• 대한토목학회논문집
• /
• 제14권6호
• /
• pp.1319-1327
• /
• 1994

레일강에 있어서 피로균열은 레일의 파괴와 그에 따른 열차탈선의 근본적인 요인으로서 실험실시험의 분석 결과에 의한 피로거동 및 파괴특성의 정량적 평가는 피로수명 추정 및 안전조사 주기설정의 기본이 된다. 따라서 본 연구에서는 살피충격시험의 결과로부터 레일강의 샬피거동 및 파괴인성거동을 평가하고 일정진폭하중하에서 피로시험의 분석 결과로부터 피로균열성장거동에 미치는 균열의 방향성, 온도, 그리고 응력비 R의 효과를 파괴역학적 수법을 도입하여 평가하였다.

• Journal of Mechanical Science and Technology
• /
• 제15권1호
• /
• pp.26-34
• /
• 2001

Most research to date concerning the cryogenic toughness of austenitic stainless steels has concentrated on the base metal and weld metal in weldments. The most severe problem faced on the conventional austenitic stainless steel is the thermal aging degradation such as sensitization and carbide induced embrittlement. In this paper, we investigate the cryogenic toughness degradation which can be occurred for austenitic stainless in welding. The test materials are austenitic stainless JN1, JJ1 and JK2 steels, which are materials recently developed for use in nuclear fusion apparatus at cryogenic temperature. The small punch(SP) test was conducted to detect similar isothermally aging condition with material degradation occurred in service welding. The single-specimen unloading compliance method was used to determine toughness degradation caused by thermal aging for austenitic stainless steels. In addition, we have investigated size effect on fracture toughness by using 20% side-grooved 0.5TCT specimens.

• Structural Engineering and Mechanics
• /
• 제19권5호
• /
• pp.519-533
• /
• 2005

The numerical simulations on the influence of mesoscopic structures on the macroscopic strength and fracture characteristics are carried out based on that the concrete is assumed to be a three-phase composite composed of matrix (mortar), aggregate and bond between them by using a numerical code named MFPA. The finite element program is employed as the basic stress analysis tool when the elastic damage mechanics is used to describe the constitutive law of meso-level element and the maximum tensile strain criterion and Mohr-Coulomb criterion are utilized as damage threshold. It can be found from the numerical results that the bond between matrix and aggregate has a significant effect on the macroscopic mechanical performance of concrete.

• 한국해양공학회:학술대회논문집
• /
• 한국해양공학회 2004년도 학술대회지
• /
• pp.326-330
• /
• 2004

Thermosetting matrix composites have disadvantages in terms of moulding time, repairability and manufacturing cost. Thus the high-performance thermoplastic composites to eliminate such disadvantages have been developed so far. As a result of environmental and economical concerns, there is a growing interest in the use of thermoplastic composites. However, since their mechanical properties are very sensitive to the environment such as moisture, temperature etc., those behaviors need to be studied. Particularly the temperature is a very important factor influencing the mechanical behavior of thermoplastic composites. The effect of temperature have not yet been fully quantified. Since engineering applications of reinforced composites necessitate their fracture mechanics characterization, work is in progress to investigate the fracture and related failure behavior. An approach which predicts the tensile strength was perpormed in the tensile test. The main goal of this work is to study the effect of temperature on the result of tensile test with respect to GF/PE composite. The tensile strength and failure mechanisms of GF/PE composites were investigated in the temperature range $60^{\circ}C\;to\;-50^{\circ}C$. The tensile strength increased as the fiber volume fraction ratio increased. The tensile strength showed the maximum at $-50^{\circ}C$, and it tended to decrease as the temperature increased from $-50^{\circ}C$. The major failure mechanisms was classified into the fiber matrix debonding, the fiber pull-out, the delamination and the matrix deformation.

