• Journal of the Korean Magnetics Society
• /
• v.4 no.1
• /
• pp.12-19
• /
• 1994

The crystallization behavior of the amorphous $Fe_{73.5}Cu_{1}Nb_{3}Si_{16.5}B_{6}$ alloy with isothermal annealing at $552^{\circ}C$ was studied by $M\"{o}ssbauer$ spectroscopy. The amorphous phase was revealed to coexist together with $Do_{3}-FeSi$ nanocrystalline and Cu-duster in annealed alloys by $M\"{o}ssbauer$ spectrum analysis. At the early stage of crystallization, Si content of FeSi is high due to the creation of Cu-cluster, and decreases with annealing until 60 minutes, which results in the increase in the mean hyperfine field of FeSi, and thereafter keeps constant. After 60 minutes, the decrease in the mean hyperfine field of the residual armrphous, in spite of a slight change in the volume fraction of the FeSi and the residual armrphous, is caused by the increase in the content of Nb and B in residual amorphous phase. Both directions of the hyperfine field, those of the FeSi and the residual amorphous, become randomly oriented in about 60 minutes. For FeSi and Cu-duster, the Avrami exponents are 0.51 and O.65, the activation energies are 2.35 eV and 2.44 eV, and the incubation times are 2.4 minutes and 0.8 minutes respectively. Earlier formation of Cu-duster than that of FeSi is coincidence with the fact that Cu atom promotes the nucleation of the FeSi.

• Bulletin of the Korean Chemical Society
• /
• v.29 no.2
• /
• pp.309-312
• /
• 2008

Two different anode composite materials comprising of Fe, Cu and Si prepared using high energy ball milling (HEBM) were explored for their capacity and cycling behaviors. Prepared powder composites in the ratio Cu:Fe:Si = 1:1:2.5 and 1:1:3.5 were characterized through X-Ray diffraction (XRD) and scanning electron microscope (SEM). Nevertheless, the XRD shows absence of any new alloy/compound formation upon ball milling, the elements present in Cu(1)Fe(1)Si(2.5)/Graphite composite along with insito generated Li2O demonstrate a superior anodic behavior and delivers a reversible capacity of 340 mAh/g with a high coulombic efficiency (98%). The higher silicon content Cu(1)Fe(1)Si(3.5) along with graphite could not sustain capacity with cycling possibly due to ineffective buffer action of the anode constituents.

• Journal of the Korean Magnetics Society
• /
• v.3 no.2
• /
• pp.130-134
• /
• 1993

The magnetic properties of the amorphous $Fe_{73.5-X}Co_{X}Cu_{1}Nb_{3}Si_{13.5}B_{9}(x=2,\;4)$ alloys, fabricated by a single roll rapid quenching technique and annealed at $400~650^{\circ}C$, have been investigated. The optimum annealing temperature is $550^{\circ}C$ for the amorphous $Fe_{71.5}Co_{2}Cu_{1}Nb_{3}Si_{13.5}B_{9}$ alloy. The properties of the nanocrystalline $Fe_{71.5}Co_{2}Cu_{1}Nb_{3}Si_{13.5}B_{9}$ alloy show the relative permeability of $1.1{\times}10^{4}$ and the coercive force of 0.22 Oe at 1 kHz. When annealed at $600^{\circ}C$, the nanocrystalline $Fe_{69.5}Co_{4}Cu_{1}Nb_{3}Si_{13.5)B_{9}$ alloy shows the relative permeability of $1.0{\times}10^{4}$ and the coercive force of 0.19 Oe at 1 kHz. From the X-ray measurement, it is found that the remarkably improved soft magnetic properties are the effect of the formation of $\alpha$-Fe(Si) grain. By the results of FMR exper-imeIlt, the optimum annealing condition is just below temperature which the peak-to-peak line width of FMR spectrum increase rapidly.

• Journal of the Korean Magnetics Society
• /
• v.1 no.2
• /
• pp.37-41
• /
• 1991

Amorphous $Fe_{68.5}Co_5M_3Cu_1Si_{13.5}B_9(M=Nb, Mo, Mn, Cr)$ alloys were prepared by using rapidly quenching techinque and were annealed above their crystallization temperatures. Coercive force, initial permeability and AC power loss of the annealed $Fe_{68.5}Co_5M_3Cu_1Si_{13.5}B_9(M=Nb, Mo, Mn, Cr)$ alloys have been studied systematically. Nanocrystallines are formed in the annealed alloys which include Mo and Nb. Remarkably improved soft magnetic properties are obtained in the alloys whose average grain size is around 10 nm. However, soft magnetic properties of the alloys are degraded when grain size is less than IOnm or larger than 15nm. It is considered that the degradation of soft magnetic properties in the alloys whose average grain size is less than 10 nm is due to the Fe-rich amorphous phase retained at grain boundary during the initial crystallization process.

• Korean Chemical Engineering Research
• /
• v.43 no.1
• /
• pp.140-145
• /
• 2005

The desulfurization abilities using GC/microreactor have been examined for $CuO-Fe_2O_3$ sorbents with respect to calcination temperatures of 700, 900 and $1,100^{\circ}C$. CuO was used as a main active component, $Fe_2O_3$ was used as an additive one and 25 wt% $SiO_2$ was used as a support. The desulfurization reaction temperature was $500^{\circ}C$ and the regeneration reaction temperature was $700^{\circ}C$. From the XRD results, the $CuFeO_2$ compound has been observed for the fresh sorbent calcined at $1,100^{\circ}C$ and the $CuFeS_2$ compound for the reacted sorbent calcined at $1,100^{\circ}C$. By the BET results, however any significant differences among sorbents calcined at the three different temperatures of 700, 900 and $1,100^{\circ}C$ haven't been observed. Especially CFS1 (CuO : $Fe_2O_3$ : $SiO_2$=67.5 wt% : 7.5 wt% : 25 wt%) sorbent calcined at $1,100^{\circ}C$ maintained about 10 g sulfur/100 g sorbent for 100 cycles by the cyclic test.

• Journal of Korea Foundry Society
• /
• v.41 no.1
• /
• pp.3-10
• /
• 2021

In the compound casting between the aluminum alloy and the cast iron, the iron component may be dissolved from the cast iron during the process and mixed into the aluminum melt, thereby forming various iron-containing intermetallic compounds and significantly deteriorating the tensile properties of the aluminum alloy. On the other hand, unlike Fe, which is added as an impurity, Cu is added to improve the mechanical properties of the aluminum alloy. In this study, the change in microstructure and tensile properties of aluminum alloys due to the addition of Fe and Cu was investigated. A large amount of iron-containing compounds such as coarse Al₅FeSi phases were formed when the iron content was 1% or more, and the tensile properties were significantly reduced. In the case of the aluminum alloy to which Cu was added, an Al₂Cu phase was additionally formed and the tensile strength was clearly improved.

• Proceedings of the Korean Magnestics Society Conference
• /
• 2000.05a
• /
• pp.40-41
• /
• 2000

• Proceedings of the Korean Magnestics Society Conference
• /
• 1991.11a
• /
• pp.24-25
• /
• 1991

• Proceedings of the Korean Magnestics Society Conference
• /
• 2003.06a
• /
• pp.86-87
• /
• 2003

• Proceedings of the Korean Vacuum Society Conference
• /
• 1994.06a
• /
• pp.23-23
• /
• 1994