• Proceedings of the Korean Vacuum Society Conference
• /
• 2014.02a
• /
• pp.386.1-386.1
• /
• 2014

The ionic polymer-metal composite (IPMC), a type of electro-active polymer material, has received enormous interest in various fields such as robotics, medical sensors, artificial muscles because it has many advantages of flexibility, light weight, high displacement, and low voltage activation, compare to traditional mechanical actuators. Mostly noble metal materials such as gold or platinum were used to form the electrode of an IPMC by using electroless plating process. Furthermore, carbon-based materials, which are carbon nanotube (CNT) and reduced graphene-CNT composite, were used to alter the electrode of IPMC. To form the electrode of IPMC, we employ the synthesized graphene on copper foil by chemical vapor deposition method and use the transfer process by using a support of PET/silicone film. The properties of graphene were evaluated by Raman spectroscopy, UV/Vis spectroscopy, and 4-point probe. The structure and surface of IPMC were analyzed via field emission scanning electron microscope. The fabricated IPMC performance such as displacement and operating frequency was measured in underwater.

• Corrosion Science and Technology
• /
• v.12 no.4
• /
• pp.185-190
• /
• 2013

In the present study, $Ni-TiO_2$ composite coatings were electrodeposited in a sulfamate bath containing $TiO_2$ particles. The influence of the ultrasonic treatment on the co-deposition of $TiO_2$ particles in the coating and the hardness of the electrodeposited $Ni-TiO_2$ composite has been investigated. Three different ultrasonic treatments (pretreatment before the electrodeposition (pre-UT), pretreatment + applied during the electrodeposition (UT), and the electrodeposition without the ultrasonic treatment (w/o UT)) were performed. The $Ni-TiO_2$ composite coatings are characterized using scanning electron microscopy (SEM), image analyzer, and hardness tester. Comparison of results indicates that the volume fraction is more important factor than the agglomerated particle size in terms of the strength improvement, and the strength of the electrodeposited $Ni-TiO_2$ composite coatings is enhanced with pre-UT condition.

• Journal of the Korean Ceramic Society
• /
• v.37 no.8
• /
• pp.731-738
• /
• 2000

KLN(K3Li2Nb5O15) has attracted a great deal of attention for their potential usefulness in piezoelectric, electro-optic, nonlinear optic, and pyroelectirc devices. Especially, the KLN single crystal has been studied in the field of optics and electronics. However it is hard to produce good quality single crystals due to the crack propagation during crystal growing. One of the solutions of this problem is prepartion of thin film. But the intensive study has not been conducted so far. In this study, after the KLN thin film were prepared by R.F. magnetron Sputtering method on SiO2/Si substrate, the post-annealing methods of RTA(rapid thermal annealin) and IPA(insitu post annealing) were employed. The deposition condition of KLN thin film was RF power(100 W), Working pressure(100 mtorr). The commonness of both RAT and IPA was that the higher were deposition and post annealing temperature, the higher was the intensity of XRD but the less surface roughness. The difference of post-annealing methods affected XRD phase and surface condition very much. And in IPA process, the influence of O2 had much effect on the formation of KLN phase.

• Journal of Advanced Marine Engineering and Technology
• /
• v.28 no.6
• /
• pp.1000-1009
• /
• 2004

The environment friendly calcareous deposit films were formed on steel plates by electrodeposition technique in natural seawater and synthetic solutions such as dissolved $\textrm{Mg}^{2+}$ and $\textrm{Ca}^{2+}$ ions at various potential conditions. The influence of potential conditions on composition ratio, structure and morphology of the electrodeposited films were investigated by scanning electron microscopy(SEM), energy dispersive spectroscopy(EDS) and X-ray diffractor (XRD). Accordingly, this study was provided a better understanding of the composition between the growth of $\textrm{Mg(OH)}_2$ and that of $\textrm{CaCO}_3$ during the formation of calcareous deposit films on steel substrate under cathodically electrodeposition in synthetic and natural seawater. The results showed that the formation of good overall calcareous deposited film in seawater can be achieved by controlling the Ca/Mg ratio according to interfacial pH with the effective use of the electro deposition technique.

• Journal of the Korean Ceramic Society
• /
• v.49 no.2
• /
• pp.191-196
• /
• 2012

In this study, tin phosphate glass system($SnO_2-(1-x)P_2O_5-xB_2O_3$) that occur during the melting of the metal oxide inhibition of the oxidation reaction, and to reduce oxides of high melting temperature in the following three methods were melting. The first is the general way in the atmosphere, and the second by injecting $N_2$ gas under a neutral atmosphere, and finally in the air were melted by the addition of a reducing agent Melt in the atmosphere when the oxidation of the metal oxide is inhibited by low temperatures were melting. In addition, the deposition of crystals within glassy or inhibit devitrification phenomenon is also improved over 80% transmittance. This phenomenon, when the melting of glass, many of $Sn^{4+}$ ions are reduced to the $Sn^{2+}$ was forming oxides SnO, because it acts as a modifier oxide.

