• 대한금속재료학회지
• /
• 제46권9호
• /
• pp.593-603
• /
• 2008

In this study, effects of alloying elements on the sticking occurring during hot rolling of five kinds of ferritic STS430J1L stainless steels were investigated by analyzing high-temperature hardness and oxidation behavior of the rolled steels. Hot-rolling simulation tests were conducted by a high-temperature wear tester which could simulate actual hot rolling. The simulation test results revealed that the sticking process proceeded with three stages, i.e., nucleation, growth, and saturation. Since the hardness continuously decreased as the test temperature increased, whereas the formation of Fe-Cr oxides in the rolled steel surface region increased, the sticking of five stainless steels was evaluated by considering both the high-temperature hardness and oxidation effects. The addition of Zr, Cu, or Si had a beneficial effect on the sticking resistance, while the Ni addition did not show any difference in the sticking. Particularly in the case of the Si addition, Si oxides formed first in the initial stage of high-temperature oxidation, worked as initiation sites for Fe-Cr oxides, accelerated the formation of Fe-Cr oxides, and thus raised the sticking resistance by about 10 times in comparison with the steel without Si content.

• 한국소성가공학회:학술대회논문집
• /
• 한국소성가공학회 2004년도 제5회 압연심포지엄 신 시장 개척을 위한 압연기술
• /
• pp.11-18
• /
• 2004

Asymmetric rolling, in which the circumferential velocities of the upper and lower rolls are different, can give rise to intense plastic shear strains and in turn shear deformation textures through the sheet thickness. The ideal shear deformation texture of fcc metals can be approximated by the <111> // ND and $\{001\}<110>$ orientations, among which the former improves the deep drawability. The ideal shear deformation texture for bcc metals can be approximated by the Goss $\{110\}<001>\;and\;\{112\}<111>$ orientations, among which the former improves the magnetic permeability along the <100> directions and is the prime orientation in grain oriented silicon steels. The intense shear strains can result in the grain refinement and hence improve mechanical properties. Steel sheets, especially ferritic stainless steel sheets, and aluminum alloy sheets may exhibit an undesirable surface roughening known as ridging or roping, when elongated along RD and TD, respectively. The ridging or roping is caused by differently oriented colonies, which are resulted from the <100> oriented columnar structure in ingots or billets, especially for ferritic stainless steels, that is not easily destroyed by the conventional rolling. The breakdown of columnar structure and the grain refinement can be achieved by asymmetric rolling, resulting in a decrease in the ridging problem.

• 한국주조공학회지
• /
• 제17권6호
• /
• pp.577-584
• /
• 1997

Evaluation of rolling contact fatigue damage as well as material development for roll of rolling mill is being studied until quite recently. In this paper, a focus has been imposed on evaluating the rolling contact fatigue damage. In order for this, the accumulating process of rolling contact damage using the ferritic, pearlitic and bainitic DCI has been analyzed by X-ray diffraction technique. The main finds are; 1) The graphite in DCI is considered to be a cause of interfering in the redistribution of stress. Eventually, it results in the branching of crack. 2) The evaluation of rolling contact fatigue damage can be estimated in terms of the change of residual stress and/or a half-value breadth on surface during rolling contact.

• 대한기계학회:학술대회논문집
• /
• 대한기계학회 2003년도 춘계학술대회
• /
• pp.13-18
• /
• 2003

Reduced activation ferritic steel, JLF-1 steel (Fe-9Cr-2W-V-Ta), is one of the promising candidate materials for fusion reactor applications. Fracture toughness ($J_IC$) and tensile tests were carried out at room temperature and elevated temperature ($400^{\circ}C$). Two types of CT specimen were prepared to examine the effect of rolling direction on the fracture toughness of JLF-1 steel. Four types of tensile specimen were also prepared to investigate the property by the rolling direction and welding. The Micro Vickers hardness was measured at various distances of a cross section of the TIG joints of JLF-1 steel according to the heating history of each position. Finally, the fracture surface was observed by scanning electron microscopy (SEM).

• 대한기계학회:학술대회논문집
• /
• 대한기계학회 2001년도 춘계학술대회논문집A
• /
• pp.181-186
• /
• 2001

JLF-1 steel (Fe-9Cr-2W-V-Ta), low activation ferritic steel, is one of the promising candidate materials fer fusion reactor applications. High temperature fatigue life and tensile strength of JLF-1 steel and its TIG welded joints were investigated at the room temperature and $400^{\circ}C$. The strength of base metal (JLF-1) is in between those of weld metal and the HAZ. When the test temperature was increased from room temperature to $400^{\circ}C$, both strength and ductility decreased for base metal, weld metal and the HAZ. The longitudinal specimens of base metal showed similar strength and ductility compared with those of the transverse specimens at room temperature and $400^{\circ}C$. Little anisotropy was observed in the JLF-1 steel base metal in terms of rolling direction. Fatigue limit of weld metal which was obtained from cross-weld specimen is 495MPa. Thus, the weld metal showed the higher fatigue limit than those of base metal at both room temperature and $400^{\circ}C$. Little anisotropy of fatigue properties was observed for JLF-1 base metal in terms of rolling direction. When the test temperature was increased from room temperature to $400^{\circ}C$, the fatigue limit of both base metal and weld metal decreased substantially.

