• Korean Journal of Materials Research
• /
• v.23 no.11
• /
• pp.643-648
• /
• 2013

Activated carbon (AC) was synthesized from rice husks using the chemical activation method with KOH, NaOH, a combination of (NaOH + $Na_2CO_3$), and a combination of (KOH + $K_2CO_3$) as the chemical activating reagents. The activated carbon with the highest surface area (around $2000m^2/g$) and high porosity, which allows the absorption of a large number of ions, was applied as electrode material in electric double layer capacitors (EDLCs). The AC for EDLC electrodes is required to have a high surface area and an optimal pore size distribution; these are important to attain high specific capacitance of the EDLC electrodes. The electrodes were fabricated by compounding the rice husk activated carbons with super-P and mixed with polyvinylidene difluoride (PVDF) at a weight ratio of 83:10:7. AC electrodes and nickel foams were assembled with potassium hydroxide (KOH) solution as the electrolyte. Electrochemical measurements were carried out with a three electrode cell using 6 M KOH as electrolyte and Hg/HgO as the reference electrode. The specific capacitance strongly depends on the pore structure; the highest specific capacitance was 179 F/g, obtained for the AC with the highest specific surface area. Additionally, different activation times, levels of heating, and chemical reagents were used to compare and determine the optimal parameters for obtaining high surface area of the activated carbon.

• Journal of the Korean Electrochemical Society
• /
• v.6 no.4
• /
• pp.255-260
• /
• 2003

The complex capacitance analysis was performed in order to examine the potential-dependent EDLC characteristics of porous carbon electrodes. The imaginary capacitance profiles $(C_{im}\;vs.\;log\lf)$ were theoretically derived for a cylindrical pore and further extended to multiple pore systems. Two important electrochemical parameters in EDLC can be estimated from the peak-shaped imaginary capacitance plots: total capacitance from the peak area and $\alpha_0$ from the peak position. Using this method, the variation of capacitance and ion conductivity in pores can be traced as a function of electric potential. The electrochemical impedance spectroscopy was recorded on the mesoporous carbon electrode as a function of electric potential and analyzed by complex capacitance method. The capacitance values obtained from the peak area showed a maximum at 0.3V (vs. SCE), which was in accordance with cyclic voltammetry result. The ionic conductivity in pores calculated from the peak position showed a maximum at 0.2 V (vs. SCE), then decreased with an increase in potential. This behavior seems due to the enhanced electrostatic interaction between ion and surface charge that becomes enriched at more positive potentials.

• Proceedings of the KIEE Conference
• /
• 2011.07a
• /
• pp.143-144
• /
• 2011

Due to enhanced demands on quality, security and reliability of the electric power energy system, a microgrid has become a subject of special interest. In this paper, output characteristics of energy storage system (ESS) with an electric double layer capacitor (EDLC) and battery energy storage system (BESS) of a renewable energy based microgrid were analyzed under grid-connected and islanded operation modes. The microgrid which consists of photovoltaic and wind power turbine generators, diesel generator, ESS with an EDLC, BESS and loads was modeled using real time digital simulator. The results present the effective control patterns of the microgrid system.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2003.07b
• /
• pp.1184-1187
• /
• 2003

Electrochemical capacitors are becoming attractive energy storage systems particularly for applications involving high power requirements such as hybrid systems consisting of batteries and electrochemical capacitors for electric vehicle propulsion. A new type electric double layer capacitor (EDLC) was constructed by using carbon nanofibers (CNFs) and DAAQ(1,5-diaminoanthraquinone) electrode. Carbonaceous materials are found in variety forms such as graphite, diamond, carbon fibers etc. While all the carbon nanofibers include impurities such as amorphous carbon, nanoparticles, catalytic metals and incompletely grown carbons. We have eliminated of Ni particles and some carbonaceous particles in nitric acid. Nitric acid treated CNFs could be covered with very thin DAAQ oligomer from the results of CV and TG analyses and SEM images. DAAQ oligomer film exhibited a specific capacity as 45-50 Ah/kg in 4M $H_2SO_4$. We established Process Parameters of the technique for the formation of nano-structured materials. Furthermore, improved the capacitive properties of the nano structured CNFs electrodes using controlled solution chemistry. As a result, CNFs coated by DAAQ composite electrode showed relatively good electrochemical behaviors in acidic electrolyte system with respect to specific capacity and scan rate dependency.

