• The Journal of Advanced Prosthodontics
• /
• 제6권5호
• /
• pp.333-345
• /
• 2014

PURPOSE. Bonding agents (BA) are the crucial weak link of composite restorations. Since the commercial materials' compositions are not disclosed, studies to formulize the optimum ratios of different components are of value. The aim of this study was to find a proper formula of BAs. MATERIALS AND METHODS. This explorative experimental in vitro study was composed of 4 different sets of extensive experiments. A commercial BA and 7 experimental formulas were compared in terms of degree of conversion (5 experimental formulas), shear bond strength, mode of failure, and microleakage (3 experimental formulas). Statistical analyses were performed (${\alpha}$=.05). The DC of selected formula was tested one year later. RESULTS. The two-way ANOVA indicated a significant difference between the shear bond strength (SBS) of two tissues (dentin vs. enamel, P=.0001) in a way that dentinal bonds were weaker. However, there was no difference between the four materials (P=.283). The adhesive mode of failure was predominant in all groups. No differences between the microleakage of the four materials at occlusal (P=.788) or gingival (P=.508) sites were detected (Kruskal-Wallis). The Mann-Whitney U test showed a significant difference between the microleakage of all materials (3 experimental formulas and a commercial material) together at the occlusal site versus the gingival site (P=.041). CONCLUSION. A formula with 62% bisphenol A-glycidyl methacrylate (Bis-GMA), 37% hydroxy ethyl methacrylate (HEMA), 0.3% camphorquinone (CQ), and 0.7% dimethyl-para-toluidine (DMPT) seems a proper formula for mass production. The microleakage and SBS might be respectively higher and lower on dentin compared to enamel.

• Restorative Dentistry and Endodontics
• /
• 제25권1호
• /
• pp.46-55
• /
• 2000

During bonding procedure of composite resin, the prepared cavity can be contaminated by saliva. In this study, marginal microleakage and shear bond strength of a composite resin to primed enamel and dentin treated with artificial saliva(Taliva$^{(R)}$) were evaluated. For the marginal microleakage test, Class V cavities were prepared in the buccal surfaces of fifty molars. The samples were randomly assigned into 5 groups with 10 samples in each group. Control group was applied with a bonding system (Scotchbond$^{TM}$ Multi-Purpose plus) according to manufacture's directions without saliva contamination. Experimental groups were divided into 4 groups and contaminated with artificial saliva for 30 seconds after priming: Experimental 1 group ; artificial saliva was dried with compressed air only, Experimental 2 group ; artificial saliva was rinsed and dried. Experimental 3 group ; cavities were etched with 35% phosphoric acid for 15 seconds after rinsing and drying artificial saliva. Experimental 4 group ; cavities were etched with 35% phosphoric acid for 15 seconds and primer was reapplied after rinsing and drying artificial saliva. All the cavities were applied a bonding agent and filled with a composite resin (Z-100$^{TM}$). Specimens were immersed in 0.5% basic fuschin dye for 24 hours and embedded in transparent acrylic resin and sectioned buccolingually with diamond wheel saw. Four sections were obtained from one specimen. Degree of marginal leakage was scored under stereomicroscope and their scores were averaged from four sections. The data were analyzed by Kruscal-Wallis test and Fisher's LSD. For the shear bond strength test, the buccal or occlusal surfaces of one hundred molar teeth were ground to expose enamel(n=50) or dentin(n=50) using diamond wheel saw and its surface was smoothed with Lapping and Polishing Machine(South Bay Technology Co., U.S.A.). Samples were divided into 5 groups. Treatment of saliva-contaminated enamel and dentin surfaces was same as the marginal microleakage test and composite resin was bonded via a gelatin capsule. All specimens were stored in distilled water for 48 hours. The shear bond strengths were measured by universal testing machine (AGS-1000 4D, Shimaduzu Co., Japan) with a crosshead speed of 5 mm/minute. Failure mode of fracture sites was examined under stereomicroscope. The data were analyzed by ANOVA and Tukey's studentized range test. The results of this study were as follows : 1. Enamel marginal microleakage showed no significant difference among groups. 2. Dentinal marginal microleakages of control, experimental 2 and 4 groups were lower than those of experimental 1 and 3 groups (p<0.05). 3. The shear bond strength to enamel was the highest value in control group (20.03${\pm}$4.47MPa) and the lowest value in experimental 1 group (13.28${\pm}$6.52MPa). There were significant differences between experimental 1 group and other groups (p<0.05). 4. The shear bond strength to dentin was higher in control group (17.87${\pm}$4.02MPa) and experimental 4 group (16.38${\pm}$3.23MPa) than in other groups, its value was low in experimental 1 group (3.95${\pm}$2.51 MPa) and experimental 2 group (6.72${\pm}$2.26MPa)(p<0.05). 5. Failure mode of fractured site on the enamel showed mostly adhesive failures in experimental 1 and 3 groups. 6. Failure mode of fractured site on the dentin did not show adhesive failures in control group, but showed mostly adhesive failure in experimental groups. As a summary of above results, if the primed tooth surface was contaminated with artificial saliva, primer should be reapplied after re-etching it.

