• Transactions of Materials Processing
• /
• v.23 no.2
• /
• pp.110-115
• /
• 2014

Low cycle fatigue characteristics are very important in the development of automobile suspension parts. Fatigue properties using the strain life approach are usually obtained from low cycle fatigue tests. However, low cycle fatigue testing requires a lot of time and cost. In the current study, an attempt to estimate low cycle fatigue properties of high strength steel sheet from tensile test and tensile simulations is performed. In addition, low cycle fatigue testing was conducted to compare the fatigue properties obtained from tensile testing and simulations. In conclusion, the results effectively predict the low cycle fatigue properties. However, some deviations still exist.

• Journal of Power System Engineering
• /
• v.14 no.6
• /
• pp.29-34
• /
• 2010

As the steam temperature of fossil power plant boiler is increasing, the use of 9Cr-1Mo high alloy material is prevalent and it is needed to investigate the characteristics of low cycle fatigue for high alloy and austenite stainless steel that has used up to recently. As a result of test, in 9Cr-1Mo high alloy steel, the relation of strain and fatigue life is non-linear and the crack mode of low cycle fatigue is brittle but in the austenite stainless steel, that of strain and fatigue life is linear and the crack mode of low cycle fatigue is ductile. Comparing the fatigue life between high alloy and austenite stainless steel, there is no consistent characteristics as to strains. But the fatigue life of 9Cr-1Mo steel is longer by 25% than that of STS304 stainless steel in the relatively low, 0.3% strain. In the other strain, the fatigue life of two materials is similar.

• Proceedings of the Korean Society for Technology of Plasticity Conference
• /
• 2009.10a
• /
• pp.467-469
• /
• 2009

In this study, fatigue samples were prepared from cylinder head parts that are actually used in domestic (A) and foreign (B) automobiles; high-temperature, high-cycle, and low-cycle fatigue characteristics were then evaluated and compared. A study on the correlation between the microstructural factor and high temperature fatigue characteristic was attempted. The chemical compositions of the heat resistant aluminum alloys above represented A356 (A) and A319 (B), respectively. The result of the tensile strength test on material B at $250^{\circ}C$ was higher by 30.8MPa compared to material A. On the other hand, elongation was 8.5% higher for material A. At $130{\circ}C$, material B exhibited high fatigue life given high cycle fatigue under high stress, whereas material A showed high fatigue life when stress was lowered. With regard to the low-cycle fatigue result ($250^{\circ}C$) showing higher fatigue life as ductility is increased, material A demonstrated higher fatigue life. Through the observation of the differences in microstructure and the fatigue fracture surface, an attempt to explain the high-temperature fatigue deformation behavior of the materials was made.

• Proceedings of the Korea Society of Design Studies Conference
• /
• 2001.10a
• /
• pp.43.2-43
• /
• 2001

• Journal of Welding and Joining
• /
• v.8 no.2
• /
• pp.40-52
• /
• 1990

Fatigue behavior of the AH, DH and EH grade TMCP(Thermo-Mechanical Control Process) steels was studied. High cycle and low cycle fatigue tests were carried out for the weldment and base metal of each steel. The results showed that the fatigue limit at 2 * $10^6$ cycles was 33 to 37 kg/$mm^2$ for the base metal and 30 to 34 kg/$mm^2$ for the weldment. The ratio of fatigue limit to tensile strength for TMCP steels was 0.65 to 0.71, which was a value close to the upper limit for the ordinary steels. It was also found that the high cycle fatigue behavior of TMCP steels could be affected by the microstructures of base metal. It will be necessary to have fine structure for TMCP steels to increase the fatigue resistance. In low cycle fatigue test, the fatigue lifetime of AH and DH steels accorded well with the ASME best fit curve, while that of EH steel was considerably lower than the fatigue lifetime of the other steels. Fatigue resistance of the weldment made by high heat input(180kJ/cm) welding was not lower than that made by low heat input(80kJ/cm) welding in case of high cycle fatigue, but the high heat input welding decreased the fatigue resistance in case of low cycle fatigue.