• Proceedings of the KIEE Conference
• /
• 2005.07c
• /
• pp.2022-2024
• /
• 2005

Electrical double-layer capacitor (EDLC) is an electrochemical energy storage device in which electric charges only accumulated by a pure electrostatic attraction force are stored on the electrolyte-electrode interface in a form of double layer and separated by the electrolyte. The composite was prepared by mixing nanosize $TiO_2$ and activated carbon through a means of ultrasonic vibration in ethanol solution for 30 min in various mass ratios of $AC:TiO_2$ to form activated carbone-semiconducting oxide composites. Either 1.0 M $LiClO_4/EC-DEC$ or $Et_4NBF_4$/EC-DEC was used as the electrolyte. It was found that with modification of $TiO_2$, the specific capacitance of activated carbon measured at $1mA/cm^2$ was increased from 40 to 50 F/g. This method is unique in comparison the conventional method because it uses semiconducting TiO2 other than electrochemically active materials such as $RuO_2$. The increase in specific capacitance could be attributed to the decrease in electric polarization, caused by the introduction of $RuO_2$.

• Journal of the Korean Electrochemical Society
• /
• v.8 no.1
• /
• pp.1-5
• /
• 2005

Electric double layer capacitors(EDLCS) based on the charge stored at the interface between a hi팀 surface area carbon electrode and an organic electrolyte solution are widely used as a maintenance-free power source for IC memories and microcomputers. The achievement of the excellent performance of the capacitor requires an electrolyte solution which provides high conductivities over a wide temperature range and good electrochemical stabilities to allow the capacitor to be operated at high voltage. The electrochemical capacitor using a carbon material as electrodes and using an organic electrolyte with $1M-LiPF_6$ in PC-GBL-DEC(volume ratio 1:1:2) has specific capacitance of 64F/g.

• Elastomers and Composites
• /
• v.47 no.4
• /
• pp.292-296
• /
• 2012

An electric double-layer capacitor (ELDC) of activated carbon electrode is prepared using a proton-conducting hydrogel polymer electrolyte, which is composed of poly(vinyl alcohol), silicotungstic acid, $H_3PO_4$, and deionized water. A solid film by evaporating the hydrogel polymer electrolyte is also prepared for comparison. The hydrogel polymer electrolyte also acts as a separator with the thickness of about $80{\mu}m$ and the room-temperature ionic conductivity of $10^{-2}S\;cm^{-1}$. The EDLC containing the symmetric electrodes of activated carbon shows the specific capacitance of $58F\;g^{-1}$ at $100mV\;s^{-1}$ with a good cycle life, implying that the hydrogel polymer electrolyte is very promising for use in EDLCs.

• Proceedings of the KIPE Conference
• /
• 2007.11a
• /
• pp.166-168
• /
• 2007

본 논문에서는 직류 지하철 급전시스템에서 발생하는 회생전력을 활용하기 위한 회생전력 제어용 양방향 DC-DC 컨버터 및 EDLC(Electric Double Layer Capacitor)를 이용한 양방향 DC-DC 컨버터의 효율적 충 방전 제어 알고리즘을 제안하였다. 가선전압의 변화에 따른 제어 방법을 제안함으로서 회생전력의 발생으로 인한 가선전압의 상승을 안정적으로 제어할 수 있도록 하였고, 실측된 가선전압과 동일한 직류 급전시스템의 모의가 가능한 가선전압 모의장치를 사용하여 철도차량용 양방향 DC-DC 컨버터의 효율성을 검증하였다.

• Proceedings of the KIEE Conference
• /
• 2008.07a
• /
• pp.994-995
• /
• 2008

It is possible to suppress voltage drops, power loading fluctuations and regeneration power lapses for DC railway systems by applying an energy storage system. A electric double layer capacitor (EDLC) of the rapid charge/discharge type has been developed and used in wide ranges. It has a long life, high efficiency and maintenance free/low pollution features as a new energy storage element. In this paper, an efficient charge and discharge control method of a bidirectional DC-DC converter using the supercapacitor is proposed.

• Proceedings of the KIPE Conference
• /
• 2008.06a
• /
• pp.97-99
• /
• 2008

It is possible to suppress voltage drops, power loading fluctuations and regeneration power lapses for DC railway systems by applying an energy storage system. Recently the electric double layer capacitor (EDLC) of the rapid charge/discharge type has been developed and used in wide ranges. The on board energy storage system with supercapacitor for railway vehicles presented in this paper seems to be a reliable technical solution with an enormous energy saving potential. In this paper, an efficient charge and discharge control method of a bidirectional DC-DC converter using the supercapacitor is proposed.