• Restorative Dentistry and Endodontics
• /
• v.25 no.1
• /
• pp.46-55
• /
• 2000

During bonding procedure of composite resin, the prepared cavity can be contaminated by saliva. In this study, marginal microleakage and shear bond strength of a composite resin to primed enamel and dentin treated with artificial saliva(Taliva$^{(R)}$) were evaluated. For the marginal microleakage test, Class V cavities were prepared in the buccal surfaces of fifty molars. The samples were randomly assigned into 5 groups with 10 samples in each group. Control group was applied with a bonding system (Scotchbond$^{TM}$ Multi-Purpose plus) according to manufacture's directions without saliva contamination. Experimental groups were divided into 4 groups and contaminated with artificial saliva for 30 seconds after priming: Experimental 1 group ; artificial saliva was dried with compressed air only, Experimental 2 group ; artificial saliva was rinsed and dried. Experimental 3 group ; cavities were etched with 35% phosphoric acid for 15 seconds after rinsing and drying artificial saliva. Experimental 4 group ; cavities were etched with 35% phosphoric acid for 15 seconds and primer was reapplied after rinsing and drying artificial saliva. All the cavities were applied a bonding agent and filled with a composite resin (Z-100$^{TM}$). Specimens were immersed in 0.5% basic fuschin dye for 24 hours and embedded in transparent acrylic resin and sectioned buccolingually with diamond wheel saw. Four sections were obtained from one specimen. Degree of marginal leakage was scored under stereomicroscope and their scores were averaged from four sections. The data were analyzed by Kruscal-Wallis test and Fisher's LSD. For the shear bond strength test, the buccal or occlusal surfaces of one hundred molar teeth were ground to expose enamel(n=50) or dentin(n=50) using diamond wheel saw and its surface was smoothed with Lapping and Polishing Machine(South Bay Technology Co., U.S.A.). Samples were divided into 5 groups. Treatment of saliva-contaminated enamel and dentin surfaces was same as the marginal microleakage test and composite resin was bonded via a gelatin capsule. All specimens were stored in distilled water for 48 hours. The shear bond strengths were measured by universal testing machine (AGS-1000 4D, Shimaduzu Co., Japan) with a crosshead speed of 5 mm/minute. Failure mode of fracture sites was examined under stereomicroscope. The data were analyzed by ANOVA and Tukey's studentized range test. The results of this study were as follows : 1. Enamel marginal microleakage showed no significant difference among groups. 2. Dentinal marginal microleakages of control, experimental 2 and 4 groups were lower than those of experimental 1 and 3 groups (p<0.05). 3. The shear bond strength to enamel was the highest value in control group (20.03${\pm}$4.47MPa) and the lowest value in experimental 1 group (13.28${\pm}$6.52MPa). There were significant differences between experimental 1 group and other groups (p<0.05). 4. The shear bond strength to dentin was higher in control group (17.87${\pm}$4.02MPa) and experimental 4 group (16.38${\pm}$3.23MPa) than in other groups, its value was low in experimental 1 group (3.95${\pm}$2.51 MPa) and experimental 2 group (6.72${\pm}$2.26MPa)(p<0.05). 5. Failure mode of fractured site on the enamel showed mostly adhesive failures in experimental 1 and 3 groups. 6. Failure mode of fractured site on the dentin did not show adhesive failures in control group, but showed mostly adhesive failure in experimental groups. As a summary of above results, if the primed tooth surface was contaminated with artificial saliva, primer should be reapplied after re-etching it.

• The Journal of Korean Academy of Prosthodontics
• /
• v.46 no.5
• /
• pp.520-527
• /
• 2008

Purpose: This study was conducted to evaluate the shear bond strength of composite resin to dentin when etched with laser instead of phosphoric acid. Material and methods: Recently extracted forty molars, completely free of dental caries, were embedded into acrylic resin. After exposing dentin with diamond saw, teeth surface were polished with a series of SiC paper. The teeth were divided into four groups composed of 10 specimens each; 1) no surface treated group as a control 2) acid-etched with 35%-phosphoric acid 3) Er:YAG laser treated 4) Er,Cr:YSGG laser treated. A dentin bonding agent (Adapter Single Bond2, 3M/ESPE) was applied to the specimens and then transparent plastic tubes (3 mm of height and diameter) were placed on each dentin. The composite resin was inserted into the tubes and cured. All the specimens were stored in distilled water at $37^{\circ}C$ for 24 hours and the shear bond strength was measured using a universal testing machine (Z020, Zwick, Germany). The data of tensile bond strength were statistically analyzed by one-way ANOVA and Duncan's test at ${\alpha}$= 0.05. Results: The bond strengths of Er:YAG laser-treated group was $3.98{\pm}0.88$ MPa and Er,Cr:YSGG laser-treated group showed $3.70{\pm}1.55$ MPa. There were no significant differences between two laser groups. The control group showed the lowest bond strength, $1.52{\pm}0.42$ MPa and the highest shear bond strength was presented in acid-etched group, $7.10{\pm}1.86$ MPa (P < .05). Conclusion: Laser-etched group exhibited significantly higer bond strength than that of control group, while still weaker than that of the phosphoric acid-etched group.

