• 한국자기학회지
• /
• 제5권5호
• /
• pp.570-574
• /
• 1995

Magnetoresistance of NiFeCo/Cu/NiFeCo/FeMn uncoupled exchange biased sandwiches has been studied. The magnetoresistance change ratio, ${\Delta}R/R_{s}$ showed 4.1 % at a saturation field as low as 11 Oe in $Si/Ti(50\;{\AA})/NiFeCo(70\;{\AA})/Cu(23\;{\AA})/NiFeCo(70\;{\AA})/FeMn(150\;{\AA})/Cu(50\;{\AA})$ spin valve structure. In this system, the magnetoresistance was affected by interlayer material and thickness. When Ti and Cu were used as the interlayer material in this structure, maximum magnetoresistance change ratio were 0.32 % and 4.1 %, respectively. 6.1 % MR ratio was obtained in $Si/Ti(50\;{\AA})/NiFeCo(70\;{\AA})/Cu(15\;{\AA})/NiFeCo(70\;{\AA})/FeMn(150\;{\AA})/Cu(50\;{\AA})$ spin valve structure. The magnetoresistance change ratio decreased monotonically as the interlayer thickness increased. It was found that the exchange bias field exerted by FeMn layer to the adjacent NiFeCo layer was ~25 Oe, far smaller than that reported in NiFe/Cu/NiFe/FeMn spin valve structure(Dieny et. al., ~400 Oe). The relationship between the film texture and exchange anisotropy ha been examined for spin valve structures with Ti, Cu, or non-buffer layer.

• E2M - 전기 전자와 첨단 소재
• /
• 제10권10호
• /
• pp.1016-1021
• /
• 1997

Magneto resistance properties in spin-valve sandwiches with various thickness of nanmagnetic layer in contact with the ferromagnetic NiFe film were investigated. The NiFe layer in contact with the NiO film was pinned by strongly exchange-biased coupling and the free NiFe layer at the film surface induced a sharp change in the magnetoresistance at -5~15Oe due to small coercivity. The NiO/NiFe/Cu/NiFe film showed a magnetoresistance ratio in the range of 2.3~2.9% and a field sensitivity above 2.2%/Oe with various of nonmagnetic layer. The NiO/NiFe/Cu/NiFe film of the field sensitivity above 2.2%/Oe suggests stang possibility of magnetic sensor matter.

• Corrosion Science and Technology
• /
• 제13권4호
• /
• pp.145-151
• /
• 2014

The objectives of this study are to investigate the effect of the concentration ratios of Ni and Fe ions on crud deposition onto the fuel cladding surface in the simulated primary environments of a pressurized water reactor. Crud deposition tests were conducted in the Ni and Fe concentration ratios of 20:20 ppm, 39:1 ppm and 1:39 ppm at $325^{\circ}C$ for 14 days. In the case of the same Ni and Fe ion ratio (20:20), nickel ferrite with a polyhedral shape was formed. Nickel oxide deposits with a needle shape were formed in the condition of high Ni to Fe ion ratio (39:1), While polyhedral iron oxide and needle-like nickel oxide formed in the condition of low Ni to Fe ion ratio (1:39). The amount of deposits increased, when Fe oxides were formed. This indicates that Fe rich oxides stimulated Ni oxide deposition.

• Journal of Magnetics
• /
• 제6권3호
• /
• pp.83-85
• /
• 2001

The magnetoresistance properties of NiO/NiFe/Cu/NiFe spin valve film deposited on MgO(100) substrate with YBa$_2$$Cu_3O_7$(YBCO) film were investigated at room temperature and at 77 K. The magnetoresistance (MR) curves of the hybrid superconductor-magnetoresistor film structure showed an exchange coupling field of 300 Oe and an inverse magnetoresistance ratio of -6.5%. The magnetization configurations of the two magnetic layers in the NiO spin valve were antiparallel due to an increment in the conduction electron flow to superconductor YBCO film. This sample showed an inverse MR ratio.

• 한국자기학회지
• /
• 제9권6호
• /
• pp.296-300
• /
• 1999

DC 마그네트론 스퍼터링 방법으로 금속 마스크를 사용하여 십자형태로 substrate/Ta/NiFe/FeMn/NiFe/CoFe/Al2O3/CoFe/NiFe와 substrate/Ta/NiFe/CoFe/Al2O3/CoFe/NiFe/FeMn/NiFe 스핀 터널링 접합 구조를 제조하였다. 이러한 구조에서 절연층(Al2O3)의 형성조건과 각 층의 두께와 파워에 대한 증착율에 변화를 주어 24.3%의 자기 저항비를 얻었다. 두 종류의 구조에 대한 자기적 특성 비교와 Corning glass 7059와 Si(111) 기판의 종류에 따른 결과를 비교하였으며 소자 제조때 수반되는 온도변화에 대한 특성변화를 알아보고자 열처리를 하였다. 열처리 결과 자기 저항비는 15$0^{\circ}C$까지는 어느 정도 일정한 값을 유지하다가 18$0^{\circ}C$ 열처리 후 갑자기 감소하는 결과를 얻었다.

