• Journal of the Korean Association of Oral and Maxillofacial Surgeons
• /
• v.34 no.2
• /
• pp.157-165
• /
• 2008

The aim of this study was to evaluate the efficacy of a topical 0.2% hyaluronic acid (HA) preparation in the management of wound after removal of arch bar for facial bone fracture and a suture site after orthognatic, oral cancer or oral surgery. Forty patients participated in a randomized, placebo controlled, double-blind trial to evaluate the efficacy of the topical HA and preparation. HA topically applied to the wound after removal of arch bar or stitch out, 3 times a day for 4 weeks. Evaluation is performed once a week for 4 weeks. For subjective evaluation, relative pain reduction in visual analog scale (VAS) and existence of heat sensation was accessed. For objective evaluation, gross evaluation, papilla index, existence of wound dehiscence, redness and swelling was checked. The same evaluation was performed in each arch bar group and suture group. For whole subject, 0.2% HA group resulted higher reduction than placebo group in pain of site in first week with significancy. Same findings were seen other weeks but there was no significancy. 0.2% HA group had better result than placebo in objective evaluation (papilla index, wound dehiscence, redness and swelling), but in gross evaluation placebo had better result than 0.2% HA group with no significancy. Subject was divided into suture group and arch bar group. Same aspect was seen, but only suture group had significancy not arch bar group in pain reduction score. 0.2% HA group resulted higher reduction than placebo group in pain of site in first week with significancy, especially in suture group. It reveals topical application of HA in wound especially suture site reduced pain in early stage. And 0.2% HA group had better result than placebo in papilla index, redness and swelling with no statistical significancy. In conclusion, HA has effect of pain reduction and healing promotion in the mucosal wound after oral surgery.

• Journal of the Korea Academia-Industrial cooperation Society
• /
• v.17 no.8
• /
• pp.624-629
• /
• 2016

A brake lever in a basic railway brake system is an important safety device that delivers braking force from the brake cylinder to the brake pad. The safety guidelines for designing rolling stock only qualitatively describe that the brake lever should have sufficient strength. Each train has a different type of brake lever. One brake lever that was designed with a factor of safety of 1.27 has failed, so the material was changed to increase the strength. Therefore, the stress distribution and weak points of the lever were identified by theoretical analysis. and structural analysis. Different brake lever designs were examined for KTX high-speed trains, which have a split-type structure, as well as for electric locomotives, which use an electric multiple unit (EMU) with a unity-type structure. A fracture test was also done to look at the relationship between the vertical stress and the bending stress during braking. The results were used to find a safety factor to apply to each train and suggest quantitative minimum guidelines. We also looked at changing the unity-type EMU brake lever to the split type under the same conditions and analyzed how much the design change affected the factor of safety.

• Journal of the Korea Academia-Industrial cooperation Society
• /
• v.21 no.4
• /
• pp.164-172
• /
• 2020

The fuel oil/heat exchanger installed in military aircraft is a device that cools the lubricant oil supplied to other devices, such as an AMAD, and a hydraulic pump using the low temperature of the fuel is cracked at the AMAD lubricant inlet port. If a crack in the heat exchanger occurs, the lubricant oil supplied to other equipment is not cooled. Therefore, the flight can no longer be performed. In this study, non-destructive inspection and microscopic examination of the fracture surface of the oil port were performed to analyze the crack tendency. The oil pipe connected to the oil port is a titanium pipe, which is fastened with over torque and has been identified as the leading cause of heat exchanger oil port cracks. In addition, it was verified as the main reason for cracking by finite element analysis. The material and diameter of the pipe were changed to improve this defect, and the applied torque was adjusted. In addition, the bending value of the pipe was adjusted to minimize the fatigue accumulation due to pulsating pressure. As a result, no cracks occurred on the heat exchanger via the ground test after the installation of an improved pipe under the same conditions.

