• 한국분말야금학회:학술대회논문집
• /
• 한국분말야금학회 2006년도 Extended Abstracts of 2006 POWDER METALLURGY World Congress Part2
• /
• pp.1241-1242
• /
• 2006

Electromagnetic properties of $CeO_2$ doped and undoped YBaCuO superconductors were evaluated to investigate the effect of pinning center on the magnetization and magnetic shielding. The variation $\DeltaM$ with doping was maximum for 3% doping and decrease with further doping. The magnetic shielding was evaluated by measuring the induced voltage in secondary coil and the voltage initially set to 0.5V, decreased to 0.17V and 0.28V respectively for the undoped and 3% $CeO_2$ doped sample. The much less change in the induced voltage for the 3% doped sample is attributed to the increased flux shielding by shielding vortex current. The $CeO_2$ was converted to fine $BaCeO_3$ particles which were trapped in YBaCuO superconductor during the reaction sintering. The trapped fine particles, $BaCeO_3$ may be acted as a flux pinning center.

• 한국전기전자재료학회논문지
• /
• 제14권2호
• /
• pp.152-157
• /
• 2001

For the fabrication of YBa$_2$Cu$_3$O$_{x}$ thick film using diffusion process between $Y_3$BaCuO$_{5}$ and BaO+CuO, each material was selected as substrate and doping material. In this paper, we investigated the characteristic of YBa$_2$Cu$_3$O$_{x}$ thick film due to both addition of CeO$_2$into substrate and initial particle size of doping material. Through X-ray diffraction patterns and SEM photographs, the variation of composition and thickness of the formed phase was observed. It was from the experiment obtained that the addition of CeO$_2$into $Y_2$BaCuO$_{5}$ substrate and the initial particle size of doping material play important part in promoting the reaction between substrate and doping material.aterial.

• Bulletin of the Korean Chemical Society
• /
• 제26권5호
• /
• pp.755-762
• /
• 2005

A series of catalysts, NiO/$CeO_2-ZrO_2/WO_3$, for ethylene dimerization was prepared by the precipitation and impregnation methods. For NiO/$CeO_2-ZrO_2/WO_3$ sample, no diffraction line of nickel oxide was observed up to 40 wt%, indicating good dispersion of nickel oxide on the surface of catalyst. The hexagonal and monoclinic phases of $WO_3$ up to the calcination temperature of 500 ${^{\circ}C}$ were observed, whereas the hexagonal phase of WO3 completely was transformed into monoclinic phase of $WO_3$ at 600 ${^{\circ}C}$ and above. The role of $CeO_2$ in the catalysts was to form a thermally stable solid solution with zirconia and consequently to give high surface area and acidity. The catalytic activities for ethylene dimerization were correlated with the acidity of catalysts measured by the ammonia chemisorption method. 25-NiO/5-$CeO_2-ZrO_2/15-WO_3$ containing 25 wt% NiO, 15 wt% $WO_3$ and 5 mol% $CeO_2$, and calcined at 400 ${^{\circ}C}$ exhibited a maximum catalytic activity due to the effects of $WO_3$ modifying and $CeO_2$ doping.

• 한국초전도ㆍ저온공학회논문지
• /
• 제10권1호
• /
• pp.1-5
• /
• 2008

The effect of $BaCeO_3$ doping on the critical current density of YBCO film by TFA-MOD method was studied. $BaCeO_3$ doping was made by two method; one is direct addition of $BaCeO_3$ nano-sized powder prepared by citrate process followed by grinding with planetary ball mill for 10 hours. Another is addition of Ba-Ce precursor solution prepared with Ba-acetate and Ce acetate dissolved in TFA to the YBCO-TFA precursor solution. The film was made by standard dip coating and heat treatment process with conversion temperature of $790^{\circ}C$ in 1000 ppm oxygen containing moisturized Ar gas atmosphere. The direct addition of $BaCeO_3$ powder resulted in YBCO film with good epitaxial growth and no evidence of second phase formation. The addition through precursor solution resulted in the increase of critical current density upto 30 at% doping and uniform dispersion of $BaCeO_3$ fine inclusion was confirmed by SEM-EDX.

• 한국분말재료학회지
• /
• 제26권1호
• /
• pp.49-57
• /
• 2019

Layered $LiNi_{0.83}Co_{0.11}Mn_{0.06}O_2$ cathode materials single- and dual-doped by the rare-earth elements Ce and Nd are successfully fabricated by using a coprecipitation-assisted solid-phase method. For comparison purposes, non-doping pristine $LiNi_{0.83}Co_{0.11}Mn_{0.06}O_2$ cathode material is also prepared using the same method. The crystal structure, morphology, and electrochemical performances are characterized using X-ray diffraction (XRD), scanning electron microscopy (SEM), energy dispersive spectrometer (EDS) mapping, and electrochemical techniques. The XRD data demonstrates that all prepared samples maintain a typical ${\alpha}-NaFeO_2$-layered structure with the R-3m space group, and that the doped samples with Ce and/or Nd have lower cation mixing than that of pristine samples without doping. The results of SEM and EDS show that doped elements are uniformly distributed in all samples. The electrochemical performances of all doped samples are better than those of pristine samples without doping. In addition, the Ce/Nd dual-doped cathode material shows the best cycling performance and the least capacity loss. At a 10 C-rate, the electrodes of Ce/Nd dual-doped cathode material exhibit good capacity retention of 72.7, 58.5, and 45.2% after 100, 200, and 300 cycles, respectively, compared to those of pristine samples without doping (24.4, 11.1, and 8.0%).