• Journal of Dental Rehabilitation and Applied Science
• /
• v.18 no.3
• /
• pp.157-170
• /
• 2002

The purpose of this study is to analyze the shear bond strength according to kinds of surface treatment agents and resin cements after acid etching of IPS Empress 2. For this purpose, test groups were classified into silane-treated bonding groups, silica-coated group and Targis link applied group. Then, nine bonding groups in total, each three groups per kind, were prepared by using three kinds of resin cements-Panavia F, Variolink II and Rely-X ARC, and thirty test specimens per group were prepared. To examine any changes in the oral environment, the shear bond strength of each test specimen was measured after dipping test for 24 hours and for five weeks, respectively, in distilled water at $37^{\circ}C$ and performing heat cycle 10,000 times in total, each 2,000 times per week, during a five weeks of dipping, under the condition similar to the oral environment. The bond failure modes were also observed by means of a scanning electron microscope. The results are summarized as follows 1. Statically significant differences between the surface conditioning materials were observed. The shear strength of the silane treatment was the highest of all three types of surface treatments(p<0.001). 2. Shear strengths varied significantly for different types of resin luting agents. But bond strength of Targis link surface treatments were not significantly different(p<0.05). 3. No significant difference of bonding strengths was found between storage time conditions(24 hours and 5 weeks). Only group II, IV, VII, IX were significantly different(p<0.05). 4. After thermocycling, the shear bond strengths of all groups were significantly decreased (p<0.05). Group III, V, VI were no significantly different. 5. On the SEM observation of fractured surfaces, all groups were shown complex failure.

• Journal of Periodontal and Implant Science
• /
• v.43 no.1
• /
• pp.41-46
• /
• 2013

Purpose: The objective of this study was to evaluate the effect of microthreads on removal torque and bone-to-implant contact (BIC). Methods: Twelve miniature pigs for each experiment, a total of 24 animals, were used. In the removal torque analysis, each animal received 2 types of implants in each tibia, which were treated with sandblasting and acid etching but with or without microthreads at the marginal portion. The animals were sacrificed after 4, 8, or 12 weeks of healing. Each subgroup consisted of 4 animals, and the tibias were extracted and removal torque was measured. In the BIC analysis, each animal received 3 types of implants. Two types of implants were used for the removal torque test and another type of implant served as the control. The BIC experiment was conducted in the mandible of the animals. The $P_1-M_1$ teeth were extracted, and after a 4-month healing period, 3 each of the 2 types of implants were placed, with one type on each side of the mandible, for a total of 6 implants per animal. The animals were sacrificed after a 2-, 4-, or 8-week healing period. Each subgroup consisted of 4 animals. The mandibles were extracted, specimens were processed, and BIC was analyzed. Results: No significant difference in removal torque value or BIC was found between implants with and without microthreads. The removal torque value increased between 4 and 8 weeks of healing for both types of implants, but there was no significant difference between 8 and 12 weeks. The percentage of BIC increased between 2 and 4 weeks for all types of implants, but there was no significant difference between 4 and 8 weeks. Conclusions: The existence of microthreads was not a significant factor in mechanical and histological stability.

• Applied Chemistry for Engineering
• /
• v.26 no.5
• /
• pp.543-548
• /
• 2015

Si/C/CNF composites as anode materials for lithium-ion batteries were examined to improve the capacity and cycle performance. Si/C/CNF composites were prepared by the fabrication process including the synthesis and magnesiothermic reduction of SBA-15 to obtain Si/MgO by ball milling and the carbonization of phenol resin with CNF and HCl etching. Prepared Si/C/CNF composites were then analysed by BET, XRD, FE-SEM and TGA. Among SBA-15 samples synthesized at reaction temperatures between 50 and $70^{\circ}C$, the SBA-15 at $60^{\circ}C$ showed the largest specific surface area. Also the electrochemical performances of Si/C/CNF composites as an anode electrode were investigated by constant current charge/discharge test, cyclic voltammetry and impedance tests in the electrolyte of LiPF6 dissolved in mixed organic solvents (EC : DMC : EMC = 1 : 1 : 1 vol%). The coin cell using Si/C/CNF composites (Si : CNF = 97 : 3 in weight) showed better capacity (1,947 mAh/g) than that of other composition coin cells. The capacity retention ratio decreased from 84% (Si : CNF = 97 : 3 in weight) to 77% (Si : CNF = 89 : 11 in weight). It was found that the Si/C/CNF composite electrode shows an improved cycling performance and electric conductivity.

