• Journal of Welding and Joining
• /
• 제23권2호
• /
• pp.75-80
• /
• 2005

The effect of chemical constituents of $(Cr,\;Fe)_7C_3$ carbide phase on its hardness in the chromium-carbide type Cr white iron hardfacing weld deposits has been investigated. In order to examine $(Cr,\;Fe)_7C_3$ carbide phase, a series of filler metals with varying chromium contents was used. The alloys were deposited once or twice on a mild steel plate using the self?shielding flux cored arc welding process. The hardness of $(Cr,\;Fe)_7C_3$ carbide phase was measured by the micro-Vickers hardness test. It was shown that hardness of $(Cr,\;Fe)_7C_3$ carbide phase increased with increasing Cr content in $(Cr,\;Fe)_7C_3$ carbide phase. This behavior of the hardness of $(Cr,\;Fe)_7C_3$ carbide phase was explained by the types of chemical bonds that hold atoms together in $(Cr,\;Fe)_7C_3$ carbide phase.

• 한국기계가공학회지
• /
• 제18권1호
• /
• pp.31-37
• /
• 2019

This study investigates the effects of long-term artificial-aging on hardness variation in the dissimilar metal weldments for nuclear power plant facilities. These dissimilar welds are inevitably required to join the components in nozzle parts of pressurized vessels, such as austenitic stainless steels and ferritic steels. A artificial thermal aging was conducted in an electrical furnace to simulate material degradation at high temperatures. The test materials were held at the temperature of $600^{\circ}C$ for 10000 hours and interrupted at various levels of degraded specimens. The degradation of hardness is a well-known phenomenon resulting from long-term aging or high-temperature degradation of structural materials. In this study, the variation of hardness at each position was different, and complicated in relation to microstructures such as twins, grains, precipitates, phase transformations, and residual stresses in dissimilar weldments. We discussed the variation of hardness in terms of microstructural changes during long-term aging.

• 한국윤활학회:학술대회논문집
• /
• 한국윤활학회 2003년도 학술대회지
• /
• pp.85-90
• /
• 2003

Although wear resistance of material improves with increasing its hardness, it is known that the wear resistance of steel is varied with hardness of counter material. In this context, wear properties of steel must be depended on the difference of hardness between the testpiece and the counter material. In this study, using the pin-on-disc type wear machine, annealed carbon steels were tested against ahoy tool steels with various levels of hardness. Then the changes of wear properties of carbon steel according to the hardness of counter material were investigated and the morphology of worn surface after test were evaluated. The results indicate that if there are no remarkable difference of hardness between them, wear resistance of carbon steel in running-in wear decreases with increasing the hardness of counter material. However, its wear properties at the range of high sliding speed have no relation with hardness of counter material. It is clear that wear properties is influenced by the formation of oxide of steel on their worn surface during wear.

• 대한설비공학회:학술대회논문집
• /
• 대한설비공학회 2008년도 동계학술발표대회 논문집
• /
• pp.642-648
• /
• 2008

In order to analyze the causes of fossil power plant facilities due to a degradation and corrosion, artificial degraded materials composed of the facilities were manufactured. Various experiment were performed based on mechanical test, microstructure observation, hardness test, electrochemical potentiokinetic reactivation test(EPR) and corrosion scale thickness measurement test. The master curves were write out using Larson-Miller parameter to evaluate the degree of degradation with the above diagnosis methods. These data were applied to materials database of fossil power plant diagnosis. Finally expert system on the fossil power plant diagnosis was developed using the master curves and diagnosis algorithms.

