• Journal of Electrochemical Science and Technology
• /
• v.10 no.4
• /
• pp.424-432
• /
• 2019

Planar BiVO₄ and 3 wt% Mo-doped BiVO₄ (abbreviated as Mo:BiVO₄) film were prepared by the facile spin-coating method on fluorine doped SnO₂(FTO) substrate in the same precursor solution including the Mo precursor in Mo:BiVO₄ film. After annealing at a high temperature of 450℃ for 30 min to improve crystallinity, the films exhibited the monoclinic crystalline phase and nanoporous architecture. Both films showed no remarkably discrepancy in crystalline or morphological properties. To investigate the effect of surface passivation exploring the Al₂O₃ layer, the ultra-thin Al₂O₃ layer with a thickness of approximately 2 nm was deposited on BiVO₄ film using the atomic layer deposition (ALD) method. No distinct morphological modification was observed for all prepared BiVO₄ and Mo:BiVO₄ films. Only slightly reduced nanopores were observed. Although both samples showed some reduction of light absorption in the visible wavelength after coating of Al₂O₃ layer, the Al₂O₃ coated BiVO₄ (Al₂O₃/BiVO₄) film exhibited enhanced photoelectrochemical performance in 0.5 M Na₂SO₄ solution (pH 6.5), having higher photocurrent density (0.91 mA/㎠ at 1.23 V vs. reversible hydrogen electrode (RHE), briefly abbreviated as V_RHE) than BiVO₄ film (0.12 mA/㎠ at 1.23 V_RHE). Moreover, Al₂O₃ coating on the Mo:BiVO₄ film exhibited more enhanced photocurrent density (1.5 mA/㎠ at 1.23 V_RHE) than the Mo:BiVO₄ film (0.86 mA/㎠ at 1.23 V_RHE). To examine the reasons, capacitance measurement and Mott-Schottky analysis were conducted, revealing that the significant degradation of capacitance value was observed in both BiVO₄ film and Al₂O₃/Mo:BiVO₄ film, probably due to degraded capacitance by surface passivation. Furthermore, the flat-band potential (V_FB) was negatively shifted to about 200 mV while the electronic conductivities were enhanced by Al₂O₃ coating in both samples, contributing to the advancement of PEC performance by ultra-thin Al₂O₃ layer.

• Korean Journal of Optics and Photonics
• /
• v.3 no.4
• /
• pp.258-265
• /
• 1992

A low loss optical waveguide of $P_{2}O_{5}-SiO_{2}$on Si substrate is produced by using the chemical vapour deposition method of $SiO_2$ thin films used in Si technology. Propagation loss of the waveguide layer was 1.65 dB/cm as produced and reduced down to 0.1 dB/cm after heat treatment at $1100^{\circ}C$. By using laser lithography and reactive ion etching method $P_{2}O_{5}-SiO_{2}$ waveguide was produced and subsequently annealed at $1100^{\circ}C$.As a result of this annealing the shape of the waveguide core was changed from rectangular to semi-circular form, and the propagation loss was reduced as down to 0.03 dB/cm at 0.6328$\mu$m and 0.04dB/cm at 1.53$\mu$m. We think that the mechanism of the reduction in propagation loss during the heat treatment is the following: 1) The hydrogen bonding in waveguide layer, which causes absorption loss, is dissociated and diffused out. 2) The roughness of the interface and the micro-structure of the waveguide layer is removed. 3) The irregularities in the cross-sectional shape of the waveguide which was induced during the lithographic process were disappeared by flowing of the waveguide core.

• Journal of IKEEE
• /
• v.20 no.3
• /
• pp.220-225
• /
• 2016

In this paer, low on-resistance and high-power trench gate MOSFET (Metal-Oxide-Silicon Field Effect Transistor) incorporating current sensing FET (Field Effect Transistor) is proposed and evaluated. The trench gate power MOSFET was fabricated with $0.6{\mu}m$ trench width and $3.0{\mu}m$ cell pitch. Compared with the main switching MOSFET, the on-chip current sensing FET has the same device structure and geometry. In order to improve cell density and device reliability, self-aligned trench etching and hydrogen annealing techniques were performed. Moreover, maintaining low threshold voltage and simultaneously improving gate oxide relialility, the stacked gate oxide structure combining thermal and CVD (chemical vapor deposition) oxides was adopted. The on-resistance and breakdown voltage of the high density trench gate device were evaluated $24m{\Omega}$ and 100 V, respectively. The measured current sensing ratio and it's variation depending on the gate voltage were approximately 70:1 and less than 5.6 %.