• Journal of the Korea institute for structural maintenance and inspection
• /
• v.23 no.7
• /
• pp.1-8
• /
• 2019

The primary purposes of this study are to understand a fundamental effects of electro-deposition on reinforcing steel in saturated Ca(OH)2 electrolyte, and evaluate the corrosion rates of rebars under cyclic 3wt.%NaCl immersion and dry corrosion environment. The three cement mortar specimens with cover thickness 5, 10 and 30mm, were prepared in the experiment. To monitor the corrosion rates of rebars in mortar, the three cement mortar specimens were exposed to 110 wet-drying cycles(8-hour-immersion in 3wt.%NaCl and 16-hour-drying in a room temperature) in the laboratory. During the wet-dry cycles, the polarization resistance, Rp, and solution resistance, Rs, were continuously measured. The instantaneous corrosion rates of rebars on the effect of electro-depositing with sat. Ca(OH)2 electrolyte were estimated from obtained R-1p and degrees of wetness were estimated from Rs values. From the experimental results, the corrosion rates of rebars were greatly accelerated by wet/dry cycles. During the mortars exposed to drying condition, the large increases in the corrosion rates were showed at all rebar surfaces in three mortar specimen, attributed from the accelerated reduction rates of dissolved oxygen in drying process. However, the corrosion rates on rebar surface electrochemically deposited with sat. Ca(OH)2 electrolyte showed the clear decreases, caused by calcium deposits in the porous rust layer.

• Journal of Surface Science and Engineering
• /
• v.37 no.5
• /
• pp.253-262
• /
• 2004

Calcareous deposits are the consequence of pH increase of the electrolyte adjacent to metal surface affected by cathodic current in seawater. It obviously has several advantages over conventional coatings, since the calcareous deposit coating is formed from coating (Mg$^{2+}$, $Ca^{2+}$) naturally existing in seawater. In consideration of this respect, environment friendly calcareous deposit films were formed by an electro deposition technique on steel substrates submerged in 48$^{\circ}C$ natural seawater. And the influence of current density, coating time and attachment of steel mesh on composition ratio, structure and morphology of the electrodeposited films were investigated by Scanning Electron Microscopy(SEM), Energy Dispersive Spectroscopy(EDS) and X-Ray Diffractor(XRD), respectively. Accordingly, this study provides a better understanding of the composition between the growth of $Mg(OH)_2$ and $CaCO_3$ during the formation of electro deposit films on steel substrate under cathodically electrodeposition in $48^{\circ}C$ natural seawater. The Mg compositions, in general, are getting decreased regardless of current density but Ca compositions are getting increased as electrodeposition time runs. That is, $Mg(OH)_2$ compounds of brucite structure shaped as flat type is formed at the initial stage of electrodeposition, but CaCO$_3$ compounds of aragonite structure shaped as flower type is formed in large scale. Besides, $Mg(OH)_2$ compounds were much formed at 5 A/$\m^2$ environment condition compared to the 3 A/$\m^2$ and 4 A/$\m^2$ environment conditions. This is because that OH- which was comparatively largely generated at the metal surface is preferably combined with $Mg^{2+}$TEX>.

• Journal of Ceramic Processing Research
• /
• v.19 no.6
• /
• pp.445-449
• /
• 2018

Chromium plating is a common surface treatment technique extensively applied in industry due its excellent properties which include substantial hardness, abrasion resistance, corrosion resistance, surface color, and luster. In this study, the effect of $MoS_2$ particles of the composite coating was investigated. To improve the lubrication of mold, $Cr-P-C/MoS_2$ composite plating was studied by varying the $MoS_2$ content. The current efficiency of the composite plating incorporated $MoS_2$ particles was increased at $MoS_2$ contents of 0.5 and 1.0 g/l due to the incorporation of fine particles. On the other hand, when the content of $MoS_2$ is 1.0 g/l or more, the current efficiency is lowered due to an increase in impact on the cathode surface. In order to evaluate the mechanical properties of Scratch test were conducted. Scratch test confirmed the lubricity and abrasion resistance characteristics revealed that the composite plating with added $MoS_2$ had relatively low surface roughness and uniform surface modification to improve its properties.

• Journal of the Korean Magnetics Society
• /
• v.24 no.6
• /
• pp.186-190
• /
• 2014

To establish the coating conditions for $^{57}Co$, non-radioactive Co ions are dissolved in an acid solution and electroplated on to a copper plate. Then, the thermal diffusion of electroplated Co into a copper matrix was studied to apply a $^{57}Co$ $M{\ddot{o}}ssbauer$ source. Nanocrystalline Co particles were coated on a Cu substrate using DC electro-deposition at a pH of 1.89 to 5 and $20{\sim}30mA/cm^2$. The average grain size was up to 54 nm as the pH increased to 5. The second phase of Co-oxide was formatted as the pH was increased above 4. The diffusion degree was evaluated by mapping using scanning electron microscopy (SEM). The influence of different annealing conditions was investigated. The diffusion depth of Co depends on the annealing temperature and time. The results obtained confirm that the deposited Co diffused almost completely into a copper matrix without substantial loss at an annealing temperature of $900^{\circ}C$ for 2 hours.

• Nuclear Engineering and Technology
• /
• v.54 no.2
• /
• pp.644-652
• /
• 2022

During the pyroprocessing operation, various signals can be collected by process monitoring (PM). These signals are utilized to diagnose process states. In this study, feasibility of using PM for nuclear safeguards of electrorefining operation was examined based on the use of machine learning for detecting off-normal operations. The off-normal operation, in this study, is defined as co-deposition of key elements through reduction on cathode. The monitored process signal selected for PM was cathode potential. The necessary data were produced through electrodeposition experiments in a laboratory molten salt system. Model-based cathodic surface area data were also generated and used to support model development. Computer models for classification were developed using a series of recurrent neural network architectures. The concept of transfer learning was also employed by combining pre-training and fine-tuning to minimize data requirement for training. The resulting models were found to classify the normal and the off-normal operation states with a 95% accuracy. With the availability of more process data, the approach is expected to have higher reliability.