• 한국콘크리트학회:학술대회논문집
• /
• 한국콘크리트학회 2001년도 가을 학술발표회 논문집
• /
• pp.719-724
• /
• 2001

In this study, wedge splitting tensile test(WST) using dye penetration method was carried out to investigate cracking criterion and fracture characteristics of concrete. For the this purpose, three levels of compressive strength of 180, 300 and 600 kgf/$\textrm{cm}^2$ and five testing age of 1, 3, 7, 14 and 28 days were selected as test variables. The specimen was loaded in a controlled manner and then dye was inserted at the load of 40%, 70% of the presumed peak load and at the load of 90% just after peak load. The fracture process zone was measured at each load step of a specimen. Test results were compared with analytic results by linear elastic fracture mechanics(LEFM) and numerical results through fictitious crack model(FCM) and finite element method(FEM).

• 콘크리트학회지
• /
• 제9권4호
• /
• pp.187-196
• /
• 1997

시멘트를 기초로하는 복합재료의 파괴거동은 주균열이 진행하기 이전에 파괴진행영역이라고 하는 미세균열대가 콘크리트 내부에 형성고기 때문에 선형파괴역하게 입각하여 해석하게 되면 실험치와 상당한 차이를 나타낸다. 이러한 문제점을 해결하기 위해 가상균열모델이나 균열띠 모델, 두 파라메터 파괴모델 등 비선형해석에 따른 여러 파괴역학모델들이 제안되었으나 이들 모델들은 2차원 해석에 근거를 두고 있기 때문에 구조체의 두께 방향으로 동일한 균열이 형성되며, 특히 콘크리트 실험에서 관찰되는 비연속적 균열발생에 대해서 설며이 어려웠다. 이에 본 연구는 콘크리트를하나의 다종복합체로 가정하고 연립변형모드 및 진행파괴모드 방향으로 구성재료를 배열한 상태에서 가상균열 이론에 근거한 비선형해석방법으로 모델링하였다. 진행파괴모드로 구성재료를 배열하면 강성이 높은 구성재료를 통과하여 균열이 진행될 때 균열선단으로부터 분포된 응력이 상층의 허용인장강도를 초과하게 되어 균열이 발생되며 이러한 균열은점진적인 균열진행과는 달리 비연속 동시 발생 균열ㄹ로 나타났다. 본 연구는 진행파괴모드에서의 파괴 해석 방법과연립변형모드에서의 해석 방법을 제시하였으며, 해석결과를 실험결과와 비교함으로써 검증하였다.

• 한국펄프종이공학회:학술대회논문집
• /
• 한국펄프종이공학회 1999년도 Pre-symposium of the 10th ISWPC Recent Advances in Paper Science and Technology
• /
• pp.232-238
• /
• 1999

The reinforcement of wheat straw pulp sheets with softwood kraft was studied, with special emphasis on the impact of softwood kraft beating and the proportion softwood kraft in straw pulp. the reinforcement was evaluated by measuring the tensile stiffness sand in-plane fracture behavior of samples. the results were compared with a mechanical pulp (TMP) and with a hardwood birch kraft, both reinforced with the same softwood kraft. Wheat straw pulp forms strong interfiber bonds. Therefore, its tensile stiffness and tensile strength are larger than TMP used. In-plane tear tests showed that a pure wheat straw pulp sheet has low fracture energy and correspondingly a narrow fracture process zone. The fracture energy of the reinforced straw sheets was found to increase linearly with the proportion of both unbeaten and beaten softwood pulps.

• Structural Engineering and Mechanics
• /
• 제80권5호
• /
• pp.553-562
• /
• 2021

In this paper, a hybrid scaled boundary finite element and finite volume method (SBFEM-FVM) is proposed for simulating hydraulic-fracture propagation in brittle concrete materials. As a semi-analytical method, the scaled boundary finite element method is introduced for modelling concrete crack propagation under both an external force and water pressure. The finite volume method is employed to model the water within the crack and consider the relationship between the water pressure and the crack opening distance. The cohesive crack model is used to analyse the non-linear fracture process zone. The numerical results are compared with experimental data, indicating that the F-CMOD curves and water pressure changes under different loading conditions are approximately the same. Different types of water pressure distributions are also studied with the proposed coupled model, and the results show that the internal water pressure distribution has an important influence on crack propagation.

• 콘크리트학회논문집
• /
• 제12권1호
• /
• pp.3-12
• /
• 2000

A fracture energy concept proposed by Ouyang and Shah's fracture mechanics approach was used to predict cracking of reinforced concrete members subjected to tension. In this approach, fracture properties in plain concrete which incorporate the presence of the fracture process zone are first determined from the generalized size effect method, then fracture energy required for crack propagation with the same dimension and material properties are evaluated using an R-curve. Subsequently taking into account the material properties in Ouyang and Shah's approach, a theoretical analysis to predict the mechanical behavior of reinforced concrete members subjected to tension was performed and compared to observed experimental results. It is seen that the predicted average crack spacing curves agree well with the experimental results, whereas the analytical method seems to predict lower values for this study. The analytical approach predicts well responses of stress-strain curves before and after the first crack is formed. It is concluded from this study that a fracture energy concept based on the R-curve and the generalized size effect method is a rational approach to predict cracking of reinforced concrete members subjected to tension.

