• 대한치주과학회:학술대회논문집
• /
• 대한치주과학회 2005년도 제45회 종합학술대회 연제초록
• /
• pp.199-200
• /
• 2005

• Restorative Dentistry and Endodontics
• /
• 제13권1호
• /
• pp.185-190
• /
• 1988

The study was designed to establish quantitative method for assessing the marginal leakage of dental restorations. 18 Class V cavities with $45^{\circ}$ bevel joint were prepared and replicas of these teeth were made with polyethylene wax. and classified with three groups. First group was filled with Scotch bond and silux. Second group was filled with glass ionomer cement:scotchbond/silux. Third group was filled with Dentin-Adhesit/Heliosit. After finishing, all specimens were subjected manually to 100 thermal cycles at $0^{\circ}C$ and $100^{\circ}C$ Samarium nitrate solution, irradiated with flux of $6{\times}12^{12}$ neutrons/$cm^2$/sec for 11 hours, woled for 200 hours, counted with the HpGe detector and the tracer uptake was determined by comparison with a standard of samarium ($10{\mu}g$). The following results were obtained. 1) The group filled with glass ionomer cement base showed least marginal leakage. 2) The group filled with Dentin-Adhesit/Heliosit showed less marginal leakage than the group filled with scotchbond/silux.

• Restorative Dentistry and Endodontics
• /
• 제27권1호
• /
• pp.12-15
• /
• 2002

The first purpose of present study was to compare the anticariogenic effect of compomer, resin modified glass ionomer cement and composite (RMGIC). The second purpose was to evaluate the recently introduced methods, which use confocal scanning micro-scope, in detecting initial caries around restoration. 2$\times$4$\times$1.5mm cavities were prepared from the recently extracted 50 human teeth on the buccal or lingual surface. The prepared teeth were randomly devided into 5 groups and restored with each filling material. Group 1: Dyract AP, Group 2: compoglass F, Group 3: F2000, Group 4: Z100. Group 5:Fuji II LC. The teeth were stored for 30 days in the distilled water, then stored in the buffer solution for artificial caries development: pH 4.3, lactic acid 100 mM, calcium 16 mM, phosphate 8mM, sodium azide 3mM. Then, the samples were sectioned longitudinally and examined with confical scanning microscope. The results showed that the use of compomer and resin modified glass ionomer cement showed caries inhibition zone whereas the composite did not. There was no difference in the width of caries inhibition zone between compomers and RMGIC. The confocal scanning microscope was useful in detecting initial caries around restoration.

• 대한치과의사협회지
• /
• 제57권5호
• /
• pp.264-268
• /
• 2019

Objectives: This study aimed to measure the water sorption / solubility of Biodentine, composite resin and glass ionomer cement. Materials and Methods: The materials used in this study were Biodentine(BD), Filtek Z250(FZ) and Ketac Molar(KM). Twenty disc-shaped specimens of each material were prepared of 6mm diameter and 1mm thickness. All specimens were desiccated for 24 hours and weighed(m1). After then, They were immersed in distilled water and stored at $37^{\circ}C$. 1 week later, They were washed with running water, wiped with absorbent paper and weighed(m2). Finally, They were dried for 24 hours and weighed(m3). Water sorption and solubility, net water uptake were calculated. Results: KM and BD showed high water sorption than FZ(P<0.05). KM and BD exhibited similar water sorption(P<0.05). BD exhibited high solubility than KM(P=0.012). BD exhibited high net water uptake than FZ(P=0.008). Conclusion: Biodentine showed higher water sorption, solubility and net water uptake than Filtek Z250 and Ketac Molar. Within limitation of this study, it is not recommended to use Biodentine for permanent restoration.

• Restorative Dentistry and Endodontics
• /
• 제48권2호
• /
• pp.19.1-19.12
• /
• 2023

Objectives: The aim of the study was to evaluate the clinical and radiographic success of the Hall technique (HT) and atraumatic restorative treatment (ART) restorations using high-viscosity glass-ionomer cement for the management of occlusal carious lesions in primary molars. Materials and Methods: This randomized clinical study observed 40 children (aged 5-6 years). For each child, one tooth was treated with HT and one with ART. The primary outcome measures for HT restorations were successful, minor, and major failure rates. Clinical evaluations of ART restorations were performed according to the modified United States Public Health Service criteria during 18-month follow-up. McNemar test was used for statistical analysis. Results: Thirty of 40 (75%) participants returned for 18 months of follow-up. In the clinical evaluations of teeth that were treated with HT, the patients did not have complaints of pain or other symptoms, all crowns remained in the oral cavity, the gums were healthy, and the teeth were functional in all evaluations. At the end of the 18-month follow-up, the surface texture and marginal integrity criteria of ART restorations were recorded as 26.7% and 33.3%, respectively. In the radiographic evaluation of 30 patients treated with ART and HT, all restorations were considered successful. Conclusions: The 18-month clinical and radiographic results after treatments applied to single-surface cavities in anxious children showed that both treatment methods were successful.