• The Journal of Advanced Prosthodontics
• /
• 제10권1호
• /
• pp.65-72
• /
• 2018

PURPOSE. The aim of this in vitro study was to investigate the fracture resistance under chewing simulation of implant-supported posterior restorations (crowns cemented to hybrid-abutments) made of different all-ceramic materials. MATERIALS AND METHODS. Monolithic zirconia (MZr) and monolithic lithium disilicate (MLD) crowns for mandibular first molar were fabricated using computer-aided design/computer-aided manufacturing technology and then cemented to zirconia hybrid-abutments (Ti-based). Each group was divided into two subgroups (n=10): (A) control group, crowns were subjected to single load to fracture; (B) test group, crowns underwent chewing simulation using multiple loads for 1.2 million cycles at 1.2 Hz with simultaneous thermocycling between $5^{\circ}C$ and $55^{\circ}C$. Data was statistically analyzed with one-way ANOVA and a Post-Hoc test. RESULTS. All tested crowns survived chewing simulation resulting in 100% survival rate. However, wear facets were observed on all the crowns at the occlusal contact point. Fracture load of monolithic lithium disilicate crowns was statistically significantly lower than that of monolithic zirconia crowns. Also, fracture load was significantly reduced in both of the all-ceramic materials after exposure to chewing simulation and thermocycling. Crowns of all test groups exhibited cohesive fracture within the monolithic crown structure only, and no abutment fractures or screw loosening were observed. CONCLUSION. When supported by implants, monolithic zirconia restorations cemented to hybrid abutments withstand masticatory forces. Also, fatigue loading accompanied by simultaneous thermocycling significantly reduces the strength of both of the all-ceramic materials. Moreover, further research is needed to define potentials, limits, and long-term serviceability of the materials and hybrid abutments.

• Nuclear Engineering and Technology
• /
• 제44권7호
• /
• pp.791-798
• /
• 2012

Since standardized fracture test specimens cannot be easily extracted from in-service components, several alternative fracture toughness test methods have been proposed to characterize the deformation and fracture resistance of materials. One of the more promising alternatives is the local approach employing the SP(Small Punch) testing technique. However, this process has several limitations such as a lack of anisotropic yield potential and tediousness in the damage parameter calibration process. The present paper investigates estimation of ductile fracture resistance(J-R) curve by FE(Finite Element) analyses using an anisotropic damage model and enhanced calibration procedure. In this context, specific tensile tests to quantify plastic strain ratios were carried out and SP test data were obtained from the previous research. Also, damage parameters constituting the Gurson-Tvergaard-Needleman model in conjunction with Hill's 48 yield criterion were calibrated for a typical nuclear reactor material through a genetic algorithm. Finally, the J-R curve of a standard compact tension specimen was predicted by further detailed FE analyses employing the calibrated damage parameters. It showed a lower fracture resistance of the specimen material than that based on the isotropic yield criterion. Therefore, a more realistic J-R curve of a reactor material can be obtained effectively from the proposed methodology by taking into account a reduced load-carrying capacity due to anisotropy.

• 수산해양기술연구
• /
• 제39권2호
• /
• pp.158-163
• /
• 2003

Thermosetting matrix composites have disadvantages in terms of moulding time, repairability and manufacturing cost. Thus the high-performance thermoplastic composites to eliminate such disadvantages have been developed so far. As a result of environmental and economical concerns, there is a growing interest in the use of thermoplastic composites. However, since their mechanical properties are very sensitive to the environment such as moisture, temperature etc., those behaviors need to be studied. Particularly the temperature is a very important factor influencing the mechanical behavior of thermoplastic composites. The effect of temperature have not yet been fully quantified. Since engineering applications of reinforced composites necessitate their fracture mechanic characterization, work is in progress to investigate the fracture and related failure behavior. An approach which predicts the tensile strength was perpormed in the tensile test. The main goal of this work is to study the effect of temperature on the result of tensile test with respect to GF/PE composite. The tensile strength and failure mechanisms of GF/PE composites were investigated in the temperature range 6$0^{\circ}C$ to -5$0^{\circ}C$. The tensile strength increased as the fiber volume fraction ratio increased. The tensile strength showed the maximum at -5$0^{\circ}C$, and it tended to decrease as the temperature increased from -5$0^{\circ}C$. The major failure mechanism was classified into the fiber matrix debonding, the fiber pull-out, the delamination and the matrix deformation.

