• Journal of Korean Tunnelling and Underground Space Association
• /
• v.14 no.6
• /
• pp.595-606
• /
• 2012

Utilization of fiber reinforced polymer(FRP) material has been increased to solve construction material problems such as corrosion, etc. However, there are still many problems in using a linear-shaped FRP material for a tunnel structure with curved section. In this study, the loading tests were performed on the curved FRP-concrete composite material to evaluate its behavior as tunnel support. These tests were based on the result from preliminary numerical analysis on FRP-concrete composite material. Also, additional numerical analysis considering interface characteristics between FRP and cement-concrete was conducted to compare the result of loading test on FRP-concrete composite material. From the results of the loading test and numerical analysis, the analysis method suggested from this study is reasonable to evaluate the mechanical behavior of FRP-concrete composite material.

• Journal of the Korea Concrete Institute
• /
• v.25 no.1
• /
• pp.45-51
• /
• 2013

Short beam tests of GFRP and CFRP specimens exposed to high temperature were conducted to measure the inter-laminar shear strength. For the phase I test, the exposure time and temperature were varied to measure reduction in the strength due to the applied conditions. As a results, the critical temperature was found to $270^{\circ}C$ for the both FRP reinforcements. The high temperature, which causes 50% loss of inter-laminar shear strength, is defined as the critical temperature in this study. It should be noted that the critical temperature for the inter-laminar shear strength is mainly dependent on resin properties not on fiber type. In the phase II test, the effect of exposure time was investigated at intervals of 0.25hour for the critical temperature. All test results demonstrate that the exposure time effect is not significant compared to the maximum exposure temperature, but it is not negligible and, moreover, is significant at the critical temperature.

• Journal of the Korea Concrete Institute
• /
• v.23 no.6
• /
• pp.749-756
• /
• 2011

Most experimental studies on durability of FRP reinforcements subjected to high temperature have focused on the effect of high temperature only on tensile properties. But FRP reinforcement used in newly constructed concrete structure is first degraded by moisture and alkaline environment of concrete. When the structure is subjected to fire, the degraded FRP reinforcement is exposed to high temperature. Therefore, the effects of concrete environment and high temperature should be simultaneously considered for evaluation of FRP reinforcement damaged by fire. In this study, FRP reinforcements submerged in simulated solutions of pH 12.3 and 7 for extended period of time were subjected to temperatures of $60^{\circ}C$, $100^{\circ}C$, $150^{\circ}C$, and $300^{\circ}C$ to be examined. In order to investigate the effect of the high temperature, interlaminar shear strengths were measured and compared to those of control ones. The experimental results demonstrated that the combined effect of concrete environment and high temperature on properties of FRP reinforcement was more significant than the effect of high temperature or concrete environment solely.

• Journal of the Korea Concrete Institute
• /
• v.26 no.1
• /
• pp.79-86
• /
• 2014

In this paper, a stress transfer mechanism between near surface-mounted (NSM) fiber reinforced polymer (FRP) plate and concrete was investigated and a reliable analytical procedure for it was presented by using bilinear bond-slip model simulating the bond behavior of NSM FRP plate. As a result, critical values in the bi-linear model such as maximum shear strength, slip at that time and failure slip at the initiation of softening de-bonding were suggested for being used in the differential equation considering he interfacial characteristic between NSM FRP and concrete. Also, it was found that the bond-slip behavior could be suitably redicted by using the proposed procedure even in the case of various bond lengths from the comparison with bond test result.

• Journal of the Korea Concrete Institute
• /
• v.21 no.1
• /
• pp.47-53
• /
• 2009

12 concrete blocks, on which hybrid fibrous sheets (carbon fiber and glass fiber) had been bonded, were subjected to tensile load in order to estimate properties of the bonded interface. the sheet length was varied by 100mm, 200mm and 400mm. It was found that more than 150mm bond length is required to achieve the maximum bearing capacity of the interface. In this study, maximum bond stress $\tau_{F,max}$, ultimate slip $S_{FU}$ of the interface were estimated $\tau_{F,max}$=3.0MPa and $S_{FU}$= 0.175mm, respectively.

• Journal of the Korea Concrete Institute
• /
• v.28 no.5
• /
• pp.535-544
• /
• 2016

This paper aims at examining the effects of sustained load and elevated temperature on the time-dependent deformation of a carbon fiber reinforced polymer (CFRP) sheets bonded to concrete as well as the pull-off strength of single-lap shear specimens after the sustained loading period using digital images. Elevated temperature during the sustained loading period resulted in increased slip of the CFRP composites, whereas increased curing time of the polymer resin prior to the sustained loading period resulted in reduced slip. Pull-off tests conducted after sustained loading period showed that the presence of sustained load resulted in increased pull-off strength and interfacial fracture energy. This beneficial effect decreased with increased creep duration. Based on analysis of digital images, results on strain distributions and fracture surfaces indicated that stress relaxation of the epoxy occurred in the 30 mm closest to the loaded end of the CFRP composites during sustained loading, which increased the pull-off strength provided the failure locus remained mostly in the concrete. For longer sustained loading duration, the failure mode of concrete-CFRP bond region can change from a cohesive failure in the concrete to an interfacial failure along the concrete/epoxy interface, which diminished part of the strength increase due to the stress relaxation of the adhesive.