• Proceedings of the KSME Conference
• /
• 2008.11a
• /
• pp.193-197
• /
• 2008

Array of micro-dimple on polyoxymethylene (POM) surface was fabricated using Q-switched Nd:YAG laser and its characteristics were studied in terms of heat affected zone (HAZ), dimple geometry, and the effect of specimen surface roughness. Process parameters such as lamp current, process time, and the stream of air in order to minimize HAZ and flow of molten polymer into cavity were extensively studied in this work. Dimple geometry was further investigated by 3-D optical microscopy to provide deep insight into morphological analysis near the dimples. This paper also presents the applicapability of micro-dimples in polymeric tribological system, such as a thrust bearing. Micro-dimples were expected to provide low coefficient of friction and enhanced lubricity at the sliding interface.

• Journal of Welding and Joining
• /
• v.16 no.4
• /
• pp.83-91
• /
• 1998

Cracking problems which high temperature plant components suffer during long-term service, occur very often at welded locations. The crack occurs due to accumulated creep damage near fusion line or at heat affected zone (HAZ). However, most of the studies on creep crack growth behavior have been performed with matrix metal not wit welded metal due to the difficulty of interpreting the test results. In this study, creep crack growth rates were measured with C(T) specimens whose cracks were formed along the fusion line or HAZ. The measured crack growth rates were characterized by {TEX}$C_{t}${/TEX}-parameter derived for elastic-primary-secondary creeping material. Since contribution of primary creep was significant for the tested 1Cr-0.5Mo steel, its effect was carefully studied. Effects of crack tip plasticity and material aging were also discussed.

• Proceedings of the KWS Conference
• /
• 2005.11a
• /
• pp.201-203
• /
• 2005

A kinetic model for particle coarsening behavior in the weld heat affected zone (HAZ) was proposed. Unlike the conventional approach, where the mean-sized particle is considered to grow continuously, the proposed model considered the critical particle size which can be derived from the Gibbs-Thomson equation. In this study, the proposed particle coarsening model was applied to study the behavior of (Ti, Nb )(C, N) complex particle in the weld HAZ. The predicted particle size distributions using the proposed model were in agreement with the experimental results.

• Proceedings of the Korean Society of Machine Tool Engineers Conference
• /
• 2002.10a
• /
• pp.170-173
• /
• 2002

The object of this study is to investigate the effect of compounded welding through the AE (Acoustic Emission) characteristics on static tensile test. This study was carried out a SM 490A, high tension steel using the low hydrogen type E4316 of electronic shield metal arc welding and compound wire of $CO_2$gas arc welding. $CO_2$welding, weak in the intensity of HAZ (Heat Affected Zone), can be improved by being combined with coated arc welding, Coated arc welding, weak in the intensity of the bead, can be improved by being combined with $CO_2$welding. Especially, electronic coated arc welding and $CO_2$welding complement the mechanical intensity of HAZ and the bead with each other. So, compounded welding increases the intensity in the special parts and enhances the quality of goods.

• Proceedings of the Korean Society for Technology of Plasticity Conference
• /
• 2003.05a
• /
• pp.240-243
• /
• 2003

Finite element analyses for bursting failure prediction in bulge forming under combined internal pressure and independent axial feeding are carried out. By means of the FEM combined with Oyane's ductile fracture criterion based on Hills quadratic plastic potential, the forming limit and bursting pressure level are investigated for a seamed tube that comprises of weldment, heat affected zone(HAZ) and base material parts. Especially, in order to determine the material property of HAZ tensile tests for the base material and the weld metal are executed based on iso-strain approach. Finally, through a series of bulge forming simulations with consideration of the weldment and HAZ it is concluded that the proposed method would be able to predict the bursting pressure and fracture initiation site more realistically, so the approach can be extended to a wide range of practical bulge forming processes.

• Journal of Welding and Joining
• /
• v.33 no.6
• /
• pp.27-35
• /
• 2015

Laser welding sector in the automotive industry has been widely recognized as one of the most important bonding processes, such as parts welding. Efforts to improve productivity and weld quality have been progressing steadily. In addition, laser welding is suitable for welding process that can produce high-quality welds suitable for flexible production and small quantity batch productions. In order to ensure the rigidity of the material, high strength material are applied to more than 1 GPa class body parts and automotive bumper beams. However, not only the situation is that the trend of domestic research, but also development is based on product molding considering freedom of shape where reinforcement is applied to meet the safety regulations and high-speed crash performance, despite the use of high strength materials. The tendency for heat-affected zone (HAZ) softening phenomenon common in areas of laser welded high tensile steel welding confirmed the occurrence of weld softening effect according to the process parameters. Based on this, range of process parameters could be selected for ensuring weld quality.

