• Journal of Welding and Joining
• /
• v.32 no.5
• /
• pp.7-12
• /
• 2014

In this study, API-X100 steel pipes were welded with various kinds of welding wires in the laser-arc hybrid welding process. 10kW fiber laser source was combined to MIG arc welding process. API X-100 steel of base metal was of 16.9mm thickness, and butt welding applied. After welding, full penetration weld was acquired by 1-pass welding. A root porosity and the lack of fusion was observed in some welding conditions. By the mixing the melted wire, acicular ferrite, polygonal ferrite, pro-eutectoid, aligned side plate, and bainite structures were observed at the weld metal. From the observation of hybrid weld, unmixed zone had more Ni and Cr. The unmixed zone was a 1/3 area of the weld metal. As the mechanical test of the hybrid welding, tensile test and impact test applied. From the tensile test, all of the welding except SM70S was fractured at the base metal. The result of the impact test at -30 degree C led 60J~320J of the absorbed energy. The result of the low-absorbed energy might be from the coarse equiaxed structures of the weld metal.

• Journal of the Korean Society for Precision Engineering
• /
• v.26 no.10
• /
• pp.108-115
• /
• 2009

Although nanosecond pulsed laser drilling and milling are rapid and non-wear processes in micromachining, the quality cannot meet the precision standard due to the recast layer and heat affected zone. On the other hand, electrical discharge machining (EDM) is a well-known high precision machining process in micro scale; however, the low material removal rate (MRR) and tool wear remain as drawbacks. In this paper, hybrid process of laser beam machining (LBM) using nanosecond pulsed laser and micro EDM was studied for micro drilling and milling. While the quality of the micro structure fabricated by this hybrid process remains as high as direct EDM, the machining time and tool wear can be reduced. In addition, variable depth of layer was introduced as an effective method improving efficiency of hybrid milling.

• ETRI Journal
• /
• v.32 no.2
• /
• pp.339-341
• /
• 2010

The fundamental transverse mode lasing of a hybrid laser diode is a prerequisite for efficient coupling to a single-mode silicon waveguide, which is necessary for a wavelength-division multiplexing silicon interconnection. We investigate the lasing mode profile for a hybrid laser diode consisting of silicon slab and InP/InGaAsP deep ridge waveguides. When the thickness of the top silicon is 220 nm, the fundamental transverse mode is lasing in spite of the wide waveguide width of $3.7{\mu}m$. The threshold current is 40 mA, and the maximum output power is 5 mW under CW current operation. In the case of a thick top silicon layer (1 ${\mu}m$), the higher modes are lasing. There is no significant difference in the thermal resistance of the two devices.

• Proceedings of the Korean Society of Precision Engineering Conference
• /
• 2005.10a
• /
• pp.706-709
• /
• 2005

A hybrid focus method with multiple laser slits has been newly proposed and it is based on the integration of DFD and DFF Rough depth information is estimated using DFD equipped with multiple laser slits, and then DFF is applied to only each specific depth range using the depth information resulting from DFD. The proposed hybrid method gives more accurate results than DFD and DFF, and faster measurement than DFF. Its performance has been verified through experiments of calibration blocks with sharp depth discontinuity.

• Laser Solutions
• /
• v.5 no.3
• /
• pp.15-20
• /
• 2002

The principal obstacle to selection of a laser processing method in production is its relatively high equipment cost and the natural unwillingness of production supervision to try something new until it is thoroughly proven. The major objective of this work is focused on the combined features of gas tungsten arc and a low-power cold laser beam. In this work, the laser beam from a 7 watts carbon monoxide laser was combined with electrical discharges from a short-pulsed capacitive discharge GTA welding power supply. When the low power CO laser beam passes through a special composition shielding gas, the CO molecules in the gas absorbs the radiation, and ionizes through a process blown as non-equilibrium, vibration-vibration pumping. The resulting laser-induced plasma(LIP) was positioned between various configurations of electrodes. The high-voltage impulse applied to the electrodes forced rapid electrical breakdown between the electrodes. Electrical discharges between tungsten electrodes and aluminum sheet specimens followed the ionized path provided by LIP. The result was well-focused melted spots.