• Restorative Dentistry and Endodontics
• /
• v.24 no.1
• /
• pp.156-165
• /
• 1999

The purpose of this study was to evaluate the effect of surface treatments on the shear bond strength between new and old composites. Circular cavities prepared on the center of acrylic resin mold and the prepared cavities were filled with composite resin. They randomly assigned into control group and 8 groups according to the difference in surface treatments of old composites; Control group: no surface treatment, Group 1: surface treated with #120 SiC paper & bonding agent, Group 2: surface treated with #400 SiC paper & bonding agent, Group 3: surface treated with #120 SiC paper, 32% $H_3PO_4$ & bonding agent, Group 4: surface treated with #400 SiC paper, 32% $H_3PO_4$ & bonding agent, Group 5: surface treated with #120 SiC paper, primer & bonding agent, Group 6: surface treated with #400 SiC paper, primer & bonding agent, Group 7: surface treated with #120 SiC paper, 32% $H_3PO_4$, primer & bonding agent, Group 8: surface treated with #400 SiC paper, 32% $H_3PO_4$, primer & bonding agent. New composites were applicated on the old composites of experimental groups. The shear bond strengths for the experimental specimen were measured and the results were analyzed by using one way ANOVA. The observations of surface morphology after SiC paper roughening and debonded surface morphology after shear bond strength test were done by SEM. The results were as follows; 1. Shear bond strengths for specimens roughened with #120 SiC paper matching with the particle size of coarse diamond bur were significantly higher than those for the specimens with #400 SiC paper(P<0.05). By SEM, the surface of the specimens roughened with #120 SiC paper was more irregular than the specimens with #400 SiC paper. 2. Shear bond strengths for specimens treated with 32% $H_3PO_4$ etchant, primer, bonding resin were significantly higher than those for specimens treated with 32% $H_3PO_4$ and bonding resin(P<0.05). 3. Shear bond strengths for the specimens treated with 32% $H_3PO_4$ etchant and bonding resin were significantly higher than those for specimens treated with only bonding resin(P<0.05). There was no remarkable change of surface morphology after 32% $H_3PO_4$ etching. 4. It was possible to observe mixed fracture patterns (the cohesive fracture of old composite and the adhesive fracture between old and new composite) in the specimens roughened with #120 SiC paper, but almost adhesive fracture in the specimens roughened with #400 SiC paper.

• Restorative Dentistry and Endodontics
• /
• v.35 no.1
• /
• pp.13-19
• /
• 2010

The purpose of this study was to compare the microshear bond strength of a self-etching primer adhesive to dentin prepared with different diamond points, carbide burs and SiC papers, and also to determine which SiC paper yield similar strength to that of dentinal surface prepared with points or burs. Fifty-six human molar were sectioned to expose the occlusal dentinal surfaces of crowns and slabs of 1.2 mm thick were made. Dentinal surfaces were removed with three diamond points, two carbide burs, and three SiC papers. They were divided into one of eight equal groups (n = 7); Group 1: standard diamond point(TF-12), Group 2: fine diamond point (TF-12F), Group 3: extrafine diamond point (TF-12EF), Group 4: plain-cut carbide bur (no. 245), Group 5: cross-cut carbide bur (no. 557), Group 6 : P 120-grade SiC paper, Group 7: P 220-grade SiC paper, Group 8: P 800-grade SiC paper. Clearfil SE Bond was applied on dentinal surface and Clearfil AP-X was placed on dentinal surface using Tygon tubes. After the bonded specimens were subjected to uSBS testing, the mean uSBS (n = 20 for each group) was statistically compared using one-way ANOV A and Tukey HSD test. In conclusion, the use of extrafine diamond point is recommended for improved bonding of Clearfil SE Bond to dentin. Also the use of P 220-grade SiC paper in vitro will be yield the results closer to dentinal surface prepared with fine diamond point or carbide burs in vivo.

