• Journal of the Korean Electrochemical Society
• /
• v.5 no.1
• /
• pp.21-26
• /
• 2002

A supercapacitor was developed using an amorphous ruthenium oxide material. The electrode of supercapacitor was prepared using an amorphous ruthenium oxide, which was synthesized from ruthenium trichloide hydrate$(RuCl_3{\cdo5}xH_2O)$. Thin film of tantalum was used as a current collector because it had wide. potential window characteristics than titanium and 575304 materials. A supercapacitor was assembled with ruthenium oxide as an electrode active material and 4.8M sulfuric acid solution as an electrolyte. The specific capacitance of the electrode was tested by a cyclic voltammetry using a half cell. The maximum differential specific capacitances during the oxidative and the reductive scans were 710 and $645\;F/g-RuO_2{\cdot}nH_2O$, respectively. The average specific capacitance was $521\;F/g-RuO_2{\cdot}nH_2O$. The assembled supercapacitor was protonated to the potential level of 0.5V vs. SCE. Super-capacitor, which was adjusted to the appropriate protonation level, had the specific capacitance of $151\;F/g-RuO_2{\cdot}nH_2O$ based on the concept of full cell.

• Journal of the Korean Electrochemical Society
• /
• v.6 no.2
• /
• pp.93-97
• /
• 2003

The electrode for a supercapacitor was prepared using an amorphous ruthenium oxide, which was synthesized from ruthenium trichloride hydrate$(RuO_2{\cdot}nH_2O)$. A supercapacitor was assembled with an electrode of ruthenium oxide material on a current collector of tantalum, and an electrolyte of 4.8 M sulfuric acid. The result of the AC impedance analyses on $Ta/H_2SO_4(4.8 M)/Pt$ cell showed that tantalum was stable at the potential range of $0.0\~1.1V(vs. SCE)$. Therefore, Ta film could be used the supercapacitor as a current collector. The irreversible hydrolysis in the supercapacitor occurred over ca. 1.0V(vs.SCE) when the supercapacitor was protonated to 0.5V(vs. SCE). The supercapacitor protonated to 0.5V(vs.SCE) showed good electrochemical properties when it was tested at the potential range of 1.0V in the charge-discharge test. The potential range of the electrodes including the positive and the negative electrode was varied between -0.004 and 0.995V(vs. SCE). The potential ranges of the positive and the negative electrode were $-0.004\~0.515V(vs.\;SCE)\;and\; 0.515\~0.995V(vs.\;SCE)$, respectively.

• Korean Journal of Materials Research
• /
• v.14 no.9
• /
• pp.607-613
• /
• 2004

This study was to investigate the surface properties of electrochemically oxidized Ti-6Al-7Nb alloy by anodic spark discharge technique. Anodizing was performed at current density 30 $mA/cm^2$ up to 300 V in electrolyte solutions containing $DL-{\alpha}$-glycerophosphate disodium salt hydrate($DL-{\alpha}$-GP) and calcium acetate (CA). Hydrothermal treatment was done at $300^{\circ}C$ for 2 hrs to produce a thin outermost layer of hydroxyapatite (HA). The bioactivity was evaluated from HA formation on the surfaces in a Hanks' solution with pH 7.4 at $36.5^{\circ}C$ for 30 days. The size of micropores and the thickness of oxide film increased and complicated multilayer by increasing the spark forming voltage. Needle-like HA crystals were observed on anodic oxide film after the hydrothermal treatment at $300^{\circ}C$ for 2 hrs. When increasing $DL-{\alpha}$-GP in electrolyte composition, the precipitated HA crystals showed the shape of thick and shorter rod. However, when increasing CA, the more fine needle shape HA crystals were appeared. The bioactivity in Hanks' solution was accelerated when the oxide films composed with strong anatase peak with presence of rutile peak. The increase of amount of Ca and P was observed in groups having bioactivity in Hanks' solution. The Ca/P ratio of the precipitated HA layer was equivalent to that of HA crystal and it was closer to 1.67 as increasing the immersion time in Hanks' solution.

