• Proceedings of the Korean Society for Technology of Plasticity Conference
• /
• 1999.08a
• /
• pp.412-422
• /
• 1999

Scale defects generated on the strip surface in a tandem finishing mill line are collected from the strip trapped among the production mills by freezing the growing scale on the strip by the melt glass coating and shutting down the line simultaneously. The samples observed of its cross sectional figure showed the process of scale defect formation where the defects are formed at the base metal surface by thicker oxidized scale during each rolling passes. The properties of the oxidized layer growth both at rolling and inter-rolling are detected down sized rolling test simulating carefully the rolling condition of the production line. The thickness of the oxidized layer at each rolling pass are simulated numerically. The critical scale thickness to avoid the defect formation is determined through the expression of mutual relation between oxidized layer thickness and the lanks of the strip called quality for the scale defects. The scale growth of scale less than the critical thickness and also to keep the bulk temperature tuning the water flow rate and cooling time appropriately. Two units of Inerstand Cooler are designed and settled among the first three stands in the production line. Two units of scale defect is counted from the recoiled strip and the results showed distinct decrease of the defects comparing to the conventionaly rolled products.

• Proceedings of the Korean Powder Metallurgy Institute Conference
• /
• 1998.10b
• /
• pp.34-35
• /
• 1998

• Proceedings of the Korean Society for Technology of Plasticity Conference
• /
• 1999.08a
• /
• pp.57-65
• /
• 1999

This document illustrates the way to control of coiling temperature(CTC) of stip tail part in minimill process. The coiling temperature (CT) is very important fact in hot rolling process because the mechnical properties of strip depend on it. In mini-mill pocess, the speed pattern of rolling is different from that of conventional hot rolling. We have a lot of difficulties in controlling the coiling temperature at strip tail part, because after the strip tail is passed out the final stand, it's impossible to control the coiling temperature by using coiling speed. So we have CT deveiation in this gauge, about 160$^{\circ}C$ below in comparison with target CT. It's clear that deviation of mechanical properties(tensile strength, vield ratio etc) of strip to direction of length is so large, so we could not produce middle carbon steel, like this temperature condition. New coiling temperature control of strip especially in strip tail was developed. An innovative method for calculate the deceleration speed of strip tail has been implemented in CTC program, so called

• Transactions of Materials Processing
• /
• v.15 no.2 s.83
• /
• pp.118-125
• /
• 2006

API steel is used for line-pipe to transport the oil and natural gas. As the recent trends in the development of API steel are towards the use of larger diameter and thicker plate, many researches have been studied to achieve higher strength, higher toughness and lower yield ratio in API steel. However, the strength of API steel after pipe forming is changed depending on the competition of the Bauschinger effect and work hardening which are affected by the strain history during pipe forming process. So, the purpose of this study is to investigate the influence of microstructure on the Bauschinger effect for API steel. To change the microstructure of API steel we have changed the hot rolling condition and the amounts of V and Cu addition. The compression-tensile test and the microstructure observation by OM and TEM were conducted to investigate the yield strength drop and the correlation between the Bauschinger effect and microstructure of API steel. The experimental results show that the increase of polygonal ferrites volume fraction increases the Baushcinger effect due to the back stress which comes from the increase of mobile dislocation density at polygonal ferrite interior during the compressive deformation. The hot rolling condition was more effective on the Bauschinger effect in API steel than the small amount of V and Cu addition.

• Journal of the Korean Society for Heat Treatment
• /
• v.22 no.1
• /
• pp.16-22
• /
• 2009

The rolling process is an efficient and economical approach for the manufacturing of plate metals. In the rolling process, the temperature variation is very critical for plate thickness accuracy. The main cause of thickness variation in hot plate mills is the non-uniform temperature distribution along the length of the slab. Also the exit plate thickness is mainly affected by the rolling conditions such as mill modulus, plate thickness and plate width. Hence the thickness variation in top-end is also dependent on these factors. Therefore this study has concentrated on determining the correct amounts of thickness variation due to top-end temperature drop and process parameters.

