Journal of the korean academy of Pediatric Dentistry
/
v.39
no.4
/
pp.383-388
/
2012
The aim of this study was to compare the compressive strength and the surface microhardness of Beautifil flow (Shofu, Kyoto, Japan) with $Filtek^{TM}$ Z350, Z350XT (3M ESPE, USA). Fifteen specimens from each material were fabricated for testing. Compressive strength was measured by using a universal testing machine at a crosshead speed of 1 mm/min. Surface microhardness values were measured by using Vickers hardness tester under 4.9 N load and 10 seconds dwelling time. The compressive strength of Group 2 $Filtek^{TM}$ Z350XT shows the highest value as $218.7{\pm}18.4$ MPa and Group 1 $Filtek^{TM}$ Z350 was $205.5{\pm}27.1$ MPa. Group 3 Beautifil flow F00 was $176.5{\pm}30.3$ MPa, and Group 4 Beautifil flow F10 was $173.4{\pm}26.2$ MPa. The compressive strength of Group 2 is higher than Group 3 and 4 (p < 0.05). The surface microhardness of Group 2 $Filtek^{TM}$ Z350XT shows the highest value as $39.1{\pm}2.1$ and Group 4 Beautifil flow F10 was $27.9{\pm}1.8$. And Group 3 Beautifil flow F00 was $23.1{\pm}1.1$, Group 1 $Filtek^{TM}$ Z350 was $20.4{\pm}0.9$. There was a statistical significant difference in surface microhardness between all groups (p < 0.05). In conclusion, the compressive strength of giomer was below the level of flowable composite resin. However, the surface microhardness of giomer is comparable to that of flowable composite resin. Giomer would be the good alternative to composite resin, if there is improvement of the compressive strength of giomer.
The purpose of this study was to investigate the effects of composite resin restorations on the stress distribution of notch shaped noncarious cervical lesion using three-dimensional (3D) finite element analysis (FEA). Extracted maxillary second premolar was scanned serially with Micro-CT (SkyScan1072 ; SkyScan, Aartselaar, Belgium). The 3D images were processed by 3D-DOCTOR (Able Software Co., Lexington, MA, USA). ANSYS (Swanson Analysis Systems, Inc., Houston, USA) was used to mesh and analyze 3D FE model. Notch shaped cavity was filled with hybrid or flowable resin and each restoration was simulated with adhesive layer thickness ($40{\mu}m$) A static load of 500 N was applied on a point load condition at buccal cusp (loading A) and palatal cusp (loading B). The principal stresses in the lesion apex (internal line angle of cavity) and middle vertical wall were analyzed using ANSYS. The results were as follows 1. Under loading A, compressive stress is created in the unrestored and restored cavity. Under loading B, tensile stress is created. And the peak stress concentration is seen at near mesial corner of the cavity under each load condition. 2. Compared to the unrestored cavity, the principal stresses at the cemeto-enamel junction (CEJ) and internal line angle of the cavity were more reduced in the restored cavity on both load con ditions. 3. In teeth restored with hybrid composite, the principal stresses at the CEJ and internal line angle of the cavity were more reduced than flowable resin.
Purpose: The purpose of this study was to evaluate the color stability of composite resins used for splinting teeth by comparing a self-cure resin cement (Superbond C&B, SB), a flowable composite resin (G-aenial Universal Flo A2, GU), and a composite resin exclusively used for splinting teeth (G-Fix, GF) before and after aging in NaOCl. Methods: Resin samples were fabricated to a size of 2 mm thickness and 8.5 mm diameter and light-cured with an LED light curing unit (G-Light, n = 12). Immediately after fabrication, CIE L*a*b* values of the resin samples were measured with a spectrophotometer (CM-5) as baseline. Then, the resin samples were immersed in 5% NaOCl at $60^{\circ}C$ and the color was measured after 23 hours every day for 4 days. Data were analyzed with one-way ANOVA followed by Duncan post hoc test (p<0.05), and color differences (${\Delta}E$) of resin samples before and after NaOCl aging were also calculated. Results: For SB, there were no changes in L* and a* values but changes were observed in b* values. For GU, there were no changes in L* and b* values but in a* values. For GF, changes were observed in L*, a*, and b* values. All resin samples showed highest ${\Delta}E$ between baseline and the 1st day of NaOCl immersion. ${\Delta}E$ of SB, GU, and GF was 4.6 - 5.8, 4.9 - 7.9, and 9.9 - 16.9, respectively. GF showed highest color change during NaOCl aging. Conclusion: The results of this color quality evaluation showed that the composite resin exclusively used for splinting teeth might be more vulnerable to color change during intraoral service.
