• Tribology and Lubricants
• /
• 제24권5호
• /
• pp.255-263
• /
• 2008

Adhesion tests were conducted to investigate the adhesion characteristics between mold and thermoplastic polymer film. Coating of anti-sticking layer (ASL), a kind of polymer material, imprint pressure, and separation velocity were considered as the process conditions. A piece of fused silica without patterns on its surface was used as a mold and the thermoplastic polymer films were made on Si substrate by spin-coating the commercial polymer solution such as mr-I PMMA and mr-I 7020. The ASL was derived from (1H, 1H, 2H, 2H - perfluorooctyl) trichlorosilane($F_{13}$-OTS) and coated on the fused silica mold in vapor phase. The pull-off force was measured in various process conditions and the surfaces of the mold and the polymer film were observed after separation. It was found that the adhesion characteristics between the mold and the thermoplastic polymer film and the release performance of ASL were changed according to the process conditions. The ASL was effective to reduce the pull-off force and the damage of polymer film. In cases of the mold coated with ASL, the pull-off force did not depend on imprint pressure and separation velocity.

• 한국재료학회지
• /
• 제11권2호
• /
• pp.137-145
• /
• 2001

수용액 매체에서 젤케스팅을 이용하여 복잡한 형상의 세라믹스를 제조하기 위한 새로운 공정을 연구하였다 용융실리카 분말과 첨가제로서 지르콘과 코디어라이트 조성으로 혼합된 현탁액을 electrosteric 방법으로 안정화시켰다. 슬립은 다성분계 세라믹 현탁액에 단량체, 이량체 그러고 분산제를 혼합하고, 볼밀하여 준비하였다. 슬립의 유동학적 특성을 평가하기 위해 점도를 측정하였으며 , 낮은 점도를 갖는 50vo1%의 고농도 다성분계 세라믹 슬립의 제조가 가능하였다. 슬립의 점도는 고분자 분산제의 함량과 단량체 및 이량체의 혼합비에 크게 의존하였다. 성형체는 안정화시킨 슬립을 몰드에 부어 상온에서 젤화시킨 후 $25^{\circ}C$, 80~85% 상대습도 분위기 하에서 48시간동안 건조시켜 제조하였으며 건조된 성형체에는 균열이 발생하지 않았다.

• 한국토양비료학회지
• /
• 제35권3호
• /
• pp.162-168
• /
• 2002

사질답에서 벼 재배시 강우, 관개수, 규산질비료 시용에 의한 규소의 유입량과 침투수에 의한 규소 유출량 및 벼의 규소 흡수량을 평가하기 위하여 포장조건에서 시험을 수행한 결과 Si 농도는 강우 $0.02{\sim}0.19mg\;L^{-1}$, 관개수 $8.4{\sim}8.6mg\;L^{-1}$, 침투수 $5.9{\sim}17.9mg\;L^{-1}$이었고, 강우 및 관개수로 공급된 Si의 량은 약 $28{\sim}29kg\;ha^{-1}$, 침투수로 유출된 양은 $63kg\;ha^{-1}$였다. 벼에 의한 규산의 흡수는 무처리구 $335.6kg\;ha^{-1}$, 삼요소구 $406.6kg\;ha^{-1}$, 삼요소+규산처리구는 $471.1kg\;ha^{-1}$였다. 규소의 유입량과 유출량의 차이는 무처리 $357.4kg\;ha^{-1}$, 삼요소구 $412.1kg\;ha^{-1}$, 삼요소+규산처리구 $238.2kg\;ha^{-1}$였다. 시험후 토양의 유효규산 함량은 시험전 $71mg\;kg^{-1}$에 비해 무처리구와 삼요소구는 $49{\sim}58mg\;kg^{-1}$으로 감소하였고, 삼요소+규산 처리구는 $97mg\;kg^{-1}$으로 증가하였다. 논토양으로부터 흡수하는 규소의 흡수량은 벼의 생육에 따라 다라질 수 있으나, 약 $300{\sim}350kg\;ha^{-1}$ 정도로 추정되므로, 토양에 의한 규소의 공급은 벼의 생육 및 규소의 흡수에 매우 큰 영향을 주는 것으로 판단된다.

• 한국세라믹학회지
• /
• 제35권1호
• /
• pp.23-32
• /
• 1998

전융실리카 분말로 소결하여 만든 sihca preform을 마그네슘이 함유된 용융 알루미늄에 침적시킨후 공기중에서 반응시켜 Al2O3/Al 복합체를 제조하였다. 복합체 제조시 반응온도의 변화에 대해 용융 알루미늄의 침투거동을 조사한 결과 3가지 영역, 즉 저온영역(75$0^{\circ}C$-85$0^{\circ}C$), 중온영역(90$0^{\circ}C$-95$0^{\circ}C$), 고온영역(100$0^{\circ}C$$\leq$)으로 구분되었다. 저온영역에서는 반응온도에 비례해서 침투속도가 증가하였으나, 중간온도 영역은 치환반응에 의해 생성된 알루미나의 상전이에 따른 영향으로 저온영역인 85$0^{\circ}C$에서보다 오히려 침투속도가 감소하였다. 고온영역중 100$0^{\circ}C$이상에서 침투가 일어나지 않는 것은 용융 알루미늄중의 마그네슘이 먼저 실리카와 반응하여 silica preform의 표면에 치밀한 스피넬층을 형성하기 때문으로 판명되었다.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2008년도 하계학술대회 논문집 Vol.9
• /
• pp.158-158
• /
• 2008