• Journal of Welding and Joining
• /
• 제8권4호
• /
• pp.46-57
• /
• 1990

TMCP steel manufactured by controlled rolling followed by accelerated cooling process is known to have extra-ordinary mechanical properties such as tensile strength and toughness. However, there is much uncertainty about the fatigue fracture characteristics, especially, in the welded state of this steel. In case of this steel, the softening zone by welding is generated in heat affected zone in contrast with the case of conventional normalized high strength steel. This softening zone is considered to play significant roles in low cycle fatigue fracture of the welded part of this steel. In this paper, the low cycle fatigue behaviors of TMCP steel were inspected in as-received and welded state using the smooth specimen. The fatigue life-time was seperately investigated on the basis of failure of the specimen and crack initiation which is detected by differential strain method. Moreover, the low cycle fatigue characteristics of TMCP steel were quantitatively compared with those of the conventional normalized steel of same strength level.

• 대한기계학회:학술대회논문집
• /
• 대한기계학회 2003년도 춘계학술대회
• /
• pp.43-48
• /
• 2003

The problem of welding stresses and fatigue behavior is the main concerns of welding research fields. The residual stresses and distortion of structures by welding is exert negative effect on the safety of mechanical structures. That is, expansion of material by high temperature and distortion by cooling during welding process is caused of tensile and compressive residual stresses on welding material, and this residual stresses reduce fracture and fatigue strength of welding structures. The accurate prediction of residual stress and relaxation due to loading and post weld heat treatment of weld zone is very important to improve the quality of weldment. In this study, a finite element modeling technique is developed to simulate the relaxation of residual stresses due to loading and post weld heat treatment of weld zone. The accuracy of finite element models is evaluated based on experimental results and the results of the analytical solution.

• 한국철도학회:학술대회논문집
• /
• 한국철도학회 2002년도 추계학술대회 논문집(I)
• /
• pp.225-231
• /
• 2002

The problem of welding stresses and fatigue behavior is the main concerns of welding research fields. The residual stresses and distortion of structures by welding is exert negative effect on the safety of mechanical structures. That is, expansion of material by high temperature and distortion by cooling during welding process is caused of tensile and compressive residual stresses on welding material, and this residual stresses reduce fracture and fatigue strength of welding structures. The accurate prediction of residual stress and redistribution due to fatigue crack propagation of weld zone is very important to improve the quality of weldment. In this study, a finite element modeling technique is developed to simulate the redistribution of residual stresses due to fatigue crack propagation of weld zone.

• 한국터널지하공간학회 논문집
• /
• 제17권3호
• /
• pp.189-204
• /
• 2015

본 논문에서는 축소 모형실험을 이용한 파쇄대의 공간적 분포 특성이 터널의 거동에 미치는 영향에 대한 내용을 다루었다. 모형실험 조건으로 터널과 파쇄대의 이격 거리 및 지표면과 이루는 경사에 대해서 실험을 수행하였다. 터널 시공 과정을 압축공기기법으로 모사하였으며 실험 중에 터널의 내부 압력을 제거 하는 동시에 터널 및 지반에 발생하는 변형을 모니터링 하였다. 실험 결과 파쇄대 이격 거리에 따라서 터널 거동에 영향을 미치며 파쇄대가 수직일 경우 터널에 가장 큰 영향이 발생하며 파쇄대 경사 45도에서 가장 작은 영향이 발생하는 것으로 나타났다.

• Nuclear Engineering and Technology
• /
• 제55권11호
• /
• pp.4112-4119
• /
• 2023

This study employs the microshear test method to examine the local mechanical properties of narrow-gap welded joints, revealing the mechanical inhomogeneity by evaluating the microshear strength, stress-strain curves, and failure strain. On this basis, the influence of weld joints micromechanical inhomogeneity on the crack tip opening displacement (CTOD) fracture toughness is investigated. From the root weld layer to the cover weld layer, the fracture toughness at the center of the weld seam demonstrates an increasing trend, with the experimental and calculated CTOD values showing a good correspondence. The microproperties of the welded joints significantly impact the load-bearing capacity and fracture toughness. During the deformation process of the "low-matching" microregions, the plastic zone expansion is hindered by the surrounding microregion strength constraints, thus reducing the fracture toughness. In contrast, during the deformation of the "high-matching" microregions, the surrounding microregions absorb some of the loading energy, partially releasing the concentrated stress at the crack tip, which in turn increases the fracture toughness.