• Journal of the Korean Wood Science and Technology
• /
• 제39권2호
• /
• pp.156-162
• /
• 2011

To evaluate the bonding performance of reinforced glulam, the textile type of glass fiber and aramid fiber, and the sheet type of glass fiber reinforced plastic (GFRP) and carbon fiber reinforced plastic (CFRP) were used as reinforcements. The reinforced glulam was manufactured by inserting reinforcement between the outmost and middle lamination of 5ply glulam. The types of adhesives used in this study were polyvinyl acetate resins (MPU500H, and MPU600H), polyurethane resin and resorcinol resin. The block shear strengths of the textile type in glass fiber reinforced glulam using MPU500H and resorcinol resin were higher than 7.1 N/$mm^2$, and these glulams passed the wood failure requirement of Korean standards (KS). In case of the sheet types, GFRP reinforced glulams using MPU500H, polyurethane resin and resorcinol resin, and CFRP reinforced glulams using MPU500H and polyurethane resin passed the requirement of KS. The textile type of glass fiber reinforced glulam using resorcinol resin after water and boiling water soaking passed the delamination requirement of KS. The only GFRP reinforced glulam using MPU500H after water soaking passed the delamination requirement of KS. We conclude that the bonding properties of adhesive according to reinforcements are one of the prime factors to determine the bonding performance of the reinforced glulam.

• 한국해양공학회지
• /
• 제14권4호
• /
• pp.49-55
• /
• 2000

This study has been investigated to apply fiber reinforced composites instead of asbestos as a friction material. the reinforced used was E-glass fiber and binder resin was phenol having good mechanical properties and heat resistance. And it has been also investigated the effect of molding conditions and some additives such and carbon black, alumina and rubber powder in E-glass fiber/phenol resin composite on the friction on the friction and wear characteristics. As a result, it was found that the molding conditions of E-glass fiber/phenol resin composites for friction materials had to be different from those of phenol resin and was found that the wear rate of E-glass fiber/phenol resin composites added alumina powder was higher than of composites added carbon black in the same wear distance. And it was found that friction coefficient of E-glass/phenol resin composites added carbon black was decreased and that of the composites added the powder of natural rubber and ABS rubber were increased compared to the composites.

• The Journal of Advanced Prosthodontics
• /
• 제4권1호
• /
• pp.1-6
• /
• 2012

PURPOSE. The aim of this study was to compare the flexural strength of polymethyl methacrylate (PMMA) and bis-acryl composite resin reinforced with polyethylene and glass fibers. MATERIALS AND METHODS. Three groups of rectangular test specimens (n = 15) of each of the two resin/fiber reinforcement were prepared for flexural strength test and unreinforced group served as the control. Specimens were loaded in a universal testing machine until fracture. The mean flexural strengths (MPa) was compared by one way ANOVA test, followed by Scheffe analysis, using a significance level of 0.05. Flexural strength between fiber-reinforced resin groups were compared by independent samples t-test. RESULTS. For control groups, the flexural strength for PMMA (215.53 MPa) was significantly lower than for bis-acryl composite resin (240.09 MPa). Glass fiber reinforcement produced significantly higher flexural strength for both PMMA (267.01 MPa) and bis-acryl composite resin (305.65 MPa), but the polyethylene fibers showed no significant difference (PMMA resin-218.55 MPa and bis-acryl composite resin-241.66 MPa). Among the reinforced groups, silane impregnated glass fibers showed highest flexural strength for bis-acryl composite resin (305.65 MPa). CONCLUSION. Of two fiber reinforcement methods evaluated, glass fiber reinforcement for the PMMA resin and bis-acryl composite resin materials produced highest flexural strength. Clinical implications. On the basis of this in-vitro study, the use of glass and polyethylene fibers may be an effective way to reinforce provisional restorative resins. When esthetics and space are of concern, glass fiber seems to be the most appropriate method for reinforcing provisional restorative resins.

