• Journal of the Korean Wood Science and Technology
• /
• v.33 no.2 s.130
• /
• pp.40-55
• /
• 2005

This study was carried out to discuss the feasibility of wood and plastic wastes as the raw materials for wood particle-plastic composites. For this purpose, composites were manufactured from coarse and fine wood particles and polypropylene fibers by nonwoven web process. And the effect of wood particle size on the performance of the composites were analyzed according to ASTM D 1037-93. In the physical properties of composites, water absorption decreased with the increase of target density and polypropylene fiber content. And the composites with fine wood particles appeared to have slightly lower water absorption than those with coarse wood particles. Thickness swelling did not vary significantly with the increase of target density but increased with the increase of wood particle content. And the composites with fine wood particles were significantly lower in thickness swelling than those with coarse wood particles. In the mechanical properties of composites, dry and wet MOR showed the increasing tendency with the increase of polypropylene fiber content and target density. Dry and wet MOE showed the increasing tendency with the increase of target density but only wet MOE exhibited the increasing tendency with the increase of polypropylene fiber content. Composites with fine wood particles appeared to be generally higher in wet MOR and MOE than those with coarse wood particles. In conclusion, composites with fine wood particles showed generally higher performance than those with coarse ones. Also, composites were significantly superior to control particleboards in the performance, especially in water absorption and thickness swelling.

• Journal of Power System Engineering
• /
• v.12 no.3
• /
• pp.55-59
• /
• 2008

In this paper, we have investigated on collection efficiency of fine particle of glass fiber-filter bag according to the surface treatment. The solution consisted of polytetrafluoroethylene(teflon), graphite powder, silicon resin and water was used as a basic surface treatment agent. Tensile strength of glass filter-bag increased with up to 3hrs and then decreased with surface treatment time. Tensile strength and initial modulus of the glass fiber-filter bag treated by iodine after basic surface treatment for 3hrs were lower than those of basic surface treatment for 3hrs, however collection efficiency and fracture strain were higher than those of basic surface treatment for 3hrs. Glass fiber-filter bag with lower initial modulus and more strain will be extend the durable period and the one treated by iodine after basic surface treatment 3or 3hrs is expected high collection efficiency of fine particle. This method makes it possible to manufacture glass fiber-filter bag of the optimum condition.

• Particle and aerosol research
• /
• v.10 no.2
• /
• pp.45-51
• /
• 2014

Fine particle capture is facing a challenge since traditional filtration which relies on the combination of impaction, interception, diffusion has a limited efficiency for fine particle capture particularly in size from 0.1 to $0.5{\mu}m$. This paper reviewed the collection efficiency of above mechanisms, as well as magnetic mechanisms for ferromagnetic particles, and mainly studied the influencing factors of magnetic filtration. Filtration velocity, magnetic field intensity and fiber size were found to be the most important parameters for magnetic filtration.

• Transactions of the Korean Society of Mechanical Engineers
• /
• v.19 no.9
• /
• pp.2342-2352
• /
• 1995

Deposition of flame-synthesized silica particles onto a target is utilized in optical fiber preform fabrication processes. The particles are convected and deposited onto the target. Falkner-Skan wedge flow was chosen as the particle laden flow. Typically the particles are polydisperse in size and follow a lognormal size distribution. Brownian diffusion, thermophoresis, and coagulation of the particles were considered and effects of these phenomena on particle deposition were studied. A moment model was developed in order to predict the particle number density and the particle size distribution simultaneously. Particle deposition with various wedge configurations was examined for conditions selected for a typical VAD process. When coagulation was considered, mean particle size and its standard deviation increased and particle number density decreased, compared to the case without coagulation. These results proved the fact that coagulation effect expands particle size distribution. The results were discussed with characteristics of thermal and diffusion boundary layers. As the boundary layers grow in thickness, overall temperature and concentration gradients decrease, resulting in decrease of deposition rate and increase of particle residence time in the flow and thus coagulation effect.

• Composites Research
• /
• v.13 no.1
• /
• pp.50-60
• /
• 2000

This paper presents an analytical method considering tensile strength enhancement in hybrid $Al_2O_3$ fiber/particle/aluminum composites(MMCs). The tensile strength and elastic modulus of the hybrid MMCs are even 20% higher than those of the fiber reinforced MMCs with same volume fraction of reinforcements. This phenomenon is explained by the cluster model which is newly proposed in this research, and the strengthening mechanisms by a cluster is analyzed using simple modified rule of mixtures. From the analysis, it is observed that cluster structure in hybrid MMCs increase the fiber efficiency factor for the tensile strength and the orientation factor for the elastic modulus. The present theory is then compared with experimental results which was performed using squeeze infiltrated hybrid MMCs made of hybrid $Al_2O_3$ short fiber/particle preform and AC8A alloy as base metal, and the agreement is found to be satisfactory.