• The Journal of Engineering Geology
• /
• v.21 no.3
• /
• pp.231-237
• /
• 2011

An active apatite drainage system has been developed at the Goro abandoned mine, comprising a grit cell, a reaction cell, and a precipitation pond. Leachate from an abandoned adit and tailing ponds is collected in a pipeline and is transported to the apatite drainage system under the influence of the hydraulic gradient. The results of a laboratory experiment performed in 2004 indicate that the reaction cell requires 38.8 ton/year of apatite and that precipitate will have to be removed from the precipitation pond every 3 months. The purpose of this study is to evaluate a laboratory test on the efficiency of limestone and apatite in removing arsenic from ARD (acid rock drainage), and to evaluate the suitability of materials for use as a precipitant for the leachate treatment disposal system. The laboratory tests show that the arsenic removal ratios of limestone and apatite are 67.4%-98.3%, and the arsenic removal ratio of apatite is inversely proportional to its grain size. The arsenic compounds are assumed to be Johnbaumnite and Ca-arsenic hydrate. Therefore, apatite and phosphorous limestone can be used as a precipitant for the removal of arsenic, although it is difficult to remove arsenic from ARD when it occurs in low concentrations.

• Journal of the Korea Concrete Institute
• /
• v.26 no.4
• /
• pp.507-515
• /
• 2014

Although the construction joints of a concrete structure are properly treated with some measures, leakage has frequently occurred. A series of tests on the bond characteristics between new and old concrete were carried out in this study, assuming that the leakage at the construction joints has certain relationship with the bond of concrete. To assess the bond characteristics under various conditions, a number of specimens were made that have an interface between new and old concrete and bond strength, flexural strength and splitting tensile strength were measured. Main test variables are type and amount of mineral admixtures, treatment method of the interface and type of waterstops. In addition, the effects of placing interval between the concrete and of the age of the strength tests were investigated. The test results showed a slightly increased bond strength when applying mineral admixtures, which can be attributed to the interface filled with the calcium silicate hydrate that is formed by pozzolanic reaction. On the other hand, the bond strength was higher when the interface was treated rough and dry, and the roughness of a waterstop affected the bond capacity of the waterstop. Also, an assessment is required that considers the type of strength test because the bond strength varied according to the test methods.

• Journal of Sericultural and Entomological Science
• /
• v.52 no.1
• /
• pp.10-15
• /
• 2014

Regenerated Antheraea pernyi silk sponge was prepared using calcium nitrate 4 hydrate melt and examined the conformational changes treated with aqueous ethanol solution. The conformation of silk sponges was changed from random coil structure to ${\beta}$-sheet and ${\alpha}$-helix conformation with low ethanol concentration (50 ~ 70%). On the other hand, that of silk sponges with 80% ethanol treatment showed ${\beta}$-sheet ($700cm^{-1}$), ${\alpha}$-helix ($625cm^{-1}$), and random coil ($660cm^{-1}$) specific peaks. Wound healing effect in vitro was observed by cytoslective wound healing kit. Therefore, regenerated Antheraea pernyi silk sponges might be used as promising wound dressing materials.

• Journal of the Korean Society for Marine Environment & Energy
• /
• v.11 no.3
• /
• pp.160-163
• /
• 2008

$CO_2$ ocean sequestration is being considered as a way to earn a frame of time to change other industrial life pattern to overcome the global warming crisis. The method is to dilute the captured $CO_2$ into ocean by ejecting the liquefied $CO_2$ through nozzles. The main issue of such method is the effectiveness and safety, and in both problems the rising speed of those LCO2 droplet is the key parameter. In this paper, the rising speed of LCO2 droplets is numerically studied including the effect of the surfactant which can be residing along the density interface of the droplets. A front tracking method with a simple surface tension model is developed and the rising speed of the droplets is carefully investigated with varying the various parameters. It is demonstrated that the variable surface tension can change the deformation of the droplet, the flow near the interface, and the rising speed.