• 대한치과보철학회지
• /
• 제45권3호
• /
• pp.310-320
• /
• 2007

Statement of the problem. The fracture of acrylic resin dentures remains an unsolved problem. Therefore, many investigations have been performed and various approaches to strengthening acrylic resin, for example, the reinforcement of heat-cured acrylic resin using glass fibers, have been suggested over the years. But problems such as poor workability, rough surface, poor adhesion of glass fiber resin complex are not solved yet. Purpose. The aim of the present study was to investigate the effect of short glass fibers on the transverse strength of heat-polymerized denture base acrylic resin and roughness of resin complex after abrasion test. Material and methods. To avoid fiber bunching and achieve even fiber distribution, glass fiber bundles were mixed with acrylic resin powder in conventional mixer with a non-cutting blade, to produce the glass fiber($10{\mu}m$ diameter, 3mm length, silane treated) resin composite. Glass fibers were incorporated at 0%, 3%, 6% and 9% by weight. Transverse strength were measured. After abrasion test, surface roughness was evaluated and scanning electron microscope view was taken for clinical application. Results. 1. 6% and 9% incorporation of 3mm glass fibers in the acrylic resin enhanced the transverse strength of the test specimens(p<0.05). 2. Before abrasion test, incorporation of 0%, 3%, 9% glass fiber in the resin showed no dirrerence in roughness statisticaly(p>0.05). 3. After abrasion test, incorporation of 0%, 3%, 6% glass fiber in the resin showed same surface roughness value statistically(p>0.05). 4. In SEM, surface roughness increased as the percentage of the fibers increased. 5. In the areas where glass fiber bunchings are formated, a remarkably high roughness was noticed. Conclusion. 6% and 9% addition of silane-treated short glass fibers into denture base acrylic resin increased transverse strength significantly. Before and after abrasion test, incorporation of 0%, 3%, 6% glass fiber in the resin showed same surface roughness value statistically.

• 폴리머
• /
• 제24권4호
• /
• pp.459-468
• /
• 2000

유리 또는 아라미드 섬유를 보강재로 사용한 섬유강화 복합재료의 기계적 물성을 증진시키기 위하여 복합재료 적층판을 서로 다른 매트릭스 수지와 섬유를 선정하여 이들의 인장, 굴곡 특성을 조사하였다. 불포화 폴리에스테르와 개질된 표면의 아라미드 섬유 복합재료의 경우, 굴곡 물성의 최대값은 실란 농도가 0.5 wt%일 때 관찰되었다. 불포화 폴리에스테르 수지와 유리섬유 복합재료의 인장 물성은 vinylester계가 가장 높게 나타났으며, 굴곡물성은 isophthalic계가 가장 높은 물성을 나타내었다. 유리섬유와 불포화 폴리에스테르 수지 복합재료의 기계적 물성을 증진시키기 위해 겹침 적층판과 기계적 물성과의 상관 관계에 대해서도 연구가 병행되었다.

• 한국농공학회논문집
• /
• 제58권3호
• /
• pp.21-27
• /
• 2016

This study was performed to evaluate engineering properties of carbon and glass fiber reinforced recycled polymer concrete. Fiber reinforced recycled polymer concrete were used recycled aggregate as coarse aggregate, natural aggregate as fine aggregate, $CaCO_3$ as filler, unsaturated polyester resin as binder, and carbon and glass fiber as fibers. The compressive and flexural strength of carbon fiber reinforced recycled polymer concrete were in the range of 68~81.5 MPa and 19.1~21.5 MPa at the curing 7days. Also, the compressive and flexural strength of glass fiber reinforced recycled polymer concrete were in the range of 69.4~85.1 MPa and 19~20.1 MPa at the curing 7days. Abrasion ratio of carbon and glass fiber reinforced recycled polymer concrete were decreased 21.6 % and 11.6 % by fiber content 0.9 %, respectively. After impact resistance test, drop numbers of initial and final fracture were increased with increase of fiber contents. Accordingly, carbon fiber and glass fiber reinforced recycled polymer concrete will greatly improve the hydraulic structures, underground utilities and agricultural structures.

• 대한치과보철학회지
• /
• 제45권4호
• /
• pp.457-468
• /
• 2007

Statements of problem: The fracture of acrylic resin dentures remains an unsolved problem. Therefore, many investigations have been performed and various approaches to strengthening acrylic resin, for example, the reinforcement of heat-cured acrylic resin using glass fibers, have been suggested over the years. Silane is important for bonding between glass fiber and resin. Purpose: The aim of the present study was to investigate the effect of various silane on the strength of PMMA resin and roughness of resin-glass fiber complex after abrasion test. Material and methods: 3mm glass fiber (Chopped strand, Hankuk fiber Co., Milyang, Korea) was treated with 3 kinds of silane (MPS, EPS, APS) (Sila-ace, Chisso chemical, Tokyo, Japan) and mixed with PMMA resin(Vertex RS, Vertex Dental B.V., Zeist, Netherlands). Transverse strength and Young's modulus was measured using Instron (Instron model 4466, Instron, Massachusetts, USA). After abrasion test (The 858 Mini Bionix II Test System, MTS System Co., Minnesota, USA) surface roughness was evaluated using tester (Form Talysurf plus, Taylor Hopson Ltd., Leicester England). Examination of scanning electron microscope was also performed. Results: Within this study, the following conclusions were drawn. 1. Surface treatment of glass fiber with MPS and APS increased transverse strength of PMMA resin complex, but surface treatment with EPS decreased transverse strength of PMMA resin complex (p<0.05). 2. Silane treated glass fiber increased Young's modulus of PMMA resin complex compared to desized glass fiber (p<0.05). 3. Roughness increased after abrasion test in case of PMMA resin reinforced with desized glass fiber (p<0.05). 4. Roughness change was not observed after abrasion test in case of PMMA resin reinforced with silane treated glass fiber (p>0.05).

