• Elastomers and Composites
• /
• v.49 no.1
• /
• pp.66-72
• /
• 2014

Carbon coating on silica particles is done by grafting expanded graphite on the silica aggregates. Successful coating of carbon is corroborated using FT-IR, TGA, XPS and TEM. Crystalline nature of coated graphite is corroborated using XRD. Influence of carbon coated silica particles on rheometric and mechanical properties of SBR composites are investigated. Carbon coated silica particles showed significant improvement in rheometric and mechanical properties, when compared to pristine silica filled system corroborating higher polymer-filler adhesion. This fact was further supported by bound rubber content and equilibrium swelling ratios of unvulcanized and vulcanized SBR composites.

• Journal of Powder Materials
• /
• v.28 no.1
• /
• pp.1-6
• /
• 2021

Accurate and effective powder compaction analyses are performed for brittle materials such as graphite, utilized as a solid lubricant, by using the discrete element method (DEM). The reliability of the DEM analysis is confirmed by comparing the results of graphite powder compaction analyses using the DEM particle bonding contact model and particle non-bonding contact model with those from the powder compaction experiment under the same conditions. To improve the characteristics, the parameters influencing the compaction properties of the metal-graphite mixtures are explored. The compressibility increases as the size distribution of the graphite powder increases, where the shape of the graphite particles is uniform. The improved compaction characteristics of the metal-graphite (bonding model) mixtures are further verified by the stress transmission and compressive force distribution between the top and bottom punches. It is confirmed that the application of graphite (bonding model) powders resulted in improved stress transmission and compressive force distribution of 24% and 85%, respectively.

• Composites Research
• /
• v.19 no.2
• /
• pp.7-12
• /
• 2006

Graphite particle/carbon fiber hybrid conductive polymer composites were fabricated by the compression molding technique. Graphite particles were mixed with an epoxy resin to impart the electrical conductivity in the composite materials. In this study, graphite reinforced conductive polymer composites with high filler loadings were manufactured to accomplish high electrical conductivity above 100S/cm. Graphite particles were the main filler to increase the electrical conductivity of composites by direct contact between graphite particles. While high filler loadings are needed to attain good electrical conductivity, the composites becomes brittle. So carbon fiber was added to compensate weakened mechanical property. With increasing the carbon fiber loading ratio, the electrical conductivity gradually decreased because non-conducting regions were generated in the carbon fiber cluster among carbon fibers, while the flexural strength increased. In the case of carbon fiber 20wt.% of the total system, the electrical conductivity decreased 27%, whereas the flexural strength increased 12%.

• Journal of Powder Materials
• /
• v.10 no.1
• /
• pp.21-25
• /
• 2003

The Sn - graphite composites were prepared by chemical encapsulation method for anode materials in Li-ion batteries. EDS and XRD analysis confirmed the presence of Sn in the graphite structure. Cyclic voltammometry (CV) measurement shows extra reduction and oxidation peaks, which might to be related to the formations of $Li_xSn$ alloy compounds. Graphite-tin composite electrodes demonstrated higher Lithium storage capacities than graphite electrodes. Due to the nature of fine Sn particles on graphite surface, the graphite-tin composite electrodes have shown a good cycle properties.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 1998.06a
• /
• pp.387-390
• /
• 1998

New Ag-deposited graphite anodes were developed using wet chemical reduction methods for depositing Ag metal onto graphite particles. In this paper, we investigated X-ray diffraction pattern and charge-discharge behavior for Ag-deposited graphite anode. The Lithium ion cello using Ag-deposited graphite anode showed a high average discharge voltage of 3.6∼3.W and a excellent cycle ability than that of conventional graphite. Little capacity loss in this battery may be due to the highly durable Ag-deposited graphite anodes.

• Analytical Science and Technology
• /
• v.6 no.2
• /
• pp.149-156
• /
• 1993

The formation of the graphite spherulites has been studied experimentally in the Ni-C liquid under high pressure and temperature. In the diamond-stable region the graphite spherulites were formed and grew stably. They were not the polycrystalline particles but the single crystals of the fullerene-type, respectively, grown spirally with much imperfection. And they were proved to be in a mixture state of carbon atoms with $sp^2$- and $sp^3$-bonding by an Auger electron spectroscope and a high resolution transmission electron microscope. As the pressure decreased from the diamond-stable region to the graphite-stable region, the shape of the graphite particles changed gradually from the sphere to the flaky shape. The formation of the graphite spherulites was attributed to the stable existence of the carbon atoms with $sp^3$ bonding in the diamond-stable region. The formation of the large fullerene-type graphite spherulites with much imperfection is well agreed with Kroto's prediction for growth of the giant fullerene.

