• 한국수소및신에너지학회논문집
• /
• 제10권3호
• /
• pp.185-189
• /
• 1999

Effects of alloy modification with the $Zr_{0.6}Ti_{0.4}V_{0.4}Ni_{1.2}Mn_{0.4}$ alloy for an electrode use have been investigated. For the alloy composition, a part of Mn was substituted by Co, Cr and Fe. The experimental results showed that Co accelerated activation of alloy, and Fe and Cr improved the discharge capacity. These results agree with P-C-T curves of each alloy. But substituting Fe for Mn showed the decrease of the discharge capacity when discharged at high rate (60mA, about 1C rate). Considering both the discharge capacity and the high rate discharge property, $Zr_{0.6}Ti_{0.4}V_{0.4}Ni_{1.2}Mn_{0.3}Cr_{0.1}$ alloy was found to be the best alloy among the alloys subjected to the test.

• 한국재료학회지
• /
• 제24권9호
• /
• pp.481-487
• /
• 2014

The effect of alpha phase on the fatigue properties of Fe-29%Ni-17%Co low thermal expansion alloy was investigated. Two kinds of alloys (Base alloy and Alpha alloy) were prepared by controlling the minimal alloy composition. Microstructure observation, tensile, high-cycle fatigue, and low-cycle fatigue results were measured in this study. The Base alloy microstructure showed typical austenite ${\gamma}$ phase. Alpha alloy represented the dispersed phase in the austenite ${\gamma}$ matrix. As a result of tensile testing, Alpha alloy was found to have higher strengths (Y.S. & T.S.) and lower elongation compared to those of the Base alloy. High cycle fatigue results showed that Alpha alloy had a higher fatigue limit (360MPa) than that (330MPa) of the Base alloy. The Alpha alloy exhibited the superior high cycle fatigue property in all of the fatigue stress conditions. SEM fractography results showed that the alpha phase could act to effectively retard both fatigue crack initiation and crack propagation. In the case of low-cycle fatigue, the Base alloy had longer fatigue life in the high plastic strain amplitude region and the Alpha alloy showed better fatigue property only in the low plastic strain amplitude region. The fatigue deformation behavior of the Fe-29%Ni-17%Co alloy was also discussed as related with its microstructure.

• 한국입자에어로졸학회지
• /
• 제8권2호
• /
• pp.83-88
• /
• 2012

The electrical wire explosion process in liquid media is promising for nano-sized metal and/or alloy particles. The hybrid Pt/Fe-Cr-Al and Pt/Ni-Cr-Fe nanoparticles for exhaust emission control system are synthesized by electrical wire explosion process in liquid media. The alloy powders have spherical shape and nanometer size. According to the wire component, while Pt/Fe-Cr-Al nanoparticles are shown the well dispersed Pt on the Fe-Cr-Al core particle, Pt/Ni-Cr-Fe nanoparticles are shown the partially separated Pt on the Ni-Cr-Fe core particle. Morphologies and component of two kinds of hybrid nano catalyst particles were characterized by transmission electron microscope and energy dispersive X-ray spectroscopy analysis.

• 한국재료학회지
• /
• 제11권11호
• /
• pp.986-990
• /
• 2001

An optimum route to fabricate the $A1_2O_3/Fe-Ni$ alloy nanocomposites with sound microstructure and enhanced mechanical properties as well as magnetism was investigated. To prepare homogeneous nanocomposite powders of Fe-Ni alloy and $Al_2O_3$, the solution-chemistry routes using $Al_2O_3 \; Ni(NO_3)_2{\cdot}6H_2O$ and $Fe(NO_3)_3{\cdot}9H_2O$ powders were applied. Microstructural observation of the powder mixture revealed that the Fe-Ni alloy particles of about 20 nm in size were homogeneously surrounded $A1_2O_3$, forming nanocomposite powder. The hot-pressed composite showed improved fracture toughness and magnetic response. These results suggest that the synergy materials with an improved mechanical properties and excellent functionality can be fabricated by controlled powder preparation and consolidation processing.

