• 한국재료학회지
• /
• 제16권5호
• /
• pp.318-322
• /
• 2006

Short-term high temperature degradation test was conducted on Hastelloy X, a candidate tube material for high temperature gas-cooled reactors (HTGR), to evaluate the variation of microstructure and mechanical property in air at $1050^{\circ}C$ during 2000 h. The dominant oxide layer was Cr-oxide and a very shallow Cr-depleted region was observed below the oxide layer. At the beginning of degradation, the island shape $M_6C$ precipitate (M=Mo-rich, Fe, Ni, Cr) was observed in matrix region. After 2000 h degradation, precipitate shape was changed to the chain shape and increased amount of precipitate. These results influenced mechanical property of the specimen which exposed in high temperature. Yield strength was decreased from 115MPa to 89 MPa after 24 h and 2000 h exposure, respectively.

• 대한금속재료학회지
• /
• 제47권2호
• /
• pp.129-137
• /
• 2009

Corrosion behaviors of TiN coated dental casting alloys have been researched by using various electrochemical methods. Three casting alloys (Alloy 1: 63Co-27Cr-5.5Mo, Alloy 2: 63Ni-16Cr-5Mo, Alloy 3: 63Co-30Cr-5Mo) were prepared for fabricating partial denture frameworks with various casting methods; centrifugal casting(CF), high frequency induction casting(HFI) and vacuum pressure casting(VP). The specimens were coated with TiN film by RF-magnetron sputtering method. The corrosion behaviors were investigated using potentiostat (EG&G Co, 263A. USA) in 0.9% NaCl solution at $36.5{\pm}1^{\circ}C$. The corrosion morphologies were analyzed using FE-SEM and EDX. Alloy 1 and Alloy 2 showed the ${\alpha}-Co$ and ${\varepsilon}-Co$ phase on the matrix, and it was disappeared in case of TiN coated Alloy 1 and 2. In the Alloy 3, $Ni_2Cr$ second phases were appeared at matrix. Corrosion potentials of TiN coated alloy were higher than that of non-coated alloy, but current density at passive region of TiN coated alloy was lower than that of non-coated alloy. Pitting corrosion resistances were increased in the order of centrifugal casting, high frequency induction casting and vacuum pressure casting method from cyclic potentiodynamic polarization test.

• 한국결정성장학회지
• /
• 제19권3호
• /
• pp.152-158
• /
• 2009

산업용 뿐만 아니라 보석용으로 가치가 있는 사파이어는 매우 다양한 방법으로 합성 사파이어를 만들어 왔다. 그 중 천연 사파이어와 매우 유사하며 보석용으로 가치가 높은 Chatham사의 플럭스 사파이어를 사용하여 천연 사파이어와 비교하였다. 먼저 WD-XRF(Wavelength dispersive x-ray fluorescence spectrometer)를 사용하여 천연과 합성의 화학 조성을 비교하였다. 천연 사파이어는 화학 조성이 매우 다양하였으나 플럭스 사파이어는 천연과 유사한 화학 성분과 특히 Mo, Pt, Pb 미량원소가 검출되었다. Pt는 플럭스 사파이어라는 결정적인 증거가 된다. 다음으로 $1300^{\circ}C$와 $1500^{\circ}C$의 고온에서 열처리를 한 후 자외선-가시광선 분광광도계(UV-VIS Spectrophotometer)를 사용하여 분광학적 특성을 조사함으로써 천연 사파이어는 $Cr^{3+}$와 관련된 약 690nm의 형광과 관련된 흡수 피크의 변화를 관찰할 수 있었고 플럭스 사파이어는 $Cr^{3+}$와 관련된 약 690nm의 피크와 376nm, 388nm의 $Fe^{3+}$의 흡수 피크가 변화함을 볼 수 있었다. 고온 열처리에 의해 플럭스 사파이어의 흡수 피크의 변화가 천연 사파이어의 흡수 피크의 변화보다 더 큰 것을 알 수 있었다 화학조성 및 분광분석 실험을 통하여 천연 사파이어와 flux 합성 사파이어의 특성을 비교 분석하였다.