• Journal of the Korea Institute of Military Science and Technology
• /
• v.7 no.1
• /
• pp.47-58
• /
• 2004

Loss factors of A356, Mn-Cu alloy and aluminum matrix composites reinforced with $SiC_p$ and Ni-coated graphite particles at various contents have been investigated using clamped-free cantilever beam method. The loss factors of half-power bandwidth of the specimens were measured over a wide range of frequencies from 50 to 3300Hz. Among the specimens, Al-10%$SiC_p$-10%$C_p$ showed the highest loss factor at the mode I, while Mn-Cu alloy showed the highest loss factors at the modes II and III. Consequently, at the mode I the Al-10%$SiC_p$--10%$C_p$ showed the loss factor of 0.00093, which is 2.64 and 1.58 times higher than those of A356 and Mn-Cu alloy, respectively.

• Journal of Korea Foundry Society
• /
• v.17 no.1
• /
• pp.93-99
• /
• 1997

A possibility of production of aluminium matrix composites by using the lost foam process was investigated. Silicon carbide particles, graphite particles, and stainless steel wires were used as reinforcement materials. The reinforcement materials were introduced to the polystyrene to form patterns via injection molding process. The results obtained from this experiment can be summarized as follows. In Al/SiCp system, the particles with the radius of $100{\mu}m$ and over were entrapped in the matrix in the case of upward freezing of which solidification direction was opposite to floating direction of the particles. And few particles were entrapped in the matrix in downward freezing. In Al/graphite system, almost no particles were entrapped in the matrix except the area chill attatched. When the thickness of polystyrene slice was 4mm in Al/stainless steel wire system, the floating tendency of fibers was observed to increase as the distance from the ingate was increased.

• Proceedings of the Korean Society For Composite Materials Conference
• /
• 2004.04a
• /
• pp.147-150
• /
• 2004

Graphite reinforced conductive polymer composites were fabricated by the compression molding technique. Graphite powder (conductive filler) was mixed with an epoxy resin to impart electrical property in composites. The ratio of graphite powder was varied to investigate electrical property of cured conductive composites. In this study, graphite filled conductive polymer composites with high filler loadings$(>60wt.\%)$ were manufactured to accomplish high electrical conductivity(> 100S/cm). Graphite powder increase electrical conductivity of composites by direct physical contact between particles. While high filler loadings are needed to attain good electrical property, the composites becomes brittle. So the ratio of filler to epoxy was varied to optimize of cured composites. The optimum molding pressure according to filler was proposed experimentally.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2015.08a
• /
• pp.190.1-190.1
• /
• 2015

Graphite has excellent mechanical and physical properties. It is known to advanced materials and is used to materials for molds, thermal treatment of furnace, sinter of diamond and cemented carbide tool etc. SiC materials are coated on the surface and holes of graphite to protect particles emitted from porous graphite with 5%~20% porosity and make graphite hard surface. SiC materials have high durability and thermal stability. Thermal CVD method is widely used to manufacture SiC thin films but high cost of machine investment and production are required. SiC thin films manufactured by Si reaction liquid and vapore with carbon are effective because of low cost of machine and production. SiC thin films made by vapor silicon infiltration into porous graphite can be obtained for shorter time than liquid silicon. Si materials are evaporated to the graphite surface in about $10^{-2}$ torr and high temperature. Si materials are melted in $1410^{\circ}C$. Si vapor is infiltrated into the surface hole of porous graphite and $Si_xC_y$ compound is made. $Si_x$ component is proportional to the Si vapor concentration. Si diffusion coefficient is estimated from quadratic equation obtained by Fick's second law. The steady stae is assumed. Si concentration variation for the depth from graphite surface is fitted to quadratic equation. Diffusion coefficient of Si vapor is estimated at about $10^{-8}cm^2s^{-1}$.