• Advances in materials Research
• /
• 제3권3호
• /
• pp.163-174
• /
• 2014

In this study, fatigue properties and crack growth characteristics of a polycarbonate (PC) were examined during cyclic loading at various mean stress (${\sigma}_{amp}$) and stress amplitude (${\sigma}_{mean}$) conditions. Different S vs. N and da/dN vs. ${\Delta}K$ relations were obtained depending on the loading condition. The higher fatigue strength and the higher resistance of crack growth are seen for the PC samples cyclically loaded at the higher mean stress and lower stress amplitude due to the low crack driving force. Non-linear S - N relationship was detected in the examination of the fatigue properties with changing the mean stress. This is attributed to the different crack growth rate (longer fatigue life): the sample loaded at the high mean stress with lower stress amplitude. Even if the higher stress amplitude, the low fatigue properties are obtained for the sample loaded at the higher mean stress. This was due to the accumulated strain energy to the sample, where severe plastic deformation occurs instead of crack growth (plasticity-induced crack closure). Shear bands and discontinuous crack growth band (DGB) are observed clearly on the fracture surfaces of the sample cyclically loaded at the high stress amplitude, where the lower the ${\sigma}_{mean}$, the narrower the shear band and DGB. On the other hand, final fracture occurred instantly immediately after the short crack growth occurs in the PC sample loaded at the high mean with the low ${\sigma}_{amp}$, i.e., tear fracture, in which the shear bands and DGB are not seen clearly.

• 대한기계학회논문집A
• /
• 제29권6호
• /
• pp.815-821
• /
• 2005

Biaxial low cycle fatigue test was carried out to predict fatigue life under combined axial-torsional-loading condition which is that of in-phase and out-of-phase for CF8M cast stainless steels. Fatemi-Socie(FS) parameter which is based on critical plane approach is not only one of methods but also the best method that can predict fatigue life under biaxial loading condition. But the result showed that, biaxial fatigue life prediction by using FS parameter with several different parameters for the CF8M cast stainless steels is not conservative but best results. So in this present research, we proposed new fatigue life prediction parameter considering effective shear stress instead of FS parameter which considers the maximum normal stress acting on maximum shear strain and its effectiveness was verified.

• Structural Engineering and Mechanics
• /
• 제53권2호
• /
• pp.311-324
• /
• 2015

The purpose of this study was to investigate experimentally the fatigue performance of reinforced concrete (RC) beams with hot-rolled ribbed fine-grained steel bars of yielding strength 500MPa (HRBF500). Three rectangular and three T-section RC beams with HRBF500 bars were constructed and tested under static and constant-amplitude cyclic loading. Prior to the application of repeated loading, all beams were initially cracked under static loading. The major test variables were the steel ratio, cross-sectional shape and stress range. The stress evolution of HRBF500 bars, the information about crack growth and the deflection developments of test beams were presented and analyzed. Rapid increases in deflections and tension steel stress occured in the early stages of fatigue loading, and were followed by a relatively stable period. Test results indicate that, the concrete beams reinforced with appropriate amount of HRBF500 bars can survive 2.5 million cycles of constant-amplitude cyclic loading with no apparent signs of damage, on condition that the initial extreme tensile stress in HRBF500 steel bars was controlled less than 150 MPa. It was also found that, the initial extreme tension steel stress, stress range, and steel ratio were the main factors that affected the fatigue properties of RC beams with HRBF500 bars, whose effects on fatigue properties were fully discussed in this paper, while the cross-sectional shape had no significant influence in fatigue properties. The results provide important guidance for the fatigue design of concrete beams reinforced with HRBF500 steel bars.

• 한국기계가공학회지
• /
• 제8권4호
• /
• pp.90-96
• /
• 2009

The loading condition of actual construction works is complex. The shear effect of mixed-mode load component are crack propagation mechanism in step larger than the crack initial mechanism. Therefore, in this study received a mixed-mode loading on fatigue crack stress ratio on crack propagation path and speed of progress to learn whether stress affects crack propagation. ${\Delta}$ P a constant state of fatigue tests in Mode I, II give the same stress ratio, frequency 10Hz, sinusoidal waveform was used. A lower stress ratio fatigue crack propagation angle is small. This is less affected by the Mode II. Therefore, a mixed-mode fatigue crack propagation is to progress by the Mode. Stress ratio in a mixed mode crack in the path of progress and found a lot of impact.

• 한국철도학회:학술대회논문집
• /
• 한국철도학회 1998년도 창립기념 춘계학술대회 논문집
• /
• pp.330-337
• /
• 1998

Bogie is mainly consisted of the bogie frame, suspensions, wheels and axles, braking system, and transmission system. The complex shapes of the bogie frame and the multiaxial loading condition induced in real operation make it difficult to design the bogie frame against the fatigue. In this study, multiaxial fatigue criteria were reviewed. Stress analysis of the bogie frame has been performed for the various loading conditions according to the UIC Code 615-4. Magnitudes of the stress amplitude and mean stress were estimated based on the stress analysis results to simulate the operating loads encountered in service. Fatigue strength of the bogie frame was evaluated by using the constant life diagram of the material. 3-D surface model ling, finite element meshing, and finite element analysis were performed by Pro-Engineer, MSC/PATRAN, and MSC/NASTRAN, respectively.

