• Proceedings of the Korean Society of Precision Engineering Conference
• /
• 2003.06a
• /
• pp.581-584
• /
• 2003

The austenitic STS 304 stainless steel was turned to clarify the effects of tool geometry on the tool wear. The wear of TiN-TiCN-TiC-TiAlN coated tungsten carbide tool was the smallest, exhibiting larger wear in the order of Si-Al-O-N ceramic, TiN coated tungsten carbide, TiN-TiCN-TiN coated tungsten carbide, TiC-TiN cermet and M20 tungsten carbide tools at the same cutting conditions. The S-type tool of M20 with large approach angle showed the longest tool life of all tools used in this tests due to preventing the groove wear of the side cutting edge. The wear of the S-type tool with the rake angle of 15$^{\circ}$became smaller than with that of -5$^{\circ}$, but the tool with the nose radius of 0.8mm did not perform much better with increasing the rake angle.

• Transactions of the Korean Society of Machine Tool Engineers
• /
• v.12 no.5
• /
• pp.8-14
• /
• 2003

The characteristics of grinding and wear behavior of diamond wheel for grinding ceramic materials was investigated in this study. In case of $Si_3N_4$, the wear of wheel was large, the finding force was relatively stable and the fluctuation of surface roughness n small. On the other hand in case of $Al_2O_3$ and $ZrO_2$, the wear of wheel and surface roughness were decreasing, the grinding force was increasing. During grinding with vitrified bond wheel, $Si_3N_4$ shows renewal of cutting edge while $Al_2O_3$ and $ZrO_2$ show glazing phenomenon of cutting grains. We have found that it possible to observe the behavior of grinding wheel by grinding ratio, grinding resistance, surface roughness and cutting edge ratio. Through the grinding experiments, it was found that grinding life of diamond wheel is 20 times for $Si_3N_4$, and 40 times fir $Al_2O_3$ and $ZrO_2$.

• Design & Manufacturing
• /
• v.16 no.3
• /
• pp.28-33
• /
• 2022

The recent increasing application rate of advanced high-strength steel(AHSS) for automotive parts makes it difficult to ensure the durability of forming tools. Significant load and friction generated during the piercing process of AHSS increase the wear rate and the damage degree to dies. These harsh process conditions also yield product failures, such as dimensional inconsistency of pierced holes and insufficient quality of hole's sheared edge. This study analyzed the effect of punch wear on the sheared surface of pierced parts and the forming load during the piercing process. Wear-shaped punches showed approximately 20% higher piercing load than normal-shaped punches, and the rollover ratio of the sheared surface also increased. It is considered that the dull edge of wear-shaped punches does not penetrate directly into the material but shears after tensioning it in a piercing direction. In addition, wear-shaped punches experienced compressive load even after completing the piercing process during the down-stroke and tensile load during the up-stroke. This load variation is related to the smaller diameter piercing holes produced by wear-shaped punches compared to normal-shaped punches. Thus, we demonstrated the predictability of the wear level of dies through a comparative analysis of the piercing load pattern.

• Tribology and Lubricants
• /
• v.6 no.1
• /
• pp.116-125
• /
• 1990

An experimental programme was established to determine the wear behaviour of TiN coatings of thickness 1 $\mu$m and 3 $\mu$m. by PECVD with the variation of applied load, sliding velocity and sliding distance. It was shown that oxidation of transferred metal as sliding speed increased formed oxide film so that it contributed in decreasing the wear rate. With the roller-on-disc tribometer employed, the wear rate of the roller specimen was decreased with the increase in sliding distance due to the reduction in effective contact pressure. Finally, the severe cracks concentrated at the trailing edge of contact surface were explained in terms of high tensile stress prevailing at the trailing edge of the contact and were identified as a dominant wear mechanism as well as the strong local welding between coating layer and the counter surface, leading to the debonding of the coating layer.

• Journal of the Korean Society of Manufacturing Process Engineers
• /
• v.14 no.5
• /
• pp.22-27
• /
• 2015

Processing of low toughness graphite material requires high-speed machine tools and DLC coating. In this study, results of investigation of the tool wear and machining properties of the DLC coating according to the thickness, and the machining time of the tool used for the machining of graphite electrodes, were as follows. 1. DLC coating thickness shows a larger wear amount of the tool center in accordance with thickness; the wear amount of the tool increases in proportion to the machining time. 2. The difference between the amount of wear depending on the processing time shows edge portions larger than the tool wear amount in the center. This amount of wear of the tool edge is formed since the rotating torque is in contact with the graphite material surface significantly more than the central portion. 3. The thicker the DLC coating, the more the coating tool eliminated of the coating area by the interface between the cemented carbide tool being coated with an increased friction of the graphite material and the DLC coating area.