• Restorative Dentistry and Endodontics
• /
• 제24권4호
• /
• pp.570-577
• /
• 1999

치질에 대한 접착수복은 건전한 치질을 보존하면서 유지력을 증가시킬 뿐 아니라 치질과 수복물 계면에서의 미세누출을 방지할 수 있다는 측면에서 임상에서 그 사용빈도가 높아지고 있다. 그러나 복합레진충전후 중합과정에서의 수축현상이 여전히 해결되지 않는 문제로 남아 있으며 이로 인한 변연누출은 술후 지각과민, 변연변색이나 이차우식과 아울러 치수병변의 유발인자로 작용할 수 있다. 치질과 레진수복물간의 접착강도를 강화시킴으로써 변연부위의 누출현상을 극복할 수 있다는 인식 하에 많은 종류의 상아질 접착제에 대한 접착강도 검사와 미세누출 검사가 행해졌으나 접착강도와 변연누출간의 관계에 대한 직접적인 연구는 미흡한 상태이다. 본 연구에서는 우치를 이용한 동일시편에서 접착강도와 미세누출의 정도를 측정 후 상호관계를 알아보고자 하였다. 소의 하악 전치를 이용하여 법랑질 또는 상아질 시편을 각 군마다 30개씩 준비하였다. 32% 인산으로 15초 처리 및 20초 수세 후 치질처리 방법에 따라 법랑질/완전 건조시킨 군, 법랑질/습윤상태의 군, 상아질/완전 건조시킨 군, 상아질/습윤상태의 군으로 나누었다. 각 군의 시편을 One-Step$^{TM}$ adhesive를 적용 후 Charisma 복합레진으로 충전하였다. 그 후 2% methylene blue에 1주일 간 침잠시킨 후 24시간 흐르는 물에 수세한 뒤 인장접착 강도를 측정하였다. 인장 접착 강도 측정 후 컴퓨터 프로그램 상에서 색소의 침투 면적을 계산하였으며 그 결과는 다음과 같이 나타났다. 1. 법랑질 및 상아질 군 공히, 접착강도와 미세누출을 비교시 유의한 음의 상관관계를 나타내어 접착강도가 높을수록 미세변연누출은 적게 나타내는 경향을 나타내었다 (r=-0.50, p<0.05). 2 법랑질 군 및 상아질 군 공히, 습윤상태의 시편이 완전히 건조된 시편에 비해 높은 집착강도를 나타내었다 (p<0.05). 3. 상아질에서는 습윤상태의 군이 건조시킨 군 사이에 유의하게 적은 미세변연 누출을 나타낸 반면(p<0.05), 법랑질에서는 습윤상태의 군과 건조시킨 군 사이에 미세변연 누출에 있어 유의한 차이가 나타나지 않았다 (p>0.05).