• Journal of Welding and Joining
• /
• v.33 no.2
• /
• pp.91-96
• /
• 2015

The laser-arc hybrid welding of SS400 steel was carried out with the use of disk laser equipment of 6.6kW maximum power and MAG equipment of pulse mode. Parameter regarding heat input is one of the most important factors that directly affect penetration characteristics and welding defect. Therefore in this study, the effects of laser power, welding speed and current, voltage and pulse correction were investigated. As experiment result, it was found that the lower heat input, the more likely humping bead is formed at the back, and such humping bead could be suppressed by increasing laser power and arc current or decreasing welding speed, thus increasing heat input. Also deep penetration could be achieved by reducing arc voltage or pulse correction parameter in the same welding condition.

• Proceedings of the Korean Society of Propulsion Engineers Conference
• /
• 2004.03a
• /
• pp.271-277
• /
• 2004

As one of the concepts of the laser/electric hybrid propulsion system, a feasibility study on possibilities of electrostatic acceleration of a laser ablation plasma induced from a solid target was conducted. Energy distributions of accelerated ions were measured by a Faraday cup. A time-of-flight measurement was also conducted for ion velocity measurement. It was found that an average speed of ions from a pure laser ablation in this case was about 20 km/sec for pulse energy of 40 $\mu$J/pulse with pulse width of 250 psec. On the other hand, through an electrostatic field with a + I ,000 V electrode, the speed could be accelerated up to 40 km/sec. It was shown that the electrode with positive potential was more effective than that with negative potential for positive-ion acceleration in laser induced plasma, or pulsed plasma, in which ions were induced with the Coulomb explosion following electrons. In addition, the ion-acceleration or deceleration strongly depended on conditions of pairs of inner diameter and electrodes gap.

• Journal of the Microelectronics and Packaging Society
• /
• v.24 no.1
• /
• pp.91-101
• /
• 2017

In this study, we conducted the preliminary research for high speed laser cutting of LED module. In particular, the feasibility of ultra-high speed laser cutting of 100 mm/s which exceeds the cutting speed of conventional dicing saw was examined. For this, copper/ceramic and silicone/ceramic hybrid substrates, which are the components of the LED module, were fabricated, and the surface morphology, surface roughness and flexural strength of the laser-cut samples were investigate and compared with the dicing-cut samples. To investigate optimal laser cutting conditions for hybrid substrates, the effects of various laser cutting conditions on cutting surface characteristics were studied using single ceramic and copper substrate. Optimal laser cutting conditions of the hybrid substrates were the use of Ar assist gas, high laser power and high assist gas pressure. Comparing the cutting surface of the hybrid substrates, the surface characteristics of the laser-cut samples are slightly inferior to those of the dicing-cut samples. The average surface roughness of the laser-cut samples was about $9{\mu}m$, and that of the dicing-cut samples was about $4{\mu}m$. However, considering very low cutting speed (3 mm/s) of the dicing saw, the surface morphology of the laser-cut sample was relatively uniform, and the surface roughness was not much different from that of the dicing-cut sample. The flexural strength of the laser-cut samples was equivalent to or slightly inferior to the flexural strength of dicing-cut samples. However, if the laser processing conditions are sufficiently optimized, the ultra-high speed laser cutting of the LED module will be possible.

• Journal of Welding and Joining
• /
• v.26 no.5
• /
• pp.29-35
• /
• 2008

In this paper concentrate on the comparison of the thermal and mechanical characteristics in Butt joint of ship structure AH32 steel by using hybrid welding and conventional SAW. For this purpose, fundamental welding phenomena of hybrid process using $CO_2$ Laser and MIG is investigated by the experiments and characteristics of thermal and welding residual stress distribution of welded joint in SAW and hybrid welding are understood from the result of FE numerical simulation and experimental values. From the result of this study, it is understood that Laser-MIG hybrid welding have high potential, make substantial saving of time and manufacturing cost and may proves its self robust in the butt joining of thick AH32 steel ship structural plate in the near future.

• Proceedings of the KWS Conference
• /
• 2006.10a
• /
• pp.216-218
• /
• 2006

The application of aluminium alloy is increasing for lightweight and high quality transport vehicle. In this study, therefore, it is intended to apply the high speed hybrid welding method for marine grade aluminium alloy(A5083) used for shipbuilding that consists of 3 kW CW Nd:YAG laser and MIG welding process. For this purpose, the characteristics of process parameters(laser & arc combine angle and focal position of hybrid head to specimen) are investigated for hybrid fillet joint. This study also describes determination of heat distribution using finite element model of the T-joint fillet weld using the in-house solver which has been validated for different type of welding problems.