The purpose of this study was to investigate the effect of cavity configurations on the marginal leakage of class 5 glass ionomer cement and composite resin restorations. Four types of cavities such as saucer shape. notch shape. combined shape(notch shape occlusally and saucer shape gingivally). and U shape were prepared on the buccal and lingual surfaces of 80 extracted premolars(40 cavities for each shape). Occlusal cavity margins were placed at enamel and cervical margins were placed at dentin. 10 cavities of each shape were restored with Ketac Fil as a conventional glass ionomer cement. Fuji II LC improved as a resin modified glass ionomer cement, Z 100 as a hybrid composite resin. and Tetric Flow as a flowable composite resin (40 cavities for each material). After thermocycling, teeth were immersed in 5% basic fuchsin solution for 6 hours and sectioned longitudinally in a buccolingual direction through the center of the restoration. The dye penetrations at the tooth restoration interface were examined by stereomicroscope. The Result were as follows 1. In saucer shape, notch shape and combined shape, composite resin restorations showed lesser leakage than glass ionomer restorations(p<0.05) and in U shape. Tetric Flow showed the least marginal leakage and others were decreased as Z 100. Fuji II LC improved, Ketac Fil in that order. There were statistically significant difference between Tetric Flow and Fuji II LC improved. Ketac Fil and between Z 100 and Ketac Fil(p<0.05). 2. In Ketac Fil restoration group, saucer shape showed the highest marginal leakage and U shape showed the least marginal leakage and others were decreased as notch shape, combined shape in that order. There were statistically significant difference between saucer shape and combined shape, U shape and between notch shape and U shape(p<0.05). 3. In Fuji II LC improved restoration group, U shape showed the least marginal leakage. There were statistically significant difference between U shape and other three shapes(p<0.05). 4. The cavity configuration had no significant effect on marginal leakage of composite resin restorations(p>0.05).
International Journal of Precision Engineering and Manufacturing
/
v.9
no.3
/
pp.64-67
/
2008
This study investigated the influence of composite resins with different elastic moduli and occlusal loading conditions on the stress distribution of restored notch-shaped non-carious cervical lesions (NCCL) using 3D finite element analysis. Two different materials, Tetric Flow and Z100, were used as representative flowable hybrid resins for the restoration of NCCL. A static point load of 500 N was applied at the buccal and palatal cusps. The ratios of stress reduction to energy dissipation were better in the compressive state than the tensile state regardless of the restorative material. The total dissipation ratios for Tetric Flow were 1.5% and 4.2% larger than those for Z100 under compression and tension, respectively. Therefore, tensile stress poses more of a risk for tooth fracture, and Tetric Flow is a more appropriate material for restoration.
Objective: To analyze the fatigue resistance, debonding force, and failure type of fiber-reinforced composite, polyethylene ribbon-reinforced, and braided stainless steel wire lingual retainers in vitro. Methods: Roots of human mandibular central incisors were covered with silicone, mimicking the periodontal ligament, and embedded in polymethylmethacrylate. The specimens (N = 50), with two teeth each, were randomly divided into five groups (n = 10/group) according to the retainer materials: (1) Interlig (E-glass), (2) everStick Ortho (E-glass), (3) DentaPreg Splint (S2-glass), (4) Ribbond (polyethylene), and (5) Quad Cat wire (stainless steel). After the recommended adhesive procedures, the retainers were bonded to the teeth by using flowable composite resin (Tetric Flow). The teeth were subjected to 10,00,000 cyclic loads (8 Hz, 3 - 100 N, $45^{\circ}$ angle, under $37{\pm}3^{\circ}C$ water) at their incisoproximal contact, and debonding forces were measured with a universal testing machine (1 mm/min crosshead speed). Failure sites were examined under a stereomicroscope (${\times}40$ magnification). Data were analyzed by one-way analysis of variance. Results: All the specimens survived the cyclic loading. Their mean debonding forces were not significantly different (p > 0.05). The DentaPreg Splint group (80%) showed the highest incidence of complete adhesive debonding, followed by the Interlig group (60%). The everStick Ortho group (80%) presented predominantly partial adhesive debonding. The Quad Cat wire group (50%) presented overlying composite detachment. Conclusions: Cyclic loading did not cause debonding. The retainers presented similar debonding forces but different failure types. Braided stainless steel wire retainers presented the most repairable failure type.