• 대한치과교정학회지
• /
• 제27권5호
• /
• pp.839-852
• /
• 1997

Crystal growth 용액인 황화이온을 함유한 폴리아크릴산 용액에 의한 법랑질 표면처리는 법랑질 표면에 crystal growth를 유도함으로써 통상적인 산부식법을 대체하여 교정용 브라켓을 접착하기 위한 법랑질 전처치의 방법으로 사용될 수 있음이 제안된 바 있다. 이 연구는 crystal growth후 교정용 브라켓 접착제로 브라켓을 접착하는 방법의 임상적용 가능성을 구명하기 위하여 시행되었다. 발거된 사람소구치의 법랑질 표면을 $25\%$ 폴리아크릴산과 0.3M 황산을 함유한 기본 crystal growth 용액, 각각 0.3M lithium sulfate, 0.3M magnesium sulfate, 0.3M potassium sulfate를 첨가한 crystal growth 용액, $37\%$ 인산용액, 퍼미스로 각각 처리한 후, 교정용 광중합형 글래스아이오노머 시멘트와 교정용 레진접착제로 금속브라켓을 접착하였다. $37^{\circ}C$의 증류수에 24시간 침지시킨 후, 브라켓 전단결합강도를 측정하고 접착 파절양태를 관찰하였으며 표면처리된 법랑질 표면과 브라켓 제거후의 법랑질 표면을 주사전자현미경으로 관찰하여 다음과 같은 결과를 얻었다. Crystal growth후 광중합형 글래스아이오노머 시멘트로 브라켓 접착시 0.3M magnesium sulfate를 함유한 군의 브라켓 전단결합강도가 가장 높았다(p<0.01). Crystal growth후 광중합형 글래스아이오노머 시멘트로 접착한 군의 브라켓 전단결합강도는 crystal growth 후 레진접착제로 접착한 군보다 높았다(p<0.001). Magnesium sulfate, 또는 potassium sulfate를 함유한 crystal growth 용액으로 법랑질 표면을 처리한 후 글래스아이오노머시멘트로 접착한 군의 브라켓 전단결합강도는 산부식 후 레진 접착제로 접착한 군과 유의한 차이를 보이지 않았다. 브라켓 제거시 잔류접착제의 양은 글래스아이오노머 시멘트로 접착한 것이 가장 적었다. 이상의 결과는 magnesium sulfate나 potassium sulfate를 함유한 crystal growth 용액으로 법랑질 표면처리 후 교정용 광중합형 글래스 아이오노머 시멘트로 브라켓을 접착하는 방법이 통상적으로 사용되는 산부식 후 교정용 레진접착제에 의한 브라켓 접착법을 대체할 수 있음을 시사한다.