• Restorative Dentistry and Endodontics
• /
• 제22권2호
• /
• pp.622-636
• /
• 1997

Glass ionomer cements, which had been developed in 1972, were widely used as an agent for cementation, base, pit and fissure sealant, and esthetic filling material with the advantages of excellent biocompatibility, anti-cariogenic fluoride release. Specimens were made to evaluate the color change of Glass ionomer cement with a newly developed improved Fuji II Le. Specimens for color change study with cement thickness of 1, 2, 3mm were made and those for the study of color shift pattern were made with the assumption that new mid-shade can be made by mixing of equal amount of both shades in 2mm thickness. After 24 hours in a $37^{\circ}C$ incubator, CIELAB color spaces were evaluated with a spectrophotometer. The results were as follows ; 1. All specimens discolored to dark and blue with an increased thickness in all shades (p<0.05). 2. There were significant $a^*$ space (red-green direction) changes in every A, B, C, D shade series except the relationship between 1mm and 2mm thickness groups in B shade series. But the changes were irregular, i.e., each shade series has its own pattern. 3. Each shade series showed its own specific color shift pattern in all $L^*$, $a^*$, $b^*$ spaces. 4. B shade series showed less amont of changes in ${\Delta}{\pm}E$ than those of A and C shade series (p<0.05), but there was no significant difference in ${\Delta}E$ within each shade series.

• Restorative Dentistry and Endodontics
• /
• 제16권1호
• /
• pp.87-105
• /
• 1991

The purpose of this experiment was to measure the leaking and solubility of commonly used dental restorative materials - Silux plus (CS), Hi-pol (CH), Clearfil F-II, Fissureseal (FS), Glass-Ionomer cement Fuji Type II (GI), Amalgam Cavex 68 (AM), Zinc Phosphate Cement (ZP) and gutta-percha (GP) and investigate the relation between the solubility and marginal leakage. Disc-shape specimens were fabricated with each material and dipped into deionized water, 0.01M lactic acid and 0.005M KOH solution, thus the total ionic concentrations in each solution was measured with ion chromatograph after 1, 3, and 7 days, respectively. For the solubility test, each specimen was immersed in 0.001M and 0.01M lactic acid for 24 hours, respectively and total weight loss was calculated. Also, Zn leaking through the margin of restorations was measured. The obtained results were as follows: 1. The amounts of eluted ion from the eight materials were most in 0.01M lactic acid and least in deionized water. 2. Of the eight materials, the fluoride release was greatest for glass ionomer cement (GI) in 0.01 M lactic acid after 7 days. 3. In analysis of the divalent cation, Mg was eluted most for zinc phosphate cement (ZP) and Ca for Clearfil F-II (CF) in 0.01M lactic acid after 7 days. 4. In analysis of transition metals, Cu and Zn were detected only. 5. The solubility rate of eight materials was greater in 0.01M lactic acid than in 0.001M for 24 hours, for zinc phosphate cement (ZP) the rate was greatest (5.4%) in 0.001M lactic acid, and amalgam least (0.01%). 6. The Zn concentration of restorative material with Z.P.C base was greater in 0.01M lactic acid than in 0.001M lactic acid.

• Restorative Dentistry and Endodontics
• /
• 제25권3호
• /
• pp.399-406
• /
• 2000

광중합형 글래스아이오노머 베이스에 대한 레진 인레이의 접착성을 증가시킬 수 있는 방법을 모색하고자, 이차 중합된 레진 인레이의 내표면을 여러 가지 방법으로 처리한 후 레진 인레이를 광중합형 글래스아이오노머 베이스에 레진 시멘트 접착시 내표면 처리방법이 이들의 접착에 미치는 영향을 평가하고자 하였다. 글래스아이오노머 베이스 제작을 위해서 플라스틱 봉에 직경 7mm, 깊이 2mm의 1급 와동을 형성하고 Fuji II LC를 충전하였으며, 수복용 레진(Charisma$^{(R)}$)을 사용하여 레진 인레이를 제작하였다. 레진 인레이 내면은 $50{\mu}m$ aluminum oxide particles를 이용한 sandblasting 및 silane 처리군, silane 처리군, sandblasting 군, 그리고 무처리 대조군 등 4군으로 나누어 표면처리하였으며 각 군은 22개씩의 시편을 사용하였다. 인레이와 베이스의 표면에 상아질 접착제(One-Step$^{TM}$)를 도포한 후 Choice$^{TM}$를 사용하여 레진시멘트 접착하였다. 접착 양상 평가를 위해 만능시험기로 전단접착강도를 측정하고 파단면을 입체현미경으로 관찰하여 다음과 같은 결과를 얻었다. 1. Sandblasting 및 silane 처리군이 가장 높은 접착강도(10.56${\pm}$1.95MPa)를 나타내었으며, 이는 sandblasting군 및 무처리 대조군에 비해 유의하게 높았다(p<0.05). 2. Silane 처리군(9.77${\pm}$2.04MPa)은 sandblasting 및 silane 처리군과는 접착력에 있어서 통계적으로 유의한 차이를 나타내지 않았으나, sandblasting 군 및 무처리 대조군에 벼해서는 유의하게 높은 접착강도를 나타내었다(p<0.05). 3. Sandblasting만 시행 한 군은 무처리 대조군과 비교시 접착강도에 있어 유의한 차이를 나타내지 않았다(p>0.05). 4. 파단면 관찰 결과, 모든 군에서 일부 접착계면에서의 파절을 포함하는 글래스아이오노머 베이스의 응집 파괴(cohesive failure) 양상이 가장 많이 나타났으며, sandblasting 및 silane 처리군과 silane 처리군에서는 sandblasting 군 및 무처리 대조군에 비해 상대적으로 적은 접 착계면에서의 파절(adhesive failure) 양상을 나타내었다. 5. 전단접착강도와 파절양상의 관계에서, 접착강도가 클수록 응집 파괴(cohesive failure) 양상이 많이 나타나는 경향을 보였다.

