• Journal of the Korea Institute of Building Construction
• /
• v.9 no.6
• /
• pp.113-119
• /
• 2009

This study is to investigate the fundamental and fireproof qualities of high strength concrete corresponding to changes in the curing factors and the PP fiber ratio. The results were as follows. For the fundamental characteristics of concrete, the fluidity was reduced in proportion to the increase in the PP fiber ratio. The compressive strength was somewhat reduced according to an increase in the PP fiber ratio. However, it had the high strength scope of more than 60 MPa at 7 days and of more than 90 MPa at 28 days. On the spalling mechanism followed by changes of the water content ratio, spalling was prevented in all combinations, except the specimen without PP fiber and subjected to 3.0% of moisture contents. When spalling was prevented at that time, the residual compressive strength ratio was 22%~41% and the mass reduction ratio was 5%~7%, which was relatively favorable. As the spalling mechanism corresponds to changes in the curing method, spalling was prevented in concrete with a PP fiber mixing ratio of more than 0.05% in the event of standard curing, and in concrete with a PP fiber mixing ratio of more than 0.10% in the case of steam curing and autoclave curing. In these cases, when spalling was prevented, the residual compressive strength ratio was 23~42% and the mass reduction ratio was 7~11%. In these results, the ease of spalling prevention in high strength concrete was inversely proportional to the water content ratio. Depending on the curing method, spalling was prevented in concrete with over 0.05% PP fiber with standard curing and in concrete with over 0.1% PP fiber with steam curing and autoclave curing.

• Journal of the Korea Concrete Institute
• /
• v.12 no.3
• /
• pp.39-46
• /
• 2000

This study is to investigate the watertightness properties of waterproofing admixture mixed redispersible polymer and siliceous powder. Series I deals with change in micro-structure of mortar by waterproofing admixture according to the water/cement ratios of 0.5, 0.6, 0.7 and 0.8 Crystal growth in micro-structure was observed through SEM to estimate on the watertightness effect of it. SeriesII deals with watertightness properties of waterproofing admixture on water permeability coefficient, crack restoration capacity and carbonation depth. SeriesII deals with watertightness properties of waterproofing admixture on water permeability coefficient, crack restoration capacity and carbonation depth. The result of this study can be summarized as follows. 1) Fluidity of mortar and concrete was increased by adding waterproofing admixture. 2) From observation through SEM. Crystals grew larger and denser in micro-structure as fiberic crystalization. 3) Waterproofing admixture is good watertightness properties in a level of high water/cement ratios and long limit of time. 4) Crack restoration capacity was appeared and durability was progressed by waterproofing admixture.

• Proceedings of the Korean Institute of Building Construction Conference
• /
• 2008.11a
• /
• pp.1-5
• /
• 2008

In this study, batcher plant composition test and mock-up test were carried out to conduct comparison and analysis on flow behavior and strength properties of concrete at early age. As a result, it was found that slump and amount of air in batcher plant composition test reached the target range. As for compressive strength, composition using HESPC showed the most excellent strength development. In mock-up test which was carried out to find out the strength properties, two methods with specimen and core test body both revealed HESPC as the most excellent composition. However, strength estimation with ultrasonic survey presented less reliable data. As a result of the previously conducted indoor composition test and the mock-up test in this study, target performance of concrete at early age was 4day/cycle. It was found that the optimum conditions that meet the required strength, 5MPa/18hr and 14MPa/36hr in mullion and transom are; curing temperature above 15℃, W/B 45%, unit-water 165kg/㎥ and CHC cement.

• Journal of the Korean Recycled Construction Resources Institute
• /
• v.4 no.3
• /
• pp.284-291
• /
• 2016

To evaluate the properties of inorganic composites using a great quantity of high-calcium fly ash generated in combined heat and power plants, high-calcium fly ash and F-class fly ash commonly used as concrete admixtures were substituted with binding materials to examine changes of fluidity and compressive strength depending on the substitution ratio for each curing temperature. According to the experimental result, CFA-mixed mortar showed a tendency to reduce its flow unlike FFA-mixed mortar as the substitution ratio was increased, but its flow loss showed smaller than FFA as time passed. As a result of examining compressive strength depending on mixing FA, FFA-mixed mortar had an optimum range within 50% when curing at ambient temperature, but it was found that the compressive strength is reduced when mixing CFA. When curing at high temperature, FFA did not relatively have a great effect on the substitution ratio, but CFA could expect a strength enhancement effect compared with 100% of OPC when using within 25% of binding materials.

• Journal of the Korea Concrete Institute
• /
• v.15 no.2
• /
• pp.217-224
• /
• 2003

It is necessary to reduce bleeding, which is a kind of segregation of fresh concrete, for improvement of quality of concrete structure. But, besides using high qualify material and adjusting mixture ratio, there is no easy solution to reduce bleeding by now. For that reason, this study is intended to develop bleeding reduction agent and to investigate its application. The test results are following. At first, recommended mixture ratio of bleeding reduction agent is proven to be MC viscosity agent : defoaming agent : superplasticyzer of 1 : 0.004 : 0.2. It goes to prove that bleeding reduction agent does not have bad effect on the quality of concrete such as fluidity, air content and the strength of hardened concrete etc, and can reduce bleeding effectively. Therefore it is thought that bleeding reduction agent can be applied to construction field effectively.