• 대한치과보철학회지
• /
• 제31권1호
• /
• pp.1-10
• /
• 1993

The purpose of this study was to evlauate the microleakage of 3 dentin bonding agents using different dentin pretreatment method under simulated physilogic pressure in cementing the porcelain laminate veneer. Noncarious 60 human maxillary molars were selected and randomly assigned to 4 groups of 15 each. The group with the margin placed on the enamel was classified as the control and the groups with the margin placed on root surface were subdivided into 3 groups according to the dentin bonding agents used. The group using All Bond 2 was classified as experimental group 1, the group using Scotchbond MP was classified as experimental group 2, and the group using Gluma was classified as experimental group 3. Roots were removed at 3mm below the cementoenamel junction, and reductions of the teeth for the porcelain laminate veneer were done on the mesial 1/2 of the buccal surface of each teeth. The pulp was extirpated and the pulp chamber was cleaned with 37% phosphoric acid for the patency of dentinal tubule. Under simulated physiologic pressure, porcelain laminate veneers were cemented to the teeth using each dentin bonding agent and luting cement. After cementation, all samples were stored at 36t in water for 24 hours and thermocycled for 1500 cycles, then immersed in 0.5% basic fuchsin solution and the teeth were sectioned longitudinally by using diamond saw and the extent of microleakage was measured. The following results were obtained, 1. Microleakage was observed in a few samples of control group but all the samples of experimental groups. 2. The control group showed the less extent of microleakage than the experimental groups. In experimental groups the experimental group 1 & the experimental group 2 showed similiar extent of microleakage and the experimental group 3 showed the greater extent of microleakage than other groups. Conclusively, practicing the porcelain laminate veneers in the clinic, although the margin of the porcelain laminate veneer should be placed on enamel, in the case that it is inevitable to place the margin of the porcelain laminate veneer on the root surface, it is recommened to use dentin bonding agents which use no dentin pretreatment or a dentin pretreatment which can leave the smear plugs.

• Restorative Dentistry and Endodontics
• /
• 제36권6호
• /
• pp.477-482
• /
• 2011

연구목적: 이 연구는 서로 다른 버로 형성한 법랑질 표면에 대한 자가부식 프라이머 접착제의 결합강도를 상호 비교함으로써 법랑질에 우수한 접착 표면을 제공하는 적절한 버를 알아보기 위해 시행하였다. 연구 재료 및 방법: 42개의 발거된 대구치 치관의 법랑질을 이용하였고, 법랑질을 삭제하는 기구의 종류에 따라 6개군, 즉 1군은 Coarse (125 - 150 ${\mu}m$) diamond bur; 2군은 standard (106 - 125 ${\mu}m$) diamond bur; 3군은 fine (53 - 63 ${\mu}m$) diamond bur; 4군은 extrafine (20 - 30 ${\mu}m$) diamond bur; 5군은 plain-cut carbide bur (no. 245); 6군은 cross-cut carbide bur (no. 557)으로 분류하였다. 각 군의 법랑질 표면에 Clearfil SE Bond를 적용한 후 Tygon tube를 이용하여 Clearfil AP-X를 접착하였다. 각 군의 미세전단 결합강도를 측정하였다. 결과: 4군의 결합강도는 모든 군중 가장 높게 나타나 1군, 2군, 3군 및 6군보다 통계학적으로 높게 나타났으며(p < 0.05), 5군과는 통계학적으로 유의한 차이를 나타내지 않았다(p > 0.05). 결론: 버의 종류와 다이아몬드 버의 입자크기는 약한 자가 산부식 프라이머 접착제의 법랑질에 대한 결합강도에 영향을 주었다. Clearfil SE Bond의 법랑질에 대한 우수한 접착을 위해서는 초미세입자 다이아몬드 버나 plain-cut 카바이드 버의 사용이 추천된다.

