• 대한금속재료학회지
• /
• 제49권4호
• /
• pp.298-303
• /
• 2011

Mg-23.5 wt%Ni-xwt%Cu (x = 2.5, 5 and 7.5) samples for hydrogen storage were prepared by melt spinning and crystallization heat treatment from a Mg-23.5 wt%Ni-5 wt%Cu alloy synthesized by the gravity casting method. They were then ground under $H_2$ to obtain a fine powder. Among these samples the Mg-23.5Ni-2.5Cu sample had the highest hydriding and dehydriding rates after activation. The Mg-23.5Ni-2.5Cu sample absorbed 3.59 and 4.01 wt%H for 10 and 60 min, respectively, at 573K under 12 bar $H_{2}$. The activated 88(87.5Mg-10Ni-2.5Cu)-$5Nb_{2}O_{5}-7NbF_{5}$ sample absorbed 2.93 wt%H for 10 min, and 3.14 wt%H for 60 min at 573K under 12 bar $H_{2}$.

• Nuclear Engineering and Technology
• /
• 제55권8호
• /
• pp.2977-2983
• /
• 2023

During normal operation, some parts of the fission product in the defective fuel rods can release into the primary loops in PWR and the escape rate coefficients are widely used to assess quantitatively the release behaviors of fission products in the industry. The escape rate coefficients have been standardized and have been validated by some drilling experiments before the 1970s. In the paper, the model to determine the escape rate coefficients of fission products has been established and the typical escape rate coefficients of noble gas and iodine have been deduced based on the measured radiochemical data in one operating PWR. The result shows that the apparent escape rate coefficients vary with the release-to-birth and decay constants for different fission products of the same element. In addition, it is found that the escape rate coefficients from the defective rod with large defects are much higher than the standard escape rate coefficients, i.e., averagely 4.4 times and 1.8 times for noble gas and iodine respectively. The enhanced release of fission products from the severe secondary hydriding of several defective fuel rods in one cycle may lead to the potential risk of the temporary shutdown of the operating reactors.

• 한국수소및신에너지학회논문집
• /
• 제16권1호
• /
• pp.25-30
• /
• 2005

수소 분위기에서 10wt.%MnO와 기계적인 분쇄(반응성 기계적 분쇄)에 의해 Mg의 수소 저장 성질을 향상시켰다. 회전 속도는 250 rpm, 밀링시간은 2 h, 그리고 시료 대 볼 중량비는 1/45이었다. 준비한 Mg-10wt.%MnO 시료는 활성화를 위한 수소화물 형성 분해 싸이클링이 필요없었으며, 첫 번째 싸이클 593k 12 bar $H_2$에서, 10분 동안에 3.12wt.%, 60분 동안에 3.95wt.%의 수소를 흡수하였다. 또한 Mg-10wt.%MnO는 593k 0.8 bar $H_2$에서 60분 동안에 2.12wt.%의 수소를 방출하였다. MnO와 Mg의 방응성 분쇄는, 핵생성을 용이케하고 (Mg 입자의 표면에 결함 형성과 첨가물에 의해), Mg 입자의 표면에 crack을 만들어 Mg의 입자 크기를 줄여 그 결과 수소 원자의 확산 거리를 작게 함으로써 수소 흡수 방출 속도를 증가시킨다. 수소화물 형성 분해 싸이클링은 Mg 입자의 표면에 crack을 만들고 Mg의 입자 크기를 줄여 수소 흡수 방출 속도를 증가시킨다.

