• 한국건축시공학회지
• /
• 제8권3호
• /
• pp.75-83
• /
• 2008

In this paper, concrete material tests were carried out to investigate influence of steel fiber volumn ratios on variations of workability and strength characteristics of steel fiber reinforced high-strength concrete, $50MPa{\sim}90MPa$ of compressive strength, according to increase of fiber volume. Test specimens were arranged with six levels of concrete compressive strength and fiber volumn ratios, 0.0%, 0.5%, 1.0%, 1.5%, 2.0%. The test results showed that steel fiber reinforced high-strength concrete($70MPa{\sim}90MPa$, 1.5% fiber volumn ratio) with good workability of slump 20cm could be used practically and effects of steel fiber reinforcement in improvement of concrete strength and toughness characteristics such as splitting tensile strength, flexural strength, and diagonal tensioned shear strength, were more distinguished in high-strength concrete than general strength concrete. And the test results indicated that splitting tensile strength of fiber reinforced concrete was proportioned to the product of steel fiber volumn ratios, $V_f(%)$ and sqare root of compressive strength, $\sqrt{f_{ck}}$, and the increasing rate was in contrast with that of flexural strength, and increase of diagonal tensioned shear strength was remarkable at steel fiber volumn ratio, 0.5%.

• 콘크리트학회논문집
• /
• 제19권5호
• /
• pp.631-637
• /
• 2007

연구의 촛점은 강섬유 보강 고강도콘크리트와 고장력 철근 사이의 부착 특성을 평가하였다. 강섬유 혼입률에 따른 2가지 종류의 고강도콘크리트에서 고장력 철근의 부착 성능을 평가하기 위하여 직접 부착 실험을 실시하였다. 또한 콘크리트의 압축강도의 영향을 최소로 고려하여 강섬유 혼입률에 따른 부착강도의 영향을 결정하기 위하여 상대 부착강도를 정의하였다. 부착 성능 실험 결과 강섬유의 혼입률이 증가할수록 증가하였으며 강도가 높은 콘크리트 배합에서 더 우수한 결과를 나타내었다. 콘크리트의 강도에 대한 영향을 최소로하여 강섬유 혼입률에 따른 영향을 분석하기 위한 상대부착강도 평가 결과 섬유의 사용량이 증가할수록 상대부착강도가 증가하여 섬유의 혼입률은 고강도콘크리트의 강도에 관계없이 부착강도가 증가하였다.

• 콘크리트학회논문집
• /
• 제11권6호
• /
• pp.35-46
• /
• 1999

The steel fiber reinforced concrete may affect substantially to the tension stiffening at post cracking behavior. Even if several tension stiffening models exist, they are for plain and normal strength concrete. Thus, the development of tension stiffening models for steel fibrous high strength RC members are necessary at this time when steel fiber reinforced and high strength concretes are common in use. This paper presents tension stiffening effects from experimental results on direct tension members with the main variables such as concrete strength, concrete cover depth, steel fiber quantity and aspect ratio. The comparison of existing models against experimental results indicated that linear reduced model closely estimated the test results at normal strength level but overestimated at high strength level. Discontinuity stress reduced model underestimated at both strength levels. These existing models were not valid enough in applying at steel fibrous high strength concrete because they couldn't consider the concrete strength nor section area. Thus, new tension stiffening models for high strength and steel fiber reinforced concrete were proposed from the analysis of experimental results, considering concrete strength, rebar diameter, concrete cover depth, and steel fiber reinforcement.

• 한국콘크리트학회:학술대회논문집
• /
• 한국콘크리트학회 2005년도 추계 학술발표회 제17권2호
• /
• pp.5-8
• /
• 2005

The purpose of this study is to investigate the mechanical characteristics of plain and steel fiber high strength concrete under uniaxial and biaxial loading condition. A number of plain and steel fiber high strength concrete cubes having 28 days compressive strength of 82.7Mpa (12,000psi) were made and tested. Four principal compression stress ratios, and four fiber concentrations were selected as major test variables. From test results, it is shown that confinement stress in minor stress direction has pronounced effect on the strength and deformational behavior. Both of the stiffness and ultimate strength of the plain and fiber high strength concrete increased. The maximum increase of ultimate strength occurred at biaxial stress ratio of 0.5 in the plain high strength concrete and the value were recorded 30 percent over than the strength under uniaxial condition. The failure modes of plain high strength concrete under uniaxial compression were shown as splitting type of failure but steel fiber concrete specimens under biaxial condition showed shear type failure.

