• 열처리공학회지
• /
• 제27권1호
• /
• pp.1-9
• /
• 2014

For connector material applications, the influence alloying elements of Mn, Cr, Fe, and Ti and cold rolling reduction on the mechanical property, electrical conductivity and bendiability of Cu-Ni-Si-P alloy was investigated. The hot rolled plates were solution treated at $980^{\circ}C$ for 1.5 h, quenched into water, cold rolled by 10% and 30% reduction in thickness, and then aged at $440{\sim}500^{\circ}C$ for 3, 4, 5 times. respectively. Cu-Ni-Si-P-x alloys cold rolled by 10 reduction before heat treatment have a good bendability compare to cold rolled by 30 reduction. Cu-3.4Ni-0.8Si-0.03P-0.1Ti shows the peak strength value of 759 MPa, an electrical conductivity of 39%IACS, an elongation of 10% and a hardness of 256 Hv aged at $440^{\circ}C$ for 6 hrs. Thus it is suitable for lead frame and connector.

• 한국분말재료학회지
• /
• 제10권1호
• /
• pp.15-20
• /
• 2003

Hybrid $A1_2O_3-TiC$ ceramic particle reinforced 6061 and 5083 Al composite powders were prepared by the combination of twin rolling and stone mill crushing process, followed by consolidating processes of cold compaction, degassing and hot extrusion. The composite bar consists of lamellar structure of ceramic particle rich area and matrix area, in which the hybrid was decomposed into each TiC of about $3-4\mutextrm{m}$ and $AI_2O_3$ particles of about $1-2\mutextrm{m}$ in diameter. It also found that fine $Mg_2Si$ precipitates of about 30 nm were embedded in the matrix, which have grains of about 3 $\mutextrm{m}$. Higher UTS was measured at the 5083 composite bar compared to the conventionally fabricated composite, due to again refinement effect by the rapid solidification. No particle was shown to form in the interface between the matrix and reinforcement, whereas carbon was diffused into the matrix.

• 한국주조공학회지
• /
• 제34권1호
• /
• pp.1-5
• /
• 2014

The austempering transformation behavior in Fe-0.7wt.%C-2.3wt.%Si-0.3wt.%Mn steel is investigated. Each specimen was austenitized for 60 min at $900^{\circ}C$, and austempered at $380^{\circ}C$ for different time periods varying from 2 min to 256 min. After the austempering heat treatment, the Stage I and II evolutions are performed using optical metallography, X-ray diffraction and image analyses. Variations in the X-ray diffraction patterns and lattice parameters of the ferrite and austenite demonstrate that the residual austenite decomposes into ferrite and carbide during the Stage II evolution; moreover the amount of ferrite increases during the Stage I evolution. While the amount of austenite increases during Stage I, it dicreases during Stage II. Overall, the variations in the volume fractions of the microstructure and carbide formation in stages I and II meet high temperature austempering reaction of the ausferrite microstructure.

• 한국초전도학회:학술대회논문집
• /
• 한국초전도학회 1999년도 High Temperature Superconductivity Vol.IX
• /
• pp.352-357
• /
• 1999

The Cu sheets were selected for the substrate of the superconductor films. Pure Cu sheets with the thickness of 50${\mu}$m were fabricated using hot and cold rolling. The Cu sheets were heat treated to induce the biaxial texturing. The z-axis and x-y plane texturing of Cu sheets heat treated at different conditions were analyzed using XRD and a best heat treatment condition for the texturing was selected. ZrO$_2$ film was dip coated on Cu sheets heat treated at the best condition to prevent possible reaction between Cu sheets and YBCO superconductors, to reduce possible cracking due to thermal expansion mismatch and to decrease the lattice mismatch for biaxial texturing. The texturing of the oxide buffer layers were also studied.

• 한국소성가공학회:학술대회논문집
• /
• 한국소성가공학회 2004년도 춘계학술대회 논문집
• /
• pp.395-399
• /
• 2004

Four microalloyed steels containing B were investigated in terms of hardenability, mechanical properties and microstructure depending upon the cooling rates in order to develop the steel grade for the cold forged fasners. The alloy with the largest DI value among 4 alloys, which contains $0.12\%\;C,\;1.54\%\;Mn,\;0.65\%\;Cr,\;0.11\%V,\;0.040\%Ti\;and\;0.0033\%B$, showed the larest shift to the right hand side in the TTT diagram, implying the wide allowable cooling rate range subsequent to hot rolling in long bar processing, Mechanical tests indicated that yield strength are dependent upon the DI value in water quenched specimens but other properties showed almost the same values. In the same grade of steel, the increase in cooling rates causes the decrease in elongation but the increase in strength, reduction of area and Charpy impact values. Microstructural examination in steel grade with the larest DI values revealed martensitic structure In the water quenched state, a mixture of martensite and bainite in the oil quenched, and ferrite + pearlite in the air cooled and the forced air cooled but the latter showed finer microstructure.

