• Corrosion Science and Technology
• /
• 제11권1호
• /
• pp.15-19
• /
• 2012

Both electrogalvanized and hot-dip galvanized steel sheets have been finally produced via organic-inorganic surface coating process on the zinc surface to enhance corrosion resistance and afford additional functional properties. Recently, POSCO has been developed a variety of chromate-free coated steels that are widely used in household, construction and automotive applications. New organic-inorganic hybrid coating solutions as chromate alternatives are comprised of surface modified silicate with silane coupling agent and inorganic corrosion inhibitors as an aqueous formulation. In this paper we have prepared new type of hybrid coatings and evaluated quality performances such as corrosion resistance, spot weldability, thermal tolerance, and paint adhesion property etc. The electrogalvanized steels with these coating solutions exhibit good anti-corrosion property compared to those of chromate coated steels. Detailed components composition of coating solutions and experimental results suggest that strong binding between organic-inorganic hybrid coating layer and zinc surface plays a key role in the advanced quality performances.

• 한국분말재료학회지
• /
• 제18권3호
• /
• pp.226-237
• /
• 2011

W-ZrC and W-HfC composite powders were fabricated by the Plasma Alloying & Spheroidization (PAS) method and the powders were sprayed into hybrid coating layers by using Low Vacuum Plasma Spray (LVPS) process, respectively. Microstructure, mechanical properties, and ablation characteristics of the fabricated coating layers were investigated. The LVPS process led to successful production of W-Carbide hybrid coatings, approximately 400 ${\mu}M$ or above in thickness. As the substrate preheating temperature increased from $870^{\circ}C$ to $917^{\circ}C$, the hardness of the W-ZrC coating layer increased due to decreased porosity. Vickers hardness showed higher value (about 108.4 HV) in W-ZrC hybrid coating material compared to that of W-HfC while adhesive strength was found to be similar in both coating layers. The plasma torch test revealed good ablation resistance of the W-Carbide hybrid coating layers. The relatively high performance W-ZrC coating layer at the elevated temperature is thought to be attributed to both the strengthening effect of ZrC particle remained in the layer and the formation of ZrO2 phase with high temperature stability.

• Corrosion Science and Technology
• /
• 제14권2호
• /
• pp.64-75
• /
• 2015

Single $TiO_2$ coating prepared by sol-gel process usually experiences cracks in coating layer. In order to prevent cracks, an inorganic-organic hybrid $TiO_2-SiO_2$ coating was synthesized by combining precursors with an organic functional group. Five different coatings with various ratios of (1:8, 1:4, 1:1, 1:0.25 and 1:0.125) titanium alkoxide (TBOT, Tetrabutylorthotitanate) to organo-alkoxysilane (MAPTS, ${\gamma}$-Methacryloxy propyltrimethoxysilane) on carbon steel substrate were made by sol-gel dip coating. The prepared coatings were analyzed to study the coating properties (surface crack, thickness, composition) by scanning electron microscope (SEM), focused ion beam (FIB), and Fourier transform infrared spectroscopy (FT-IR). Potentiodynamic polarization tests and electrochemical impedance spectroscopy (EIS) were also performed to evaluate the corrosion characteristics of the coatings. Crack free $TiO_2-SiO_2$ hybrid coatings were prepared with the optimization of the ratio of TBOT to MAPTS. The corrosion rates were significantly decreased in the coatings for the optimized precursor ratio without cracks.

• 공업화학
• /
• 제5권5호
• /
• pp.857-861
• /
• 1994

독성이 있는 아크릴 모노머를 비닐에테르로 대체시켜 우레탄아크릴레이트와 배합시키는 것을 특징으로 하는 자외선 경화형 하이브리드 시스템을 조사하였다. 일반적으로 하이브리드 시스템의 코팅 물성은 자유 라디칼계보다은 우수하나 양이온계보다는 열세하게 나타났다. 아크릴계 올리고머 함량이 70% 이상으로 배합된 경우의 하이브리드계는 코팅물성과 경화물성면에서 자유라디칼계와 양이온계보다 뛰어나게 나타났다. 다양한 코팅 시스템의 경화과정을 조사하기 위해서 광열분석기를 적용하였다. 그 결과 코팅 배합물의 경화속도에 미치는 결정적인 인자는 배합물 특성에 따라 달라짐을 알 수 있었다. 동류의 하이브리드계의 경우에는 광경화개시제의 효율보다는 모노머/올리고머 비가 더욱 중요함을 알 수 있었다.

• 한국정보디스플레이학회:학술대회논문집
• /
• 한국정보디스플레이학회 2009년도 9th International Meeting on Information Display
• /
• pp.1453-1456
• /
• 2009

Transparent sol-gel hybrid dielectric material (hybrimer) coating films were fabricated by spin coating and photo or thermal curing of sol-gel derived oligosiloxane resins. Hybrimer coating films are suitable as the passivation layer of TFT in AMLCD due to low dielectric constant, small loss tangent, low leakage current density, high transmittance and thermal stability.