• Progress in Superconductivity
• /
• 제4권1호
• /
• pp.10-13
• /
• 2002

We report the effect of Ca doping in $YBa_2Cu_3O_{7-\delta}$ (YBCO) thin films grown on the Rolling- Assisted, Biaxially Textured Substrates (RABiTS) with the architecture of $CeO_2/YSZ/CeO_2/Ni$. Critical currents of bilayer and trilayer structures of $YBCO/Y_{0.7}Ca_{0.3}Ba_2Cu_3O_{7-\delta}$/(YCaBCO) as well as undoped YBCO for comparison have been measured in a wide range of temperatures and fields. For $6-8^{\circ}$ grain boundaries, 30% Ca-doping in bilayer structure enhances $J_c$ as high as 35%. The enhancement is larger at low temperatures and at magnetic fields. On the other hand, 30% Ca-doping in trilayer structure reduces $J_c$ as high as 60%. Combined with slightly lower $T_c$, this indicates that Ca is overdoped in this structure and degrades GBs.

• Progress in Superconductivity
• /
• 제11권1호
• /
• pp.67-71
• /
• 2009

The effect of Cu substitution on the structural and superconducting properties of the $(Ru_{1-x}Cu_x)Sr_2(Eu_{1.34{\cdot}}Ce_{0.66})Cu_2O_z$ system with x = 0, 0.25 and 0.5 prepared under ambient pressure have been investigated. The X-ray diffraction patterns indicated that the Ru ions are replaced by the Cu ions. It is found that the Cu substitution for Ru significantly reduces the ferromagnetic component of field-cooled magnetic susceptibility, but results in a small change in diamagnetic onset transition temperature of zero-field-cooled magnetic susceptibility. In contrast to the Ru $Sr_2(Eu_{1.34{\cdot}}Ce_{0.66})Cu_2O_z$, bulk Meissner effect is observed in the field-cooled magnetization measurements of the Cu doped samples. The experimental results are discussed in connection with the spontaneous vortex phase interpretation.

• 한국세라믹학회지
• /
• 제52권6호
• /
• pp.521-526
• /
• 2015

$Ce_{0.8}Gd_{0.2}O_{1.9}$(GDC20) powder was prepared from a mixture of submicron-sized $CeO_2$ powder and Gd precipitates using ammonium carbonate $((NH_4)_2CO_3)$ as a precipitant. The mixture was calcined at $700^{\circ}C$ for 4 h followed by ball-milling that resulted in the GDC powder with an average particle size of $0.46{\mu}m$. The powder had a very uniform particle size distribution with particle sizes ranging from $0.3{\mu}m$ to $1{\mu}m$. Sintering of undoped GDC samples did not show a relative density of 99.2% until the temperature was increased to $1500^{\circ}C$, whereas GDC samples doped with 5 mol% CoO exhibited a significant densification at lower temperature reaching a relative density of 97.6% at $1100^{\circ}C$ and of 98.8% at $1200^{\circ}C$.

• Steel and Composite Structures
• /
• 제24권1호
• /
• pp.15-22
• /
• 2017

A green biosynthesis method is described for the preparation of Polyaniline (PANI)-cerium dioxide ($CeO_2$) nanocomposites in different media via in-situ oxidative polymerization procedure. The effect of various media including use of HCl, Lemon Juice, Beverage, White Vinegar, Verjuice and Apple vinegar extracts on the particles size, morphology as well as the conductivity of $PANI-CeO_2$ nanocomposites was investigated. The electron-withdrawing feature of $CeO_2$ increases doping level of PANI and enhances electron delocalization. These cause a significantly blue shift of C = C stretching band of quinoid from $1570cm^{-1}$ to $1585cm^{-1}$. The optical properties of the pure material and polymeric nanocomposites as well as their interfacial interaction in nanocomposite structures analyzed by UV-visible spectroscopy. The DC electrical conductivity (${\sigma}$) of as-prepared HCl doped PANI and a $PANI-CeO_2$ nanocomposite measured by a four-probe method at room temperature was studied.

• 반도체디스플레이기술학회지
• /
• 제16권4호
• /
• pp.86-90
• /
• 2017

$Tb^{3+}$ or $Eu^{3+}$ or $Ce^{3+}$-doped $CaYAlO_4$ phosphor were synthesized by solid-state method. $CaYAlO_4:Tb^{3+}$ is shown that the $Tb^{3+}$-doping concentration has a significant effect on the $^5D_4/^5D_3{\rightarrow}7F_J$ (J=6,...,0) emission intensity of $Tb^{3+}$. The $CaYAlO_4:Tb^{3+}$ phosphors show tunable photoluminescence from blue to yellow with the change of doping concentration of $Tb^{3+}$ ions. The $CaYAlO_4:Eu^{3+}$ phosphors exhibit a red-orange emission of $Eu^{3+}$ corresponding to $^5D_0$, $_{1,2}{\rightarrow}^7F_J$ (J=4,...,0) transitions. The $CaYAlO_4:Ce^{3+}$ phosphors show a blue emission due to $Ce^{3+}$ ions transitions from the 5d excited state to the $^2F_{5/2}$ and $^2F_{7/2}$ ground states. The decay time of $CaYAlO_4:Tb^{3+}$ phosphors decrease from 1.33 ms to 0.97 ms as $Tb^{3+}$ concentration increases from 0.1 mol% to 7 mol%. The decay time of $CaYAlO_4:Eu^{3+}$ phosphors increase from 0.94 ms to 1.17 ms as $Eu^{3+}$ concentration increases from 1 mol% to 9 mol%.