Single phase La1-xSrxCoO3 (x≤0.2) was synthesized as a uniform sized 100 nm particulates with relatively high surface area of 20-30 m2/g, at low temperature (≥600 ℃), from a polymeric gel precursors prepared by using poly(vinyl alcohol) as homogenizer. No minor phase developed during the crystallization when polymer/metal mole ratio was higher than 3. As the polymer/metal mole ratio was raised in the gel, the amount of carbonaceous residues in the amorphous solid precursor prepared by heating the gel at 300 ℃ increased. Most of the residues were eliminated by exothermic thermal decomposition around 400 ℃. The amount of residual carbon (less than 1%) left in the crystalline La1-xSrxCoO3 decreased as more polymer was used, eliminating detrimental effect which might be posed by using large amount of organic homogenizer. The crystal structure of La1-xSrxCoO3 synthesized at temperature lower than 800 ℃ was observed to be shifted from rhombohedral to more symmetric cubic. The structure shifted back to rhombohedral as the cubic sample was annealed at 1000 ℃.

• Journal of the Korean Ceramic Society
• /
• 제28권11호
• /
• pp.859-864
• /
• 1991

High quality lead titanate thin films were fabricated by spin coating on a silicon substrate. The resulting dried gel layers were uniform in thickness through 2$\times$2 $\textrm{cm}^2$ area, and polycrystalline perovskite structures developed almost crack free with a heat treatment above 50$0^{\circ}C$ in films with thickness above 360 nm. Metastable pyrochlore structures were observed in films with thickness of 160 nm when heat treated at 500 and $600^{\circ}C$, but these structure did not appear in films with thickness of 360 nm. The thickness dependence in crystal structure of films was studied. by varying the substrate condition and analyzing the interface between the film and substrate. In native oxide films on silicon stbstrates, amorphous dried gel layers were heterogeneously nucleated. Metastable cubic pyrochlore structure could be crystallized in amorphous native oxide.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 한국전기전자재료학회 1997년도 추계학술대회 논문집
• /
• pp.52-55
• /
• 1997

In this study, PLZT stock solutions were prepared by sol-gel processing to fabricate PLZT thin films. The stock solutions were spin-coated on ITO-glass and the film were annealed by rapid thermal annealing(RTA). The variation of tile crystallographic structure of the thin films and the phase transition with respect to it were observed using Raman spectra. Raman result showed that the band of spectra are broad as the amount of Zr substitution increased and specially, abrupt change occurs in the raman spectra upon crossing the tetragonal-rhombohedral phase boundry at 2/55/45 PLZT thin film. So, the fact that the crystallographic structure was transitted from tetragonal to rhombohedral structure was certified.

• Journal of the Korean Ceramic Society
• /
• 제45권10호
• /
• pp.644-650
• /
• 2008

It has been proposed that the Cao-$SiO_2$ binary system can be good basic composition of bioactive glasses and glass-ceramics. In the present study, various kinds of Cao-$SiO_2$ gels were prepared by sol-gel method in order to control the microstructure which are related to their dissolution rate, induction period of apatite formation in body environment. Characterization of the gels were done by wet chemical analysis, SEM observation, FT-IR spectroscopy and XRD. The gelation time decreased with CaO content. However, the volume of all the dried gel decreased to 50% of the wet gels irrespective of increasement of CaO content. All the Cao-$SiO_2$ gels were amorphous and contained a large amount of silanol groups on their surfaces after heat treatment up to $800^{\circ}C$. The interconnected structure of the gel changed to agglomerated spherical powders when Ca content exceed to 20 mol%. Most of the Cao-$SiO_2$ gel showed amorphous when heat-treated up to $900^{\circ}C$. However, quartz and cristobalite was produced when heat-treated at $1000^{\circ}C$ and resultant microstructure of the gel contained microporous structure.

• Proceedings of the Korea Concrete Institute Conference
• /
• 한국콘크리트학회 2008년도 추계 학술발표회 제20권2호
• /
• pp.449-452
• /
• 2008

Reinforced concrete structure with supplementary relation is a distinguished material. But in this structure, crack is generated by many factors and caused decadence of durability, safety, function, and so on. Hence structure is in need of repair. Preexistence injection of chemical grouting for using repair of crack not enough performance. In this study, Setting time test of Acryl Gel was carried out According to a Catalyzer quantity. The result of test showed that gel time of Acryl Gel decreased with the increased of catalyzer quantity. The result of this study could be used as the basic data for the repair of crack using Acryl Gel.

