• Applied Chemistry for Engineering
• /
• v.27 no.4
• /
• pp.386-390
• /
• 2016

The surface of carbon nanotubes (CNTs) was modified by fluorination and applied to conductive materials to improve the energy efficiency of a capacitive desalination (CDI) electrode. CNTs were fluorinated at room temperature with a mixed gas of fluorine and nitrogen, and activated carbon based CDI electrodes were then prepared by adding 0-0.5 wt% of untreated CNTs or fluorinated CNTs with respect to the activated carbon. Fluorinated CNTs showed improved dispersibility in the electrode and also slurry as compared to untreated CNTs, which was confirmed by the zeta potential and scanning electron microscopy. Fluorinated CNTs added electrodes showed higher desalination efficiency but lower energy consumption than those of using untreated CNTs added electrodes. This was attributed to the decrease in the resistance of CDI electrodes due to the improved dispersibility of CNTs by fluorination.

• Korean Chemical Engineering Research
• /
• v.54 no.6
• /
• pp.830-837
• /
• 2016

In order to improve the compressive strength of graphite foams (GFms), mesophase pitch (MP) was stabilized in air atmosphere and then fluorinated at different conditions. The Fluorine/Carbon (F/C) in surface-chemical contents of fluorinated MP has range of 23.75%~61.48% according to the different fluorine partial pressure. The compressive strengths of GFms prepared from fluorinated MP were increased in proportion to the apparent densities. The compressive strength of the GFm produced from MP with 35.93% of F/C (%) showed maximum value in $2.93{\pm}0.06MPa$, which was increased up to 27.95% than that of the GFm prepared from un-fluorinated MP. This result was attributed that the interface bonding between of MPs due to fluorine functional groups with high surface energy helped to improve compressive strength of the GFm.

• Applied Chemistry for Engineering
• /
• v.32 no.1
• /
• pp.55-60
• /
• 2021

Fluorination was carried out to improve the adsorption performance of pitch-based activated carbon fibers (ACFs) onto acetic acid. Both plasma and direct gas fluorination were used for fluorination, and the acetic acid gas adsorption performance of fluorinated ACFs was investigated. X-ray photoelectron spectroscopy (XPS) is analyzed to determine the surface characteristics of ACFs, and the pore characteristics were analyzed by 77 K nitrogen adsorption. An adsorption performance was measured through gas chromatography, and it was confirmed that the breakthrough time of plasma fluorinated sample was 790 min and that the breakthrough time was delayed compared to that of using untreated one of 650 min. However, the breakthrough time of direct gas fluorinated sample was 390 min, indicating that the adsorption performance was inhibited. The plasma fluorinated ACFs showed an increase in the adsorption performance due to an electrostatic attraction between the acetic acid gas (CH3COOH) with the fluorine group introduced to the surface without changing its specific surface area. On the other hand, the specific surface area of the direct gas fluorinated ACFs decreased significantly up to 55%, and the physical adsorption effect on the acetic acid gas also reduced.

• Journal of the Korean institute of surface engineering
• /
• v.34 no.5
• /
• pp.378-383
• /
• 2001

An out line of the material process with using the atmospheric pressure glow plasma is described as follows : (1) TiO powder coating with SiO$_2$ (2) Surface treatment of Fluorinated polymers and (3) Surface cleaning of electronic circuit board with using splay type.

• Bulletin of the Korean Chemical Society
• /
• v.30 no.9
• /
• pp.2071-2076
• /
• 2009

The single-walled carbon nanotubes (SWCNTs) produced by chemical vapor deposition (CVD) were directly fluorinated with fluorine ($F_2$) gas in a temperature range 20 ~ 400 ${^{\circ}C}$. The surface properties and morphology of the SWCNTs were investigated in terms of fluorination temperature. As a result, Raman spectra showed a pair of bands at 1340 and 1590 $cm^{-1}$ peculiar to disordered $sp^2$-carbons. These results indicated that C-F bonds were formed on the rear surfaces of the nanotubes by fluorination, while the external surfaces as well as the layers between the internal and external surfaces retained their $sp^2$-hybridization. XPS analysis exhibited that fluorine atoms were bonded to carbon atoms on internal surfaces (rear surfaces) of the nanotubes and the amount of fluorine attached on the nanotubes was increased with increasing the fluorination temperature. Consequently, the direct fluorination of carbon nanotubes led to functionalization and modification of pristine nanotubes with respect to surface and morphological properties.

