• Journal of Korea Foundry Society
• /
• v.3 no.3
• /
• pp.174-180
• /
• 1983

The matrix changes and graphite formation in high manganese cast iron (Fe-12Mn-3.5C) are studied with increasing nickel and silicon content. Also, the decomposition of carbides and graphite precipitation are studied by adequate heat treatment.The results obtained in this work are as follows. 1. In high manganese cast iron, fine flakes graphite appeared by adding 5 wt% nickel and A-type flakes graphite can be obtained by adding 7 wt% nickel. 2. Nodular graphite are obtained by graphite spheroidizing treatment with same melt. 3. In high manganese cast iron containing 7 wt% nickel, full austenitic matrix with nodular graphite can be achieved by water quenching after 10 hours' solution heat treatment at $1050^{\circ}C$ in case of containing 2.0 wt% silicon, and 6 hours' at the same temperature in case of containing 2.5 wt% silicon.

• Journal of the Korean Society for Heat Treatment
• /
• v.37 no.3
• /
• pp.121-127
• /
• 2024

We investigate the effect of T6 heat treatment on the microstructure and mechanical properties of AA365 (Al-10.3Si-0.37Mg-0.6Mn-0.11Fe, wt.%) alloy fabricated by vacuum-assisted high pressure die casting by means of thermodynamic calculation, X-ray diffraction, scanning and transmission electron microscopy, and tensile tests. The as-cast alloy consists of primary Al (with dendrite arm spacing of 10~15 ㎛), needle-like eutectic Si, and blocky α-AlFeMnSi phases. The solution treatment at 490 ℃ induces the spheroidization of eutectic Si and increase in the fraction of eutectic Si and α-AlFeMnSi phases. While as-cast alloy does not contain nano-sized precipitates, the T6-treated alloy contains fine β' and β' precipitates less than 20 nm that formed during aging at 190℃. T6 heat treatment improves the yield strength from 165 to 186 MPa due to the strengthening effect of β' and β' precipitates. However, the β' and β' precipitates reduce the strain hardening rate and accelerate the necking phenomenon, degrading the tensile strength (from 290 to 244 MPa) and fracture elongation (from 6.6 to 5.0%). Fractography reveals that the coarse α-AlFeMnSi and eutectic Si phases act as crack sites in both the as-cast and T6 treated alloys.

• Korean Journal of Metals and Materials
• /
• v.47 no.12
• /
• pp.866-872
• /
• 2009

The effects of magnetic powder thickness on electromagnetic wave absorption characteristics in Fe-6.5Si-0.9Cr (wt%) alloy flakes/polymer composite sheets available for quasi-microwave band have been investigated. The atomized FeSiCr powders were milled by using attritor for 12, 24, and 36 h, powder thickness changed from $40{\mu}m$ to $3{\mu}m$ upon 36 h milling. The composite sheet, including thinned magnetic flakes, exhibited higher power loss in the GHz frequency range as compared with the sheets having thick flakes. Moreover, both the complex permeability and the loss factor increased with the decrease in thickness of the alloy flakes. Therefore, the enhanced power loss property of the sheets containing thin alloy flakes was attributed to the flakes of high complex permeability, especially their imaginary part. Additionally, the complex permittivity was also increased with the reduction of flake thickness, and this behavior was considered to be helpful for improvement of the electromagnetic wave absorption characteristics in the composite sheets, including thin alloy flakes.

• Journal of the Korean institute of surface engineering
• /
• v.52 no.6
• /
• pp.364-370
• /
• 2019

Fe-Mn-Si-Ni-Cr-TiC alloys have a shape memory property, recovering initial shape by heating. With an aim to improve a durability and stability of building and infrastructure, this Fe-based shape memory alloy (FSMA) can be employed to reinforce concrete structure with creation of compressive residual stress. In this work, corrosion resistance of FSMA was compared with general rebar and S400 carbon steel to evaluate the stability in concrete environment. Potentiodynamic polarization test in de-ionized water, tap-water and 3.5 wt.% NaCl solution with variations of pH was used to compare the corrosion resistance. FSMA shows better corrosion resistance than rebar and S400 in tested solutions. However, Cl-containing solution is critical to significantly reduce the corrosion resistance of FSMA. Therefore, though FSMA can be a promising candidate to replace the rebar and S400 for the reinforcement of concrete structure, serious cautions are required in marine environments.