• Journal of the Korean Applied Science and Technology
• /
• 제21권2호
• /
• pp.164-173
• /
• 2004

The capacity and long life of gel electrolyte batteries is connected with gas recombination producting $PbO_2$ and Pb electrode. We prepared with sulfuric acid gel electrolyte to know gel characteristics per density to assemble valve regulated lead-acid (VRLA) batteries. We studied on actions of sulphuric acid gel electrolyte by measuring electrolyte dispersion using Brewster-angle microscope (BAM), charge-discharge cycle, and electrode structure using scanning election microscope (SEM). Sulphuric acid density 1.210 showed excellent gel dispersion in sol condition, electrode condition after fifty cycles in this study.

• Journal of the Korean Ceramic Society
• /
• 제45권2호
• /
• pp.126-131
• /
• 2008

In this study, we prepared zirconia gel by the sol-gel method and investigated its photoluminescence properties by varying pyrolysis temperature. The addition of acetic acid into a Zr-alkoxide solution resulted in forming the bidentate ligands with Zr ions and producing a stable gel. At the pyrolysis temperature of $350^{\circ}C$, the zirconia nanocrystals with tetragonal structure gradually appeared in the gel. The PL intensity of the zirconia gel increased with increasing the pyrolysis temperature up to $350^{\circ}C$, but decreased above the temperature. Concurrently, its PL peak wavelength continuously shifted from ${\sim}440\;nm$ to ${\sim}550\;nm$ with the temperature. The PL characteristics of the zirconia gels were closely associated with decomposition of residual organic groups, the formation of the zirconia nanocrystals, and the tetragonal to monoclinic phase transformation.

• Journal of dental hygiene science
• /
• 제10권5호
• /
• pp.373-378
• /
• 2010

To test the effects of representative fluoride vanishes-1.23% APF gel and 5% NaF Fluoride Varnish-on the surface structure of pit and fissure sealant, this study classified samples of pit and fissure sealant into five groups: Group I deposited in distilled water for ten minutes, Group II treated with APF gel for one minute, Group III treated with APF gel for four minutes, Group IV treated with Fluoride Varnish for one minute, and Group V treated with Fluoride Varnish for four minutes. An abrasion test was carried out to measure changes in weight, along with observation of the surface structure by using an optical microscope, consequently drawing the following conclusions. 1. The results of the abrasion test using pit and fissure sealant, Concise, showed that Group III had the reduction in weight more increased than Group I and that Group V had less reduction in weight (p<0.05); the results of the abrasion test using Eco-S showed Group III had the reduction in weight more increased than Group I and that Group V had less reduction in weight (p<0.05). 2. The results of observation using an optical microscope showed that application of APF gel made the filler remarkable due to loss of substrate and that Group III treated with APF gel for four minutes had the toughest surface, followed by Group II treated with APF gel for one minute, Group I deposited in distilled water for ten minutes, Group IV treated with Fluoride Varnish for one minute, and Group V treated with Fluoride Varnish for four minutes.

• Journal of the Korean Institute of Illuminating and Electrical Installation Engineers
• /
• 제23권2호
• /
• pp.168-174
• /
• 2009

In this paper Gel polymer electrolyte using Poly(Vdf-HFP) was fabricated and compared with liquid type electrolyte. The chemical structure and ingredients of fabricated gel electrolyte was investigated and identified to gel polymer electrolyte by FTIR, gel electrolyte was verified to polymer state by SEM From the experiment result, the better component ratio of Propylene carbonate and Diethyl carbonate for gel type electrolyte was 5 : 5. The conversion efficiency of fabricated DSCs using gel electrolyte was $3{\sim}4[%]$, expected to alternate with liquid type electrolyte.

• Bulletin of the Korean Chemical Society
• /
• 제33권8호
• /
• pp.2489-2493
• /
• 2012

A new fluorescent system (acridine/RTIL hybrid gel) confined in the 3D micro-structure of a poly(lactic acid) membrane were prepared from 1-butyl-3-methylimidazolium-based ionic liquids ([bmim]X (X = $SbF_6$, $NTf_2$, Cl); RTILs), poly(lactic acid) (PLA), and acridine via the sol-gel route. SEM images showed that, in the presence of [bmim]$SbF_6$ and [bmim]$NTf_2$, 3D-ly paticulated structures were created inside the PLA membranes and acridine/RTIL hybrid gels were confined in gabs of particulates. However, the use of [bmim]Cl induced the formation of a 3D-ly porous structure containing the hybrid gel of acridine/[bmimCl in the micropores. The three fluorescent systems exhibited different fluorescence behaviors (fluorescence maximum and intensity) depending on the C2-H acidity scale of the RTILs (or their anion type). Acridine gels hybridized with [bmim]$SbF_6$ and [bmim]$NTf_2$ showed blue fluorescence with relative high intensity, whereas the hybrid gel with [bmim]Cl exhibited almost no fluorescence under dry conditions. However, the acridine/[bmim]Cl hybrid system in the micro-porous PLA membrane started to emit fluorescent light under humid conditions and showed a possible response, indicating that it could be applied as a humidity sensor.