• Transactions of the Korean Society of Mechanical Engineers
• /
• v.19 no.3
• /
• pp.631-638
• /
• 1995

In this study, mechanical characteristics test of Functionally Gradient Materia (FGM) was performed by means of Modified Small Punch (MSP) Test with FGM; NiCrAlY-8YSZ and PSZ-Ni. To determine fracture mechanic factor, it was carried out MSP test that has possibility with small specimen (10*10*0.5 mm$^{t}$ ) and AE test to analyze micro fracture mechanism. As a result, fracture behavior became varied from brittle fracture to ductile as the content of Ni(or NiCrAlY) composition was increased and fracture energy was increased too. AE characteristics demonstrated that AE technique can detect the onset of fracture processes and AE energy was suddenly increased in the vicinity of maximum load. Since Young's modulus, fracture stress and fracture toughness was determined by MSP test, it can be known that the composition of NiCrAly 75%/8YSZ25% has the best mechanical property and furthermore this result is supported with fracture surface observation.

• Transactions of the Korean Society of Automotive Engineers
• /
• v.19 no.6
• /
• pp.90-96
• /
• 2011

In this study, the characteristic of fractured portion and shape on solder joints were investigated according to the thermal shock test for Automotive Application Component using Sn-3.0Ag-0.5Cu solder, which has a outstanding property as Lead-free solder. The value of pull and shear strength was decreased in principle after 432 cycles thermal shock test. In addition, fracture mode was verified by using EDS and SEM to observe fractured shape on the solder joints before and after thermal shock. In before thermal shock test, the fracture mode revealed typically solder layer's fracture mode. In after thermal shock test, we identified multiple fracture mode of the ductile and brittle fracture. Even though same composition of solder was used to experimental for estimating. the fracture mode varied on the fracture portion's height and the directional angles of shear strength. In conclusion, we identified that mechanical strength was affected on the solder layer's fracture mode.

• Journal of Mechanical Science and Technology
• /
• v.18 no.9
• /
• pp.1604-1613
• /
• 2004

This paper presents an effective and reliable evaluation method for fracture strength and material degradation of the micro-structure of high temperature service steel weldment using advanced small punch (ASP) test developed from conventional small punch (CSP) test. For the purpose of the ASP test, a lower die with a minimized ${\Phi}$1.5 mm diameter loading ball and an optimized deformation guide hole of ${\Phi}$3 mm diameter were designed. The behaviors of fracture energy (E$\_$sp/), ductile-brittle transition temperature (DBTT) and material degradation from the ASP test showed a definite dependency on the micro-structure of weldment. Results obtained from ASP test were compared and reviewed with results from CSP test, Charpy impact test, and hardness test. The utility and reliability of the proposed ASP test were verified by investigating fracture strength, behavior of DBTT, and fracture location of each micro-structure of steel weldment for test specimen in ASP test. It was observed that the fracture toughness in the micro-structure of FL＋CGHAZ and ICHAZ decreased remarkably with increasing aging time. From studies of all micro-structures, it was observed that FGHAZ microstructure has the most excellent fracture toughness, and it showed absence of material degradation.

• Journal of the Korea Institute of Military Science and Technology
• /
• v.16 no.4
• /
• pp.449-455
• /
• 2013

When a missile is launched, a fracture-type canister cover should be properly broken by a collision with a missile or inner pressure of a canister. The fracture performance of a canister cover should be evaluated by a test using a real missile; however, it is unrealistic due to high cost and time restriction in a design stage. In this study, a test technique is newly developed to predict fracture performance of a canister cover. The test was design to have same kinetic energy with a real missile test when the cover is collide with a missile. The effectiveness of the suggested test technique was proved by comparing the test result with that of a real missile test.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2002.05a
• /
• pp.335-340
• /
• 2002

By the recently, Environmental pollution is serious by the highly economic growth and expansion of lively country basic industry. Especially, in case of industrial waste and life waste leaped into a pollution source. Also, research for processing of waste and recycling countermeasure is a pressing question on national dimension because it is prohibited an ocean disposal and reclamation. In this study, it looked for fracture characteristic value of recycling a coal ash to decrease environmental pollution by picky and exhaustion of natural resources and to reduce self-weight to prepare for a tall building and earthquake. So a coal ash examined to be possible to do as construction material. It achieved compressive strength test and three points bending test with initial notch depth rate and age for variables to show a basic research data. From the basis of the three points bending test, the fracture parameters - notch sensitivity, fracture energy, initial compliance were experimentally proposed. From the results of the compressive strength test, the elastic modulus was experimentally proposed. Also on the basis of the three points bending test, the fracture parameters - notch sensitivity, fracture energy, initial compliance were experimentally proposed. The results that the strength and fracture energy value are lower than concrete or mortar is described in this paper. Also, it shows that the deflection at fracture decreases as the age increases and the notch sensitivity decrease. However, it is judged to be available to construction material if research is continuously gone forward.