• 대한소아치과학회지
• /
• 제27권2호
• /
• pp.237-245
• /
• 2000

최근의 심미적 수복재료는 단순히 글래스아이오노머나 레진으로 구분되지 않는다. 대신에, 이들은 두 가지 전통적 재료 사이의 광범위한 한 범주 내에 위치한다. 유치 수복 재료를 선택함에 있어 임상가는 각각의 상황에 적합한 몇 가지 항목들을 고려해야 한다. 이들 중 한가지가 결합력이다. 이 연구는 특별히 상아질과 법랑질과의 상대적 인장강도를 재료별로 비교해보고자 하였다. 실험재료로는 resin-modified glass ionomer로 Fuji II LC-I와 Vitremer를, compomer로는 Dyract AP, Compoglass F 2000등이 사용되었다. 140개의 발거된 유치를 실험대상으로 각 재료의 시편을 평활하게 연마된 법랑질과 상아질 표면에 제조회사의 지시대로 부착한 후 상아질과 법랑질에 대한 상대적 전단결합강도를 측정하였다. 파절편은 실패유형 평가를 위해 주의깊게 검사되었다. 실험결과는 one-way ANOVA& Sheffe's test와 student t-test(p=0.05)로 검증하였다. 본 연구의 결과는 다음과 같았다. 1. 유치 법랑질과 상아질에 대한 전단결합강도를 측정한 결과, 법랑질에 대해서는 Z100과 Fuji II LC-I에서, 상아질에 대해서는 Z100과 Dyract AP에서 가장 높은 결합력이 나타났으며 다른 재료간에는 유의한 차이를 관찰할 수 없었다(P>0.05). 2. 각 재료내의 법랑질과 상아질에 대한 상대적 결합력을 비교평가한 결과, Dyract AP와 Vitremer를 제외한 모든 재료에서 법랑질에서 보다 높은 결합력이 관찰되었으며, Dyract AP에서는 상아질에 대한 결합력이 법랑질에 대해서보다 높게 관찰되었다(P<0.05). 3. 각 재료들의 결합실패가 일어난 파절단면을 조직학적으로 관찰한 결과, 대부분 cohesive failure를 보였고, 파절면은 치면과 매우 근접해 있었다. 일부 화학중합형 glass ionomer cement와 Vitremer에서 adhesive failure가 관찰되었다.

• Restorative Dentistry and Endodontics
• /
• 제19권1호
• /
• pp.124-134
• /
• 1994

The shade of restorative materials is very important for successful restoration esthetically harmonized with the natural tooth. The purpose of this study was to evaluate the color stability and the opacity change of conventional chemical setting and visible light curing glass-ionomer cements for restorative esthetic filling. Specimens of each brand (GC Fuji II and Fuji II LC) were uniformly prepared and divided into three groups: In group l(control group), the specimens received no surface treatment; in group 2, the specimens were coated with varnish and the excess gently blown off; and in group 3. the specimens were coated with light-cured bonding resin and irradiated by a visible light curing unit for 20 seconds on both sides. All specimens were stored in distilled water at $37^{\circ}C$ and checked after for 24 hours. 2 months. 4 months, 6 months. and 8 months. The color characteristics($L^*,\;a^*,\;b^*$) and the opacity(Y%) of all the samples were measured by a spectrocolorimeter and the total color differences(${\Delta}E^*$) and opacity changes(${\Delta}Y%$) were computed. The following results were obtained : 1. The total tolor differences in all groups increased with time. 2. The total color differences of the LC groups after immersion for 8 months in distilled water at $37^{\circ}C$ were lower than those of GC groups(p<0.01), and the total color differences of the varnish or the light-cured bonding resin coated groups were lower than those of the control group with glass-ionomer cements which had no surface treatment(p<0.01). 3. In all groups the translucency decreased with time. 4. In the control group and the varnish coating group. the opacity changes of the GC groups were lower than those of the LC groups(p<0.01) and in the light-cured bonding resin coated group, there was no significant difference between the GC group and the LC group. 5. The opacity changes of the varnish or the light-cured bonding resin coated groups were lower than those of the control group(p<0.01). These results suggest that color change and opacity of conventional chemical setting and light cured glass-ionomer cement were increased with time, and the color changes and the opacity changes of a control group after immersion for 8 months in distilled water at $37^{\circ}C$ were greater than those of the varnish or the light-cured bonding resin coated groups.