• Proceedings of the Korean Society of Precision Engineering Conference
• /
• 1992.04a
• /
• pp.306-312
• /
• 1992

The prevention of roll breakage in hot rolling process is improtant to reduce maintenance cost and production loss. Rolling conditions such as the roll force and torque have been intensively studied to overcome the roll breakage. in the present work, a model for life prediction of work rolls under working condition was developed and discussed. The model consists of stress analysis, crack propagation, wear and fatigue calculation model. Roll life can be predicted by stress, crack depth and fatigue damage calculated from this model. The reliability of stress analysis is backed up by the FEM analysis. From the result of simulation using by pressent model, although the fatigue damage of back up roll reachs 80% of practical limit, that of workroll was less than 40%. In edge section of workroll stress amplification is found by wear and bender effect. We can judge that workroll failures are not due to fatigue damage, crack propagation by bending stress but stress amplification by wear and bender in present working condition.

• Journal of Advanced Marine Engineering and Technology
• /
• v.35 no.2
• /
• pp.244-251
• /
• 2011

Pipe rolling process using the planetary rolling mill for AISI 304 stainless steel has been studied by using finite element method. Mannesmann method using three-roll is applied to this rolling process. Commonly, rolling process has started from the cold working and finished to the hot working. This rolling process has more advantage that make reduction of process and cost than existing extrusion process. This process includes various and complex process parameters. Each of the process parameters affects forming result. Therefore, all of the process parameters should be considered in FEA. In this study, possibility and productivity of forming pipe for AISI 304 stainless steel had been investigated. Also, preheating process and variations of rotation velocity and product thickness were considered in FEA. Rolling process for AISI 304 stainless steel pipe was successfully simulated and it should be useful to determine optimal rolling condition.

• Transactions of Materials Processing
• /
• v.18 no.1
• /
• pp.45-51
• /
• 2009

Shape memory alloy has been used to improve the tensile strength of composite by the occurrence of compressive residual stress in matrix using its shape memory effect. In order to fabricate shape memory alloy composite, TiNi alloy fiber and Al2024 sheets were used as reinforcing material and matrix, respectively. In this study, TiNi/Al2024 shape memory alloy composite was made by using hot press method. In order to investigate bonding condition between TiNi reinforcement and Al matrix, the micro-structure of interface was observed by using optical microscope and diffusion layer of interface was measured by using Electron Probe Micro Analyser. And the mechanical properties of composite with three parameters(volume fraction of fiber, cold rolling amount and test temperature) were obtained by tensile test. The most optimum bonding condition for fabrication the TiNi/Al2024 composite material was obtained as holding for 30min. under the pressure of 60MPa at 793K. The strength of composite material increased considerably with the volume fraction of fiber up to 7.0%. And the tensile strength of this composite increased with the reduction ratio and it also depends on the volume fraction of fiber.

• Journal of the Korean Society for Nondestructive Testing
• /
• v.23 no.1
• /
• pp.7-13
• /
• 2003

A hot press method was use for the optimal manufacturing condition for a shape memory alloy(SMA) composite. The bonding between the matrix and the reinforcement within the SMA composite by the hot press method was strengthened by cold rolling. In this study, the objective was to develop an on-line monitoring system for the prevention of the crack initiation and propagation by shape memory effort of SMA composite. Shape memory effect was used to prevent the SMA composite from cracking. For the system to be developed, an optimal hE parameter should be determined based on the degree of damage and crack initiation. When the SHA composite was heated by the plate heater attached at the composite, the propagating cracks appeared to be controlled by the compressive force of SMA.

• Resources Recycling
• /
• v.9 no.2
• /
• pp.46-52
• /
• 2000

Aluminum can to can recycling was divided into two stpes. The first step was composed of the processes such as collection of used beverage cans (UBC), shredding, magnetic separation, De-laquiring, melting and casting. The second one was remelting and casting, heat treating, hot and cold rolling, annealing, and can making. In this study, the effect of alloying elements on the microstructure and texture of the secondary ingots made by Al UBC was investigated. In aluminum can to can recycling, the second phase particles appeared in the solidification stage must be controlled by heat treatment. The optimum heat treatment condition was $615^{\circ}C$ for 5hrs. the texture in hot rolled sheet was depressed with increasing Mn content, on the other hand, Si and Fe elements promoted the texture development. The textures of can-body sheet should be controlled in the hot rolling and annealing stage because can was formed from cold rolled sheet without heat treatment.