• 한국수산과학회지
• /
• 제50권4호
• /
• pp.388-395
• /
• 2017

We investigated the toxicity of zinc and aluminum hot-dip galvanized sheet steel to abalone Haliotis discus hannai via changes in the gill and hepatopancreas using histological and transmission electron microscopy analysis. Experimental groups were composed of one control and four exposure conditions (direct or indirect exposure to zinc and aluminum hot-dip galvanized sheet steel). In the control group, aluminum exposure groups (direct and indirect), and indirect zinc exposure group, abalone mortality was not observed until the end of the experiment, and no histopathological changes were observed in the gill and hepatopancreas. However, the direct zinc exposure group exhibited 100% mortality. Ultrastructural analysis of the cytoplasm of ciliated and microvilli-bearing epithelial cells from gill filaments revealed electron-dense vesicles near the cell membrane and disruption of the nuclear membrane. We also observed swollen mitochondria and a loss of mitochondrial cristae. The hepatopancreas showed similar changes, and we detected highly electron-dense particles within the vesicles. These results suggest that abalone exposed directly to zinc hot-dip galvanized sheet steel experience acute toxicity, causing damage to cell organelles in the gill and hepatopancreas and, finally, inducing mortality.

• Corrosion Science and Technology
• /
• 제23권2호
• /
• pp.121-130
• /
• 2024

In recent years, Zn-Al-Mg alloy galvanized steel sheets have been widely used as coated steel sheets to support social capital in the infrastructure field. A feature of Zn-Al-Mg alloy-coated steel sheets is that they provide a better corrosion protection period than Zn-coated steel sheets. In this study, the corrosion resistance of a new Zn-Al-Mg alloy-coated steel sheet was investigated and compared to that of conventional commercially available coated steel sheets. The investigation confirmed that increasing the Mg concentration in the Zn-Al-Mg-coated steel sheet improved corrosion resistance, which was more than 10 times that of the galvanized steel sheet specified in JIS G 3302. The study findings also confirmed that the corrosion resistance reached more than twice that of the coated steel sheet specified in JIS G 3323. If such galvanized steel sheets are applied to social infrastructures that are exposed to severely corrosive environments, the service life of the infrastructure might be extended.

• 한국표면공학회:학술대회논문집
• /
• 한국표면공학회 1998년도 춘계학술발표회 초록집
• /
• pp.80-81
• /
• 1998

• 한국표면공학회:학술대회논문집
• /
• 한국표면공학회 2001년도 추계학술발표회 초록집
• /
• pp.13-13
• /
• 2001

• 한국표면공학회:학술대회논문집
• /
• 한국표면공학회 2000년도 추계학술발표회 초록집
• /
• pp.30-31
• /
• 2000

• 한국표면공학회:학술대회논문집
• /
• 한국표면공학회 2003년도 추계학술발표회초록집
• /
• pp.38-39
• /
• 2003

• 한국표면공학회지
• /
• 제24권1호
• /
• pp.18-24
• /
• 1991

In the present work the adhesion failure of a hot-dip galvanized coating has been studied as a function gas composition temperature of strip and of atmospheric gas in furnace. The adhesion failure of the hot-dip galvani-zed coating is classified as three mechanisms : carbon deposition, oxide film formation and alloy layer formation. The adhesion failure due to oxide film formation decreased markedly by increasing the gases temperature of direct fired furnace(DFF) in order to improve the reducing ability of steel strip. Optimum conditions of operating and manufacturing facilities for improving the coating adherence are suggested by analyzing the interface between steel substrate and coating layer.

• 한국표면공학회지
• /
• 제27권3호
• /
• pp.149-157
• /
• 1994

The formation of spangles on a hot dip galvanized sheet steel by spray cooling the molten zinc coating with air, water and 2.0wt% $NH_4H_2PO_4$ solution has been studied performing laboratory experiments, and their coating properties have been evaluated. Minimized spangles were easily formed by mist spraying the solution for 1 second at the low nozzle spray pressure onto the molten zinc at 420~$422^{\circ}C$ because the solute $NH_4H_2PO_4$ in the sprayed solution imparted a highly rapid cooling effect to the coating through its endothermic de-composition reactions and because the decomposed products acted as numerous nucleation sites for the mini-mized spangles on the coating. Good surface appearances sand sound coating properties were obtained on this coating. Only regular spangles were formed on the coating by the forced convective air cooling. At the high nozzle spray pressure, zero spangles were formed on the coating by the pure water spray cooling. However, the coating had a dull and rough surface with craters sand cracks.

• 한국표면공학회지
• /
• 제36권6호
• /
• pp.466-474
• /
• 2003

To develop a method of detecting dross in coating layer on hot-dip galvanizing steel, chemical etching behavior of the artificial coating layers with top and bottom dross were investigated. After chemical etching with the mixture of picric acid and sodium thiosulfate, each of the top and bottom dross take its distinct color, and alloy layer in coating is also observed. Defects in the coating layers of HGI(hot rolled galvanized iron), CGI(continuous galvanized steel sheet) and GA(galvannealed steel) were analysed, and methods of dross detection which can be applied to inspection process in manufacture were suggested.

• 한국표면공학회지
• /
• 제27권6호
• /
• pp.347-358
• /
• 1994

Estimation of durability for corrugated steel pipe(CSP) has been evaluated by using several analytical methods. This study, using a plain hot-dip galvanized CSP as the base line, addresses additional coatings such as polymers sand bituminous coatings that may be used to achieve a desired design life of at least 50years. The behavior of both the soil side and the effluent side of the pipe have been studied. It is estimated that CSP generally provides outstanding dura-bility with regard to soil side effects, and that virtually any required service life can be attained by selecting appropri-ate coatingss and/or thickness of steel substrate. This study is limited to storm drainage systemss carrying naturally oc-curring surface water only. The recommendation in this report do not apply to sanitary or industrial waste sewers or other conduits used to carry corrosive effluents.