• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2017.05a
• /
• pp.119.1-119.1
• /
• 2017

Fe-(10, 24 wt.%) Gd-B 합금을 진공 주조하고 상분석과 내식성 평가 및 표면 경도를 측정하였다. 주조된 Fe-10 wt.% Gd-B 합금의 상은 주로 $Fe_2Gd$, $Fe_3Gd$, $B_4FeGd$, $GdB_2$이었으며, Fe-24 wt.% Gd-B 합금은 주로 $Fe_2Gd$, $Fe_3Gd$, $Fe_9Gd$, $Fe_{17}Gd_2$, $B_4FeGd$, $GdB_2$이었다. 인공해수 분위기에서의 부식 속도와 부식 전위는 각각 2.771, 2.914 [$mA/cm^2$]과 -623.9, -607.8 [$mV_{SHE}$]이었다. 표면 경도는 각각 220, 208 [Hv] 이었다. Gd 함량이 증가할수록 부식 속도는 증가하였고 표면 경도는 감소하는 경향을 보였다.

• Progress in Superconductivity and Cryogenics
• /
• v.23 no.2
• /
• pp.14-18
• /
• 2021

We investigated the structural suitability of GdFeO₃ (GdFO) as a buffer layer for the GdBa₂xCu₃O_7-x (GdBCO) superconducting films. GdFO films with different thicknesses and GdBCO thin films were all prepared by using a pulsed laser deposition technique. The analyses of X-ray diffraction and EXAFS data indicates that the c-axis parameter increases and the Fe-O bond length decreases with the GdFO thickness due to the compressive stain induced by the lattice mismatch between GdFO and STO substrate and as a result, the Debye-Waller factor, an index of disorder in the local structure near the Fe-O bond, increases with the GdFO thickness. However, for the GdBCO/GdFO bilayer structure, the Debye-Waller factor decreases as the GdFO thickness increases indicating a diminished disorder by the structural coupling between GdFO and GdBCO. These results indicate that an appropriate thickness of GdFO is required to be utilized as a magnetic buffer layer for the GdBCO superconducting films.

• Korean Journal of Materials Research
• /
• v.5 no.3
• /
• pp.364-370
• /
• 1995

ex-AUC U$O_{2}$ 분말과 $Gd_{2}$O_{3}$ 분말을 기계적으로 혼합하여 소결한 U$O_{2}$-$Gd_{2}$O_{3}$ 소결체의 밀도 변화와 재소결 후 밀도변화를 기공크기 및 분포의 변화로 서술하였다. 수소분위기에서 175$0^{\circ}C$, 4시간 동안 소결하였을 때, 순수 U$O_{2}$의 소결밀도는 97.2% T.D.였으나 6wt% $Gd_{2}$O_{3}$ 첨가까지는 U$O_{2}$-$Gd_{2}$O_{3}$의 소결밀도는 $U^{+4}$와 $Gd^{+4}$의 상호확산 때문에 약 90% T.D.로 급격히 감소하였다. 그러나 6wt% 이상의 $Gd_{2}$O_{3}$가 첨가되면 우라늄이온 산화아와 산소침입으로 인하여 소결밀도는 오히려 증가하였다. 1$700^{\circ}C$에서 재소결시킬 때 순수 U$O_{2}$ 소결체에서는 재소결 시간에 따라 밀도증가가 발생하였다. U$O_{2}$-$Gd_{2}$O_{3}$ 소결체 경우에는 재소결시 밀도가 감소하였으나 재소결 시간이 증가함에 따라 다시 밀도는 증가하였고, 6wt%$Gd_{2}$O_{3}$가 첨가된 U$O_{2}$-$Gd_{2}$O_{3}$ 소결체에서 밀도가 가장 많이 감소하였다.

• Progress in Superconductivity and Cryogenics
• /
• v.14 no.4
• /
• pp.28-31
• /
• 2012