• 대한치과보철학회지
• /
• 제46권2호
• /
• pp.148-156
• /
• 2008

자가부식 접착제는 사용하기 쉽고, 술식 민감성이 적은 장점이 있으나 특히 산도가 약한 자가부식 접착제의 법랑질에 대한 결합력은 논란이 되고 있다. 본 연구에서는 2단계 자가부식 접착제인 Clearfil SE Bond (Kuraray, Okayama, Japan)의 연마 법랑질에 대한 미세인장 결합강도를 측정하여 3단계 산부식수세 접착제인 Scotchbond Multi-Purpose (3M ESPE, St. Paul, MN, USA) 및 1단계 자가부식 접착제인 iBond (Heraeus Kulzer Gmbh, Hanau, Germany)의 결합강도와 비교하고자 하였고, 2단계 자가부식 접착제에 산부식 전처리를 시행하는 것이 법랑질에 대한 결합강도를 높일 수 있는지 알아 보고자 하였다. 실험군은 2단계 자가부식 접착제인 Clearfil SE Bond만 사용한 비산부식 군과 35% 인산 (Scotchbond Etchant, 3M ESPE)으로 산부식 후 Clearfil SE Bond를 사용한 산부식 군, 그리고 1단계 자가부식 접착제인 iBond를 사용한 군으로 나누었다. 대조군은 3단계 산부식수세 접착제인 Scotchbond Multi-Purpose를 사용한 군으로 정하였다. Bovine 전치의 순면을 십자가형으로 4등분하여 각 군으로 무작위로 배분하였다. 각 치아의 순면을 800-grit 실리콘 카바이드 지로 연마한 후 삭제된 법랑질면에 제조사의 설명서에 따라 각 군의 접착제를 적용하고 Light-Core (Bisco)로 적층 충전하였다. 시편은 $37i{\acute{E}}$, 증류수에 일주일 동안 보관한 후 low speed precicion diamond saw (TOPMENT Metsaw-LS, R&B, Daejeon, Korea)를 이용하여 약 $0.8{\times}0.8mm$ 단면이 되도록 시편을 절단하여 미세시편을 제작하였다. 일주일마다 증류수를 교환하면서 한 달, 세 달 동안 $37i{\acute{E}}$, 증류수에 미세시 편을 보관한 후 각각의 미세인장결합강도를 측정하였다. 미세인장결합강도 (MPa)는 파절 시에 가해진 힘 (N)을 접착면적 ($mm^2$)으로 나누어 계산하였다. 접착계면에서의 파절 양상은 실물현미경 (Microscope-B nocular, Nikon)을 이용하여 분류하였다. 미세인장결합강도에 대한 통계분석은 one-way ANOVA를 이용하여 유의수준 5%에서 검정하였고, 사후감정은 Least Significant Difference 방법을 이용하였다. 중합 후 1개월 뒤 측정된 각각의 접착제의 평균 미세인장결합강도는 유의수준 5%에서 모든 접착제 간에 유의한 차이가 없었다. 3개월 뒤 측정된 각각의 접착제의 평균 미세인장결합강도는 유의수준 5%에서 iBond 와 Clearfil SE Bond 비산부식 군과 Scotchbond Multi- Purpose 간에는 각각 유의한 차이가 없었다. 본 연구에서는 2단계 자가부식 접착제인 Clearfil SE Bond의 연마 법랑질에 대한 미세인장결합강도가 3단계 산부식수세 접착제인 Scotchbond Multi-Purpose 와 비교하여 유의한 차이가 없었으며 (P>0.05), 3개월 후의 결과에서 Clearfil SE Bond 비산부식 군의 미세인장결합강도가 Clearfil SE Bond 산부식 군보다 유의하게 낮았다 (P<0.05). 즉 35% 인산으로 산부식 전처리를 시행한결과 Clearfil SE Bond 의 법랑질에 대한 결합강도가 증가하였다.

• 대한치과교정학회지
• /
• 제40권4호
• /
• pp.260-266
• /
• 2010

본 연구의 목적은 서로 다른 종류의 접착시스템과 법랑질 보호제 등이 설측 브라켓의 인장강도에 영향을 미치는지 알아보는데 있다. 75개의 발치된 하악 전치를 5개의 그룹으로 임의로 나눈 후 설측 브라켓을 부착하였다. Group 1은 Transbond XT를, Group 2는 Transbond XT와 함께 불소 유리레진(Ortho-coat)을 Group 3는 Transbond XT와 Chlorohexidine varnish (Cervitec Plus)를 Group 4는 광중합 접착제(Aegis Ortho)를 Group 5는 antimicrobial self-etching primer (Clearfil Protect Bond)을 사용하였다. 불소유리 레진이나 Chlorohexidine varnish의 사용유무는 접착력에 영향을 미치지 못하였다. Group 5이 다른 그룹에 비해 접착력과 접착제 잔류지수(adhesive remnant index, ARI)가 통계적으로 유의하게 높았다 (p < 0.001). 법랑질 보호제 적용 시 설측 브라켓의 접착력에 부정적인 영향을 미치지 못하였다. 이상의 결과로 이번에 사용한 제품들은 설측 교정치료 기간 동안 환자의 구강위생을 개선시킬 수 있어 환자와 술자에게 도움을 줄 수 있을 것이다. 그러나 에나멜 층이 얇은 경우 Clearfil Protect Bond의 과도한 접착강도에 대해 고려해야 할 것이다.