The aim of study was to investigate the effect of flow, specimen geometry and adhesion on the measurement of linear polymerization shrinkage of light cured composite resins using linear shrinkage measuring device. Four commercially available composites - an anterior posterior hybrid composite Z100, a posterior packable composite P60 and two flowable composites, Filtek flow and Tetric flow-were studied. The linear polymerization shrinkage of composites was determined using 'bonded disc method' and 'non-bond-ed' free shrinkage method at varying C-factor in the range of 1∼8 by changing specimen geometry. These measured linear shrinkage values were compared with free volumetric shrinkage values. The viscosity and flow of composites were determined and compared by measuring the dropping speed of metal rod under constant load. In non-bonded method, the linear shrinkage approximated one third of true volumetric shrink-age by isotropic contraction. However, in bonded disc method, as the bonded surface increased the linear shrinkage increased up to volumetric shrinkage value by anisotropic contraction. The linear shrinkage value increased with increasing C-factor and approximated true volumetric shrinkage and reached plateau at about C-factor 5∼6. The more flow the composite was, reduced linear shrinkage was measured by compensation radial flow.
Carlos Alberto Kenji Shimokawa ;Paula Mendes Acatauassu Carneiro ;Tamile Rocha da Silva Lobo;Roberto Ruggiero Braga ;Miriam Lacalle Turbino;Adriana Bona Matos
Restorative Dentistry and Endodontics
/
v.48
no.3
/
pp.30.1-30.11
/
2023
Objectives: This study verified the possibility of cementing fiberglass-reinforced posts using a flowable bulk-fill composite (BF), comparing its push-out bond strength and microhardness with these properties of 3 luting materials. Materials and Methods: Sixty endodontically treated bovine roots were used. Posts were cemented using conventional dual-cured cement (CC); self-adhesive cement (SA); dual-cured composite (RC); and BF. Push-out bond strength (n = 10) and microhardness (n = 5) tests were performed after 1 week and 4 months of storage. Two-way repeated measures analysis of variance (ANOVA), 1-way ANOVA, t-test, and Tukey post-hoc tests were applied for the push-out bond strength and microhardness results; and Pearson correlation test was applied to verify the correlation between push-out bond strength and microhardness results (α = 0.05). Results: BF presented higher push-out bond strength than CC and SA in the cervical third before aging (p < 0.01). No differences were found between push-out bond strength before and after aging for all the luting materials (p = 0.84). Regarding hardness, only SA presented higher values measured before than after aging (p < 0.01). RC and BF did not present 80% of the maximum hardness at the apical regions. A strong positive correlation was found between the luting materials' push-out bond strength and microhardness (p < 0.01, R2 = 0.7912). Conclusions: The BF presented comparable or higher push-out bond strength and microhardness than the luting materials, which indicates that it could be used for cementing resin posts in situations where adequate light curing is possible.