• 한국콘크리트학회:학술대회논문집
• /
• 한국콘크리트학회 2009년도 춘계 학술대회 제21권1호
• /
• pp.241-242
• /
• 2009

본 연구에서 초고강도 콘크리트에 높은 연성을 얻기 위하여 Steel Fiber을 혼입하여 초고성능 콘크리트를 연구하였다. 기존의 Steel Fiber 와 Liquid Metal Fiber를 혼합한 초고강도 모르타르 시험체를 휨강도실험을 통하여 결과를 비교 검토 하였다. ASTM C 1018 방법, JSCE- SF4방법으로 인성지수 평가를 통해 Liquid Metal Fiber은 기존의 Bundrex Steel Fiber 보다 우수한 결과를 얻었다.

• 콘크리트학회논문집
• /
• 제12권2호
• /
• pp.13-20
• /
• 2000

In this study, the compression test of steel fiber reinforced high-strength concrete have been performed with varying strengths and volume factions of steel fiber. Three types of matrices including low strength concrete( c'=30 MPa), medium strength concrete( c'=50 MPa), and high strength concrete( c'=70 MPa) were selected. Five types of fiber fractions were studied including 0.0%, 0.5%, 0.75%, 1.0%, and 1.5% by volume. From the results of the compressive strength test, the post-peak characteristics of the stress-strain relationship were investigated, and the existing equations to predict the elastic modulus were experimentally evaluated.

• 한국공간구조학회논문집
• /
• 제23권2호
• /
• pp.69-78
• /
• 2023

This paper investigates the effects of aspect ratio and volume fraction of hooked-end normal-strength steel fibers on the compressive and flexural properties of high-strength concrete with specified compressive strength of 60 MPa. Three types of hooked-end steel fibers with aspect ratios of 64, 67 and 80 were considered and three volume fractions of 0.25%, 0.50% and 0.75% for each steel fiber were respectively added into each high-strength concrete mixture. The test results indicated that the addition of normal-strength steel fibers is effective to improve compressive and flexural properties of high-strength concrete but fiber aspect ratio had little effect on the modulus of elasticity and compressive strength. As steel fiber content and aspect ratio increased, flexural beahvior of notched high-strength concrete beams was effectively improved.

• 한국구조물진단유지관리공학회 논문집
• /
• 제12권3호
• /
• pp.101-109
• /
• 2008

본 연구에서는 마이크로 입자들로 구성된 매트릭스의 강섬유 보강 시멘트 복합체에서 강섬유가 압축강도에 미치는 영향을 규명하고자 하였으며, 강섬유의 섬유혼입률과 섬유형상비에 따른 영향을 파악하고 혼입률과 형상비를 동시에 고려한 변수인 섬유보강지수(RI)에 따른 압축강도의 변화를 살펴보았다. 실험결과에 따르면 마이크로 입자로 구성된 매트릭스의 강섬유보강 복합체에서는 섬유보강지수가 증가에 따라 압축강도가 선형적으로 증가하였다. 이와 같은 결과로부터 섬유보강지수와 압축강도와의 관계를 나타내는 모델식을 제안하였다.

• 한국콘크리트학회:학술대회논문집
• /
• 한국콘크리트학회 2004년도 춘계 학술발표회 제16권1호
• /
• pp.308-311
• /
• 2004

Many researchers have reported that adding steel fiber to concrete improved its tensile and flexural strength significantly, but relatively few studies have been made on the compressive behavior of SFRC(steel fiber reinforced concrete). It is still less in case of high strength SFRC. The main objective of this research is to examine the effect of adding steel fiber on the compressive strength of high strength SFRC using fiber reinforcing index$(RI,\;V_f(l/d))$. It was found from the study that compressive strength was noticeably increased in proportion to RI.

• 한국구조물진단유지관리공학회 논문집
• /
• 제8권3호
• /
• pp.141-148
• /
• 2004

본 논문에서는 고성능 감수제, 증점제, 광물질 혼화재 및 강섬유의 양과 종류가 고강도 섬유보강 시멘트 복합체의 워커빌리티에 미치는 영향을 실험적으로 검토하였다. 그 결과, 고강도 강섬유 보강 시멘트 복합체의 워커빌리티는 고성능 감수제, 증점제 및 광물질 혼화재를 적절히 사용함으로써 향상된다. 그리고 강섬유의 형상계수가 작을수록 섬유보강 시멘트 복합체의 워커빌리티가 향상되었으며, 또한 워커빌리티가 향상된 강섬유 보강 시멘트 복합체의 압축강도와 휨강도는 향상되는 것으로 나타났다.