Synthesis of $La_{1-x}Sr_xCoO_3$ (x≤0.2) at Low Temperature from PVA-polymeric Gel Precursors

  • Published : 1997.12.20
Download PDF
⟨ Previous Next ⟩

Abstract

Single phase La1-xSrxCoO3 (x≤0.2) was synthesized as a uniform sized 100 nm particulates with relatively high surface area of 20-30 m2/g, at low temperature (≥600 ℃), from a polymeric gel precursors prepared by using poly(vinyl alcohol) as homogenizer. No minor phase developed during the crystallization when polymer/metal mole ratio was higher than 3. As the polymer/metal mole ratio was raised in the gel, the amount of carbonaceous residues in the amorphous solid precursor prepared by heating the gel at 300 ℃ increased. Most of the residues were eliminated by exothermic thermal decomposition around 400 ℃. The amount of residual carbon (less than 1%) left in the crystalline La1-xSrxCoO3 decreased as more polymer was used, eliminating detrimental effect which might be posed by using large amount of organic homogenizer. The crystal structure of La1-xSrxCoO3 synthesized at temperature lower than 800 ℃ was observed to be shifted from rhombohedral to more symmetric cubic. The structure shifted back to rhombohedral as the cubic sample was annealed at 1000 ℃.

Keywords

References

  1. Science v.171 Libby, W. F.
  2. Advanced Materials in Catalysis Voorhoeve, R. J. H.
  3. Adv. Catal. v.36 Tejuca, L. G.;Fierro, J. G.;Tascon, J. M.
  4. Nature v.226 Meadowcroft, D. B.
  5. J. Electrochem. Soc. v.124 Kodo, T.;Obayashi, H.;Yoshida, M.
  6. J. Am. Ceramic Soc. v.76 Minh, N. Q.
  7. Bull. Chem. Soc. Jpn. v.61 Nitadori, T.;Ichiki, T.;Misono, M.
  8. Jpn. J. Appl. Phys. v.13 Obayashi, H.;Kudo, T.;Gejo, T.
  9. Phys. Status Solidi B v.67 Marx, R.;Happ, H.
  10. J. Mater. Sci. v.17 Baythoun, M. S. G.;Sale, F. R.
  11. Chem. Lett. Zhang, H. M.;Teraoka, Y.;Yamazoe, N.
  12. J. Catal. v.98 Nitadori, T.;Kurihara, S.;Misono, M.
  13. J. Mater. Sci. v.22 Tabata, K.;Matsumoto, I.;Kohiki, S.
  14. Chem. Lett. Teraoka, Y.;Nobunaga, T.;Yamazoe, N.
  15. J. Chem. Soc., Faraday Trans. v.88 Mizuno, N.;Tanaka, M.;Misono, M.
  16. Powder Metallurgy v.1 Anderton, D. J.;Sale, F. R.
  17. Mater. Sci. Eng. v.B18 Li, X.;Zhang, H.;Chi, F.;Li, S.;Xu, B.;Zhao, M.
  18. J. Solid State Chem. v.104 Taguchi, H.;Yoshioka, H.;Matsuda, D.;Nagao, M.
  19. J. Mater. Sci. Lett. v.13 Taguchi, H.;Yoshioka, H.;Nagao, M.
  20. J. Am. Ceramic Soc. v.75 Taguchi, H.;Matsuda, D.;Nagao, M.
  21. J. Mater. Sci. Lett. v.14 Taguchi, H.;Matsuda, D.;Nagao, M.;Tabata, K.
  22. US Patent -08/298 Kweon, H. J.;Kim, K.;Chun, H. S.;Kuk, S. T.;Park, H. B.
  23. J. Mater. Sci. Lett. v.15 Kewon, H. J.;Kuk, S. T.;Park, H. B.;Park, D. G.;Kim, K.
  24. J. Mater. Sci. Lett. v.14 Saha, S. K.;Pathak, A.;Pramanik, P.
  25. Coll. Czech. Chem. Commun. v.38 Pechanec, V.
  26. Coll. Czech. Chem. Commun. v.39 Pechnec, V.
  27. J. Chem. Soc. (A) Gregg, S. J.;Ramsay, J. D.
  28. Trans. Faraday Soc. v.63 Evans, J. V.;Whateley, T. L.
  29. Infrared Spectra of Inorganic Compounds Nyquist, R. A.;Kagel, R. O.
  30. Powder Diffraction File v.36 McClune, W. F.
  31. Ceramic Bull v.68 Lessing, P. A.
  32. X-ray diffraction procedure Klung, H. P.;Alexander, L. E.
  33. Nature v.357 Kinoshita, K.;Yamada, T.
  34. Physica C v.179 Zandbergen, H. W.;Cava, R. J.;Krajewski, J. J.;Peck, W. F., Jr.
  35. Hydrogen-peroxide assisted sol-gel synthesis of forsterite and metal-doped forsterite and electrostatic spray synthesis of anatase nano-particles Park, D. G.
  36. Ceramic Processing and Sintering Rahman, M. N.