The aim of this study was to evaluate the marginal adaptation of direct class II sandwich restoration with packable composites(P-60), resin modified glass ionomer cement(Fuji-II LC), flowable compomer(Dyract Flow), flowable composites(Filtek Flow) in comparison with total bond restorations. In addition, for sandwich restorations, influence of different sandwich techniques was also evaluated. Large butt-joint box typed class II cavites with cervical margins 1mm below the cemento-enamel junction were cut into 70 extracted human molars. The cavities(7 groups, n=10) were filled using a closed/open sandwich restoration or total bond restoration technique with materials according to the manufacturer's recommandation using the single-component bonding agent for each system. Teeth were thermocycled 500 times between 5$^{\circ}C$ and 55$^{\circ}C$ with 30-second dwell time. The teeth were then coated with nail polish 1mm short of the restoration, placed in a 2% methylene blue for 24 hours, and sectioned with diamond wheel. Sections were examined with a stereoscope to determine the extent of microleakage. Dentine /Cementum margins were analyzed for microleakage on scale of 0(no leakage) to 4(entire axial wall) and interface between materials, on scale of 0(no leakage) to 3(axial wall). Results were evaluated with Kruskal Wallis Test, corrected for ties, to determine whether there were statistically significant differences among the seven groups. Pairs of groups were analyzed using the Student-Newman-Keuls Method and Dunn s Method. The results were as follows : 1. All groups showed some micoleakage in cervical portion. But there were no microleakage in interface between materials. 2. Closed sandwich restorations with Fuji-II LC and Filtek Flow had significantly lower leakage rating than total restorations with only P-60. However, open sandwich restorations with Dyract Flow showed significantly higher (P<0.05) 3. Closed sandwich restorations had significantly lower leakage rating than total restorations. However open sandwich restoration s showed significantly higher (P<0.05). 4. Sandwich restorations with Fuji-II LC were iou$.$or leakage than only P-60. Filtek Flow, Dyract Flow. But there were no statistically differences among the materials. From the results above, it could be concluded, closed sandwich restorations was effective in reducing microleakage of class II restorations. The best results showing the least microleakage were for the closed sandwich technique with Fuji-II LC and Filtek Flow.
This study evaluate the influence of food staining food and bleaching on the color (CIELAB) and reflectivity of two-way (anterior & posterior) composite resin and flowable composite resin. There were 6 immersion media: kimchi, red pepper paste, blueberry, tea, curry and distilled water. A total of 36 specimens ($11{\times}11{\times}2$ mm) were prepared and immersed in each immersion media for 8 days at $37^{\circ}C$. Their color and reflectivity measured with the spectrophotometer at baseline and every 24 hours. Data from the color change and reflectivity were collected and subjected to statistical analysis by ANOVA, ANCOVA and RM-ANOVA. Curry showed the highest influence on color change and blueberry on brightness (p<0.001) on both resins. Bleaching after polishing made color change more than polishing or bleaching independently on two-way (anterior & posterior) composite resin, but not on flowable composite resin. It was suggested cleaning the mouth after taking curry and blueberry be needed to maintain the original color of composite resin.
본 웹사이트에 게시된 이메일 주소가 전자우편 수집 프로그램이나
그 밖의 기술적 장치를 이용하여 무단으로 수집되는 것을 거부하며,
이를 위반시 정보통신망법에 의해 형사 처벌됨을 유념하시기 바랍니다.
[게시일 2004년 10월 1일]
이용약관
제 1 장 총칙
제 1 조 (목적)
이 이용약관은 KoreaScience 홈페이지(이하 “당 사이트”)에서 제공하는 인터넷 서비스(이하 '서비스')의 가입조건 및 이용에 관한 제반 사항과 기타 필요한 사항을 구체적으로 규정함을 목적으로 합니다.
제 2 조 (용어의 정의)
① "이용자"라 함은 당 사이트에 접속하여 이 약관에 따라 당 사이트가 제공하는 서비스를 받는 회원 및 비회원을
말합니다.
② "회원"이라 함은 서비스를 이용하기 위하여 당 사이트에 개인정보를 제공하여 아이디(ID)와 비밀번호를 부여
받은 자를 말합니다.
③ "회원 아이디(ID)"라 함은 회원의 식별 및 서비스 이용을 위하여 자신이 선정한 문자 및 숫자의 조합을
말합니다.
④ "비밀번호(패스워드)"라 함은 회원이 자신의 비밀보호를 위하여 선정한 문자 및 숫자의 조합을 말합니다.
