• 대한용접접합학회:학술대회논문집
• /
• 대한용접접합학회 2002년도 Proceedings of the International Welding/Joining Conference-Korea
• /
• pp.826-830
• /
• 2002

In the civil engineering and architecture fields, welding for large sectional members, such as I section steel and H section steel, are usually performed. a flash welding system, by which large I section steel or H section steel can be welded for a short time, was newly developed. In order to know the basic characteristics of welded joints, the specimens were cut out from flash welded joints, and tensile and fatigue experiments were carried out. The joint efficiency of welded joints by flash welding is 100% for the specimens with reinforcements and 93% for without reinforcements. The fatigue strength of welded joints with reinforcement was about 50% of that of the base metal. Removing the reinforcement generated by flash welding, fatigue strength of flash welded joints became 75% of that of the base metal. In case of flash welded joints with reinforcements, after a couple of fatigue cracks had propagated, ductile fracture occurred at the toe. In flash welded joints without reinforcements, fracture occurred at the bond or at HAZ (Heat Affected Zone). In case of fracture at the bond, fracture was brittle, and in case at HAZ, fracture was ductile.

• International Journal of Korean Welding Society
• /
• 제4권1호
• /
• pp.1-9
• /
• 2004

Continuously welded tracks, first introduced on train lines, are being used increasingly in Europe. And the different arc welding methods are only used on minor lines, private tracks and in the manufacturing of switches and crossings. Mobile flash butt welding belongs the future in rail welding on side if new tracks have to be erected. The following contribution reviews the processes available, usual test methods for welded rail joints and various applications.

• 대한용접접합학회:학술대회논문집
• /
• 대한용접접합학회 2006년도 춘계 학술대회 개요집
• /
• pp.118-120
• /
• 2006

• Journal of Welding and Joining
• /
• 제12권1호
• /
• pp.80-93
• /
• 1994

The microstructure and fractography of the friction welded joint of Al to Cu have been investigated in order to understand the formation of intermetallic compounds and their effects on the failure in tensile test of the joint. The variation of welding pressure did not affect significantly the tensile strength of joint. However, the tensile strength of joint decreaed as welding time increased. The thickness of reaction layers of welded joints was several micro-meters and mainly composed of intermetallic compounds of $CuAl_2$, $Cu_9Al_4$ and Al+$CuAl_2$. The thickness of $CuAl_2$, $Cu_9Al_4$ was increased with welding time. However, $CuAl_2$ was gradually changed to $Cu_9Al_4$ which caused the decrease of tensile strength . Even though the morphology of fractured surfaces depended upon the welding time, the failure occurred along $CuAl_2$ intermetallic compound itself or between $CuAl_2$ and $Cu_9Al_4$ in most cases.

• 한국생산제조학회지
• /
• 제21권6호
• /
• pp.932-937
• /
• 2012

In the presented study, SM45C carbon steel parts were joined by friction welding. The welding process was carried out under optimized conditions using statistical approach. The study of SM45C is conducted with various combinations of process parameters. Parameter optimization, microstructure and mechanical property correlation are the major contribution of the study. The welded joints were produced by varying spindle revolution speed, friction pressure, upset pressure and burn-off length. Tension tests were applied to welded parts to obtain the strength of the joints. Fracturs properties were additionally obtained experimentally under fluctuated tensile loads. Microstructures using microphotographs were examined in the weld interface and weld region and heat affected zone and base metal and flash zone of welded parts. Finally, Hardness variations in welding zone and base metal were also obtained. Through these tests, the optimum conditions of parameters for ${\phi}20$ SM45C in friction welding were obtained when the friction spindle revolution was 1,950 rpm, the friction pressures was 30 MPs, upset pressures was 50 MPs.

• International Journal of Korean Welding Society
• /
• 제3권2호
• /
• pp.24-28
• /
• 2003

This study was aimed to evaluate the quality of flash welded joints and optimize the welding process for flash butt welding of 780MPa grade high strength steel. And then the relationship between the welding process variables and the joint quality would be established. The effect of process variables between flashing and upsetting process was elucidated. Microstructure observation of the joint indicated that the decarburized band was mainly changed with upsetting process. Width of HAZ was also related to the upsetting conditions rather than the flashing conditions. Generally maximum hardness at HAZ was correlated with Ceq of steel and the empirical relationship was obtained to estimate the HAZ properties. Tensile elongation at the joint was usually decreased with increasing the initial clamping distance. Investigation of fracture surface after tensile and bending tests reveal that the origin of cracking at the joint was oxide inclusions composed of $SiO_2$, MnO, $Al_2O_3$, and/or FeO. The amount of inclusions was dependent on the composition ratio of Mn/Si in steel. If this ratio was above 4, the amount of inclusions was low and then the resistance to cracking at the joint was enough to maintain the joint performance. It was obtained that the flashing process influenced the conditions for the energy input to establish uniform or non­uniform molten layer, while the upsetting conditions influenced the joint strength. Heat input variable during flashing process was also discussed with the joint properties.

• 한국소성가공학회:학술대회논문집
• /
• 한국소성가공학회 2004년도 추계학술대회논문집
• /
• pp.301-304
• /
• 2004

Friction welding was used to weld the turbine wheel and shaft and have a good welding quality. Friction welding was conducted an the two dissimilar material, Nimonic 80A and SNCrW. The control of friction welding process parameter such as flywheel energy, interface temperature, amount of upset have an effect on the mechanical properties of the welded joint. FE simulation can be a useful tool to optimize the weld geometry and process parameters. Flash shape and thickness weld is consistent with the simulated results. Process analysis was performed by the commercial code DEFORM 2D. Mechanical property of weld joints was evaluated by microstructure, chemical component, tensile, impact, hardness test so on.