• Journal of the Korea Academia-Industrial cooperation Society
• /
• v.14 no.8
• /
• pp.4033-4038
• /
• 2013

Sedimentary rocks from construction waste are discarded through open storage and landfilling, which causes an increase in construction cost and inefficient of execution of works. Some sandstone are selected and utilized as aggregates, but shale is buried as industrial waste. Therefore, in this research, we evaluated weathering properties of shale aggregate that is widely distributed throughout Daegu-Kyeongbuk region and freeze-thaw characteristics of concrete according to the replacement ratio of shale aggregate, in an effort to stabilize aggregate supply-demand in Daegu-Kyeongbuk region and develop alternative aggregates. We used red shale and black shale in the experiment, which were exported from a construction site in Deagu. We verified the usage of shale as a concrete aggregate by comparing andesite, which is broadly used as a thick aggregate for concrete, to hornfels, which is a metamorphic sedimentary rock. As a result of the experiment, we observed no degradation phenomenon for andesite and hornfels. However, a part of country rock containing black shale was found to be exfoliated. Red shale started having cracks in the direction of stratification after 1.5 months of direct exposure, and it broke into smaller pieces after approximately 4 months. After 300 cycles of freeze-thaw process on the concrete manufactured according to the replacement ratio of shale aggregate, the modulus of elasticity was 97% for plain and 95% for hornfels. In the case of RS_100, it was 57% after 210 cycles, and for BS_100, it was 54% after 240 cycles. Therefore, we established that, as the number of repetition increases, the freeze-thaw resistance decreases dramatically.

• International Journal of Highway Engineering
• /
• v.17 no.4
• /
• pp.77-87
• /
• 2015

PURPOSES: It is theoretically well known all over the world, that porous hot mixed asphalt (HMA) with hydrated Lime improves moisture and rutting resistance, and reduces pothole occurrence frequency, as well as the life cycle cost (LCC). METHODS : Addictive in the two different formations of the liquid anti-stripping Agent and powder Hydrated-Lime was applied in this investigation in order to obtain relatively clear results according to their types and conditions. Firstly, the moisture conditions were set, and applied to the porous HMA mixtures with hydrated lime (anti-stripping agent). Next, it was followed by a non-destructive test with the application of three freeze-thaw cycles, which were individually carried out thrice to compare the results of the dynamic moduli. Lastly, the hydrated lime effect related to moisture sensibility to porous HMA has been verified through the analysis of the modulus results regarding the change rate of dynamic modulus per n-cycle. RESULTS: It is clear from this investigation, that the dynamic modulus is inversely proportional to the change in temperature, as the graph representing the rigidity of the thermorheologically simple (TRS) material showed gradual decline of the dynamic modulus with the increase in temperature. CONCLUSIONS: The porous HMA mixture with the anti-stripping agent (hydrated Lime) has been found to be more moisture resistant to freezing and thawing than the normal porous HMA mixture. It is clear that the hydrated lime helps the HMA mixture to improve its fatigue resistance.

• Journal of the Korean Recycled Construction Resources Institute
• /
• v.7 no.1
• /
• pp.69-75
• /
• 2012

The study was conducted to determine the effects of adding pig blood as an admixture to both mortar and concrete. The mortar tests included the determination of its unit weight, flow and its compressive strength. Moreover, the concrete test includes the determination of air content, slump, bleeding, setting time compressive strength and freeze-thaw resistance of the material. As the test result, the utilization of pig blood, as an additive to both mortar and concrete mixtures causes air entrainment. The mortar flow increased and both the unit weight and the compressive strength of mortar decreased. As the blood replacement rate increases, the air content decreases over time, the setting and amount of bleeding showed a tendency to decline and reduced compressive strength, and the freeze-thaw resistance of the concrete increased.