• Journal of the Korean Magnetics Society
• /
• v.20 no.4
• /
• pp.143-148
• /
• 2010

This study examined the effects of sheet thickness on electromagnetic wave absorption characteristics and internal microstructure in 92.6%Fe-6.5%Si-0.9%Cr (wt%) alloy flakes/polymer composite sheets available for quasi-microwave band. The composite sheets with the thickness of 0.3, 0.4 and 0.5 mm were prepared by tape casting. A significant decrease in transmission parameter $S_{21}$ and a large increase in power loss were observed for the thick composite sheet in the frequency range of 1~5 GHz. However the permeability properties were not affected by thickness variation, while the imaginary part of complex permittivity increased with the increase of sheet thickness at 1~5 GHz. The enhanced electromagnetic wave absorption characteristics in the thicker composite sheets was attributed to the changed microstructure and the higher dielectric loss.

• Korean Journal of Materials Research
• /
• v.21 no.1
• /
• pp.1-7
• /
• 2011

Methods of producing hydrogen include steam reforming, electrochemical decomposition of water, and the SI process. Among these methods, the Sulfur iodine process is one of the most promising processes for hydrogen production. The thermochemical sulfur-iodine (SI) process uses heat from a high-temperature-gas nuclear reactor to produce $H_2$ gas; this process is known for its production of clean energy as it does not emit $CO_2$ from water. But the SI-process takes place in an extremely corrosive environment for the materials. To endure SI environments, the materials for the SI environment will have to have strong corrosion resistance. This work studies the corrosion resistances of the Fe-Si, Ni-Ti and Ni Alloys, which are tested in SI-process environments. Among the SI-process environments, the conditions of boiling sulfuric acid and decomposed sulfuric acid are selected in this study. Before testing in boiling sulfuric acid environments, the specimens of Fe-4.5Si, Fe-6Si, Ni-4.5Si, Ni-Ti-Si-Nb and Ni-Ti-Si-Nb-B are previously given heat treatment at $1000^{\circ}C$ for 48 hrs. The reason for this heat treatment is that those specimens have a passive film on the surface. The specimens are immersed for 3~14 days in 98wt% boiling sulfuric acid. Corrosion rates are measured by using the weight change after immersion. The corrosion rates of the Fe-6Si and Ni-Ti-Si-Nb-B are found to decrease as the time passes. The corrosion rates of Fe-6si and Ni-Ti-Si-Nb-B are measured at 0.056 mm/yr and 0.16 mm/yr, respectively. Hastelloy-X, Alloy 617, Alloy 800H and Haynes 230 are tested in the decomposed sulfuric acid for one day. Alloy 800H was found to show the best corrosion resistance among the materials. The corrosion rate of Alloy 800H is measured at -0.35 mm/yr. In these results, the corrosion resistance of materials depends on the stability of the oxide film formed on the surface. After testing in boiling sulfuric acid and in decomposed sulfuric acid environments, the surfaces and compositions of specimens are analyzed by SEM and EDX.

• Korean Journal of Metals and Materials
• /
• v.46 no.1
• /
• pp.44-51
• /
• 2008

The effects of magnetic powder size on electromagnetic wave absorption characteristics in Fe-6.5Si-0.9Cr(wt%) alloy flakes/polymer composite sheets available for quasi-microwave band have been investigated. The composite sheet including small magnetic flakes with the size less than $26{\mu}m$ exhibited high power loss in the GHz frequency range as compared with the sheets having large alloy flakes of $45{\sim}75{\mu}m$. Moreover, both the complex permeability and the loss factor increased with the decrease in size of the alloy flakes. The large power loss of the sheets containing small magnetic flakes was attributed to the high complex permeability, especially their imaginary part. The high complex permeability of the sheets composed of small flakes was considered to be due to the highly thin shape of the flakes inducing low eddy-current loss.