• Journal of Electrochemical Science and Technology
• /
• v.9 no.4
• /
• pp.282-291
• /
• 2018

The pristine fluorine-doped $SnO_2$ (abbreviated as FTO) inverse opal (IO) was developed using a 410 nm polystyrene bead template. The nanolayered copper tungsten oxide ($CuWO_4$) was decorated on the FTO IO film using a facile electrochemical deposition, subsequently followed by annealing at $500^{\circ}C$ for 90 min. The morphologies, crystalline structure, optical properties and photoelectrochemical characteristics of the FTO and $CuWO_4$-decorated FTO (briefly denoted as $FTO/CuWO_4$) IO film were investigated by field emission scanning electron microscopy, X-ray diffraction, UV-vis spectroscopy and electrochemical impedance spectroscopy, showing FTO IO in the hexagonally closed-pack arrangement with a pore diameter and wall thickness of about 300 nm and 20 nm, respectively. Above this film, the $CuWO_4$ was electrodeposited by controlling the cycling number in cyclic voltammetry, suggesting that the $CuWO_4$ formed during 4 cycles (abbreviated as $CuWO_4$(4 cycles)) on FTO IO film exhibited partial distribution of $CuWO_4$ nanoparticles. Additional distribution of $CuWO_4$ nanoparticles was observed in the case of $FTO/CuWO_4$(8 cycles) IO film. The $CuWO_4$ layer exhibits triclinic structure with an indirect band gap of approximately 2.5 eV and shows the enhanced visible light absorption. The photoelectrochemical (PEC) behavior was evaluated in the 0.5 M $Na_2SO_4$ solution under solar illumination, suggesting that the $FTO/CuWO_4$(4 cycles) IO films exhibit a photocurrent density ($J_{sc}$) of $0.42mA/cm^2$ at 1.23 V vs. reversible hydrogen electrode (RHE, denoted as $V_{RHE}$), while the FTO IO and $FTO/CuWO_4$(8 cycles) IO films exhibited a $J_{sc}$ of 0.14 and $0.24mA/cm^2$ at $1.23V_{RHE}$, respectively. This difference can be explained by the increased visible light absorption by the $CuWO_4$ layer and the favorable charge separation/transfer event in the cascading band alignment between FTO and $CuWO_4$ layer, enhancing the overall PEC performance.

• 한국정보디스플레이학회:학술대회논문집
• /
• 2008.10a
• /
• pp.107-108
• /
• 2008

The spectacular development of AMLCDs, been made possible by a-Si:H technology, still faces two major drawbacks due to the intrinsic structure of a-Si:H, namely a low mobility and most important a shift of the transfer characteristics of the TFTs when submitted to bias stress. This has lead to strong research in the crystallization of a-Si:H films by laser and furnace annealing to produce polycrystalline silicon TFTs. While these devices show improved mobility and stability, they suffer from uniformity over large areas and increased cost. In the last decade we have focused on microcrystalline silicon (${\mu}c$-Si:H) for bottom gate TFTs, which can hopefully meet all the requirements for mass production of large area AMOLED displays [1,2]. In this presentation we will focus on the transfer of a deposition process based on the use of $SiF_4$-Ar-$H_2$ mixtures from a small area research laboratory reactor into an industrial gen 1 AKT reactor. We will first discuss on the optimization of the process conditions leading to fully crystallized films without any amorphous incubation layer, suitable for bottom gate TFTS, as well as on the use of plasma diagnostics to increase the deposition rate up to 0.5 nm/s [3]. The use of silicon nanocrystals appears as an elegant way to circumvent the opposite requirements of a high deposition rate and a fully crystallized interface [4]. The optimized process conditions are transferred to large area substrates in an industrial environment, on which some process adjustment was required to reproduce the material properties achieved in the laboratory scale reactor. For optimized process conditions, the homogeneity of the optical and electronic properties of the ${\mu}c$-Si:H films deposited on $300{\times}400\;mm$ substrates was checked by a set of complementary techniques. Spectroscopic ellipsometry, Raman spectroscopy, dark conductivity, time resolved microwave conductivity and hydrogen evolution measurements allowed demonstrating an excellent homogeneity in the structure and transport properties of the films. On the basis of these results, optimized process conditions were applied to TFTs, for which both bottom gate and top gate structures were studied aiming to achieve characteristics suitable for driving AMOLED displays. Results on the homogeneity of the TFT characteristics over the large area substrates and stability will be presented, as well as their application as a backplane for an AMOLED display.