• Korean journal of food and cookery science
• /
• v.27 no.5
• /
• pp.507-522
• /
• 2011

In this study, samples of wheat flour and dough were prepared by adding of 1, 3, or 5% branched dextrin, which is produced from the amylopectin of waxy corn starch using a cyclization reaction with a branching enzyme. The samples were then evaluated qualitatively in terms of farinogram, viscogram, and extensogram characteristics. The fermentation power of dough expansion, extensogram characteristics, specific volume, baking loss, external/internal surface appearance, and sensory qualities were also examined after 4 weeks of storage at -20$^{\circ}C$ to determine the effect on freeze-thaw stability and quality improvement of branched dextrins in the soft roll bread formulation. Furthermore, the samples along with a control were compared regarding their quality characteristics, including changes in moisture content, water activity, color, and textural characteristics during a storage period of 4 days at 20$^{\circ}C$ to determine the effect on preventing retrogradation of the branched dextrin. As the branched dextrin content increased, area and extensibility increased, whereas water absorption, fermentation power of dough expansion, resistance/extensibility ratio, baking loss, and brownness of the crust decreased. However, the control group presented significantly higher peak viscosity, resistance, specific volume, taste, overall acceptability, moisture content, water activity, springiness, cohesiveness, and resilience values than those of the branched dextrin samples, whereas lightness, hardness, and chewiness showed the reverse effect. As the storage period increased, lightness, hardness, and chewiness increased, whereas cohesiveness decreased. In conclusion, the results indicate that adding 1~3% branched dextrin into a soft roll bread formulation from frozen dough had no positive effect on freeze-thaw stability or preventing retrogradation but may provide good nutritional properties.

• Journal of the Architectural Institute of Korea Structure & Construction
• /
• v.35 no.9
• /
• pp.199-206
• /
• 2019

Experimental study on the durability characteristics to examine the feasibility of concrete with high water-tightness and self-healing performance to minimize maintenance of concrete for artificial ground is as follows. 1) When blending agent, swelling agents, and curing accelerator were added on the ternary system cement with blast-furnace slag fine particles and fly ash to give a self-healing property, higher blending strengths by 82% at design standard strength of 24MPa and by 74% at design strength of 30MPa, respectively could be obtained. 2) The permeability test for the specimens having high water-tightness and no shrinkage showed that the permeability was reduced at maximum of 98%. However, the permeability was decreased as the design strength was increased, showing the reduction rate of 87% at the design strength of 50MPa. 3) The depth of carbonation of blast-furnace slag and fly ash was increased in all the specimens compared with those of OPC only. However, as the material age was increased, carbonation penetration depth was decreased compared with the reference blend. 4) Compared with the reference blending using only OPC, the freeze-thaw resistance was higher in the case of blending with 40% of blast-furnace slag and 10% of fly ash at the design standard strength of 50MPa. In addition, the freeze-thaw resistance in general was superior in the design standard strength of 50MPa with the lower water-binder ratio (W/B) as compared with the design standard strength of 24MPa and 30MPa with the high water-binder ratios.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2003.11a
• /
• pp.54-57
• /
• 2003

Scaling deterioration of port concrete structures due to the combined effects of chemical actions by seawater and the freeze-thaw action is also a problem which has not yet been fundamentally solved. Furthermore, deterioration of concrete surface was considered as accelerate factor of concrete durability tended to decrease. Therefore, we considered the scaling measuring method and decreasing influence of durability of concrete according to kind of binders, such as OPC, Slag, Slag+Fa, due to freeze and haw of sea water. As a results of this study, it was effective method of scaling deterioration of concrete, and confirmed the salt deterioration resistance effect to use slag binder against to sea water.

• Journal of the Society of Disaster Information
• /
• v.20 no.2
• /
• pp.390-397
• /
• 2024

Purpose: In this study, PCM was used to give thermal performance to concrete and analyze its effect on durability to prevent disasters that may occur in concrete when exposed to hot and cold environments. Method: After preparing concrete specimens containing 10, 30, and 50% of the two types of PCMs compared to the cement volume, the pore volume, freeze melting resistance, and scaling resistance were evaluated. Result: Regardless of the type, when PCM powder was mixed with concrete, the amount of pores decreased, and when 10% and 30% were mixed, the freeze-melting resistance was also improved. It was also confirmed that the higher the mixing amount, the better the scaling resistance. Conclusion: When mixing powdered PCM into concrete, it is believed that durability can be improved to a certain level by the filling effect, and additional various studies should be supported for actual field application.