• Journal of the Korean Chemical Society
• /
• v.47 no.2
• /
• pp.147-154
• /
• 2003

In this study, the fluorinated carbon blacks(CB) were used to reduce the negative temperature coefficient (NTC) phenomenon of the CB-filled high density polyethylene(HDPE) compounds in the fluorination pressure of 0.1-0.4 MPa. The changes in surface properties of the CB were investigated by using FT-IR, XPS and contact angle measurements. From the FT-IR results, the fluorinated CB showed the C-F absorption peak at 1400-1000 cm$^{-1}$ and the peak intensity was increased with increasing the fluorination pressure. Also, the analysis of XPS spectra of the fluorinated CB indicated that fluorine content was increased with increasing the fluorination pressure. Meanwhile, the surface free energy of the fluorinated CB was decreased with increasing the fluorination pressure. Consequently, the increase of fluorine contents on CB made a disappearance of NTC behaviors of CB/HDPE compounds, which was probably due to the reduction of CB reaggregation after melting point of the HDPE, resulting from decreasing the surface free energy of CB particles.

• Polymer(Korea)
• /
• v.39 no.3
• /
• pp.403-411
• /
• 2015

A series of hydrophobically associating fluorinated amphiphilic polyacrylamide copolymers with remarkably high heat resistance and salt tolerance were synthesized by free radical micellar copolymerization, using acrylamide (AM) and sodium 2-acrylamido-tetradecane sulfonate ($AMC_{14}S$) as amphiphilic monomers, and 2-(perfluorooctyl) ethyl acrylate (PFHEA) as hydrophobic monomer. The structure of the terpolymer was characterized by FTIR, $^1H$ NMR and $^{19}F$ NMR. The solution properties of the terpolymers were investigated in details, and the results showed that the terpolymer solution had strong intermolecular hydrophobic association as the concentration exceeded the critical association concentration 1.5 g/L. The terpolymer solution possessed high surface activity, viscoelasticity, excellent heat resistance, salt tolerance and shearing resistance. The viscosity retention rate of copolymer solution was as high as 59.9% under the condition of fresh wastewater, $85^{\circ}C$ and a 60-days aging test.

• Applied Chemistry for Engineering
• /
• v.21 no.4
• /
• pp.475-478
• /
• 2010

Fluorinated polymeric membranes were prepared by direct surface modification of PDMS with fluorine gas ($50{\sim}2000\;{\mu}mol/mol$ in nitrogen). The formed fluorinated polymeric membranes were characterized by FT-IR spectroscopy, GC (Gas chromatography), atomic force microscopy, and scanning electron microscopy. Direct fluorination resulted in the change of permeability and selectivity of various gases (pure gases such as $CO_2$, $O_2$, $N_2$, $C_2H_4$, mixture of He, Ne, Kr, Xe) through PDMS membranes. Fluorination resulted in the maximum 50% increase of selectivity through PDMS membrane.

• Applied Chemistry for Engineering
• /
• v.26 no.1
• /
• pp.92-98
• /
• 2015

In this study, phenol-based activated carbons (ACs) were fluorinated at various fluorine partial pressures (0.01~0.03 MPa) and the $Cr^{6+}$ ion adsorption of fluorinated ACs was investigated. According to BET and XPS results, the specific surface area and total pore volume of fluorinated ACs increased by 24.7 and 55.8%, respectively, and fluorine functional groups were introduced to AC surface. The most optimized condition of $Cr^{6+}$ ion adsorption was confirmed at the fluorine partial pressure of 0.02 MPa. And also the removal efficiency of $Cr^{6+}$ ion was up to 98% at 300 mg/L of the initial concentration, and these results showed an approximately three-fold increase compared to that of using untreated ACs. Furthermore, the $Cr^{6+}$ ion adsorption of fluorinated ACs was completed in less than 30 min in contrast with untreated ACs, which was expected to be an increase of the affinity between $Cr^{6+}$ ions and ACs surfaces by fluorination.

• Membrane Journal
• /
• v.30 no.5
• /
• pp.326-332
• /
• 2020

In this study, polymer-fluorinated silica composite hollow fiber membranes were fabricated and applied to a membrane contactor for the recovery of methane dissolved in the anaerobic effluent. To prepare the composite membranes, porous hollow fiber substrates were fabricated with Ultem^®, a commercial polyetherimide (PEI). Subsequently, fluorinated silica particles were synthesized and coated on the surface via strong covalent bonding. Due to the high porosity, our membrane showed a CH₄ flux of 8.25 × 10^-5 ㎤ (STP)/㎠·s at the liquid velocity of 0.03 m/s which is much higher that that of commercial polypropylene membrane designed for degassing processes. This is attributed to our membrane's high porosity as well as a superior surface hydrophobicity (120~122°) resulted from the coating with fluorinated silica nanoparticles.