• The Journal of Advanced Prosthodontics
• /
• 제5권4호
• /
• pp.471-478
• /
• 2013

PURPOSE. The aim of the study was to evaluate the effect of annealing on the nanostructure and hardness of Co-Cr metal ceramic samples that were fabricated with a direct metal laser sintering (DMLS) technique. MATERIALS AND METHODS. Five groups of Co-Cr dental alloy samples were manufactured in a rectangular form measuring $4{\times}2{\times}2$ mm. Samples fabricated by a conventional casting technique (Group I) and prefabricated milling blanks (Group II) were examined as conventional technique groups. The DMLS samples were randomly divided into three groups as not annealed (Group III), annealed in argon atmosphere (Group IV), or annealed in oxygen atmosphere (Group V). The nanostructure was examined with the small-angle X-ray scattering method. The Rockwell hardness test was used to measure the hardness changes in each group, and the means and standard deviations were statistically analyzed by one-way ANOVA for comparison of continuous variables and Tukey's HSD test was used for post hoc analysis. P values of <.05 were accepted as statistically significant. RESULTS. The general nanostructures of the samples were composed of small spherical entities stacked atop one another in dendritic form. All groups also displayed different hardness values depending on the manufacturing technique. The annealing procedure and environment directly affected both the nanostructure and hardness of the Co-Cr alloy. Group III exhibited a non-homogeneous structure and increased hardness ($48.16{\pm}3.02$ HRC) because the annealing process was incomplete and the inner stress was not relieved. Annealing in argon atmosphere of Group IV not only relieved the inner stresses but also decreased the hardness ($27.40{\pm}3.98$ HRC). The results of fitting function presented that Group IV was the most homogeneous product as the minimum bilayer thickness was measured (7.11 ${\AA}$). CONCLUSION. After the manufacturing with DMLS technique, annealing in argon atmosphere is an essential process for Co-Cr metal ceramic substructures. The dentists should be familiar with the materials that are used in clinic for prosthodontics treatments.

• 한국표면공학회지
• /
• 제47권1호
• /
• pp.13-19
• /
• 2014

The various surface treated conditions of Fe-3.0%Ni-0.7%Cr-1.4%Mn-X steel such as as-received, ion nitriding, DLC coated, DLC coated after nitriding for 3 hrs and 6 hrs were investigated to evaluate the beneficial effect for plastic mold steel. Micro Vickers hardness tester was used to estimate nitriding depth from the hardness profile and to measure hardness on the surface. Elastic modulus and residual stress were measured by a nanoindentator. Scratch test and SP (small ball punch test) were utilized to assess the adhesive strength of DLC coating. The depth of nitriding layer was measured as $50{\mu}m$ for the condition of 3 hrs nitriding and $90{\mu}m$ for that of 6 hrs nitriding. Hardness, elastic modulus, residual stress of DLC coating were 20.37 GPa, 162.78 GPa and -1456 MPa respectively. Residual stress on the surface of DLC coating after nitriding could increase to -3914 MPa by introducing nitriding before DLC coating. During the 'Ball-On-Disc' test ${\gamma}^{\prime}$ particles pulled out from the surface of nitrized layer tend to enhance abrasive wear mode since the fraction of ${\gamma}^{\prime}$ (Fe4N) in ion-nitrized layer is known to increases with nitriding time. Thus the specific wear rate of the nitriding layer increased. Comparing with nitriding the specific wear rate in work piece disc as well as ball decreased prominently in DLC coating due to the remarkable reduction in friction coefficient.

• 비파괴검사학회지
• /
• 제25권5호
• /
• pp.368-376
• /
• 2005

자동차용 냉각기 호스는 열과 기계적 하중 하에서 공기와 부동액의 접촉 스트레스로 인해 노화와 고장이 일어날 수 있다. 본 연구에서는 냉각기 호스재료인 EPDM(ethylene-propylene diene monomer)고무에 대해 열가속 및 산소 스트레스, 전기화학적 스트레스에 의한 표피층의 노화거동을 비파괴 평가하였다. 열가속 및 산소노화 시험결과 신장률의 저하와 함께 IRHD(International Rubber Hardness Degrees)경도가 증가하였다. 전기화학적 노화(electro-chemical degradation: ECD) 시험에서는 에틸렌글리콜 수용액의 침투로 인해 무게가 증가하였으며 신장률과 경도는 크게 저하되었다 또한 에틸렌글리콜 수용액이 표피층뿐만이 아니라 내부에까지 침투하여 고무내부구조와 미크로경도분포가 깊이에 따라 변화되었다. 즉, 열가속 및 산소노화와 ECD 노화는 미크로 경도와 화학구조분석에 의해 비파괴적 특성 평가가 가능함을 보였다.