• 자원환경지질
• /
• 제28권3호
• /
• pp.251-257
• /
• 1995

영국의 2개 화력발전소로부터 석탄연소 폐기물 시료를 17년, 약40년 풍화된 것 그리고 풍화되지 않은 것의 구분으로 각각 채취하였다. 이 시료들과 증류수, 인공 침출수등을 이용, 뱃치 실험을 실시하였다. 통화되지 않은 시료의 증류수를 통한 실험에서는 Ca, Na, K, S, B, Cr, Cu, Li, Ni, Mo 그리고 $Cl^-$ 등 원소가 다량으로 방출되는 것이 관찰되었으며 이는 이들 원소들이 주로 표면에 수반된다는 증거가 된다. Mg, Al, Ba, Si, V, As 그리고 Se등은 이러한 다량방출을 하지 않는바 이들 원소들은 입자 표면보다는 PFA 입자의 유리질에 수반되는 것으로 생각된다. 풍화 PFA시료를 통한 실험에서는 유리질과 같은 상온에서 불안정한 상에 수반되는 용융성원소들이 용액으로 방출됨이 증명되었다. 인공 침출수를 이용한 실험에서는 Fe, Ca, Cr, Cu, Ni, Zn 그리고 Hg등이 제거되는것이 관찰되었으며 이는 용액으로부터 제거되어 고체 PFA의 성분에서 증가하는것을 통하여도 확인된다. 중금속 제거정도는 Meaford>Drax 풍화시료>Drax 신선한 시료의 순이며 이는 풍화의 정도와도 일치한다. 즉 풍화를 많이 받은 시료에서 더 많은 중금속이 제거되는 결과를 보여준다.

• 공업화학
• /
• 제9권5호
• /
• pp.774-780
• /
• 1998

스피넬 구조인 $LiMn_2O_4$의 안정성을 향상시키기 위해서 망간과 비슷한 이온반경을 갖는 여러 가지 금속원소, Mg, Fe, V, W, Cr, Mo들을 일부 치환하였으며 ($LiM_xMn_{2-x}O_4(0.05{\leq}x{\leq}0.02)$), 이 결과 $LiM_xMn_{2-x}O_4$ 정극은 정극물질로 사용할 경우 $LiMn_2O_4$보다 낮은 용량감소를 나타냈다. 그리고 화학확산계수의 측정 결과 $LiMg_{0.05}Mn_{1.9}O_4$와 $LiCr_{0.1}Mn_{1.9}O_4$의 화학확산계수는 $LiMn_2O_4$보다 약 10배 이상 크게 나타났다. 이러한 결과를 볼 때 $LiMn_2O_4$에 여러 가지 금속원소를 치환시킴으로 구조적인 안정화로 인한 전기화학적 성능을 향상시킬 수 있었다.

• 대한기계학회논문집A
• /
• 제26권12호
• /
• pp.2565-2573
• /
• 2002

A basic research was performed to ensure the usefulness of Small Punch-creep(SP-creep) test for residual life evaluation of heat resistant components effectively. This paper presents analytical results of initial stress and strain distributions in SP specimen caused by constant loading for SP-creep test and its experimental correlations with uniaxial creep(Ten-creep) test on 9Cr1MoVNb steel. It was shown that the initial maximum equivalent stress, ${\sigma}_{eq{\cdot}max}$ from FE analysis was correlated with steady-state equivalent creep strain rate, ${\epsilon}_{qf-ss'}$ rupture time, $t_r$, activation energy, Q and Larson-Miller Parameter, LMP during SP-creep deformation. The simple correlation laws, ${\sigma}_{sp}-{\sigma}_{TEN}$, $P_{sp}-{\sigma}_{TEN}\; and\; Q_{sp}-Q_{TEN}$ adopted to established a quantitative correlation between SP-creep and Ten-creep test data. Especially, the activation energy obtained from SP-creep test is linearly related to that from Ten-creep test at $650^{\circ}C$ as follows : $Q_{SP-P}\;{\risingdotseq}\;1.37 \;Q_{TEN},\; Q_{SP-{\sigma}}{\risingdotseq}1.53\; Q_{TEN}$.