• The Journal of Korean Academy of Prosthodontics
• /
• v.42 no.4
• /
• pp.386-396
• /
• 2004

Statement of problem: It is not clear how to make a stable bonding between zirconia ceramic and resin cement. And the study about surface treatment of zirconia ceramic or bonding resin cement are not enough. Purpose: To measure and compare the shear bond strength of some resin cements on zirconia ceramic after different surface treatments. Material and method: 48 ceramic discs were made of 3 ceramic materials, zirconia ceramics (Zi-Ceram), heat-pressed ceramics (IPS Empress 2) and slip cast alumina ceramics (In-Ceram). According to the surface treatments of ceramic specimens and resin cements, specimens were classified into 6 groups and each group was composed of 8 specimens. For the surface treatment of Zi-Ceram group (test group), sandblasting and diamond bur preparation were applied and Superbond C&B and Panavia F were bonded respectively. For IPS Empress 2 group (control group), Variolink II was bonded after sandblasting, acid etching, silanization and for In-Ceram ALUMINA group (control group), Panavia F was bonded after sandblasting. After storing specimens in distilled water for 24 hours, the shear bond strength was measured by the universal testing machine. Results and conclusion: 1. Zi-Ceram group with Superbond C&B cement showed higher bond strength than with Panavia F cement regardless to the surface treatments (p<0.05). 2. In Zi-Ceram group with Superbond C&B cement, sandblasting treatment group (12.1MPa) showed higher bond strength than diamond bur treatment group (7.7MPa) (p<0.05). In Zi-Ceram group with Panavia F cement, there were no significant differences in the bond strength according to the surface treatments (p>0.05). 3. Zi-Ceram group with sandblasting and Superbond C&B cement (12.1MPa) showed the highest bond strength. The bond strength of this group was not significantly different from In-Ceram ALUMINA group (10.4MPa) (p>0.05) and lower than IPS Empress 2 group (15.9MPa) (p<0.05).

• The korean journal of orthodontics
• /
• v.26 no.3
• /
• pp.309-316
• /
• 1996

The purpose of this study was to determine the effect of salivary contamination of etched enamel on shear bond strength of a bracket adhered to etched enamel. Eighty extracted human permanent premolars were used in this study. These samples were divided into two groups. Buccal surface of samples were etched in vitro with 38% phosphoric acid for 15 seconds and 60 seconds. Each group was divided into four subgroups. Etched enamel surfaces were contaminated with saliva for 0, 1, 20, 60 seconds, washed and dried. Test surfaces were examined using scanning electron microscope(SEM). The shear bond strength of each sample was determined with a universal testing instrument(Instron Co. Model 4201). Results were as follows; 1. Salivary contamination for 1, 20, 60 seconds did not affect shear bond strength when compared with the uncontaminated enamel group. 2 There was no significant difference(P>.05) in shear bond strength between 15 sec. and 60 sec. etching in uncontaminated enamel groups. 3. When samples were examined using SEM, organic materials coated enamel surface masked the etched pattern partially.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2014.02a
• /
• pp.150.1-150.1
• /
• 2014

Showerhead is used as a main part in the semiconductor equipment. The face plate flatness should remain constant and the cleaning performance must be gained to keep the uniformity level of etching or deposition in chemical vapor deposition process. High operating temperature or long period of thermal loading could lead the showerhead to be deformed thermally. In some case, the thermal deformation appears very sensitive to showerhead performance. This paper describes the methods for robust design using computational fluid dynamics. To reveal the influence of the post distribution on flow pattern in the showerhead cavity, numerical simulation was performed for several post distributions. The flow structure appears similar to an impinging flow near a centered baffle in showerhead cavity. We took the structure as an index to estimate diffusion path. A robust design to reduce the thermal deformation of showerhead can be achieved using post number increase without ill effect on flow. To prevent the showerhead deformation by heat loading, its face plate thickness was determined additionally using numerical simulation. The face plate has thousands of impinging holes. The design key is to keep pressure drop distribution on the showerhead face plate with the holes. This study reads the methodology to apply to a showerhead hole design. A Hagen-Poiseuille equation gives the pressure drop in a fluid flowing through such hole. The assumptions of the equation are the fluid is viscous-incompressible and the flow is laminar fully developed in a through hole. An equation can be expressed with radius R and length L related to the volume flow rate Q from the Hagen-Poiseuille equation, $Q={\pi}R4{\Delta}p/8{\mu}L$, where ${\mu}$ is the viscosity and ${\Delta}p$ is the pressure drop. In present case, each hole has steps at both the inlet and the outlet, and the fluid appears compressible. So we simplify the equation as $Q=C(R,L){\Delta}p$. A series of performance curves for a through hole with geometric parameters were obtained using two-dimensional numerical simulation. We obtained a relation between the hole diameter and hole length from the test cases to determine hole diameter at fixed hole length. A numerical simulation has been performed as a tool for enhancing showerhead robust design from flow structure. Geometric parameters for the design were post distribution and face plate thickness. The reinforced showerhead has been installed and its effective deposition profile is being shown in factory.