun fibers were immersed in a boiling water and then dried at $100^{\circ}C$ in a convection oven to make a crimp phenomenon. The crimps with a diameter of $2.0{\pm}0.08{\mu}m$ were observed for the PVDF/PU fibers after hydrothermal treatment without sacrificing the extent of ${\beta}$ crystal phase. All the PU, PVDF and PVDF/PU fibers exhibited average cell viability of more than 98 %. The cell proliferation results suggested that L-929 cells adhered well to the PU, PVDF and PVDF/PU fibers and proliferated continuously with increasing time, indicating that the PVDF/PU fibers are highly applicable to the biomedical applications.

• Journal of the Mineralogical Society of Korea
• /
• v.17 no.2
• /
• pp.115-121
• /
• 2004

The surface microtopography of pyrophyllite collected from the Gussi deposit, Korea was observed by mean of transmission electron microscopy (TEM) with the gold decoration technique. As results, closed step patterns with malformed circular islands were characteristically observed on the (001) surface of pyrophyllite, contrasting with spiral step patterns common in illite and kaolinite. Gussi pyrophyllite was likely crystallized from hydrothermal solution of higher temperature and/or higher supersaturation than those of other clay minerals. Comparing with micro-topographies of pyrophyllite from the Shokozan and the Uku deposits, southwest Japan, growth mechanism of Gussi pyrophyllite is almost equivalent to those from the Shokozan and the Uku deposits.