• Composites Research
• /
• 제35권2호
• /
• pp.61-68
• /
• 2022

복합재료는 비강도, 비강성 및 내부식성 등이 우수하여 항공우주산업뿐만 아니라 다양한 산업에서 사용되고 있다. 그러나 복합재료는 충격에 취약하고 이러한 충격은 복합 재료 내부의 균열 형성과 균열 성장으로 이어져 구조 파단의 원인이 된다. 본 논문에서는 음향 방출 신호 및 유한요소해석(Finite element analysis, FEA)을 이용하여 복합재 적층판의 Mode I 파괴 모드의 특성을 분석하였다. DCB 시험은 탄소/에폭시 적층판의 Mode I 파괴 특성을 분석하기 위하여 수행되었고 시편의 파괴에 의해서 발생되는 탄성파를 측정하기 위하여 시편에 음향 방출 센서를 부착하였다. 누적 음향 방출 에너지와 균열 선단 위치의 관계를 이용하여 시편의 파괴 인성(Fracture toughness, G_I)을 계산하였다. 계산된 파괴 인성 값을 유한요소모델에 적용하여 해석을 수행하였고 하중-변위 곡선 및 균열 길이-변위 곡선을 통하여 DCB 시험 결과와 비교/분석하였다. 유한요소해석 및 DCB 시험의 결과가 잘 일치함을 보였다.

• 풍력에너지저널
• /
• 제14권3호
• /
• pp.83-90
• /
• 2023

The purpose of this study is to evaluate the inter-laminar fracture toughness characteristics of CFRP pultrusion spar cap materials reinforced with non-woven glass fabric. Test specimens were fabricated by the infusion technique. A non-woven glass fabric and artificial defects were embedded on the middle surface between two pultruded CFRP panels. Double cantilever beam (DCB) and End Notched Flexure (ENF) tests were performed according to ASTM standards. Fracture toughness and crack propagation characteristics were evaluated with load-displacement curves and delamination resistance curves (R-Curve). The fracture toughness results were calculated by compliance calibration (CC) method. The initiation and propagation values of Mode-I critical strain energy release rate value G_Ic were 1.357 kJ/m2 and 1.397 kJ/m2, respectively, and Mode-II critical strain energy release rate values G_IIc were 4.053 kJ/m2 for non-precracked test and 4.547 kJ/m2 for precracked test. It was found that the fracture toughness properties of the CFRP pultrusion spar-cap are influenced by the interface between the layers of CFRP and glass fiber non-woven.

• 한국복합재료학회:학술대회논문집
• /
• 한국복합재료학회 2000년도 춘계학술발표대회 논문집
• /
• pp.67-70
• /
• 2000

Mechanical properties of (10%$AI_20_3{\cdot}SiO_2$+5%Ni)/Al hybrid composites fabricated by the reaction squeeze casting were compared with those of (15%$AI_20_3{\cdot}SiO_2$)/Al composites. Intermetallic compound formed by reaction between molten aluminum and reinforcing powder was uniformly distributed in the Al matrix. These intermetallic compounds were identified as $Al_3$NI using EDS and X-ray diffraction analysis. Microhardness and flexural strength of hybrid composites were higher than that of (15%$AI_20_3{\cdot}SiO_2$)/Al Composite. In-Situ fracture tests were Conducted on (15%$AI_20_3{\cdot}SiO_2$)/Al Composites and (10%$AI_20_3{\cdot}SiO_2$+5%Ni)/Al hybrid composites to identify the microfracture process. It was identified from the in-situ fracture test of (10%$AI_20_3{\cdot}SiO_2$+5%Ni)/Al composites, microcracks were initiated mainly at the short fiber / matrix interfaces. As the loading was continued, the crack propagated mainly along the separated interfacial regions and the well developed shear bands. It was identified from the in-situ fracture test of (10%$AI_20_3{\cdot}SiO_2$+5%Ni)/Al hybrid composites, microcracks were initiated mainly by the short fiber/matrix interfacial debonding. The crack proceeded mainly through the intermetallic compound clusters