모바일 정보통신기기를 중심으로 실장모듈의 초소형화, 고집적화로 인해 접속단자의 피치가 점점 미세화 됨에 따라 플립칩 본딩용 접착제에 함유되는 무기충전제인 실리카 필러의 크기도 미세화되고 있다. 본 연구에서는 NCP (non-conductive paste)의 실리카 필러의 크기가 COB(chip-on-board) 플립칩 패키지의 신뢰성에 미치는 영향을 조사하였다. 실험에 사용된 실리카 필러는 Fused silica 3 종과 Fumed silica 3종이며 response surface 실험계획법에 따라 혼합하여 최적의 혼합비를 정하였다. 테스트베드로 사용된 실리콘 다이는 투께 $700{\mu}m$, 면적 5.2$\times$7.2mm로 $50\times50{\mu}m$ 크기의 Au 도금범프를 $100{\mu}m$ 피치, peripheral 방식으로 형성시켰으며, 기판은 패드를 Sn으로 finish 하였다. 기판을 플라즈마 전처리 후 Panasonic FCB-3 플립칩 본더를 이용하여 플립칩 본딩을 수행하였다. 패키지의 신뢰성 평가를 위해 $-40^{\circ}C{\sim}80^{\circ}C$의 열충격시험과 $85^{\circ}C$/85%R.H.의 고온고습시험을 수행하였으며 Die shear를 통한 접합 강도와 4-point probe를 통한 접속저항을 측정하였다.

• 한국정보디스플레이학회:학술대회논문집
• /
• 한국정보디스플레이학회 2004년도 Asia Display / IMID 04
• /
• pp.552-554
• /
• 2004

Barrier ribs of plasma display panel (PDP) are glass matrix composite reinforced with alumina particles. Mechanical properties of the ribs are very crucial for the improvement in reliability of the panel as the ribs might fracture during transportation and service. In this study, therefore, the effects of filler type and content on the mechanical properties of the ribs were investigated. The fillers used include $Al_2O_3$, $TiO_2$, $ZrO_2$ and fused silica. The content of the filler was changed from 0 to 40 vol.%. The mechanical properties of the ribs measured were hardness, Young's modulus, fracture toughness, and 3-point bending modulus. The fracture toughness evaluated by micro-Vicker's indentation of the composites, in general, was measured to increase with the content of the filler until the sintered density does not decrease significantly. The improvement, however, was dependent on the type of filler employed.

• 한국환경과학회지
• /
• 제12권4호
• /
• pp.477-480
• /
• 2003

Pesticides were extracted from samples with 70% acetone and methylene chloride in order, and then cleaned up via open-column chromatography apparatus packed with florisil, and finally analyzed simultaneously the organochlorine and pyrethroid pesticides using GC(ECD). An ultra-2 fused silica capillary column was used to separate and identify the products. The resolution between the last isomeric peak of cypermethrin(59.987min) and the first isomeric peak of flucythrinate(60.043min) was not satisfactory. The last isomeric peak of fenvalerate(62.344min) and the first isomeric peak of fluvalinate(62.397min) were overlapped. Recoveries of soybean sample fer the most pesticides were 73.3% to 102.4%. Detection limits were between 0.004 and 0.063 ${\mu}$g/mg when this method was used.

• 한국재료학회지
• /
• 제17권6호
• /
• pp.303-307
• /
• 2007

ZnO thin films were prepared by pulsed laser deposition on amorphous fused silica substrates at different ambient $O_2$ pressures varying from 0.5 to 500 mTorr, to observe the effect of ambient gas on their crystalline structure, morphology and optical properties. Results of X-ray diffraction, scanning electron microscopy, atomic force microscopy and photoluminescence studies showed that crystallinity, surface features and optical properties of the films significantly depended on the oxygen background pressure during growth. A low oxygen pressure (0.5 mTorr) seems to be suitable for the growth of highly c-axis oriented and smoother films possessing a superior luminescent property. The films grown at the higher $O_2$ pressures (50-500 mTorr) were found to have many defects probably due to an excessive incorporation of oxygen into ZnO lattice. We speculate that the film crystallinity could be affected by the kinetics of atomic arrangement during deposition at the higher oxygen pressures.

• 대한화학회지
• /
• 제28권4호
• /
• pp.244-250
• /
• 1984

산${\cdot}$염기용매분배법과 규소산 칼럼 크로마토그라피법 및 용융 실리카모세관 칼럼크로마토그라피, 질량분석법을 사용하며 셀룰로오스와 리그닌의 열분해생성물중의 여러고리 방향족 화합물의 분리와 동정을 수행하였다. 16가지의 여러고리 방향족 화합물이 머무른 계수와 질량스펙트럼데이타에 의해서 확인되었다. 두가지 물질 모두에서 같은 종류의 여러고리 방향족 화합물이 생성되었으며, 그 함량에 있어서는 리그닌에서 훨씬 많은량이 생성되었다. 극히 발암성인 질소 및 유황을 함유하는 헤테로 고리 방향족 화합물은 거의 생성되지 않았다.

• Mass Spectrometry Letters
• /
• 제4권4호
• /
• pp.83-86
• /
• 2013

A new interface for coupling CIEF and MS using a four-way cross has been developed in a single mechanical system. This new interface could be operated without the electric discontinuity and reinstallation of lines. Additionally, a bare fused silica capillary was facilitated as a spray needle to produce electrospray and to guide catholyte or sheath liquid. Focusing for CIEF was completed in a hanging droplet at the end of spray needle. This capillary spray needle also provided stable spray, enhanced the ionization efficiency and increased sensitivity. Results with carbonic anhydrase I showed that focusing and spraying were well completed with the new interface and the new spray needle.