• 한국수소및신에너지학회논문집
• /
• 제16권3호
• /
• pp.238-243
• /
• 2005

Mg and Mg-based alloys are most important hydrogen storage materials. It is a lightweight and low-cost materials with high hydrogen storage capacity. However, the formation of hydride at high temperature, the deterioration effect, the hydriding and dehydriding kinetics are bad factor for application. In this study, Mg and Ni have been produced by hydrogen induced mechanical alloying(HIMA) process. The raw materials, Mg(purity 99.9%) chip and Ni(purity 99.95%) chip was prepared by using a planetary ball mill apparatus(FRITSCH pulverisette 5). The balls to chips mass ratio(BCR) are 30:1. The hydrogen pressure induced 2.0MPa and milling times were 12, 24, 48, 72, 96 hours with a rotating speed of 200rpm. X-ray diffraction(XRD) analysis was made to characterize the crystallite size and misfit strain. The crystallite size measured by laser particle size analysis(PSA). Microstructure changes were investigated by scanning electron microscopy(SEM) and the transmission electron microscopy(TEM). The hydrogen storage properties were evaluated by using an Sivert's type automatic pressure-composition-therm(PCT) apparatus.

• 방사성폐기물학회지
• /
• 제11권1호
• /
• pp.31-39
• /
• 2013

핵연료는 원자로 운전 중 예기치 못한 상황에서 연료 결함을 초래할 수 있다. 핵연료 결함은 연료봉의 수소화나 이물질에 의한 금속 마모, 그리고 펠렛과 피복관의 상호작용에 의해 피복관이 손상된다. 이렇게 손상된 핵연료의 결함원인을 규명하는 것은 원자력발전의 안전운전에 중요하다고 사료된다. 핵연료가 손상되면 원자로 냉각재가 오염되어 원자로 출력을 낮추거나, 발전소를 정지할 수도 있다. 모든 사용후연료는 건식저장고로 이동 보관되어야 하나, 결함연료는 이동할 수 없으므로 이 연구의 목적은 중수로형 원자로에서 연료가 인출된 후 사용후연료 저장조에서 보관된 연료에 대하여 결함 여부를 판단할 수 있는 기술을 개발하고자 하였다. 이 연구를 통하여 핵종 누설 검출 기술을 이용한 사용후연료 검사기술을 개발하였으며, 이 기술을 월성발전소에 적용함으로써, 검사기술 및 검사시스템에 대한 성능을 입증하였다.

• 한국수소및신에너지학회논문집
• /
• 제24권5호
• /
• pp.367-372
• /
• 2013

Hydrogen storage as a metal hydride is the most promising alternative because of its relatively large hydrogen storage capacities near room temperature. TiMn2-based C14 Laves phases alloys are one of the promising hydrogen storage materials with easy activation, good hydriding-dehydriding kinetics, high hydrogen storage capacity and relatively low cost. In this work, multi-component, hyper-stoichiometric $Ti_{0.85}Zr_{0.13}(Fe_x-V)_{0.56}Mn_{1.47}Ni_{0.05}$ C14 Laves phase alloys were prepared by a vacuum induction melting for a hydrogen storage tank. Since pure vanadium (V) is quite expensive, the substitution of the V element in these alloys has been tried and some interesting results were achieved by replacing V by commercial ferrovanadium (FeV) raw material. In addition, the melt-spinning process, which was applied to the manufacturing of some of these alloys, could make the plateau slopes much flatter, which resulted in the increase of reversible hydrogen storage capacity. The improvement of sloping properties of melt-spun $Ti_{0.85}Zr_{0.13}(Fe_x-V)_{0.56}Mn_{1.47}Ni_{0.05}$ alloys was mainly attributed to the homogeneity of chemical composition.

• 한국수소및신에너지학회논문집
• /
• 제13권2호
• /
• pp.151-158
• /
• 2002

The hydorgen storage alloys were produced by melting in arc melting furnace and then solution heat treated at $1,100^{\circ}C$ followed by pulverization. The chemical analysis on the samples showed that the major elements of misch metal(Mm) were La, Ce, Pr and Nd with impurity less than 1wt.%. X-ray diffraction indicated that the structure for these samples were a single phase of hexagonal with $CaCu_5$ type. Compared to the initial particle size $100{\sim}110{\mu}m$, the many fine cracks were found and particle size decreased to $14{\mu}m$ for $MmNi_{4.5}Mn_{0.5}$ after hydriding/dehydring test run. To activate the sample the vessel filled with hydrogen storage alloys was first evacuated for for at $70^{\circ}C$ and then treated for 10.5hr under hydrogen pressure of 20atm for $MmNi_{4.5}Mn_{0.5}$ alloy. The experimental data showed that the hydrogen storage alloy of $MmNi_{4.5}Mn_{0.5}$ had superior adsorption and description properties within a temperature rang of $40^{\circ}C{\sim}80^{\circ}C$ and also they had a good P-C-T curve.