• Korean Journal of Materials Research
• /
• v.31 no.3
• /
• pp.139-149
• /
• 2021

In this study, three kinds of bainitic steels are fabricated by controlling the contents of vanadium and boron. High vanadium steel has a lot of carbides and nitrides, and so, during the cooling process, acicular ferrite is well formed. Carbides and nitrides develop fine grains by inhibiting grain growth. As a result, the low temperature Charpy absorbed energy of high vanadium steel is higher than that of low vanadium steel. In boron added steel, boron segregates at the prior austenite grain boundary, so that acicular ferrite formation occurs well during the cooling process. However, the granular bainite packet size of the boron added steel is larger than that of high vanadium steel because boron cannot effectively suppress grain growth. Therefore, the low temperature Charpy absorbed energy of the boron added steel is lower than that of the low vanadium steel. HAZ (heat affected zone) microstructure formation affects not only vanadium and boron but also the prior austenite grain size. In the HAZ specimen having large prior austenite grain size, acicular ferrite is formed inside the austenite, and granular bainite, bainitic ferrite, and martensite are also formed in a complex, resulting in a mixed acicular ferrite region with a high volume fraction. On the other hand, in the HAZ specimen having small prior austenite grain size, the volume fraction of the mixed acicular ferrite region is low because granular bainite and bainitic ferrite are coarse due to the large number of prior austenite grain boundaries.

• Journal of the Korean Society for Heat Treatment
• /
• v.12 no.4
• /
• pp.303-312
• /
• 1999

An investigation of the CrMoV rotor steel weldment which experienced by cyclic thermal aging heat treatment and as-received condition was performed. This evaluation was carried out to confirm whether this type of weldment is appropriate for the service environment in terms of microstructural examinations, microhardness measurements and tensile tests. The cyclic thermal aging heat treatment, containing continuous heating and cooling thermal cycle was programmed to simulate the real rotor service condition. The heat treatment was performed for 40 cycles(5920hrs). The results indicated that the weldment was composed of 4 different regions such as heat affected zone of the base metal, butter weld(initial weld), full thickness weld(final weld) and the base metal. The double welding process was applied to eliminate the susceptibility of reheat cracking at heat affected zone of base metal. The grain refinement at the HAZ due to the welding process could reduce the possibility of cracking susceptibility, but its tensile properties was appeared to be low due to the weld metal in as-received condition. The benefit effect, grain refinement was extended with carbides coarsening during the cyclic thermal aging heat treatment. However the poor mechanical properties of the weldment was more degraded as undergoing the heat treatment.

• Proceedings of the KSME Conference
• /
• 2001.06a
• /
• pp.274-279
• /
• 2001

Creep-fatigue crack growth behavior was experimentally measured particularly when a crack was located in the heat affected region of 1Cr-0.5Mo steel. Load hold times of the tests for trapezoidal fatigue waveshapes were varied among 0, 30, 300 and 3,600 seconds. Time-dependent crack growth rates were characterized by the $C_t$-parameter. It was found that the crack growth rates were the highest when the crack path was located along the fine-grained heat affected zone(FGHAZ). Cracks located in other heat affected regions had a tendency to change the crack path eventually to FGHAZ. Creep-fatigue crack growth law of the studied case is suggested in terms of $(da/dt)_{avg}$ vs. $(C_t)_{avg}$ for residual life assessment.

• Journal of Ocean Engineering and Technology
• /
• v.13 no.3 s.33
• /
• pp.68-76
• /
• 1999

The welding residual stresses produced by the welding frequently caused a crack and promote stress corrosion etc. in HAZ(heat affected zone) contained with external load and weakness of material. Therefore, PWHT(post welding heat treatment) is widely used to reduce wekdubg residuss, to relax hardening of heat affected zone and to get rid of impurity. In this study, in order to define the effect on shappes of T-welded joint, during the post welding heat treatment, we have carried out numerical analyses on the several test pieces by using computer program which was based on thermal-elasto-plato-plasto-creep theories for the study. The main results obtained form this study is as follows: 1) The mechanical difference for change the thickness of plate and groove angle did not appear. 2) The distribution modes of welding residual stresses are same on the all test specimens during the post welding heat treatment. 3) In a mecharical point of view, minimum groove groove angle($40^{circ}$) is more suitable than maximum groove angle($60^{circ}$). 4) Therefore, it is appropriate to minimize the size of groove shape in strength and safety.