• Journal of the Korea Concrete Institute
• /
• v.14 no.3
• /
• pp.307-314
• /
• 2002

Utilization of demolished-concrete as recycled aggregate has been researched for the purpose of substituting for insufficient natural aggregate, saving resources and protecting environment. There, however, are some Problems not only the large difference of dualities in recycled aggregates but also a little deterioration of mechanical properties in recycled aggregate concrete in comparison with that of natural aggregate concrete. In this study, the test results of freez and thaw durability of concrete with demolished-concrete recycled aggregate(DRA) arc as follows. Improvement of crushing process is an important assignment because that adhered mortar on source-concrete recycled aggregate(SRA) and DRA highly affects thc qualifies of recycled aggregate. The compressive strength of recycled aggregate concrete was not highly different in comparison with that of control concrete. But the resistance to penetration of Cl in recycled aggregate concrete was shown smaller than that of control concrete because of adhered mortar on recycled aggregate. The resistance to frcezing and thawing of recycled aggregate concrete was highly different due to adhered mortar on recycled aggregate, and durability factor of concrete with NA-SRA and DRA was more decreased than that of control concrete. On the other hand, durability factor of concrete with AA-SRA was larger than that of control concrete. It, therefore, is necessarily required that recycled aggregate including adequate entrained air should be used for satisfying the freez and thaw durability of recycled aggregate concrete.

• Proceedings of the Korea Concrete Institute Conference
• /
• 1997.10a
• /
• pp.339-344
• /
• 1997

During recent years the durability of concrete structures has attracted considerable interest in concrete practice, material research and long-term deformation. To preserve the brittleness of concrete as well as energy absorption and impact resistance, amount of fiber usage has greatly increased year to year in the field of public works. When fly ash, fine powder, mixed into concrete, it condensed the void of concrete structure. Expecially, there's a great effect for strength improvement of concrete by initial pozzolanic reactions. Pozzolan reaction, between cement particle and fly ash, can elaborate the micro structure of matrix. So it was able to improve the effect of fiber reinforced by increased adhesion between cement paste and steel fiber. And so, in this paper, we dealt SFRC for the purpose of efficiently using of industrial by-products and its economical manufacturing. Also we performed the test for durability such as chemical resistance, freeze-thaw resistance and accelerated carbonation of SFRC using fly ash.

• Advances in concrete construction
• /
• v.9 no.4
• /
• pp.367-374
• /
• 2020

Concrete surfaces, industrial floors, sidewalks, roads and parking lots are typically subjected to abrasions. Many studies indicated that the abrasion resistance is directly related to the ultimate strength of the cured concrete. Chemical reactions, freeze-thaw cycles, and damages under abrasion are among many factors negatively affecting the concrete strength and durability. One of the major solutions to address the abrasive resistance of the concrete is to use fibers. Fibers are used in the concrete mix to improve the mechanical properties, strength and limit the crack propagations. In this study, implementation of the steel fibers in concrete to enhance the abrasive resistance of the concrete is investigated in details. The abrasive resistance of the concrete with and without steel fibers is studied with the sandblasting technique. For this purpose, different concrete samples are made with various hooked steel fiber ratios and investigated with the sandblasting method for two different strike angles. In total, 144 ASTM verified cube samples are investigated and it is shown that those samples with the highest steel fiber ratios have the highest abrasive resistance. In addition, the experiments determine that there is a meaningful correlation between the steel fiber percentage in the mix, strike angle and curing time which could be considered for improving structural behavior of the fiber-reinforced concrete.