• 한국재료학회지
• /
• 제20권10호
• /
• pp.543-549
• /
• 2010

The hydrogen energy had recognized clean and high efficiency energy source. The research field of hydrogen energy was production, storage, application and transport. The commercial storage method was using high pressure tanks but it was not safety. However metal hydride was very safety due to high chemical stability. Mg and Mg alloys are attractive as hydrogen storage materials because of their lightweight and high absorption capacity (about 7.6 wt%). Their range of applications could be further extended if their hydrogenation properties and degradation behavior could be improved. The main emphasis of this study was to find an economical manufacturing method for Mg-Ti-Ni-H systems, and to investigate their hydrogenation properties. In order to examine their hydrogenation behavior, a Sievert's type automatic pressure-compositionisotherm (PCI) apparatus was used and experiments were performed at 423, 473, 523, 573, 623 and 673 K. The results of the thermogravimetric analysis (TGA) revealed that the absorbed hydrogen contents were around 2.5wt.% for (Mg8Ti2)-10 wt.%Ni. With an increasing Ni content, the absorbed hydrogen content decreased to 1.7 wt%, whereas the dehydriding starting temperatures were lowered by some 70-100 K. The results of PCI on (Mg8Ti2)-20 wt.%Ni showed that its hydrogen capacity was around 5.5 wt% and its reversible capacity and plateau pressure were also excellent at 623 K and 673 K.

• 한국수소및신에너지학회논문집
• /
• 제20권6호
• /
• pp.505-511
• /
• 2009

The hydriding and electrochemical characteristics of Zr-based $AB_2$ alloy produced by gas atomization have been extensively examined. For the particle morphology of the as-cast and gas-atomized powders, it can be seen that the mechanically crushed powders are irregular, while the atomized powder particles are spherical. The increase of jet pressure of gas atomization process results in the decrease of hydrogen storage capacity and the slope of plateau pressure significantly increases. TEM and EDS studies showed the increase of jet pressure in the atomization process accelerated the phase separation within grain of the gas-atomized alloy, which brought about a poor hydrogenation property. However, the gas-atomized $AB_2$ alloy powders produced by jet pressure of 50 bar kept up the reversible $H_2$ storage capacity and discharge capacity similar to the mechanically crushed particles. In addition, the electrode of gas-atomized Zr-based $AB_2$ alloy of 50 bar showed improved cyclic stability over that of the cast and crushed particulate, which is attributed to the restriction of crack propagation by grain boundary and dislocation with ch/discharging cycling.

• 한국수소및신에너지학회논문집
• /
• 제21권2호
• /
• pp.81-88
• /
• 2010

Hydrogen energy applications have recognized clean materials and high energy carrier. Accordingly, Hydrogen energy applies for fuel cell by Mg and Mg-based materials. Mg and Mg-based materials are lightweight and low cost materials with high hydrogen storage capacity. However, commercial applications of the Mg hydride are currently hinder by its high absorption/desorption temperature, and very slow reaction kinetics. Therefore one of the most methods to improve kinetics focused on addition transition metal oxide. Addition to transition metal oxide in $MgH_x$ powder produce $MgH_x$-metal oxide composition by mechanical alloy and it analyze XRD, EDS, TG/DSC, SEM, and PCT. This report considers kinetics by transition metal oxide rate and Hydrogen pressure. In this research, we can see behavior of hydriding/dehydriding profiles by addition catalyst (transition metal oxide). Results of PCI make a excellent showing $MgH_x$-5wt.% Sc2O3 at 623K, $MgH_x$-10wt.% $Sc_2O_3$ at 573K.