• Journal of the Korea Concrete Institute
• /
• v.22 no.5
• /
• pp.675-684
• /
• 2010

The reinforced concrete members are designed to fail in flexural to lead ductile fracture. In the building structures, the failure is typically imposed on beams to prevent damages in columns. However, progression of plastic collapse mechanism may ultimately develop, a plastic hinge at the bottem end of the first floor column, which then can be subjected to shear or bond finally due to large axial force and small shear span-to-depth ratio. In this study, 10 RC column specimens failed in shear after flexural yielding was investigated to determine the factors affecting the plastic hinge length. The findings of this study showed that the most effective factor affecting the plastic hinge length was an axial force. As an axial force increase, an axial strain and a ductility ratio were decreased obviously. The test also shows the observed plastic hinge length was about 0.8~1.2d and the this result has difference compared with forward research.

• Journal of the Korean Wood Science and Technology
• /
• v.43 no.4
• /
• pp.463-469
• /
• 2015

In this study, to improve bending strength performance of Korean white pine, we made the curved composite glulam that was reinforced with glass fiber materials and larch lamina. Five types of Korean white pine curved glulams were made depending on whether they had been reinforced or not and how they had been reinforced. Type-A, reference specimen, was produced only with Korean white pine lamina, and Type-B was with larch lamina in the same thickness. Type-C was made by inserting a glass fiber cloth of textile shape between the each layer. Type-D was reinforced with two glass fiber cloths, which were placed inside and outside of the outermost lamina. Type-E was reinforced with GFRP sheet in the same way as Type-D. As a result of this bending strength test, the modulus of rupture (MOR) of Type-B, Type-C and Type-E were increased by 29%, 6%, and 48% in comparison with Type-A. However, MOR of Type-D was decreased by 2% in comparison with Type-A. In the failure modes, Type-A, Type-B and Type-C were totally fractured at the maximum load. However, load values of Type-D and Type-E decreased slowly because of reinforcement of fracture suppression, and the GFRP sheet (Type-E) had better reinforcing effect on compressive stress and tensile stress than the glass fiber cloth (Type-D).

• Korean Journal of Materials Research
• /
• v.4 no.2
• /
• pp.194-205
• /
• 1994

In this research, we attempt to fabricate an excellent CFRC(Carbon Fiber Reinforced Carbon), which has good thermal and mechanical properties, with 8H/satin woven fabric prepreg, high modulus and high strength type continuous carbon fiber and raw coal tar pitch(RCTP) matrix or THF soluble fraction(THFSP) matrix which has good graphitizability. Green bodies were fabricated with hot press molding technique and CFRC samples were made after carbonization, impregnation, recarbonization and graphitization steps. For the purpose of characterization of the physical properties, SEM, polarized light microscope, TGA were observed, and tested flexural strength, modulus and ILSS. After heat treating the THFSP matrix up to $2300^{\circ}C$, the value of $C_0$/2 was 3.380$\AA$, which is analogous to the structure of natural graphite and the value of 2$\theta$ is $26.276^{\circ}$ approached to the Bragg's angle of natural graphite. As a result of TGA to test the high temperature air oxidation, the THFSP matrix, graphitized up to $2300^{\circ}C$, exhibited the best air oxidation resistance. And mechanical properties were increased up to 65~70% as fiber volume fraction increased. Because of the good orientation graphitizability, the fracture surface of THFSP matrix CFRC is very good.

• Korean Journal of Materials Research
• /
• v.10 no.2
• /
• pp.111-116
• /
• 2000

Fracture mode and carbide reactions of cast alloy 738LC during thermal exposure and creep at 816$^{\circ}C$/440MPa and 982$^{\circ}C$/152MPa were investigated. Crystallographic transgranular failure was observed in the specimen crept at 816$^{\circ}C$ due to shearing on the slip plane. Because selective oxidation at the grainboundaries which was exposed at the surface leads reduction in surface energy, however, early initiation of crack at the grainboundaries and intergranular failure were observed in the specimen crept at 982$^{\circ}C$/152MPa. As a result of decomposition of MC carbide at the tested temperatures, M(sub)23C(sub)6 carbide precipitated either on the grainboundaries or on the deformation band. The applied stress enhanced decomposition of MC. $\sigma$phase nucleated from Cr(sub)23C(sub)6 then grew to the ${\gamma}$+${\gamma}$\\` matrix. Precipitation of $\sigma$was accelerated by increasing temperature and applied stress.