• Journal of the Korean Wood Science and Technology
• /
• 제31권5호
• /
• pp.23-34
• /
• 2003

본 연구는 국산소경재인 소나무(Pinus densiflora)재와 낙엽송(Larix kaemferi)재로 제조된 유리섬유강화 집성재의 강도적 성질을 조사해 보기 위하여 실시되었다. 먼저, 직물 유리섬유를 수성고분자-이소시아네이트계(MPU-500) 접착제를 사용하여 control재와 유리섬유를 각각 1층과 2층 함입하였다. 본 연구의 결과는 다음과 같다. 1. 수성고분자-이소시아네이트 수지는 집성재 제조용으로 적합하였으며, 특히 유리섬유를 2층 함입한 소재를 제외하고는 구조용 집성재의 품질기준(KS F 3021)을 만족시켰다. 2. 직물유리섬유를 함입할 경우 휨강도, 전단강도에서 control재보다 크게 뛰어나지는 않았지만, 비례한도 휨응력은 유리섬유의 함입 층수에 비례하여 증가하였다. 그러므로, 직물 유리섬유의 mesh수와 두께를 집성재 소재의 형태에 따라 적절히 조정한다면, 휨강도와 전단강도를 좀더 향상시킬 수 있을 것으로 판단되었다.

• 대한치과기공학회지
• /
• 제42권1호
• /
• pp.27-33
• /
• 2020

Purpose: This study is to compare and analyze the precision of glass fiber resin dentures. Methods: A lower edentulous model was prepared. Ten study models were produced using Type IV stone. Ten wax lower resin dentures containing artificial teeth were prepared. The lower wax denture was buried with plaster and deflasking was performed to remove the wax. Five conventional lower resin dentures and five glass fiber lower resin dentures were produced. The scanning spray was coated on the impression surface and then scanned. Independent sample t-test were performed using statistical software. Results: In the color different map, which is a qualitative evaluation, the green area of the precision of the conventional lower resin denture occupied the whole. The glass fiber conventional resin dentures had many negative and positive area. In quantitative evaluation, the RMS of conventional lower resin was 89.83 ㎛ and that of fiberglass resin was 224.92 ㎛. The two groups showed statistically significant differences (p<0.05). Conclusion: Conventional lower resin dentures were superior in precision, and glass fiber resin dentures would have to improve the process.

• 대한치과기공학회지
• /
• 제31권4호
• /
• pp.37-43
• /
• 2009

This study evaluated the effect of concentration of glass fiber reinforcement on the flexural properties of auto and heat polymerized denture base resin. The test specimens($64{\times}10{\times}3.3mm$) were made of auto and heat polymerized resin(Vertex, Dentimax, Netherlands). Glass fiber(ER 270FW, Hankuk Fiber Glass, Korea) were used to reinforce the denture base resin. The 2.6%, 5.3% and 7.9% volume pre-impregnated fiber were located at the bottom of specimen. The test specimens(n=7) of each group were stored in distilled water at $37^{\circ}C$ for 50 hours before test. The flexural strength and modulus were measured by an universal testing machine(Z020, Zwick, Germany) at a crosshead speed of 5 mm/min in a three-point bending mode. The data was analyzed by one-way ANOVA and the Duncan's multiple range test(${\alpha}$=0.05). The difference of auto polymerized resin groups and heat polymerized resin groups were statistically analyzed by t-test(${\alpha}$=0.05). Glass fiber showed significant reinforcing effects on auto and heat polymerized resin. For flexural strength and modulus, auto polymerized resin was the highest in 7.9% volume, while heat polymerized resin was the highest in 5.3% volume. In this study, glass fiber at 7.9% volume ratio showed most effective reinforcing effect on auto polymerized resin and glass fiber at 5.3% volume ratio showed most effective reinforcing effect on heat polymerized resin in terms of flexural strength and flexural modulus.