• 한국표면공학회지
• /
• 제36권2호
• /
• pp.116-121
• /
• 2003

Ti-Si-N coating layers were deposited onto WC-Co substrates by a hybrid system of arc ion plating (AIP) and sputtering techniques. The tribological behaviors of Ti-Si-N coating layers with various Si contents were investigated by the dry sliding wear experiments, which were conducted at three different sliding speeds, 0.1, 0.3, 0.5 m/s, against the steel and alumina balls. In the case of steel ball, the average friction coefficient slightly decreased with increasing the sliding speed regardless of Si content due to adhesive wear behavior between coating layer and steel ball. At constant sliding speed, the average friction coefficient decreased with increase of Si content. On the contrary, in the case of alumina ball, the average friction coefficient increased with increasing the sliding speed regardless of Si content, indicating that the abrasive wear behavior was more dominant when the coating layers slide against alumina ball. Through these experimental results, it was found that the tribological behaviors of Ti-Si-N coating layers were effected by factors such as Si content, sliding speed, and kinds of counterpart materials rather than the hardness of coating layer.

• 한국전기전자재료학회논문지
• /
• 제29권1호
• /
• pp.40-43
• /
• 2016

Transparent color coating films were fabricated on a glass substrate by using sol-gel hybrid binder and organic dye. Sol-gel hybrid binder coating film fabricated with PTMS of 0.03 mole showed a very high pencil hardness of 9 H. As the withdrawal speed increased from 1.0 mm/s to 5.0 mm/sec, The yellowness ($b^*$) of coating glass also gradually increased. The transmittance of yellow color coating glass was 82.6% and the haze of coating glass was 0.35%. Red and blue color coating glasses also showed the high transmittance of 62.4% and 80.6% respectively. The surface hardness of color coating films was 6 H.

• Journal of Industrial and Engineering Chemistry
• /
• 제68권
• /
• pp.209-219
• /
• 2018

Colloidally stable organic-inorganic (O-I) hybrid nanoparticles could be prepared using an alkoxysilanefunctionalized amphiphilic polymer (AFAP) precursor. O-I hybrid sols could maintain colloidal stability for six months even at 45% solid content and be coated onto glass as well as PET film to form transparent O-I hybrid films. The formation of O-I hybrid nanoparticles dispersed in cured coating films could be confirmed using scanning electron microscopy. The cured coating film showed 3H and 5H pencil hardness on PET and glass, respectively. Nanoindentation measurements also showed that their modulus and hardness was varied with the type of AFAP used in its preparation.

• Korean Chemical Engineering Research
• /
• 제52권3호
• /
• pp.388-394
• /
• 2014

출발물질인 TTIP로부터 이산화티탄 졸을 합성하여 무기물로 사용하고 유기물로서 실란커플링제인 methacryloxypropyl trimethoxysilane (MPTMS), aminopropyl triethoxysilane (APS), glycidoxypropyl trimethoxysilane (GPTMS), vinyltriethoxysilane (VTES)을 2종 혹은 3종씩 복합 사용하여 유-무기 하이브리드 코팅 용액을 제조하였다. 그 후 코팅 용액을 기재인 PC시트 위에 스핀 코팅시키고, 열경화 시켜 하드코팅 막을 제조하였다. 2종 실란커플링제를 혼합하여 제조된 코팅 막들은 기재와의 부착력과 연필경도가 우수하지 못했으나, 3종 실란커플링제를 혼합하여 제조한 코팅 막은 2H~4H의 향상된 연필경도와 5B의 우수한 부착력을 나타내었다. 이산화티탄 졸의 첨가량이 20 g인 코팅 막의 굴절률은 550 nm에서 1.56을 나타내었으나 이산화티탄 졸의 첨가량을 20 g에서 30 g으로 증가시킨 경우, 코팅 막의 굴절률이 1.63으로 향상되었다.

• 한국정보디스플레이학회:학술대회논문집
• /
• 한국정보디스플레이학회 2009년도 9th International Meeting on Information Display
• /
• pp.806-809
• /
• 2009

Epoxy functionalized organic-inorganic hybrid materials (hybrimers) were synthesized by sol-gel reaction for application in OLED barrier coating. By using the calcium degradation method, the oxygen transition rate (OTR) and water vapor transition rate (WVTR) measured so far is $10^{-2}cc/m^2$-day for oxygen and $10^{-1}g/m^2$-day for water molecules with single hybrimer coating film, respectively. Encapsulated OLED devices have life time of 14hrs of a single hybrimer barrier coating and 29hrs of hybrimer/inorganic double barrier coatings at $25^{\circ}C$ and 60% relative humidity.