• Nuclear Engineering and Technology
• /
• v.26 no.3
• /
• pp.425-432
• /
• 1994

Voltammogram analysis of U(VI) reduction at electrochemically non-pretreated/pretreated Ti electrodes in nitric acid and hydrazine($N_2$H$_4$)/protonated hydrazine($N_2$H$_{5}$$^{＋}$) media was done in order to determine the effect of hydrazine form and Ti electrode condition on the reduction of U(VI) in nitric acid. In the case of non-pretreated Ti electrode, the reduction in nitric acid and hydrazine mono-hydrate solution needed a high activation overpotential and was affected by the ratio of hydrazine to nitric acid rather than by only absolute amount of hydrazine because of the decrease of solution conductivity and increase of iR drop, which were caused by proton consumption in the solution by the hydrazine. In the case of pretreated Ti electrode in nitric acid and protonated hydrazine solution, the reduction current peaks of U(VI) were clearer and higher enough to perform a kinetic analysis, compared with the case with the non-pretreated Ti electrode at the same potential, and the behavior was strongly affected by nitric acid. The presence of hydrazine was important in the reduction of U(VI) at the pretreated Ti electrode for preventing the reoxidation of U(IV), but the concentration of protonated hydrazine was not.t.

• Journal of the Mineralogical Society of Korea
• /
• v.17 no.3
• /
• pp.277-288
• /
• 2004

Alkali-silica reaction (ASR) is a chemical reaction between alkalies in cement and chemically unstable aggregates and causes expansion and cracking of concrete. In the Present study, we studied the effects of metakaolin, which is a newly introduced mineral admixture showing excellent pozzolainc reaction property, on the inhibition of ASR. We prepared mortar-bars of various replacement ratios of metakaolin and conducted alkali-silica reactivity test (ASTM C 1260), compressive strength test and flow test. We also carefully analyzed the mineralogical changes in hydrate cement paste by XRD qualitative analysis. The admixing of metakaolin caused quick pozzolanic reaction and hydration reaction that resulted in a rapid decrease in portlandite content of hydrated cement paste. The expansion by ASR was reduced effectively as metakaolin replaced cement greater than 15%. This resulted in that the amounts of available portlandite decreased to less than 10% in cement paste. It is considered that the inhibition of ASR expansion by admixing of metakaolin was resulted by the combined processes that the formation of deleterious alkali-calcium-silicate gel was inhibited and the penetration of alkali solution into concrete was retarded due to the formation of denser, more homogeneous cement paste caused by pozzolanic effect. Higher early strength (7 days) than normal concrete was developed when the replacement ratios of metakaolin were greater than 15%. And also, late strength (28 days) was far higher than normal concrete for the all the replacement ratios of metakaolin. The development patterns of mechanical strength for metakaolin admixed concretes reflect the rapid pozzolanic reaction and hydration properties of metakaolin.

• Geophysics and Geophysical Exploration
• /
• v.10 no.1
• /
• pp.1-18
• /
• 2007

Non-linear elastic wavefield inversion is a powerful method for estimating elastic parameters for physical constraints that determine subsurface rock and properties. Here, I introduce six elastic-wave velocity models by reconstructing elastic-wave velocity variations from real data and a 2D elastic-wave velocity model. Reflection seismic data information is often decoupled into short and long wavelength components. The local search method has difficulty in estimating the longer wavelength velocity if the starting model is far from the true model, and source frequencies are then changed from lower to higher bands (as in the 'frequency-cascade scheme') to estimate model elastic parameters. Elastic parameters are inverted at each inversion step ('simultaneous mode') with a starting model of linear P- and S-wave velocity trends with depth. Elastic parameters are also derived by inversion in three other modes - using a P- and S-wave velocity basis $('V_P\;V_S\;mode')$; P-impedance and Poisson's ratio basis $('I_P\;Poisson\;mode')$; and P- and S-impedance $('I_P\;I_S\;mode')$. Density values are updated at each elastic inversion step under three assumptions in each mode. By evaluating the accuracy of the inversion for each parameter set for elastic models, it can be concluded that there is no specific difference between the inversion results for the $V_P\;V_S$ mode and the $I_P$ Poisson mode. The same conclusion is expected for the $I_P\;I_S$ mode, too. This gives us a sound basis for full wavelength elastic wavefield inversion.