• 한국분말재료학회지
• /
• 제21권4호
• /
• pp.266-270
• /
• 2014

Metal foams have a cellular structure consisting of a solid metal containing a large volume fraction of pores. In particular, open, penetrating pores are necessary for industrial applications such as in high temperature filters and as a support for catalysts. In this study, Fe foam with above 90% porosity and 2 millimeter pore size was successfully fabricated by a slurry coating process and the pore properties were characterized. The Fe and $Fe_2O_3$ powder mixing ratios were controlled to produce Fe foams with different pore size and porosity. First, the slurry was prepared by uniform mixing with powders, distilled water and polyvinyl alcohol(PVA). After slurry coating on the polyurethane(PU) foam, the sample was dried at $80^{\circ}C$. The PVA and PU foams were then removed by heating at $700^{\circ}C$ for 3 hours. The debinded samples were subsequently sintered at $1250^{\circ}C$ with a holding time of 3 hours under hydrogen atmosphere. The three dimensional geometries of the obtained Fe foams with an open cell structure were investigated using X-ray micro CT(computed tomography) as well as the pore morphology, size and phase. The coated amount of slurry on the PU foam were increased with $Fe_2O_3$ mixing powder ratio but the shrinkage and porosity of Fe foams were decreased with $Fe_2O_3$ mixing powder ratio.

• 한국분말야금학회:학술대회논문집
• /
• 한국분말야금학회 2006년도 Extended Abstracts of 2006 POWDER METALLURGY World Congress Part2
• /
• pp.918-920
• /
• 2006

Metal sulfide powders such as MnS, $MoS_2$ and FeS are simply used to the machinery processing improvement agent and solid lubricant in powder metallurgy industrial. And then, metal sulfide powders have received relatively little attention from powder metallurgy. Recently, the portable machine is one of the important interfaces between human or human and electronic machine. With the increase of the intelligent activity, the social and industrial demands for information display device and power source are increasing. The transition metal sulfide materials (FeS, ZnS) have received considerable attention due to the large variety of its electric, optical and magnetic properties. Among the metal sulfide, $FeS_2$ is appealing superior material for applications in $Li-2^{nd}$ battery because of high capacity. ZnS is also a famous phosphor material with various luminescence properties, such as photoluminescence (PL) and electroluminescence (EL). So generally used in the fields of display, sensors and laser. Metal sulfide materials, therefore, are provided for most widely application in all industries. In recent years, material researchers have become increasingly interested in studying with synthesis of metal sulfide.

• 한국세라믹학회지
• /
• 제28권2호
• /
• pp.93-100
• /
• 1991

For determination the optimum manufacturing condition Fe4N powder for magnetic recording media, we have studied the following important conditions : the effect of particle size of metal powder on the nitridation, the condition of nitridation on the formation and magnetic properties of Fe4N, and stability of Fe4N powder against temperature and change on standing. The results can be summarized as : 1) Single phase Fe4N is formed at 50v/o of ammonia concentration during the nitridation reaction, 2) Single phase Fe4N is formed above 40$0^{\circ}C$, 15min regardless of the metal powder sizes, 3) Coercivity and saturation magnetization of Fe4N powder almost constant value until 20 day-passing from preparation date.

• 자원리싸이클링
• /
• 제26권6호
• /
• pp.97-101
• /
• 2017

메탈폼은 매우 많은 기공을 포함하는 세포상 구조를 갖는 고체금속을 일컫는다. 특히 관통 기공 같은 개기공들은 고온용 필터 및 촉매 지지체 등으로 산업적으로 많이 사용되고 있다. 본 연구에서는 슬러리 코팅공정으로 90% 이상의 기공율과 2 mm 이상의 기공크기를 갖는 Fe 폼을 제조하였다. 이때 Fe 분말과 $Fe_2O_3$ 분말의 혼합비를 달리하여 기공율과 기공크기를 제어하였다. 이를 위해 우선 분말, 증류수 및 폴리비닐알콜(PVA)를 균일하게 혼합하여 슬러리를 제조하였다. $Fe_2O_3$ 분말의 혼합 비율이 증가할수록 PU 폼에 코팅된 슬러리의 양이 증가한 반면 Fe 폼의 수축 및 기공율은 각각 감소하였다.

