Effect on Shear Strength of Ceramic Surface Treatment Materials and Three Resin Cements to IPS Empress 2

The purpose of this study is to analyze the shear bond strength according to kinds of surface treatment agents and resin cements after acid etching of IPS Empress 2. For this purpose, test groups were classified into silane-treated bonding groups, silica-coated group and Targis link applied group. Then, nine bonding groups in total, each three groups per kind, were prepared by using three kinds of resin cements-Panavia F, Variolink II and Rely-X ARC, and thirty test specimens per group were prepared. To examine any changes in the oral environment, the shear bond strength of each test specimen was measured after dipping test for 24 hours and for five weeks, respectively, in distilled water at $37^{\circ}C$ and performing heat cycle 10,000 times in total, each 2,000 times per week, during a five weeks of dipping, under the condition similar to the oral environment. The bond failure modes were also observed by means of a scanning electron microscope. The results are summarized as follows 1. Statically significant differences between the surface conditioning materials were observed. The shear strength of the silane treatment was the highest of all three types of surface treatments(p<0.001). 2. Shear strengths varied significantly for different types of resin luting agents. But bond strength of Targis link surface treatments were not significantly different(p<0.05). 3. No significant difference of bonding strengths was found between storage time conditions(24 hours and 5 weeks). Only group II, IV, VII, IX were significantly different(p<0.05). 4. After thermocycling, the shear bond strengths of all groups were significantly decreased (p<0.05). Group III, V, VI were no significantly different. 5. On the SEM observation of fractured surfaces, all groups were shown complex failure.

표면 처리재와 레진 시멘트가 IPS Empress 2의 전단결합강도에 미치는 영향

IPS Empress 2의 산 부식 후 표면 처리재와 레진 시멘트 종류에 따른 전단 결합 강도를 비교 분석하기 위해서 실란 처리, 실리카 코팅 그리고 Targis link 처리군으로 분류하고 Panavia F, Variolink II와 Rely-X ARC 레진 시멘트 세종류를 이용해서 9개군에 각 군당 30개의 시편을 제작하였다. 그리고 구강환경에서의 변화를 알아보기 위해서 구강환경과 유사한 조건으로 $37^{\circ}C$ 증류수에서 24시간 수중침지, $37^{\circ}C$ 증류수에서 5주간 수중 침지, 그리고 5주간 수중침지 중 매주 2000회씩 10,000회의 열 순환을 한 다음 각 시편의 전단결합강도를 측정하고 파절면을 주사 전자현미경으로 관찰하여 다음과 같은 결론을 얻었다. 1. 표면처리에 따른 전단결합강도는 모든 군에서 유의한 차이를 보였다. 실란 처리, 실리카 코팅, 그리고 Targis link의 순으로 유의한 결합력의 감소를 보였다(p<0.001). 2. 레진 시멘트의 종류에 따른 차이를 비교한 결과에서 Targis link 도포한 군만 제외하고 나머지 군에서는 레진 시멘트의 종류에 따른 결합강도의 차이를 보였다(p<0.05). 3. 수중 침지 시간에 따른 전단 결합강도는 모든 군에서 유의한 차이를 보이지는 않았지만 실란을 처리 후 Panavia를 사용한 군, 실리카 코팅 처리 후 Variolink를 사용한 군, Targis link 처리 후 Rely-X ARC와 Variolink를 사용한 군에서는 결합력의 감소를 나타내었다(p<0.05). 4. 열 순환 시행시에는 실란과 실리카 코팅 처리후 Rely-X ARC를 사용한 군과 실리카 코팅 처리후 Panavia F를 사용한 군만 제외하고 나머지는 유의한 결합력의 감소를 보였다(p<0.05). 5. 파절 시험 후 시편에 대한 주사 전자 현미경 관찰결과 모든 군에서 복합성 파절 양상을 보였다.