• Journal of Korea Foundry Society
• /
• v.14 no.1
• /
• pp.52-61
• /
• 1994

The effect of Ni addition, on the mechanical properties and fracture characteristics of Mo-Cu and Mo-Ni-Cu alloyed ductile iron austenitized at $900^{\circ}C$ and austempering temperatures of $250^{\circ}C$, $300^{\circ}C$ and $350^{\circ}C$. The tensile strength, yield strength and hardness are decreased and elongation and impact value are increased in both Mo-Cu and Mo-Ni-Cu alloyed austempered ductile iron, with increased austempering temperature. According to the austempering temperature are increased, the amount of retained austenite are increased. Maximum value of fracture toughness is obtained at $350^{\circ}C$ austempering temperature at this condition, the amount of retained austenite came to 40% in Mo-Ni-Cu alloyed ADI and 34% in Mo-Cu alloyed ADI. The fracture surface of ADI which had represented high toughness are showed a quasi-cleavage pattern and a dimple pattern with micro void. Comparing the fracture characteristics of Mo-Cu alloyed ADI with that of Mo-Ni-Cu alloyed ADI, the latter was superior to the former.

• Journal of Korea Foundry Society
• /
• v.13 no.2
• /
• pp.175-186
• /
• 1993

In this study, the effect of Mo addition on the microstructure and mechanical properties of ductile cast iron have been investigated. The amounts of Mo and the thickness of specimen have been varied from 0 to 4.79wt% and 13mm, 10mm and 6mm, respectively. As the casting thickness decreases, the average size of spheroidal graphite is decreased and the hardness increases. By increasing the Mo content, the tensile strength of ferrite and pearlite matrix increases and shows maximum which is about $30{\sim}40%$ higher than ordinary ductile cast iron. After the maximum, adding more Mo results in gradual transformation of ferrite and pearlite to bainite and thus tensile strength decreases again. The elongation decreases continueously with Mo content. The addition of Mo about $0.5{\sim}1.0wt%$ improves the wear resistance and tensile strength of thin ductile cast iron.

• Journal of Veterinary Clinics
• /
• v.22 no.2
• /
• pp.100-107
• /
• 2005

This study was carried out to investigate the physical and chemical properties of teat cup liners. The hardness of the liners was $50\~67$, and their fatigue to failure 38-1,185 cycles. The elongation and tensile strength of these liners were about $134 kgf/cm^2\;and\;473\%$, respectively. The infrared spectrum and the gas chromatogram revealed that the liner A was consisted of NR, SBR, and BR, with a composition ratio of 60:20:20 (part per hundred rubber). The raw rubber materials used for liners B to G, on the other hand, were NBR only. However, the liner H was made of silicon rubber. The thermogravimetric analysis showed that the liners tested in this study contained raw rubber material, carbon black, organic compounds and metallic compounds.

• Elastomers and Composites
• /
• v.55 no.1
• /
• pp.13-19
• /
• 2020

4,4'-Methylenebis(2-chlorobenzenamine) (MOCA)-free fast curing polyurethanes were prepared. In this study, the processibility of a fast curing polyurethane system was characterized by assessing the pot life. The obtained pot life of the polyurethane was 6-8 s, indicating that this prepolymer-curative system is appropriate for ribbon flow casting. The influence of the NCO index on the viscosity and mechanical properties was evaluated. The viscosity, tensile strength, tear strength, and hardness of the as-prepared polyurethanes showed an increasing trend, with an increase in the NCO index, whereas the elongation at break increased initially and then decreased with an increase in the NCO index. The gel fraction and crosslink density showed a direct correlation with the NCO index, which substantiated the improved mechanical properties at the higher NCO index. The coefficients of friction and abrasion deteriorated with an increase in the NCO index.

• Transactions of Materials Processing
• /
• v.30 no.2
• /
• pp.91-98
• /
• 2021

The present study deals with the microstructure and mechanical properties of 700 MPa-grade high-strength seismic resistant reinforced steel bars fabricated by various TempCore process conditions. For the steel bars, in the surface region tempered martensite was formed by water cooling and subsequent self-tempering during TempCore process, while in the center region there was ferrite-pearlite or bainite microstructure. The steel bar fabricated by the highest water flow and the lowest equalizing temperature had the highest hardness in all regions due to the relatively fine microstructure of tempered martensite and bainite. In addition, the steel bar having finer microstructures as well as the high fraction of tempered martensite in the surface region showed the highest yield and tensile strengths. The presence of vanadium precipitates and the high fraction of ferrite contributed to the improvement of seismic resistance such as high tensile-to-yield strength ratio and high uniform elongation.