• The Journal of Engineering Geology
• /
• v.8 no.3
• /
• pp.261-273
• /
• 1998

Multiple well log analysis technique consisting of geophysical well log and geological core log has been made to analysis the discontinuities of a test borehole-PABH1 located in Pungam sedimentary basin, Sosok, Hongchon-gun, Kangwon Province. Well log methods consist of normal resistivity log, focussed log, single point resistance log, SP log, gamma log, natural gamma log as well as acoustic televiewer log and borehole television log. Core scanning technique was used as an aid for geological core log. The analysis was made by comparing firstly the televiewer and core discontinuities, and then the results from conventional geophysical log analysis were compared to those from core log and acoustic televiewer log. Fractures deduced from the acoustic televiewer log coincide well with discontinuities shown on the core and conventional geophysical logs. Particularly close coincidence could be observed between fractures derived from acoustic televiewer and conventional geophysical log analysis. It has been noted that the geophysical logs such as, caliper, resistivity, density and high resolution gamma gamma curves are effective in delineating the fractures. For example the ratio between density and resistivity (BRD/SHN) provides also an alternative indicator for discerning the fracture condition in the study area.

• The Journal of Engineering Geology
• /
• v.25 no.3
• /
• pp.357-368
• /
• 2015

Brittle failure of Mesozoic granite in the Daejeon region is predicted using empirical analysis and numerical modeling techniques. The input parameters selected for these techniques were based on the results of laboratory tests, including damage-controlled tests. Rock masses that were considered to be strong during laboratory testing were assigned to "group A" and those considered to be extremely strong were assigned to "group B". The properties of each group were then used in the analyses. In-situ stress measurements, or the ratio of horizontal to vertical stress (k), were also necessary for the analyses, but no such measurements have been made in the study area. Therefore, k values of 1, 2, and 3 were assumed. In the case of k=1, empirical analysis and numerical modeling show no indication of brittle failure from the surface to1000 m depth. When k=2, brittle failure of the rock mass occurs at depths below 800 m. For k=3, brittle failure occurs at depths below 600 m. Although both the Cohesion Weakening Friction Strengthening (CWFS) and Mohr-Coulomb models were used to predict brittle failure, only the CWFS model performed well in simulating the range and depth of the brittle failure zone.

• Journal of the Korean Society for Heat Treatment
• /
• v.5 no.1
• /
• pp.41-49
• /
• 1992

The effects of alloying elements on the superplastic properties of Al-Li based alloys had been investigated. The intermediate thermo-mechanical treated (ITMT) Al-2.0wt%Li, Al-2.0wt%Li-1.0wt%Mg, Al-2.0wt%Li-0.12wt%Zr and Al-2.0wt%Li-1.2wt%Cu-1.0wt%Mg-0.12wt%Zr alloys were tested in tension at various temperature (400, 450, 500 and $550^{\circ}C$) and strain rate($6.7{\times}10^{-3}$, $1.0{\times}10^{-2}$, $1.6{\times}10^{-2}$ and $5.0{\times}10^{-2}/sec$). The results were as follows : The superplasticity in binary, ternary and pentanary alloys appeared at 500 to $550^{\circ}C$, and good strain rate for superplasticity. $1.6{\times}10^{-2}/sec{\sim}1.0{\times}10^{-2}/sec$ for a binary alloy and $1.0{\times}10^{-2}/sec{\sim}6.7{\times}10^{-3}/sec$ for ternary and pentanary alloys. A Zr-added ternary alloy had best value of elongation (730%) in four alloys at $550^{\circ}C$ of tension temperature and $1.0{\times}10^{-2}/sec$ of strain rate. The strain rate was greatly dependent on tension temperature and true strain rate was more than 1.0 at all test temperature and strain rate. In binary and Mg-added teranry alloys. the necks were slightly formed and their fracture surface had lips shape, but Zr-added ternary and pentanary alloy fractured along the grain boundary without necking. Their dislocations moved to grain boundary during superplasticity deformation and arranged perpendicular to grain boundary. Super plastic deformation was made by grain boundary slip of dislocation slip creep and model of core and mantle.