We report the solid-liquid phase equilibria on the $GdBa_2Cu_3O_{7-{\delta}}$ (GdBCO) stability phase diagram in low oxygen pressures ($PO_2$) ranging from 1 to 100 mTorr. On the basis of the GdBCO stability phase diagram experimentally determined in low oxygen pressures, the isothermal sections of three different phase fields on log $PO_2$ vs. 1/T diagram were schematically constructed within the $Gd_2O_3-Ba_2CuO_y-Cu_2O$ ternary system, and the solid-liquid phase equilibria in each phase field were described. The invariant points on the phase boundaries include the following three reactions; a pseudobinary peritectic reaction of $GdBCO{\leftrightarrow}Gd_2O_3$ + liquid ($L_1$), a ternary peritectic reaction of $GdBCO{\leftrightarrow}Gd_2O_3+GdBa_6Cu_3O_y$ + liquid ($L_2$), and a monotectic reaction of $L_1{\leftrightarrow}GdBa_6Cu_3O_y+L_2$. A conspicuous feature of the solid-liquid phase equilibria in low $PO_2$ regime (1 - 100 mTorr) is that the GdBCO phase is decomposed into $Gd_2O_3+L_1$ or $Gd_2O_3+GdBa_6Cu_3O_y+L_2$ rather than $Gd_2BaCuO_5+L$ well-known in high $PO_2$ like air.

• Korean Journal of Materials Research
• /
• v.23 no.6
• /
• pp.309-315
• /
• 2013

$GdBa_2Cu_3O_{7-y}$(Gd123) powders were synthesized by the solid-state reaction method using $Gd_2O_3$ (99.9% purity), $BaCO_3$ (99.75%) and CuO (99.9%) powders. The synthesized Gd123 powder and the Gd123 powder with $Gd_2O_3$ addition ($Gd_{1.5}Ba_2Cu_3O_{7-y}$(Gd1.5)) were used as raw powders for the fabrication of Gd123 bulk superconductors. The Gd123 and Gd1.5 bulk superconductors were fabricated by sintering or a top-seeded melt growth (TSMG) process. The superconducting transition temperature ($T_{c,onset}$) of the sintered Gd123 was 93 K and the transition width was as large as 20 K. The $T_{c,onset}$ of the TSMG processed Gd123 was 82 K and the transition width was also as large as 12 K. The critical current density ($J_c$) at 77 K and 0 T of the sintered Gd123 and TSMG processed Gd123 were as low as a few hundreds A/$cm^2$. The addition of 0.25 mole $Gd_2O_3$ and 1 wt.% $CeO_2$ to Gd123 enhanced the $T_c$, $J_c$ and magnetic flux density (H) of the TSMG processed Gd123 sample owing to the formation of the superconducting phase with high flux pinning capability. The $T_c$ of the TSMG processed Gd1.5 was 92 K and the transition width was 1 K. The $J_cs$ at 77 K (0 T and 2 T) were $3.2{\times}10^4\;A/cm^2$ and $2.5{\times}10^4\;A/cm^2$, respectively. The H at 77 K of the TSMG-processed Gd1.5 was 1.96 kG, which is 54% of the applied magnetic field (3.45 kG).

• Resources Recycling
• /
• v.13 no.2
• /
• pp.24-32
• /
• 2004

Solvent extraction equilibria of Gd with PC88A from chloride solutions were analyzed by considering chemical equilibria. phase equilibria, mass and charge balance equations. The following solvent extraction reaction and equilibrium constant were evaluated from the experimental data performed in this study. $Gd^{3+}$ $+2H_2$$A_2$,$or=GdA_3$HA.or+3 $H^{+}$ , K=3.3 A procedure was suggested to calculate the initial concentration of chloride ion from initial pH and initial concentration of Gd. By applying ionic equilibria, the distribution of Gd complexes with Gd and HCl concentration was obtained. The predicted distribution coefficients of Gd agreed well with the experimental results.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.13 no.3
• /
• pp.111-116
• /
• 2003

The red emitting phosphors for low voltage cathode luminescent, fine $(Y,Gd)_2O_2$S : Eu powders were synthesized and investigated the effect of $Gd^{3+}$as sensitizer at variety of sintering temperature. The highly intense emission line of $(Y,Gd)_2O_2$S : Eu at 627 nm is attributed in the transition from $^5D_o to ^7F_2$ energy levels. It showed the maximum value at the doping level of 5 mole% of $Gd^{3+}$at $950^{\circ}C$ of sintering temperature and then, it was degraded rapidly. The mean particle size of $(Y,Gd)_2O_2$S : Eu was obtained around 1 fm and the cathode luminescent properties of (Y,Gd)$_2$O$_2$S : Eu were better than those of $(Y,Gd)_2O_2$S : Eu.