• Korean Journal of Materials Research
• /
• v.22 no.4
• /
• pp.169-173
• /
• 2012

Recently, various attempts to produce a heat sink made of Al 6xxx alloys have been carried out using die-casting. In order to apply die-casting, the Al alloys should be verified for die-soldering ability with die steel. It is generally well known that both Fe and Mn contents have effects on decreasing die soldering, especially with aluminum alloys containing substantial amounts of Si. However, die soldering has not been widely studied for the low Si aluminum (1.0~2.0wt%) alloys. Therefore, in this study, an investigation was performed to consider how the soldering phenomena were affected by Fe and Mn contents in low Si aluminum alloys. Each aluminum alloy was melted and held at $680^{\circ}C$. Then, STD61 substrate was dipped for 2 hr in the melt. The specimens, which were air cooled, were observed using a scanning electron microscope and were line analyzed by an electron probe micro analyzer. The SEM results of the dipping soldering test showed an Al-Fe inter-metallic layer in the microstructure. With increasing Fe content up to 0.35%, the Al-Fe inter-metallic layer became thicker. In Al-1.0%Si alloy, the additional content of Mn also increased the thickness of the inter-metallic layer compared to that in the alloy without Mn. In addition, EPMA analysis showed that Al-Fe inter-metallic compounds such as $Al_2Fe$, $Al_3Fe$, and $Al_5Fe_2$ formed in the die soldering layers.

• Journal of the Korean Society for Heat Treatment
• /
• v.10 no.4
• /
• pp.246-254
• /
• 1997

The 6.5wt %Si-Fe alloy sheets were made by the twin roll process. The magnetic properties and microstructures of sheets annealed in the sulfur atmosphere were studied. In the as-prepared sheet, non-oriented columnar grains about $10{\mu}m$ in diameter were observed, which grew from the surface to the inner part of the sheet. When the annealing temperature was around $700^{\circ}C$, the primary recrystallization was formed around the middle part of the sheet thickness, and the grain size increased with increasing annealing temperature. At the annealing temperature of $900^{\circ}C$, the grain size became $30{\sim}40{\mu}m$. Around the annealing temperature, the motive force of the grain growth is the grain boundary energy. However, above $1000^{\circ}C$ the surface energy played an important role in the observed grain growth. When the sheet were annealed at $1200^{\circ}C$, the grains whose (100) planes were paralled to the thin plate surface grew, and all sheet surfaces were covered with these grains after 1 hour annealing. This phenomenon is called tertiary recrystallization. A difference in surface energy between (100) and (110) surfaces provides a driving force for growth of tertiary grains. The coercive force was 0.27 mOe and the AC core loss $W_{12/50}$ was 0.38w/kg for the 6.5wt%Si-Fe alloy.

• Journal of Korea Foundry Society
• /
• v.42 no.6
• /
• pp.337-346
• /
• 2022

In order to optimize the solution treatment conditions of Al-7Si-(0.3~0.5)Mg-(0~0.5)Cu alloys, a series of heat treatment experiments were conducted under various solution treatment times up to 7 hours at 545℃, followed by a microstructural analysis using optical microscopy, FE-SEM, and Brinell hardness measurements. Rapid coarsening of eutectic Si particles was observed in the alloys during the first 3 hours of solution treatment but the size of those Si particles did not change at longer solution treatment conditions. Meanwhile, the degree of spheroidisation of eutectic Si particles increased until the solution treatment time was increased up to 7 hours. Q-Al5Cu2Mg8Si6 andθ-Al2Cu were observed in as-cast Cu-containing Al alloys but the intermetallic compounds were dissolved completely after 3 hours of solution treatment at 545℃. Depending on the initial Mg composition of the Al alloys, π-Al8FeMg3Si either disappeared in the alloy with 0.3wt% of Mg content after 5 hours of solution treatment or remained in the alloy with 0.5wt% of Mg content after 7 hours of solution treatment time. Mg and Cu content in the primary-α phase of the Al alloys increased until the solution treatment time reached 5 hours, which was in accordance with the dissolution behavior of Mg or Cu-containing intermetallic compounds with respect to the solution treatment time. From the results of microstructural changes in the Al-7Si-Mg-Cu alloys during solution treatment, it was concluded that at least 5 hours of solution treatment at 545℃ is required to maximize the age hardening effect of the present Al alloys. The same optimal solution treatment conditions could also be derived from Brinell hardness values of the present Al-7Si-Mg-Cu alloys measured at different solution treatment conditions.