• Proceedings of the KSME Conference
• /
• 2001.06a
• /
• pp.345-350
• /
• 2001

In order to perform elastic-plastic fracture mechanical analyses, fracture resistance curves for concerned materials are required. 1T-CT specimen was used to obtain fracture resistance curves. But the fracture resistance curve by the 1T-CT specimen was very conservative to evaluate the integrity of the structure. And fracture resistance curve was affected by the specimen geometry and crack plane orientation. The objective of this paper is to be certain the conservativeness of the fracture resistance curve by the 1T-CT specimen and to provide the additional safety margin. For these, the fracture tests using the real pipe specimen and standard 1T-CT specimen test were performed. 4-point bending jig was manufactured for pipe test and direct current potential drop method was used to measure the crack extension and length for pipe test. From the pipe and the 1T-CT specimen test results, it was observed that the J-integral of the 1T-CT specimen test at the crack initiation point was very small compare to that of the pipe specimen test.

• Journal of the Korean Wood Science and Technology
• /
• v.18 no.3
• /
• pp.6-16
• /
• 1990

The objectives of this study were to investigate the relative effects of specific gravity and particle size on internal bond and tensile strengths and fracture toughness of particleboard and to compare mechanical strength with fracture toughness. The particleboard was manufactured with three different particle sizes at specific gravity levels of 0.6, 0.7, and 0.8 with a resin content of 10% based on oven dry weight. The results were summarized as follows: 1. Internal bond strength. fracture toughness in internal bond test. maximum tensile strength, and fracture toughness in tension test increased with the increase of specific gravity of particleboard. 2. As partcle size increased, internal bond strength, fracture toughness. maximum tensile strength. and fracture toughness in tension test increased. 3. The maximum tensile strength and fracture toughness appeared to be in a direct relationship, and then maximum tensile strength could be used for predicition of fracture toughness for tension test. 4. The fracture toughness in internal bond test was somewhat independent on induced crack length.

• International Journal of Safety
• /
• v.11 no.1
• /
• pp.19-21
• /
• 2012

In this thesis, fracture test was performed in order to investigate the fracture strength of SFRC(steel fiber reinforced concrete) structures. The relationship between the compressive force and strain value of SFRC specimens were observed under the compressive strength test. From the fracture test results, the relationship between percentage of fiber by volume, compressive strength, elastic modulus, and tensile strength of SFRC beams were studied, and the measured elastic modulus of SFRC were compared with the calculated elastic modulus by ACI committee 544.

• Journal of Mechanical Science and Technology
• /
• v.16 no.9
• /
• pp.1093-1101
• /
• 2002

Continuous fiber ceramic composites (CFCCs) have advantages over monolithic ceramics : Silicon Nitride composites are not well used for application because of their low fracture toughness and fracture strength, but CFCCs exhibit increased toughness for damage tolerance, and relatively high stiffness in spite of low specific weight. Thus it is important to characterize the fracture resistance and properties of new CFCCs materials. Tensile and flexural tests were carried out for mechanical properties and the fracture resistance behavior of a SCS6 fiber reinforced Si$_3$N$_4$ matrix CFCC was evaluated. The results indicated that CFCC composite exhibit a rising R curve behavior in flexural test. The fracture toughness was about 4.8 MPa$.$m$\^$1/2 , which resulted in a higher value of the fracture toughness because of fiber bridging. Mechanical properties as like the elastic modulus, proportional limit and the ultimate strength in a flexural test are greater than those in a tensile test. Also a numerical modeling of failure process was accomplished for a flexural test. This numerical results provided a good simulation of the cumulative fracture process of the fiber and matrix in CFCCs.

• Computers and Concrete
• /
• v.9 no.2
• /
• pp.81-97
• /
• 2012

This paper presents development of double-K fracture model for the split-tension cube specimen for determining the unstable fracture toughness and initial cracking toughness of concrete. There are some advantages of using of split-tension cube test like compactness and lightness over the existing specimen geometries in practice such as three-point bend test, wedge splitting test and compact tension specimen. The cohesive toughness of the material is determined using weight function having four terms for the split-tension cube specimen. Some empirical relations are also suggested for determining geometrical factors in order to calculate stress intensity factor and crack mouth opening displacement for the same specimen. The results of double-K fracture parameters of split-tension cube specimen are compared with those obtained for compact tension specimen. Finally, the influence of the width of the load-distribution of split-tension cube specimen on the double-K fracture parameters for laboratory size specimens is investigated. The input data required for determining double-K fracture parameters for both the specimen geometries are obtained using well known version of the Fictitious Crack Model.