• The Journal of Advanced Prosthodontics
• /
• 제5권2호
• /
• pp.110-117
• /
• 2013

PURPOSE. Polymethyl methacrylate (PMMA) is the most commonly used denture base material despite typically low in strength. The purpose of this study was to improve the physical properties of the PMMA based denture base resins (QC-20, Dentsply Ltd., Addlestone, UK; Stellon, AD International Ltd, Dentsply, Switzerland; Acron MC; GC Lab Technologies Inc., Alsip, Japan) by copolymerization mechanism. MATERIALS AND METHODS. Control group specimens were prepared according to the manufacturer recommendations. In the copolymer groups; resins were prepared with 5%, 10%, 15% and 20% acrylamide (AAm) (Merck, Hohenbrunn, Germany) content according to the moleculer weight ratio, respectively. Chemical structure was characterized by a Bruker Vertex-70 Fourier transform infrared spectroscopy (FTIR) (Bruker Optics Inc., Ettlingen, Germany). Hardness was determined using an universal hardness tester (Struers Duramin, Struers A/S, Ballerup, Denmark) equipped with a Vickers diamond penetrator. The glass transition temperature ($T_g$) of control and copolymers were evaluated by Perkin Elmer Diamond DSC (Perkin Elmer, Massachusetts,USA). Statistical analyses were carried out using the statistical package SPSS for Windows, version 15.0 (SPSS, Chicago, IL, USA). The results were tested regarding the normality of distribution with the Shapiro Wilk test. Data were analyzed using ANOVA with post-hoc Tukey test (P<.01). RESULTS. The copolymer synthesis was confirmed by FTIR spectroscopy. Glass transition temperature of the copolymer groups were higher than the control groups of the resins. The 10%, 15% and 20% copolymer groups of Stellon presented significantly higher than the control group in terms of hardness. 15% and 20% copolymer groups of Acron MC showed significantly higher hardness values when compared to the control group of the resin. Acrylamide addition did not affect the hardness of the QC-20 resin significantly. CONCLUSION. Within the limitation of this study, it can be concluded that copolymerization of PMMA with AAm increased the hardness value and glass transition temperature of PMMA denture base resins.

• Earthquakes and Structures
• /
• 제8권3호
• /
• pp.619-637
• /
• 2015

A field based non-destructive hardness method is being developed to determine plastic strain in steel elements subjected to seismic loading. The focus of this study is on the active links of eccentrically braced frames (EBFs). The 2010/2011 Christchurch earthquake series, especially the very intense February 22 shaking, which was the first earthquake worldwide to push complete EBF systems into their inelastic state, generating a moderate to high level of plastic strain in EBF active links for a range of buildings from 3 to 23 storeys in height. Plastic deformation was confined to the active links. This raised two important questions: what was the extent of plastic deformation and what effect does that have on post-earthquake steel properties? A non-destructive hardness test method is being used to determine a relationship between hardness and plastic strain in active link beams. Active links from the earthquake affected, 23-storey Pacific Tower building in Christchurch are being analysed in the field and laboratory. Test results to date show clear evidence that this method is able to give a good relationship between plastic strain and demand. This paper presents significant findings from this project to investigate the relationship between hardness and plastic strain that warrant publication prior to the completion of the project. Principal of these is the discovery that hot rolled steel beams carry manufacturing induced plastic strains, in regions of the webs, of up to 5%.

• 대한통합의학회지
• /
• 제10권1호
• /
• pp.129-136
• /
• 2022

Purpose : The purpose of this study was to investigate the effect of applying intensity on the muscle activity and muscle hardness of the upper trapezius muscle in adult males when TENS (transcutaneous electrical nerve stimulation) was applied. In addition, this study intends to prepare the scientific basic data of TENS for the purpose of relaxation based on the experimental results. Methods : Eighty-seven healthy adult males participated in the experiment, and they were randomly divided into an experimental group and a control group. All subjects in this study were healthy subjects without musculoskeletal or nervous system damage. All subjects were subjects who voluntarily consented to the purpose and method of the experiment. All subjects were provided with a load by typing for 20 minutes, and muscle activity and muscle hardness of the upper trapezius muscle were measured immediately. Afterwards, TENS was given to each groups for 15 minutes, and the experimental group received stimulation at the motor threshold level, and the control group received a placebo stimulation. After stimulation, muscle activity and muscle hardness of the upper trapezius muscle were measured in the same method. The measured data were compared between groups through an independent t-test and dependent t-test. The statistical significance level was set at .05. Results : The application of TENS statistically significantly decreased the muscle activity and muscle hardness of the trapezius muscle in the experimental group, and the results showed a significant difference from the control group. Conclusion : Application of TENS significantly decreased the muscle activity and muscle stiffness of the upper trapezius muscle. The application of TENS of applying intensity that induces muscle contraction may induce relaxation by reducing the muscle activity and muscle hardness of the trapezius muscle.