• 한국기계가공학회지
• /
• 제2권4호
• /
• pp.53-60
• /
• 2003

Large sized marine structures are used under corrosion environment of seawater and applied by severe service loading such as an ocean current, a billow and a tempest. Marine structures are usually constructed by lots of thick wall steel pipes joining welded joints. The thickness of such as steel pipes is usually more than 40mm. The such as steels are called "Thermo-Mechanical Control Process steel (TMCP steel)" strengthened by a heat treatment in process of steel manufactures. The failure, especially crack initiation, of marine structures was starting at weld joints under service condition. Then they should be designed by basis of the fatigue strength under seawater corrosion environment of weld joints. To clarity the fatigue crack initiation behavior is important more than to clarify the crack propagation behavior on the strength design of marine structures, because it is very difficult to find out the crack initiation and propagation phenomena and then even if it will be able to find out, it is considered that the refit of the damaged parts of welded joints have a technical difficulty under the sea. Therefore, it is most important to clarify the corrosion fatigue crack initiation behavior under the seawater condition. But, there is one big difficulty to make a test for thick plate specimen, for example thicker than 40mm. Because, it is need large capacity loading apparatus to test such as thick plate specimen. In this research, the new configuration specimen for fatigue crack initiation tests was proposed. Using this new specimen, it is easy to carry out the fatigue clack initiation tests with relatively low cyclic loading and to observe a fatigue crack initiation behavior.

• 한국철도학회:학술대회논문집
• /
• 한국철도학회 2009년도 춘계학술대회 논문집 특별세미나,특별/일반세션
• /
• pp.421-426
• /
• 2009

Recently, the design process for a railway bogie frame in Europe has been carried out according to the norm EN 13749. The activities in the norm EN shall demonstrate that the design of the bogie frame fulfills the acceptances of 4 steps of the program such as structural calculation, static tests, fatigue test and on-tracks tests. At the end of the acceptance program, the on-tracks tests have the aim to measure the real stress history generated in operation and to verify that they are reasonably next to those calculated and measured on the test rig. Therefore, in order to assure the safety of the railway vehicle, it is important to examined the durability of that under load histories measured from on-tracks tests. In this study, under variable amplitude loading based on the actual acceleration history, fatigue analysis of the welding bogie frame is investigated by using durability software. Moreover, the fatigue life of the frame under the loading in the norm EN fatigue test condition is evaluated and compared with the life under variable amplitude loading.

• 한국콘크리트학회:학술대회논문집
• /
• 한국콘크리트학회 2000년도 가을 학술발표회논문집(I)
• /
• pp.697-700
• /
• 2000

Fatigue damage to reinforced concrete bridge decks have been found in many bridges. Failure mode of most reinforced concrete decks is caused by local punching shear rather than flexural moment due to cumulated damage. In this study, mechanical degradation of unstrengthened and strengthened bridge deck specimens is experimentally investigated. The unstrengthened deck specimens were damaged under the pulsating loading condition. After the test, deteriorated deck specimens were strengthened with Carbon Fiber Sheet, then loaded to observe the improvement of the fatigue behavior. It is shown that fatigue damaged specimens are similar to real bridge rather than static damaged specimens.

• 대한용접접합학회:학술대회논문집
• /
• 대한용접접합학회 2006년도 춘계 학술대회 개요집
• /
• pp.83-85
• /
• 2006

The purpose of this study is to evaluate the fatigue life at the rib weldment of generator shaft. In order to do it, the stress distributions at the weldment under design loading condition were evaluated using FEA and analytical approach. The fatigue strengths of the as welded and toe machined rib specimen were estimated using 3-points bending fatigue test. Based on the fatigue test results, the S-N curve far the rib weldment of the generator shaft with post treatment was established.

• 대한기계학회논문집A
• /
• 제34권9호
• /
• pp.1193-1199
• /
• 2010

점용접은 자동차 산업에서 차체 구조물의 대표적 접합방법으로서 차량에 피로하중이 작용할 경우 구조물 전체의 파손 발생이전에 점용접부 일부에 조기 피로파손의 발생가능성이 존재한다. 이러한 점용접부의 국부적 파손은 차량 구조물의 동적 반응 및 이에 따른 피로거동의 변화를 야기할 가능성이 존재한다. 따라서 차량과 같이 스펙트럼하중을 받는 구조물의 피로수명 평가를 위해서는 이러한 점용접부의 국부적 파손에 의한 동적 반응의 변화를 고려하여야 한다. 본 논문에서는 점용접부의 누적피로손상으로 인한 동적반응의 변화를 고려한 진동피로해석을 수행하였다. 이에 필요한 S-N 선도는 전단 점용접 시험편에 대한 일정진폭 피로시험을 통하여 획득하였다. 또한 스펙트럼하중하의 점용접부의 피로수명은 유한요소해석에 기반한 진동피로해석을 통하여 평가하였다.