• Journal of the Korean Ceramic Society
• /
• v.50 no.6
• /
• pp.528-532
• /
• 2013

Well-dispersed slurries of submicron-sized alumina powders were pressure-infiltrated in 3D preforms of mullite fibers and the effects of the particle size and infiltration pressure on the particle packing characteristics were investigated. Infiltration without pressure showed that the packing density increased as the particle size decreased due to the reduction of the friction between the particles and the fibers. The infiltrated preforms contained large pores in the large voids between the fiber tows and small pores in the narrow voids between the individual fibers. Pressure infiltration resulted in a packing density of 77% regardless of the particle size or the infiltration pressure(210 ~ 620 kPa). Pressure infiltration shortened the infiltration time and eliminated the large pores in preforms infiltrated with the slurries of smaller particles. The slurry pressure-infiltration process is thus an efficient method for the packing of matrix materials in various preforms.

• Proceedings of the Korean Society of Marine Engineers Conference
• /
• 2000.05a
• /
• pp.122-126
• /
• 2000

In particle or short-fiber reinforced composites cracking of the reinforcements is a significant damage mode because the broken reinformcements lose load carrying capacity . The average stress in the inhomogeneity represents its load carrying capacity and the difference between the average stresses of the intact and broken inhomogeneities indicates the loss of load carrying capacity due to cracking damage. The composite in damage process contains intact and broken reinforcements in a matrix, An incremental constitutive relation of particle or short-fiber reinforced composites including the progressive cracking damage of the reinforcements have been developed based on the Eshelby's equivalent inclusion method and Mori-Tanaka's mean field concept. influence of the cracking damage on the Eshelby's equivalent inclusion method and Mori-Tanaka's mean field concept. Influence of the cracking damage on the stress-strain response of the composites is demonstrated.

• Journal of the Korean Ceramic Society
• /
• v.32 no.7
• /
• pp.846-852
• /
• 1995

The multiply reinforced mullite-zirconia composites were prepared with addition of Al2O3 particles, platelets, and fibers. The sinter-HIP specimens (presintered at 1$700^{\circ}C$ and hipped at 1$600^{\circ}C$) showed that the fracture toughness of Al2O3 fiber reinforcement (4.4 MPa.{{{{ SQRT {m} }}) was higher than those of platelet (4.0 MPa.{{{{ SQRT {m} }}) and of particle (3.9MPa.{{{{ SQRT {m} }}) reinforcement, whereas the fracture strength of Al2O3 particle reinforcement (304 MPa) was higher than those of platelet (293MPa) and of fiber (248MPa) reinforcement.

• Journal of Power System Engineering
• /
• v.10 no.1
• /
• pp.46-51
• /
• 2006

Present study was investigated the effect of the particle of the counterface of unidirectional carbon fiber reinforced composite. The friction coefficient of composite and the specific wear rate different sliding velocity were measured for this materials. The friction track of counterface was observed by an optical microscope and scanning electron microscope. There were insignificant effects of the specific wear rate under lower Sic abrasive particle, however it showed high effect on $30{\mu}m$ abrasive particle size. There were significant effects of friction and wear behavior of the fiber direction under 0.3m/s sliding speed. Major failure mechanisms can be classified such as microfracture, plowing, microcutting, cutting and cracking.

• Proceedings of the Korean Fiber Society Conference
• /
• 2003.10a
• /
• pp.65-66
• /
• 2003

Ternary blend fibers (TBFs) based on melt blends of PEN, PET, and TLCP were prepared by melt blending and spinning to achieve high performance fibers. The reinforcement effect and the TLCP fibrillar structure resulted in the improvement of mechanical properties for TBFs. Molecular orientation was an important factor in determining the tensile strength and modulus of TBFs. Another part of this research is silica nano-particle filled PEN composites were melt-blended to improve mechanical and physicalproperties, and processability. The tensile modulus and strength were improved adding silica nano-particles to the PEN. The decreased melt viscosity by the fumed silica resulted in the improvement of the processability. The fumed silica may act as a nucleating agent in the PEN matrix.