• 한국재료학회지
• /
• 제12권1호
• /
• pp.16-20
• /
• 2002

In this study, the 95W heavy alloys of 3/7, 5/5 and 7/3 of Ni/Fe ratio were sintered at the temperature range between 1420 and $1480^{\circ}C$ for 1h and their microstructures were discussed for an effect of the ${\mu}$-phase $(Fe_7W_6)$ on the microstructure. The ${\mu}$-phase was observed in the only 95W-1.5Ni-3.5Fe alloy of 3/7 and it is thought to be formed and grown from the surface of the W particle. The W particle was surrounded with the ${\mu}$-phase and there were only the W particles and this phase without Ni-Fe-W matrix at the most part. The ${\mu}$-phase changed the interphase structure in the alloy and the grain growth of the W was suppressed because of interrupting the solution-reprecipitation of the W. The W content in the matrix was considered to be lowered due to the interruption of the solution-reprecipitation and the formation of the ${\mu}$-phase in the .

• 한국분말재료학회지
• /
• 제8권1호
• /
• pp.49-54
• /
• 2001

The synthesis and characteristics of W-Ni-Fe nanocomposite powder by hydrogen reduction of ball milled W-Ni-Fe oxide mixture were investigated. The ball milled oxide mixture was prepared by high energy attrition milling of W blue powder, NiO and $Fe_2O_3$ for 1 h. The structure of the oxide mixture was characteristic of nano porous agglomerate composite powder consisting of nanoscale particles and pores which act as effective removal path of water vapor during hydrogen reduction process. The reduction experiment showed that the reduction reaction starts from NiO, followed by $Fe_2O_3$ and finally W oxide. It was also found that during the reduction process rapid alloying of Ni-Fe yielded the formation of $\gamma$-Ni-Fe. After reduction at 80$0^{\circ}C$ for 1 h, the nano-composite powder of W-4.57Ni-2.34Fe comprising W and $\gamma$-Ni-Fe phases was produced, of which grain size was35nm for W and 87 nm for $\gamma$-Ni-Fe, respectively. Sinterability of the W heavy alloy nanopowder showing full density and sound microstructure under the condition of 147$0^{\circ}C$/20 min is thought to be suitable for raw material for powder injection molding of tungsten heavy alloy.

• 한국재료학회지
• /
• 제24권10호
• /
• pp.515-519
• /
• 2014

The aim of this paper is to consider the effect of annealing on the coefficient of thermal expansion (CTE) of electroplated Invar Fe-Ni alloy. The CTE of the as-electroplated alloy is lower than those of alloys annealed at $400^{\circ}C$ and $800^{\circ}C$. XRD peaks become sharper as the as-electroplated alloy is annealed, which means the grain growth. The average grain sizes of as-electroplated and as-annealed alloys at $400^{\circ}C$ and $800^{\circ}C$ are 10 nm, 70 nm, and $2{\mu}m$, respectively, as determined by TEM and EBSD analyses. The CTE variation for the various grain sizes after annealing may come from the magnetostriction effect, which generates strain due to changes in the magnetization state of the alloys. The thermal expansion coefficient is considered to be affected by nano grain size in electroplated Fe-Ni Invar alloys. As grain size decreases, ferromagnetic forces might change to paramagnetic forces. The effect of lattice vibration damping of nano grain boundaries could lead to the decrease of CTE.