제 3 조 (이용약관의 효력 및 변경)
① 이 약관은 당 사이트에 게시하거나 기타의 방법으로 회원에게 공지함으로써 효력이 발생합니다.
② 당 사이트는 이 약관을 개정할 경우에 적용일자 및 개정사유를 명시하여 현행 약관과 함께 당 사이트의
초기화면에 그 적용일자 7일 이전부터 적용일자 전일까지 공지합니다. 다만, 회원에게 불리하게 약관내용을
변경하는 경우에는 최소한 30일 이상의 사전 유예기간을 두고 공지합니다. 이 경우 당 사이트는 개정 전
내용과 개정 후 내용을 명확하게 비교하여 이용자가 알기 쉽도록 표시합니다.
제 4 조(약관 외 준칙)
① 이 약관은 당 사이트가 제공하는 서비스에 관한 이용안내와 함께 적용됩니다.
② 이 약관에 명시되지 아니한 사항은 관계법령의 규정이 적용됩니다.
제 2 장 이용계약의 체결
제 5 조 (이용계약의 성립 등)
① 이용계약은 이용고객이 당 사이트가 정한 약관에 「동의합니다」를 선택하고, 당 사이트가 정한
온라인신청양식을 작성하여 서비스 이용을 신청한 후, 당 사이트가 이를 승낙함으로써 성립합니다.
② 제1항의 승낙은 당 사이트가 제공하는 과학기술정보검색, 맞춤정보, 서지정보 등 다른 서비스의 이용승낙을
포함합니다.
제 6 조 (회원가입)
서비스를 이용하고자 하는 고객은 당 사이트에서 정한 회원가입양식에 개인정보를 기재하여 가입을 하여야 합니다.
제 7 조 (개인정보의 보호 및 사용)
당 사이트는 관계법령이 정하는 바에 따라 회원 등록정보를 포함한 회원의 개인정보를 보호하기 위해 노력합니다. 회원 개인정보의 보호 및 사용에 대해서는 관련법령 및 당 사이트의 개인정보 보호정책이 적용됩니다.
제 8 조 (이용 신청의 승낙과 제한)
① 당 사이트는 제6조의 규정에 의한 이용신청고객에 대하여 서비스 이용을 승낙합니다.
② 당 사이트는 아래사항에 해당하는 경우에 대해서 승낙하지 아니 합니다.
- 이용계약 신청서의 내용을 허위로 기재한 경우
- 기타 규정한 제반사항을 위반하며 신청하는 경우
제 9 조 (회원 ID 부여 및 변경 등)
① 당 사이트는 이용고객에 대하여 약관에 정하는 바에 따라 자신이 선정한 회원 ID를 부여합니다.
② 회원 ID는 원칙적으로 변경이 불가하며 부득이한 사유로 인하여 변경 하고자 하는 경우에는 해당 ID를
해지하고 재가입해야 합니다.
③ 기타 회원 개인정보 관리 및 변경 등에 관한 사항은 서비스별 안내에 정하는 바에 의합니다.
제 3 장 계약 당사자의 의무
제 10 조 (KISTI의 의무)
① 당 사이트는 이용고객이 희망한 서비스 제공 개시일에 특별한 사정이 없는 한 서비스를 이용할 수 있도록
하여야 합니다.
② 당 사이트는 개인정보 보호를 위해 보안시스템을 구축하며 개인정보 보호정책을 공시하고 준수합니다.
③ 당 사이트는 회원으로부터 제기되는 의견이나 불만이 정당하다고 객관적으로 인정될 경우에는 적절한 절차를
거쳐 즉시 처리하여야 합니다. 다만, 즉시 처리가 곤란한 경우는 회원에게 그 사유와 처리일정을 통보하여야
합니다.
제 11 조 (회원의 의무)
① 이용자는 회원가입 신청 또는 회원정보 변경 시 실명으로 모든 사항을 사실에 근거하여 작성하여야 하며,
허위 또는 타인의 정보를 등록할 경우 일체의 권리를 주장할 수 없습니다.