• The Journal of Advanced Prosthodontics
• /
• 제9권2호
• /
• pp.85-92
• /
• 2017

PURPOSE. The aim of this study was to evaluate the effect of tooth surface pre-treatment steps on shear bond strength, which is essential for understanding the adhesive cementation process. MATERIALS AND METHODS. Shear bond strengths of different cements with various tooth surface treatments (none, etching, priming, or etching and priming) on enamel and dentin of human teeth were measured using the Swiss shear test design. Three adhesives (Permaflo DC, Panavia F 2.0, and Panavia V5) and one self-adhesive cement (Panavia SA plus) were included in this study. The interface of the cement and the tooth surface with the different pre-treatments was analyzed using SEM. pH values of the cements and primers were measured. RESULTS. The highest bond strength values for all cements were achieved with etching and primer on enamel ($25.6{\pm}5.3-32.3{\pm}10.4MPa$). On dentin, etching and priming produced the highest bond strength values for all cements ($8.6{\pm}2.9-11.7{\pm}3.5MPa$) except for Panavia V5, which achieved significantly higher bond strengths when pre-treated with primer only ($15.3{\pm}4.1MPa$). Shear bond strength values were correlated with the micro-retentive surface topography of enamel and the tag length on dentin except for Panavia V5, which revealed the highest bond strength with primer application only without etching, resulting in short but sturdy tags. CONCLUSION. The highest bond strength can be achieved for Panavia F 2.0, Permaflo DC, and Panavia SA plus when the tooth substrate is previously etched and the respective primer is applied. The new cement Panavia V5 displayed low technique-sensitivity and attained significantly higher adhesion of all tested cements to dentin when only primer was applied.

• Restorative Dentistry and Endodontics
• /
• 제26권5호
• /
• pp.399-408
• /
• 2001

Tooth bleaching has been prevailing recently for its ability to recover the color and shape of natural teeth without reduction of tooth material. However, it has been reported that bleaching procedure adversely affects the adhesive bond strength of composite resin to tooth. At the same time the bond strength was reported to be regained by application of some chemical agents. The purpose of this in vitro study was to investigate the effect of the removal of residual peroxide on the composite- enamel adhesion and also evaluated fracture mode between resin and enamel after bleaching. Sixty extracted human anterior and premolars teeth were divided into 5 groups and bleached by combined technique using of office bleaching with 35 % hydrogen peroxide and matrix bleaching with 10% carbamide peroxide for 4 weeks. After bleaching, the labial surfaces of each tooth were treated with catalase, 70% ethyl alcohol, distilled water and filled with composite resin. Shear bond strength was tested and the fractured surfaces were also examined with SEM. Analysis revealed significantly higher bond strength values. (p＜0.05) for catalase-treated specimens, but water-treated specimens showed reduction of bond strength, alcohol- treated specimens had medium value between the two groups(p＜0.05). The fracture mode was shown that the catalase group and the alcohol group had cohesive failure but the water sprayed group had adhesive failure. It was concluded that the peroxide residues in tooth after bleaching seems to be removed by gradual diffusion and the free radical oxygen from peroxide prevents polymerization by combining catalyst in the resin monomer. Therefore it may be possible to eliminate the adverse effect on the adhesion of composite resin to enamel after bleaching by using water displacement solution or dentin bonding agent including it for effective removal of residual peroxide.