• 한국분말재료학회지
• /
• 제28권4호
• /
• pp.293-300
• /
• 2021

We investigate the effect of phosphorous content on the microstructure and magnetic properties of Fe_83.2Si_5.33-0.33xB_10.67-0.67xP_xCu_0.8 (x = 1-4 at.%) nanocrystalline soft magnetic alloys. The simultaneous addition of Cu and P to nanocrystalline alloys reportedly decreases the nanocrystalline size significantly, to 10-20 nm. In the P-containing nanocrystalline alloy, P atoms are distributed in an amorphous residual matrix, which suppresses grain growth, increases permeability, and decreases coercivity. In this study, nanocrystalline ribbons with a composition of Fe_83.2Si_5.33-0.33xB_10.67-0.67xP_xCu_0.8 (x = 1-4 at.%) are fabricated by rapid quenching melt-spinning and thermal annealing. It is demonstrated that the addition of a small amount of P to the alloy improves the glass-forming ability and increases the resistance to undesirable Fe_x(B,P) crystallization. Among the alloys investigated in this work, an Fe_83.2Si₅B₁₀P₁Cu_0.8 nanocrystalline ribbon annealed at 460℃ exhibits excellent soft-magnetic properties including low coercivity, low core loss, and high saturation magnetization. The uniform nanocrystallization of the Fe_83.2Si₅B₁₀P₁Cu_0.8 alloy is confirmed by high-resolution transmission electron microscopy analysis.

• 한국분말재료학회지
• /
• 제16권3호
• /
• pp.191-195
• /
• 2009

The calcination and hydrogen-reduction behavior of Fe- and Ni-nitrate have been investigated. $Fe_2O_3$/NiO composite powders were prepared by chemical solution mixing of Fe- and Ni-nitrate and calcination at $350^{\circ}C$ for 2 h. The calcined powders were hydrogen-reduced at $350^{\circ}C$ for 30 min. The calcination and hydrogen-reduction behavior of Fe- and Ni-nitrate were analyzed by TG in air and hydrogen atmosphere, respectively. TG and XRD analysis for hydrogen-reduced powders revealed that the $Fe_2O_3$/NiO phase transformed to $FeNi_3$ phase at the temperature of $350^{\circ}$. The activation energy for the hydrogen reduction, evaluated by Kissinger method, was measured as 83.0 kJ/mol.

• 한국분말야금학회:학술대회논문집
• /
• 한국분말야금학회 2001년도 추계학술강연 및 발표대회
• /
• pp.11-11
• /
• 2001

• 한국분말야금학회:학술대회논문집
• /
• 한국분말야금학회 1994년도 추계학술대회강연 및 발표대회 강연및 발표논문 초록집
• /
• pp.18-18
• /
• 1994

• 한국분말야금학회:학술대회논문집
• /
• 한국분말야금학회 2003년도 춘계학술강연 및 발표대회
• /
• pp.36-37
• /
• 2003

No Abstract, See Full Text

• 한국분말재료학회지
• /
• 제8권3호
• /
• pp.157-162
• /
• 2001

An optimum route to fabricate the ferrous alloy dispersed $Al_2O_3$ nanocomposites such as $Al_2O_3$/Fe-Ni and $Al_2O_3$/Fe-Co with sound microstructure and desired properties was investigated. The composites were fabricated by the sintering of powder mixtures of $Al_2O_3$ and nano-sized ferrous alloy, in which the alloy was prepared by solution-chemistry routes using metal nitrates powders and a subsequent hydorgen reduction process. Microstructural observation of reduced powder mixture revealed that the Fe-Ni or Fe-Co alloy particles of about 20 nm in size homogeneously surrounded $Al_2O_3$, forming nanocomposite powder. The sintered $Al_2O_3$/Fe-Ni composite showed the formation of Fe$Al_2O_4$ phase, while the reaction phases were not observed in $Al_2O_3$/Fe-Co composite. Hot-pressed $Al_2O_3$/Fe-Ni composite showed improved mechanical properties and magnetic response. The properties are discussed in terms of microstructural characteristics such as the distribution and size of alloy particles.