② 당 사이트가 관계법령 및 개인정보 보호정책에 의거하여 그 책임을 지는 경우를 제외하고 회원에게 부여된
ID의 비밀번호 관리소홀, 부정사용에 의하여 발생하는 모든 결과에 대한 책임은 회원에게 있습니다.
③ 회원은 당 사이트 및 제 3자의 지적 재산권을 침해해서는 안 됩니다.
제 4 장 서비스의 이용
제 12 조 (서비스 이용 시간)
① 서비스 이용은 당 사이트의 업무상 또는 기술상 특별한 지장이 없는 한 연중무휴, 1일 24시간 운영을
원칙으로 합니다. 단, 당 사이트는 시스템 정기점검, 증설 및 교체를 위해 당 사이트가 정한 날이나 시간에
서비스를 일시 중단할 수 있으며, 예정되어 있는 작업으로 인한 서비스 일시중단은 당 사이트 홈페이지를
통해 사전에 공지합니다.
② 당 사이트는 서비스를 특정범위로 분할하여 각 범위별로 이용가능시간을 별도로 지정할 수 있습니다. 다만
이 경우 그 내용을 공지합니다.
제 13 조 (홈페이지 저작권)
① NDSL에서 제공하는 모든 저작물의 저작권은 원저작자에게 있으며, KISTI는 복제/배포/전송권을 확보하고
있습니다.
② NDSL에서 제공하는 콘텐츠를 상업적 및 기타 영리목적으로 복제/배포/전송할 경우 사전에 KISTI의 허락을
받아야 합니다.
③ NDSL에서 제공하는 콘텐츠를 보도, 비평, 교육, 연구 등을 위하여 정당한 범위 안에서 공정한 관행에
합치되게 인용할 수 있습니다.
④ NDSL에서 제공하는 콘텐츠를 무단 복제, 전송, 배포 기타 저작권법에 위반되는 방법으로 이용할 경우
저작권법 제136조에 따라 5년 이하의 징역 또는 5천만 원 이하의 벌금에 처해질 수 있습니다.
제 14 조 (유료서비스)
① 당 사이트 및 협력기관이 정한 유료서비스(원문복사 등)는 별도로 정해진 바에 따르며, 변경사항은 시행 전에
당 사이트 홈페이지를 통하여 회원에게 공지합니다.
② 유료서비스를 이용하려는 회원은 정해진 요금체계에 따라 요금을 납부해야 합니다.
제 5 장 계약 해지 및 이용 제한
제 15 조 (계약 해지)
회원이 이용계약을 해지하고자 하는 때에는 [가입해지] 메뉴를 이용해 직접 해지해야 합니다.
제 16 조 (서비스 이용제한)
① 당 사이트는 회원이 서비스 이용내용에 있어서 본 약관 제 11조 내용을 위반하거나, 다음 각 호에 해당하는
경우 서비스 이용을 제한할 수 있습니다.
- 2년 이상 서비스를 이용한 적이 없는 경우
- 기타 정상적인 서비스 운영에 방해가 될 경우
② 상기 이용제한 규정에 따라 서비스를 이용하는 회원에게 서비스 이용에 대하여 별도 공지 없이 서비스 이용의
일시정지, 이용계약 해지 할 수 있습니다.
제 17 조 (전자우편주소 수집 금지)
회원은 전자우편주소 추출기 등을 이용하여 전자우편주소를 수집 또는 제3자에게 제공할 수 없습니다.
제 6 장 손해배상 및 기타사항
제 18 조 (손해배상)
당 사이트는 무료로 제공되는 서비스와 관련하여 회원에게 어떠한 손해가 발생하더라도 당 사이트가 고의 또는 과실로 인한 손해발생을 제외하고는 이에 대하여 책임을 부담하지 아니합니다.
제 19 조 (관할 법원)
서비스 이용으로 발생한 분쟁에 대해 소송이 제기되는 경우 민사 소송법상의 관할 법원에 제기합니다.
[부 칙]
1. (시행일) 이 약관은 2016년 9월 5일부터 적용되며, 종전 약관은 본 약관으로 대체되며, 개정된 약관의 적용일 이전 가입자도 개정된 약관의 적용을 받습니다.