• Transactions of Materials Processing
• /
• v.19 no.1
• /
• pp.11-16
• /
• 2010

The influence of pre-strain on low cycle fatigue behavior of Fe-18Mn-0.05Al-0.6C TWIP steel was studied by conducting axial strain-controlled tests. As-received plates were deformed by rolling with reduction ratios of 10 and 30%, respectively. A triangular waveform with a constant frequency of 1 Hz was employed for low cycle fatigue test at the total strain amplitudes in the range of ${\pm}0.4\;{\sim}\;{\pm}0.6$ pct. The results showed that low-cycle fatigue life was strongly dependent on the amount of pre-strain as well as the strain amplitude. Increasing the amount of prestrain, the number of reversals to failure was significantly decreased at high strain amplitudes, but the effect was negligible at low strain amplitudes. A new model for predicting fatigue life of pre-strained body has been suggested by adding ${\Delta}E_{pre-strain}$ to the energy-based fatigue damage parameter. Also, high-cycle fatigue lives predicted using the low-cycle fatigue data well agreed with the experimental ones.

• Journal of the Korean Society of Manufacturing Technology Engineers
• /
• v.24 no.6
• /
• pp.589-593
• /
• 2015

The demand of high cycle fatigue behavior on plate material is increasing because of its various applications. However, the high-cycle fatigue life data of the plate material is very rare compared to the rod material. Thus, in this study, a plate specimen is designed for the ultrasonic fatigue test because it is time efficient as compared to the conventional fatigue test. To apply the ultrasonic fatigue test, the specimen design is required to resonate at 20 kHz. Therefore, the dynamic elastic modulus was determined by measuring the resonance frequency with a piezoelectric element and laser doppler vibrometer (LDV). As a result, the plate specimen is designed and demonstrated using the ultrasonic fatigue testing machine. The ultrasonic fatigue test results were compared with the hydraulic fatigue test results.

• Journal of Welding and Joining
• /
• v.31 no.4
• /
• pp.47-53
• /
• 2013

SCMH2 steel is widely used in the industrial members of car and tractor. This study focused on material properties and evaluation technology of the SCMH2 steel regarding the surface treatment followed by carburizing and nitriding, by means of impact test, hardness test. and fatigue test including HCF (high cycle fatigue) and VHCF (very high cycle fatigue). Drop weight impact tester (Instron, 9250 Hv) and Cantilever type rotating-bending fatigue tester (YRB200, 3150 rpm) were used to characterize the SCMH2 standard specimen before and after carburizing/nitriding. In order to understand those effects on fatigue characteristics and material properties, the fractured surfaces were carefully observed and analyzed by SEM (scanning electron microscope) and EDS (energy-dispersive X-ray spectroscopy).

• Journal of the Korean Society of Safety
• /
• v.33 no.3
• /
• pp.8-14
• /
• 2018

Ni-base superalloy has excellent resistance to extreme environments such as high temperatures and high stresses and are used as materials for large gas turbines. In this paper, the specimens were taken from the blade that were used for a long time, and their life span was studied by microstructure analysis and avoidance of cursing. The microstructural analysis of the specimens was carried out using a OM and SEM to observe the coarsening, carbides on gamma prime. Low-cycle fatigue tests were performed on new material and airfoil of long time-used blade. The test was conducted under various deformation conditions and temperature conditions of $760^{\circ}C$ and $870^{\circ}C$. The low cycle fatigue test was carried out using the Coffin-Manson equation and the fatigue life was predicted. After the test, crack path and fracture surface were analyzed using SEM.

• Proceedings of the Korean Society of Agricultural Engineers Conference
• /
• 1998.10a
• /
• pp.113-118
• /
• 1998

The relation of cycle loading to deflections on the mid-span, the crack propagation and the modes of failure according to cycle number, fatigue life and S-N curve were observed through the fatigue test. Based on the fatigue test results, high-strength reinforced concrete beams failed to 57 ~ 66 percent of the static ultimate strength. Fatigue strength about two million cycles from S-N curves was certified by 60 percent of static ultimate strength.