• 한국재료학회지
• /
• 제7권3호
• /
• pp.218-223
• /
• 1997

과냉각액체구역(${\Delta}T_{x}=T_{x}-T_{g}$)을 갖는 $Fe_{80}P_{10}C_{6}B_{4}$ 조성에 천이금속(Ti, Zr, Hf, V, Nb, Ta, Cr, Mo, W, Mn, Co, Ni, Pd, Pt및 Cu)를 첨가하여 이들 원소가 유리화온도($T_{g}$), 결정화온도($T_{x}$) 및 과냉액체구역 (${\Delta}T_{x}$)에 미치는 영향에 \ulcorner여 조사하였다. $Fe_{80}P_{10}C_{6}B_{4}$ 합금의 ${\Delta}T_{x}$ 값은 27K였으나 이 합금에 Hf, Ta 및 Mo을 각각 4at%첨가하면 그 값이 40k 이상으로 증가하였다. 이같은 ${\Delta}T_{x}$ 값의 증가는 유리화온도($T_{g}$의 상승보다 결정화온도($T_{x}$)의 상승폭이 크기 때문이다. $T_{g}$ 및 $T_{x}$는 외각전자밀도(e/a)가 약 7.38에서 7.05로 감소할수록 상승하였다. e/a의 감소는 천이금속과 다른 구성원소(반금속)사이의 상호결합상태를 의미한다. 즉 $T_{g}$ 및 $T_{x}$의 상승은 강한 상호결합력에 기인하는 것으로 사료된다.

• 한국방사성폐기물학회:학술대회논문집
• /
• 한국방사성폐기물학회 2005년도 춘계 학술대회
• /
• pp.121-128
• /
• 2005

방사성 폐기물의 핵종 재고량 평가에 필요한 정량분석을 위하여 다양한 매질의 방사성 폐기물 시료로부터 $^{99}Tc,\;^{94}Nb,\;^{55}Fe,\;^{90}Sr$ 및 $^{59}Ni(^{63}Ni)$의 선택적 분리에 관한 연구가 수행되고있다. 방사성 폐기물 용해용액의 화학조성을 모사하여 만든 모의 방사성 폐기물 용해용액을 사용하여 음이온교환수지법과 Sr-Spec 추출 크로마토그래피로 Re ($^{99}Tc$ 대용원소), Nb, Fe 및 Sr을 분리해 낸 후 Ni과 함께 회수되는 Ce, Ca, Mg, Al, Cr, Ti, Mn 및 Cu와 Ni의 분리 거동을 Ni-Spec 추출크로마토그래피와 양이온교환수지법으로 조사하였다. 공존원소들로부터 Ni의 선택적 분리와 기체비례계수법에 의한 방사능 측정에 적합한 radionuclide source를 만들기 위하여 공존원소들에 대한 가리움제로 ammonium citrate 및 tartaric acid를 사용하는 dimethylglyoxime 침전법의 적용에 관하여 기술하였다.

• 열처리공학회지
• /
• 제13권6호
• /
• pp.412-419
• /
• 2000

There has been a considerable attention on Invar alloys due to its low thermal expansion property. A low thermal expansion property of Invar alloys, lower than $10^{-6}$ near the room temperature, is attractive for electric transmission lines and precision machine tools. However, the expansion property of Invar alloys is limited below about 520K, and mechanical properties are relatively low to apply to electric transmission line. In order to improve mechanical properties in this alloy, Ti alloying element was added to the $Ni_{38}-Mo_2-Cr_1-Fe$ invar alloy. The microstructure Ti added alloy showed finer than that of the unalloyed one. It was found that the (Mo, Ti), Mo carbide formed by Ti addition obstacled grain growth by pinning effect and supplyed recrystallization sites during heat-treatment. Optimum heat-treatment conditions with Ti addition were also discussed in the modified Invar alloy.

• 한국주조공학회지
• /
• 제15권3호
• /
• pp.283-290
• /
• 1995

Molybdenum ingot of 50mm in diameter were obtained from sintered Mo bars by EB drip melting technique. Macroscopic observation of EB remelted ingot indicates that coarse and columnar grains grow in the direction parallel to ingot pulling direction. This can be explained by slow solidification (3mm/min), large temperature gradient and heat flow to this direction. The orientation of columnar structure was found to be <110>, <200> and <211> by the analysis of X-ray diffraction patterns. The contents of typical metallic impurities in Mo sintered bar are 1.2ppm Cr, 3ppm Fe, 44ppm Zr, 150ppm W. Most of metallic impurities were reduced below the order of ppm except zirconium and tungsten by the selective evaporation. In the removal of nonmetallic impurities, oxygen and carbon impurities were lowered from 120 to 6ppm and from 157 to 106ppm, respectively, after first melting. Although the purification effect was not significant with the number of remelting, Vickers hardness was reduced from 217 to 195 and 184 in sequence with increasing the number of remelting.