• Resources Recycling
• /
• v.29 no.1
• /
• pp.53-61
• /
• 2020

This study aimed to develop a foam concrete material for a ground repair system that has low strength and low fluidity by using an eco-friendly binder, which substitutes industrial by-products for more than 90% of cement. Basic properties were evaluated after substituting a small amount of calcium sulfo aluminate (CSA) for the binder to improve the sinking depth rate and volume change, commonly found when it had a large amount of industrial by-products. The substitution rates of CSA for the eco-friendly binder used for the foam concrete were 2.5, 5, and 10%. Fresh properties, hardened properties, pore structure, and hydrates were analyzed. Experimental results showed that using only 2.5% of CSA could improve the deep sinking depth which occurred when using an eco-friendly binder. As a result, the weight difference between the upper, middle, and lower parts of cast specimens was improved even after being hardened. The addition of CSA also contributed to the formation of small, uniformly sized closed pores and improved initial strength. However, when the proportion of CSA increased, the long-term strength decreased. However, it satisfied the target strength when 5% or less of CSA was used. The results of this study revealed that it was possible to manufacture foam concrete with low strength and high fluidity for repairing ground satisfying target qualities by adding 2.5% of CSA to the eco-friendly binder containing a large amount of industrial by-products.

• Magazine of the Korea Concrete Institute
• /
• v.7 no.3
• /
• pp.156-163
• /
• 1995

In the previous study, styrene mdleic dnhydride copolymer(SMA) as synthesized flom styrene and rnale~c dnhydr~de and further redcted with sulfuric acid to obtam water soluble SMA. In thls study, the flow dnd strcngth tests of cement mortar rmxed wth copolymers wele carried out to evaluate the capability of copolymers as high range water reducer for the con crete. It was found from flow exper~ment that the fluidity of cenient mortar rmxed wth sulfonated SMA(SSMAj was larger thdn that mxed ulth amnophenol substituted SSMA (SmSMAj. The decreasing rate of the flow of cement mortar rmxed ulth SSMA and SmSMA was significantly lower than that mixed ulth naphthalene condensate(NSC) The compressslve strength of the hardened cement mortars containing 0.5% copolymers after 28 dys curing was exarmned. 'The compressive strength of hdrdened cement mortar containing SSMA and SmSMA was mcreased up to 31% and 13%, respectively, when omp pared to the plain. As the results, the copolyniers(SSMA and SrnSMA) used in thls study are greatly expected as a good high range water reducers for the concrete.

• Journal of the Korea Concrete Institute
• /
• v.14 no.1
• /
• pp.92-99
• /
• 2002

This paper is Intended to investigate physical properties and surface glossing of exposed concrete incorporating granulated blast furnace slag(BS). According to test results there is no remarkable variations in fluidity and air content with increase of BS, but unit weight shows decline tendency Compressive strength at later age gains considerably due to potential hydraulicity reaction of BS. It shows that drying shrinkage increases. It is found that low W/B, surface coating and high BS content lead to favorable effects on the surface glossing of exposed concrete because of filling effects on the voids of the concrete. It is improved by about 7 ％ with increase every 10 ％ of BS content. The effects of form pannel kinds on the improvement of surface glossing are in order for acryl, fancy, steel and wood.

• Journal of the Korea Concrete Institute
• /
• v.15 no.6
• /
• pp.785-793
• /
• 2003

This study is intended to analyze the effectiveness of expansive additive, shrinkage reducing agent and combination of the two to reduce the autogenous and drying shrinkage of high performance concrete using mineral admixture such as fly ash, blast furnace slag powder and silica fume. According to results, when expansive additive and shrinkage reducing agent are mixed within an appropriate mixing ratio, fluidity and air content are not influenced, and the enhancement of compressive strength is favorable at the age of 91 and 180days. At the mixing ratio of expansive additive of 5% and 10%, the autogenous and drying shrinkage is reduced by 32∼68% and 25∼49% respectively in comparison with plain concrete. And they are reduced by 18∼34% and 16∼26% respectively at the mixing ratio of shrinkage reducing agent of 0.5% and 1.0%, compared with plain concrete. The mixture of EA-SR combined with expansive additive and shrinkage reducing agent is most effective for reduction of shrinkage. Therefore, it is considered that the using method in combination with expansive additive and shrinkage reducing agent is effective to reduce the shrinkage of high performance concrete using mineral admixture such as fly ash, blast slag powder and silica fume.

• Proceedings of the Korean Institute Of Construction Engineering and Management
• /
• autumn
• /
• pp.222-227
• /
• 2001

Full scale construction tests of CFT(concrete filled steel tube) column to solve construction problem and to confirm quality were performed in apartment site. To improve construction efficiency, the tests has been accomplished two stages after the tests for material mixing design had been completed. In the first stage, the experimental variables were the placing methods, existence of guiding pipe, placing velocity and drop height and the height of specimen were $3.6{\cal}m$. In the second stage, Filling steel tube of 9.6m height with concrete was performed by two ways, that is, the pump-up method and the dropping method. The filled condition of the concrete and concrete strength distribution according to the column height were checked and the quality of the CFT column was confirmed.