• IMMUNE NETWORK
• /
• v.3 no.2
• /
• pp.118-125
• /
• 2003

Background: Disialoganglioside GD2 is a tumor-associated antigen that is overexpressed on tumor cells of neuroectodermal origin, such as melanoma and neuroblastoma. Anti-idiotypic antibodies that mimic GD2 may induce more effective immune responses than GD2 antigen itself, because they are protein antigens and are known to be able to break immune tolerance. In this study, to explore the potential of anti-idiotypic antibodies as tumor vaccines, the ability of anti-idiotypic antibodies (Ab2) to induce anti-anti-idiotypic antibodies (Ab3) that bind to the original antigen GD2 was investigated. Methods: Six monoclonal anti-idiotypic antibodies (1A8, 1G5, 2B6, 3A4, 3D6, 3H9) to monoclonal antibody M2058, which is a monoclonal antibody to GD2, were produced in mice. Three (1A8, 3A4, 3H9) of them were selected based on their ability to inhibit the binding of Ab1 to D142.34 (murine melanoma cell expressing GD2). These 3 different Ab2 were injected into rabbits, and rabbit Ab3 induced by each of them were characterized. Results: Ab3-containing sera from two rabbits immunized with 1A8, 3A4, or 3H9 bound significantly (P<0.05) to D142.34 but not to B78.96 (GD2-negative cell), and bound significantly (P<0.05) to isolated GD2 but not to GD1a. Ab3-containing sera from two rabbits immunized with 3A4 or 3H9 inhibited significantly (P<0.05) the binding of Ab1 M2058 to D142.34, and inhibited significantly (P<0.05) the binding of Ab1 M2058 to the Ab2. Conclusion: These results suggest that anti-idiotypic antibodies 3A4 and 3H9 have a potential to be used as vaccines against tumors expressing GD2 by inducing GD2-specific antibodies (Ab3).

• Progress in Superconductivity and Cryogenics
• /
• v.20 no.4
• /
• pp.46-49
• /
• 2018

To improve in-field critical current densities ($J_c$) of $GdBa_2Cu_3O_{7-{\delta}}$ (GdBCO) coated conductors(CCs) fabricated by the reactive co-evaporation by deposition and reaction (RCE-DR) process, employing the nominal composition of Gd:Ba:Cu=1:1:2.5, we tried to refine the $Gd_2O_3$ particles trapped in the GdBCO superconducting matrix. For this purpose, we carefully selected the processing conditions on the stability phase diagram of GdBCO for this composition. By lowering the growth temperature of $Gd_2O_3$ in the liquid, we could refine the average particle size of $Gd_2O_3$ particles trapped in the GdBCO matrix and also achieve the zero-resistive transition temperatures ($T_{c,zero}$) of 92.3~94.2 K. Unfortunately, however, it was unsuccessful to achieve enhanced in-field $J_c$ values from these samples because of an air-contamination of the amorphous precursor film before its conversion into crystalline GdBCO film, suggesting that any exposure of the amorphous precursor film to air is fatal in obtaining high performance GdBCO CCs via the RCE-DR process.

• Nuclear Engineering and Technology
• /
• v.30 no.2
• /
• pp.128-139
• /
• 1998

The effect of UO$_2$ powder property and oxygen potential on characteristics of sintered UO$_2$-Gd$_2$O$_3$ fuel pellets has been investigated. Two types of powder, mixture of AUC-UO$_2$ and Gd$_2$O$_3$powders (type I) and mixture of ADU-UO$_2$ and Gd$_2$O$_3$powders (type II), have been prepared, pressed, and sintered at 168$0^{\circ}C$ for 4 hours. Four sintering atmospheres with different mixing ratios of $CO_2$to H$_2$ gas ranging from 0 to 0.3 have been used. UO$_2$-Gd$_2$O$_3$ fuel has lower sintered density than UO$_2$ fuel, and the density drop is larger for powder type I than for powder type II. As the oxygen potential increases, the sintered density of UO$_2$-2wt% Gd$_2$O$_3$pellets increases but that of UO$_2$-10wt% Gd$_2$O$_3$ pellets decreases. It is found that pores are newly formed in UO$_2$-10wt% Gd$_2$O$_3$ pellets in accordance with the decrease in density. The grain size of UO$_2$-Gd$_2$O$_3$ fuel increases and a short range G4 distribution becomes homogeneous as the oxygen potential increases. A long range ed distribution and grain structure are inhomogeneous for powder type II. The lattice parameter of (U,Gd)O$_2$solid solution decreases linearly with Gd$_2$O$_3$ content. The dependence of UO$_2$-Gd$_2$O$_3$fuel characteristics on powder type and sintering atmosphere have been discussed.