• 한국소성가공학회:학술대회논문집
• /
• 한국소성가공학회 2003년도 추계학술대회논문집
• /
• pp.136-137
• /
• 2003

Recrystallization textures of ferritic stainless steel sheets of STS 430, the crystallographic texture was modified by means of cross rolling and subsequent annealing. The conventional normal rolling led to the formation of ｛334｝＜483＞ in the final recrystallization texture. Cross rolling in the present work was performed by a 45$^{\circ}$rotation of RD around ND. After recrystallization annealing the cross-rolled samples displayed stronger｛111｝//ND orientations. The cross rolled sample displayed a higher resistance against ridging.

• 한국소성가공학회:학술대회논문집
• /
• 한국소성가공학회 2004년도 춘계학술대회 논문집
• /
• pp.225-227
• /
• 2004

Recrystallization textures of ferritic stainless steel sheets of STS 430 were varied by means of different cold rolling procedures. The conventional normal rolling led to the evolution of strong through-thickness texture gradients in the final recrystallization texture, while the cross-rolling led to a decrease in texture gradients. Micro-texture observation by EBSD revealed that the formation of band-like orientation colonies formed close to the center layer was responsible for ridging. Modification of the recrystallization texture and microstructure by cross-rolling destroyed band-like orientation colonies and consequently reduced the ridging height.

• 대한기계학회논문집A
• /
• 제27권9호
• /
• pp.1444-1450
• /
• 2003

The fatigue life and tensile strength of JLF-1 steel (Fe-9Cr-2W-V-Ta) and its TIG weldment were investigated at the room temperature and $400^{\circ}C$. Four kinds of test specimens, which associated with the rolling direction and the TIG welding direction were machined. The base metal of JLF-1 steel represented almost anisotropy in the tensile properties for the rolling direction. And the base metal of JLF-1 steel showed lower strength than that of TIG weldment. Also, the strength of all materials entirely decreased in accordance with elevating test temperature. Moreover, the fatigue limit of weld metal was largely increase than that of base metal at both temperatures. The fatigue limit of JLF-1 steel decreased in accordance with elevating test temperature. The fatigue limit of JLF-1 steel decreased in accordance with elevating test temperature. The SEM fractography of tensile test specimen showed conspicuous cleavage fracture of a radial shape. In case of fatigue life test specimen, there were so many striations at crack initiation region, and dimple was observed at final fracture region as a ductile fracture mode.

• 대한금속재료학회지
• /
• 제47권10호
• /
• pp.621-628
• /
• 2009

Thermomechanical processes were carried out to evaluate their effects on the mechanical and the microstructural property of a ferritic-martensitic steel. Modified 9Cr-1Mo steels were hot-rolled at a temperature of either $780^{\circ}C$ or $850^{\circ}C$ after normalizing at $1050^{\circ}C$ and then were air-cooled. Continuous annealing at $850^{\circ}C$ for 2 hours immediately after the hot rolling was also performed and they were compared to the specimens without thermomechanical process. The result showed that there were little differences between the hot rolled specimens in terms of the precipitation density and size. However, V content inside the MX precipitates increased in the case of the specimen rolled at $850^{\circ}C$. The application of the continuous annealing induced coarsening of the Nb-rich MX precipitation as well as an increase in the amount of V-rich MX precipitation, which is expected to enhance high temperature mechanical properties of the ferritic-martensitic steel.

• 한국소성가공학회:학술대회논문집
• /
• 한국소성가공학회 1999년도 제3회 압연심포지엄 논문집 압연기술의 미래개척 (Exploitation of Future Rolling Technologies)
• /
• pp.366-372
• /
• 1999

The deformation behavior of commercial stainless steels under hot rolling conditions was investigated by means of hot compression tests performed in the temperature range 800$^{\circ}C$ to 1200$^{\circ}C$. The measured flow stress-strain curves were analyzed by using a simple flow stress model. It was found that the reference strength of stainless steels are much higher than that of carbon steel and that nitrogen and molybdenum alloying greatly increases flow stress of austenitic stainless steel. Ferritic and duplex stainless steel showed comparatively low flow stresses. The flow stress model, which correlates the flow stress with temperature and strain rate, was applied to predict roll forces during hot-plate rolling of stainless steels.