• Journal of Welding and Joining
• /
• v.22 no.5
• /
• pp.38-45
• /
• 2004

The present study is to investigate the effect of heat input on the microstructure, tensile properties and toughness of single-pass submerged arc bead-in-groove welds produced on SA508 class 3 steels. The heat input was varied in the range of 1.6, 3.2 and 5.0 kJ/mm. The toughness of weld metals was evaluated by using subsize Charpy V-notch specimens in the temperature range of -19$0^{\circ}C$ to 2$0^{\circ}C$. The weld microstructure and fractography were observed by optical and scanning electron microscopies, respectively. With increasing heat inputs, tensile strength and hardness of weld metals were decreased while elongation was increased. The poor notch toughness at 1.6 kJ/mm was attributed to the formation of ferrite with aligned second phase and banitic microstructure with high yield strength while that at 5.0 kJ/mm was due to the presence of grain boundary and polygonal ferrites. The microstructure of the intermediate energy input welds consisted of a high proportion of acicular ferrite with limited polygonal ferrites, which provide improved notch toughness.

• Journal of Korea Foundry Society
• /
• v.16 no.6
• /
• pp.503-512
• /
• 1996

Austempered ductile irons(ADI) are characterized by their relatively high retained austenite content which has a significant effect on mechanical properties and performance, such as ductility, toughness, wear resistance and machinability. Austenitising treatment at $900^{\circ}C$ for $1{\sim}2hours$, and austempering treatment within the temperature range $240{\sim}400^{\circ}C$ on ductile cast iron alloyed with Cu and Mo were carried out, and the effects of retained austenite content on the mechanical properties and wear resistance were investigated. In consequence, the amount of retained austenite was found to be 13.5% at the austempering temperature of $240^{\circ}C$, and was increased 28% at $400^{\circ}C$. Tensile strength and hardness of austempered ductile iron were decreased as the retained austenite content increased, but elongation was increased. The retained austenite content at the austenitising time of 2hours was more than at 1hour. The amounts of rolling wear loss were increased as the retained austenite content increased, and the wear surface was become to be rough.

• Journal of Korea Foundry Society
• /
• v.24 no.2
• /
• pp.94-100
• /
• 2004

Gas porosity which is a common defect in aluminum alloy casting, is also thought to be severer in aluminum alloy castings produced by lost foam process due to the pyrolysis of the polystyrene foam pattern during pouring. Fundamental experiments were carried out to evaluate the effect of process variables such as the melt treatment, the cooling rate and pouring temperature on the density and mechanical properties in A356.2 castings with simple bar shape. The density of grain refined specimen was slightly lower than that of degassed one, but was higher than that of no treated one and that of shot ball packed specimen was higher than the other specimens. The tensile strength and elongation were in the ranges of $200{\sim}230MPa$ and $0.5{\sim}1.5%$ respectively. The density and hardness of lost foam cast specimens decreased with increase in pouring temperature.

• Journal of the Korean Society for Heat Treatment
• /
• v.19 no.3
• /
• pp.156-162
• /
• 2006

The aim of this study is to investigate the full annealing parameter for A3003 Al alloy welded tubes. The A3003 Al alloy tubes with 34 mm in external diameter and 1.3 mm in thickness for OPC drum were manufactured by high frequency induction welding with the V shaped convergence angle $6.7^{\circ}$ and power input 50 kW. The tensile and yield strength decreased with increasing the annealing temperature and time remarkably, but elongation increased remarkably. Vickers hardness in welds and base metal decreased with increasing the annealing temperature and time remarkably. In a certain experimental condition, the welds line in A3003 alloys disappeared at $520^{\circ}C$ for 4hr because of the same mechanical properties and structures between welds and base metal.

• Journal of Welding and Joining
• /
• v.25 no.5
• /
• pp.51-57
• /
• 2007

The present work was aimed to examine the variation of microstructure and mechanical properties by annealing($100{\sim}620^{\circ}C$, $2{\sim}8hr$) in A3003 Al alloy welded pipes. The A3003 Al alloy pipes with 34 mm in external diameter and 1.3 mm in thickness were manufactured by high frequency induction welding with the V shaped convergence angle $6.7^{\circ}$ and power input 50 kW. The tensile and yield strength decreased with increasing the annealing temperature remarkably, but elongation increased remarkably. Vickers hardness in welds decreased with increasing the annealing temperature remarkably. The primary intermetallic compound of $Al_{12}(Fe,\;Mn)_2Si$ was precipitated in welds as the same base metal. In a certain experimental condition, the welds line in A3003 alloys disappeared at $450^{\circ}C$ for 2 hr because of the same mechanical property and structure between welds and base metal.