• 한국표면공학회지
• /
• 제29권3호
• /
• pp.195-202
• /
• 1996

The composition, the microstructure and the magnetic properties(HC and Hk) of Fe-Co-Ni alloy electrodeposits were investigated according to the electrolysis conditions using sulfate bath paddle agitated. The current efficiency of the alloys electrodeposition was considerably low in the range of 16∼50%. The Fe content(wt.%) of the alloy increased from 20% to 57% with current density, while Ni content of them decreased in the range of 70∼24% respectively, and Co content was nearly constant. As a result, Fe/Ni ratio of the alloy increased from 0.3 to 2.0 showing the anomalous codeposition. The structure of the alloy changed from fcc to the mixed one of fcc+bcc with the increase of Fe/Ni ratio. The preferred orientation of the alloy with fcc and bcc structure were (220) and (110) respectively. The alloy with Fe/Ni ratio(0.3∼l.2) had the lowest coercivity of 0.4∼0.8 Oe.

• 한국자기학회지
• /
• 제14권1호
• /
• pp.25-28
• /
• 2004

Ta/NiFe/Cu/Co 구조의 Pseudo 스핀밸브 박막을 제작하여 NiFe, Cu, Co 각 층들의 두께변화에 따른 자기저항비(MR-ratio), 보자력, 자기 민감도(sensitivity), 반전자장(Switching Field)의 크기 등의 자기적 특성을 연구하였다. 각 층들의 두께를 변화시키면서 측정한 결과 Ta(4 nm)/NiFe(7.5 nm)/Cu(3 nm)/Co(5 nm)에서 최대 자기저항비 7.26 %를 얻을 수 있었다. 또한 각 층들의 독립적인 자화 과정을 통해 자기저항 특성을 조절할 수 있었다. 특히 Co의 두께를 변화시켜 자기저항비를 비교적 일정하게 유지하면서 보자력의 크기를 조절할 수 있음을 알게 되었다.

• 한국결정성장학회지
• /
• 제9권5호
• /
• pp.486-492
• /
• 1999

본 실험에서는 D.C magnetron sputtering을 사용하여 Mn-Ir/Ni-Fe/buffer/Si 다층박막의 교환결합 자계와 보자력에 영향을 주는 인자를 미세구조의 관점에서 분석하였다. (111) 우선방위에 상관없이 모든 시편에서 155 Oe 이상의 교환결합 자계가 발생하였다. Mn-Ir/Ni-Fe 의 계면에서 Mn-Ir의 결정립 크기와 게면 거칠기가 Mn-Ir/Ni-Fe 다층박막의 교환결합 자계와 보자력에 가장 많은 영향을 주는 것을 알 수 있었다. Mn-Ir/Ni-Fe/Cu/Ni-Fe/buffer/Si spin-valve 다층박막에서 각 층의 두께와 하지층에 따른 자기저항비와 coulping field을 분석하였다. Mn-Ir(10 nm)/Ni-Fe(7.5 nm)/Cu(2 nm)Ni-Fe(6 nm)/Ta (5 nm)/Si에서 최대 자기저항비가 발생하였다. 강자성체의 결정립 크기가 거대자기저항비에 영향을 주는 것을 알 수 있었다. 그리고 계면 거칠기와 강자성체의 결정립 크기가 coulping field 에 많은 영향을 주는 것을 알 수 있었다.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2000년도 추계학술대회 논문집
• /
• pp.355-358
• /
• 2000

Magnetoresistance changes of NiFe thin films were investigated as a function of deposition temperature. DC magnetron sputtering was employed to fabricate Ta/NiFe(t)/Ta thin films on Si(001) substrates with in-situ field or with no-field. The thickness(t) of NiFe films was a range of 4 to 15nm. Substrate temperature was a range of 30 to 400$^{\circ}C$. MR measurement was carried out as a function of angle $\theta$, between external field and current direction. MR ratio increased with increasing substrate temperature, also, max. MR ratio was observed in samples deposited at 300$^{\circ}C$. With increasing upto 400$^{\circ}C$, MR ratio was rapidly decreased in the case of thinner NiFe films. In non-field deposited NiFe films, both angle $\theta$=0, 90。, there was no significant change in MR curves. However, MR curves of in-situ field deposited NiFe films were different in both angles $\theta$=0 and 90。

• 한국자기학회지
• /
• 제8권5호
• /
• pp.288-294
• /
• 1998

기판/Ta/NiFe/Cu/NiFe/FeMn/Ta 스핀밸브에서 Ta 성막 후에 자유층 NiFe 스퍼터 증착시 가해진 기판 바이어스 전압에 의해 야기된 Ta/NiFe 계면에서의 원자섞임이 자기저항에 미치는 영향에 대해 조사하였다. 최대 자기 저항비 (MR ratio)를 나타내는 자유층의 적정두께는 바이어스 전압이 증가함에 따라 증가하였다. 이러한 현상의 원인은 바이러스 전압이 증가함에 따라 Ta과 NiFe의 원자섞임으로 계면에 있는 NiFe층 일부가 약한 강자성 또는 상자성화되어 스핀 비의존 산란을 하는 원자섞임층의 두께가 증가하였기 때문이다. 원자섞임층의 존재는 전기저항 변화와 자화량 변화로부터 증명하였다. 또 본 실험에서 비록 NiFe 증착시 기판 바이어스 전압이 변화더라도 최대 자기저항비를 갖는 최적 "유효" 자유층 두께는 기판 바이어스 전압에 무관하게 일정하였다.관하게 일정하였다.