• 한국분말재료학회지
• /
• 제13권3호
• /
• pp.178-186
• /
• 2006

The effect of use of $H_2O$ as PCA(process control agent) to prevent the carbon contamination during mechanical alloying process and the precipitation behavior in Ni-20Cr-20Fe-5Nb bulk alloy after aging were investigated. NbC and $Cr_2O_3$ were formed during mechanical alloying and consolidation processes in the Ni-20Cr-20Fe-5Nb alloy in which methanol($CH_3OH$) was added as PCA. Formation of NbC in this alloy decreased the amount of Nb dissolved in the Ni matrix. The use of $H_2O$ as PCA in Ni-20Cr-20Fe-5Nb alloy prevented the formation of NbC and increased the hardness. The increase of hardness in this alloy was attributed to the increased amount of Nb dissolved in the Ni matrix. After aging treatment for 20 hours at $600^{\circ}C\;and\;720^{\circ}C$ of Ni-20Cr-20Fe-5Nb bulk alloy in which $H_2O$ added as PCA, ${\gamma}"$$(Ni_3Nb,\;tetragonal)\;and\;{\delta}\;(Ni_3Nb,\;orthorhombic)$ precipitates were formed, respectively. The precipitation temperatures of ${\gamma}"$ and ${\delta}$ in this bulk alloy were lower than those in commercial IN 718 alloy. It seemed that the lower precipitation temperatures for ${\gamma}"$ and ${\delta}$ in this bulk alloy than in commercial IN 718 alloy were due to severe plastic deformation during mechanical alloying.

• 한국재료학회지
• /
• 제16권2호
• /
• pp.137-143
• /
• 2006

The effects of Cu and Fe additions on the thermal stability, microstructure and mechanical properties of $Al_{85}-Ni_{8.5}-Mm_{6.5},\;Al_{84}-Ni_{8.5}-Mm_{6.5}Cu_1,\;Al_{84}-Ni_{8.5}-M_{m6.5}Fe_1$ alloys, manufactured by gas atomization, degassing and hot-extrusion were investigated. Gas atomization, with a wide super-cooled liquid region, allowed the alloy powders to exhibit varying microstructure depending primarily on the powder size and composition. Al hotextruded alloys consisted of homogeneously-distributed fine-grained fcc-Al matrix and intermetallic compounds. A substitution of 1 at.% Al by Cu increased the thermal stability of the amorphous phase and produced alloy microstructure with smaller fcc-Al grains. On the other hand, the same substitution of 1 at.% Al by Fe decreased the stability of the amorphous phase and produced larger fcc-Al grains. The formation of intermetallic compounds such as $Al_3Ni,\;Al_{11}Ce_3\;and\;Al_{11}La_3$ was suppressed by the addition of Cu or Fe. Among the three alloys examined, the highest Vickers hardness and compressive strength were obtained for $Al_{84}-Ni_{8.5}-M_{m6.5}Cu_1$ alloy, and related to the finest fcc-Al grain size attained from increased thermal stability with Cu addition.

• 한국수소및신에너지학회논문집
• /
• 제9권4호
• /
• pp.135-141
• /
• 1998

Fe-Ti계 수소저장합금 전극의 방전특성을 개선하기 위하여 Ni을 첨가한 $TiFe_{1-x}Ni_x$ 합금을 제조하여 방전특성과 열처리 온도에 따른 변화를 조사하였다. 합금의 조성은 x = 0.1에서 0.6까지 0.1 단위씩 변화시킨 6가지 조성을 선택하여 각각에 대한 초기방전용량과 충방전사이클에 따른 용량변화를 조사하였다. 초기방전용량은 Ni의 조성이 클수록 증가하다가 x = 0.6 에서 다시 감소하였으며 Ni의 조성이 증가함에 따라 사이클특성은 전반적으로 매우 악화되었다. 열처리온도가 사이클 특성에 미치는 영향을 조사하기 위하여 초기용량이 가장 우수한 $TiFe_{0.5}Ni_{0.5}$ 합금에 대하여 $700{\sim}900^{\circ}C$ 의 온도범위에서 열처리를 시행한 후 방전특성을 조사하였다. 열처리에 의해서 초기용량은 감소되지만 사이클 특성은 현저히 개선되었다. $700{\sim}850^{\circ}C$의 온도범위에서 1시간 열처리한 전극의 경우에 사이클이 진행되면서 방전용량이 크게 회복되었으며, 열처리한 표면조직을 SEM 으로 관찰해 본 결과 이는 충분한 전극강도 및 기공율에 기인한 것으로 생각되었다. $900^{\circ}C$에서 1시간 열처리한 전극은 충분한 기공율을 갖지 못하여 방전특성이 좋지 않음을 알 수 있었다.