• 제어로봇시스템학회:학술대회논문집
• /
• 제어로봇시스템학회 2005년도 ICCAS
• /
• pp.1431-1434
• /
• 2005

In the steel production line, the molten metal of a furnace is transformed into billet and then moves to the heating furnace of the hot rolling mill. This paper describes about the development of recognition system for the characters, which was marked at the billet material by use template-marking plate and hand written method, in the steel plant. For the recognition of template-marked characters, we propose PSVM algorithm. And for the recognition of hand written character, we propose combination methods of CCD algorithm and PSVM algorithm. The PSVM algorithm need some more time than the conventional KLT or SVM algorithm. The CCD algorithm makes shorter classification time than the PSVM algorithm and good for the classification of closed curve characters from Arabic numerals. For the confirmation of algorithm, we have compared our algorithm with conventional methods such as KLT classifier and one-to-one SVM. The recognition rate of experimented billet characters shows that the proposing PSVM algorithm is 97 % for the template-marked characters and combinational algorithm of CCD & PSVM is 95.5 % for the hand written characters. The experimental results show that our proposing method has higher recognition rate than that of the conventional methods for the template-marked characters and hand written characters. By using our algorithm, we have installed real time character recognition system at the billet processing line of the steel-iron plant.

• 한국주조공학회지
• /
• 제33권1호
• /
• pp.1-7
• /
• 2013

The effect of the Mo addition on the high temperature creep properties of the 9Cr-3W steel was also evaluated. Two experimental steels, (9Cr-3W and 9Cr-3W-0.5Mo), were prepared using a vacuum induction melting process, followed by hot rolling and heat treatment processes. Three types of precipitates, ($M_{23}C_6$, Nb-rich MX and V-rich MX) were observed in a typical tempered martensitic matrix. Significant effects of the Mo addition on the tensile properties were not observed. However, the creep properties at $650^{\circ}C$ under applied stresses of 140 and 150 MPa were considerably enhanced by the Mo addition. The microstructural observation after the creep test indicated that the addition of Mo could function to retain the recovery of the martensitic matrix, thus resulting in the enhanced creep properties of the 9Cr-3W-0.5Mo steel. Furthermore coarsening of the $M_{23}C_6$ carbides and formation of Laves phases were observed in both samples after the creep tests.

• 한국소성가공학회:학술대회논문집
• /
• 한국소성가공학회 2004년도 제5회 압연심포지엄 신 시장 개척을 위한 압연기술
• /
• pp.216-222
• /
• 2004

The caster roll shells have the good thermal conductivity and the low thermal expansion and have to exhibit high enough strength and good ductility at temperature up to $600^{\circ}C$. Thermal stress in particular is very high due to the contact with the liquid aluminium. The main stresses are of thermal origin, which bring a plastic fatigue on surface. This paper will represent one survey about the investigation of the failure of roll shells for continuous casters and an analysis using the simulation of the temperature distribution and the state of stress during hot rolling. Moreover, there will be a discussion on the roll shell of Mod. HAR 5 which is developed by heat treatment process. Mod. HAR 5 has advantages of high strength, high toughness and increased thermal stress resistance while maintaining the same productivity as the conventional roll.

• 한국소성가공학회:학술대회논문집
• /
• 한국소성가공학회 1999년도 제3회 압연심포지엄 논문집 압연기술의 미래개척 (Exploitation of Future Rolling Technologies)
• /
• pp.119-125
• /
• 1999

At Wire Rod Mill Plant, wire is made of the billet produced at continuous casting machine, or rolled bloom produced at billeting mill, and the product can be classified of wire of 5.5${\Phi}$ and bar in coil of 14∼42${\Phi}$ in diameter(bar in coil will be referred to as coil as below). At present, wire is produced at POSCO No.1, 2, 3 WRM, coil at garret line of No. 2 WRM. Head and tail of coil are properly cut and treated to scrap to fulfill the customer's satisfaction. This above cutting is done off line, and small size coil can be cut manually with clipper, large size coil with hydraulic cutter. Nowadays, it is being investigated to cut automatically in line with trimming shear after passing mill stand. At the moment, Because the coil produced at the garret line of No.2 WRM is hot 400∼600$^{\circ}C$ and trimming is done manually with cutter, there are always interference from manual operation or safety problem of bad working condition. Not only because of the diversity of the coil size 14∼42${\Phi}$ in diameter, but because of the rolling speed 2.5∼22m/sec, it is required to be equipped with several trimming shear. But this can be accomplished with only one shear installed proper place at this paper.

• 한국전산유체공학회:학술대회논문집
• /
• 한국전산유체공학회 2008년도 춘계학술대회논문집
• /
• pp.705-706
• /
• 2008

When heat generated inside a large factory building is not discharged due to a stagnant flow, the working environment of workers becomes worse and the cooling of high-temperature products such as hot-rolling coils is delayed. To investigate the natural ventilation inside a large factory building, experimental studies were carried out using wind-tunnel tests. The scale-down factory building models were placed in an atmospheric boundary layer (ABL) and the mean and fluctuating velocity fields were measured using a particle image velocimetry (PIV) technique. For the prototype factory model, the outdoor air is only entrained into the factory building through the one-third open windward wall, and stagnant flow is formed in the rear part of the target area. In order to improve the indoor ventilation environment of the factory building, three different louver-type ventilators were attached at the upper one-third open windward wall of the factory model. Among the three louver ventilators tested in this study, the ventilator model #3 with the outer louver (${\theta}_o$ = 90$^{\circ}$) and the inner louver (${\theta}_i$ = -70$^{\circ}$) was found to improve the natural ventilation inside the factory building model effectively. The flow rate of the entrained air was increased with aligning the outer louver blades with the oncoming wind and guiding the entrained air down to the ground surface with elongated inner louver blades.