• Transactions of the Korean Society of Mechanical Engineers
• /
• v.19 no.3
• /
• pp.705-712
• /
• 1995

The wear characteristics and wear mechanisms in TiN coating deposited on high speed steel and alloy tool steel by ion plating were investigated. Pin on V-block wear tester was used for a wear test method. The specimen was composed of three kinds of high speed steel and alloy tool steel which had different hardness by changing the heat treating condition. Three kinds of coating thickness were also applied to each specimen. Microscopic observation of worn surfaces was made by SEM. The scratch test of coating surface by the ion plating showed that critical load to break the coating interface was greater than 50N. The critical load increased with both substrate hardness and coating thickness. The wear resistance of TiN coated high speed steel became 10 times greater than that of non-coated ones. SEM observation showed that leading edge of contact was compressive and trailing edge was under maximum tensile stress and then surface cracking broke out perpendicular to sliding direction.

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.31 no.11
• /
• pp.1083-1092
• /
• 2007

The objective of the present paper is to evaluate the effect of the evolution of contact surface profile caused by fretting wear on fatigue life of press-fitted shaft by means of an analytical method based on experimental data. A finite element analysis was performed to analyze the stress states of press-fitted shaft, considering the worn contact profiles of shaft. The fatigue lives of the press-fitted shaft reflecting the evolution of contact stress induced by fretting wear were evaluated by stress-life approach using fatigue notch factor. It is found that the stress concentration of contact edge in press-fitted shaft decreases rapidly at the initial stage of total fatigue life, and its location shifts from the contact edge to the inside with increasing number of fatigue cycles. Thus the change of crack nucleation position in press-fitted shaft is mainly caused by the stress change of contact edge due to the evolution of contact surface profile by fretting wear. Furthermore, the estimated fatigue lives by stress-life approach at the end of running-in period of the fretting wear process corresponded well to the experimental results. It is thus suggested that the effect of fretting wear on fatigue life in press fits is strongly related to the evolution of surface profile at the initial stage of total fatigue life.

• Journal of Power System Engineering
• /
• v.20 no.4
• /
• pp.5-11
• /
• 2016

This study analyzed the damage to a slitting knife after cutting steel sheets. Damages to the structure were observed and wear tests were conducted. In addition, the degradation on the damaged and undamaged parts was compared with a micro Vickers hardness test. Weibull statistical analysis was carried out in order to evaluate the reliability of the micro Vickers hardness measured data. Spalling of the edge portion occurred by degradation during use over a long period. Rough parts in the specimens were caused by damage because the slitting knife was used for 1 year. The friction coefficient and wear loss at the damaged parts of the knife edge were slightly larger from shock due to repetitive cutting operation. The micro Vickers hardness followed a two-parameter Weibull probability distribution.

• Journal of the Korean Society of Manufacturing Process Engineers
• /
• v.20 no.9
• /
• pp.48-56
• /
• 2021

Tungsten carbide (WC) circular saws have been widely used to cut plywood. Recently, expensive polycrystalline diamond (PCD) were adopted to extend the tool life of circular saws. This study developed a PCD-WC combination circular saw and compared its performance with that of existing WC and PCD saws. Flank wear of WC saw blades and edge chipping of rectangular PCD was observed during the experiments. The PCD-WC saw replaced half of the chamfered teeth with PCD and applied tough WC for all rectangular teeth. In the experiments, edge chipping was not observed in rectangular WC teeth and the flank wear of chamfered teeth was decreased compared with that of conventional circular saws.

• Transactions of the Korean Society of Machine Tool Engineers
• /
• v.11 no.4
• /
• pp.75-81
• /
• 2002

In this study, experiments were carried out to investigate the characteristics of grinding and wear process of diamond wheel during grinding ceramic materials. Normal component of grinding resistance was decreasing while increase of spindle speed. The resistance of vitrified bond wheel was less then that of resinoid bond wheel because of imbedded large holes on the surface of cutting edge. Surface roughness was decreasing while increase of spindle speed. The surface roughness using vitrified bond wheel was less than that of resinoid bond wheel because of small elastic deformation. After continuous finding of ceramics, cutting edge ratio of resinoid bond wheel decreased. For the case of vitrified bond wheel, cutting edge ratio did not change.