• Proceedings of the KWS Conference
• /
• 2006.05a
• /
• pp.33-35
• /
• 2006

The interactions between Cu/Sn-Ag-(Cu) and Sn-Ag-(Cu)/Ni interfacial reactions were studied during isothermal aging at $150^{\circ}C$ for up to 1000h using Cu(ENIG)/Sn-3.5Ag-(0.7Cu)/Cu(ENIG) sandwich solder joints. A typical scallop-type Cu-Sn intermetallic compound (IMC) layer formed at the upper Sn-Ag/Cu interface after reflowing, whereas a $(Cu,Ni)_6Sn_5$ IMC layer was observed at the Sn-Ag/ENIG interface. The Cu in the $(Cu,Ni)_6Sn_5$ IMC layer formed on the Ni side was sourced from the dissolution of the opposite Cu metal pad or Cu-Sn IMC layer. When the dissolved Cu arrived at the interface of the Ni pad, the $(Cu,Ni)_6Sn_5$ IMC layer formed on the Ni interface, preventing the Ni pad from reacting with the solder. Although a long isothermal aging treatment was performed at $150^{\circ}C$, no Ni was detected in the Cu-Sn IMC layer formed on the Cu side. Compared to the single Sn-Ag/ENIG solder joint, the formation of the $(Cu,Ni)_6Sn_5$ IMC layer of the Cu/sn-Ag/ENIG sandwich joint effectively retarded the Ni consumption from the electroless Ni-P layer.

• Journal of the Microelectronics and Packaging Society
• /
• v.27 no.3
• /
• pp.29-34
• /
• 2020

The behavior of brittle fracture of electroless nickel immersion gold (ENIG) /Sn-3.0wt.%Ag-0.5wt.%Cu (SAC305) solder joints was evaluated. The pH of the electroless nickel plating solution for ENIG surface treatment was changed from 4.0 to 5.5. As the pH of the Ni plating solution increased, pin hole in the Ni-P layer increased. The thickness of the interfacial intermetallic compound (IMC) of the solder joint increased with pH of Ni plating solution. The high speed shear strength of the SAC305 solder joint on ENIG surface finish decreased with the pH of the Ni plating solution. In addition, the brittle fracture rate of the solder joint was the highest when the pH of the Ni plating solution was 5.

• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2009.10a
• /
• pp.179-180
• /
• 2009

본 연구에서는 ENIG, ENEPIG 의 Pad 표면처리가 고속전단시험에 미치는 영향에 대해 연구하고자 하였다. Pad의 표면처리를 ENIG와 ENEPIG로 하여 고속전단시험을 수행하여 그에 따른 Shear force와 Shear energy를 측정하였다. 고속전단시험결과 ENEPIG 표면처리 시편이 ENIG의 표면처리시편보다 shear force와 shear energy의 값이 높게 나타났다.

• The Journal of Korean Association of Computer Education
• /
• v.3 no.1
• /
• pp.169-176
• /
• 2000

This paper presents ENIG Agent can gather distributed educational newspaper information in the web as well as provide teachers and student those information for the NIE. ENIG Agent gleans newspaper headline of appropriate educational news portal site for real-time provision of those information. The optimized extraction of headline is performed through the pre-process of educational news site, information noise filtering, pattern matching. The educational newspaper headline information that is gotten through previous process will be shown to students by web-browser. To increase the usage of those information, intelligent education methods and visualized classification techniques are used. By experiment, the performance of this ENIG Agent was evaluated.

• Korean Journal of Materials Research
• /
• v.24 no.3
• /
• pp.166-173
• /
• 2014

The effects of printed circuit board electroless nickel immersion gold (ENIG) and organic solderability preservative (OSP) surface finishes on the electromigration reliability and shear strength of Sn-3.5Ag Pb-free solder bump were systematically investigated. In-situ annealing tests were performed in a scanning electron microscope chamber at 130, 150, and $170^{\circ}C$ in order to investigate the growth kinetics of intermetallic compound (IMC). Electromigration lifetime and failure modes were investigated at $150^{\circ}C$ and $1.5{\times}10^5A/cm^2$, while ball shear tests and failure mode analysis were conducted under the high-speed conditions from 10 mm/s to 3000 mm/s. The activation energy of ENIG and OSP surface finishes during annealing were evaluated as 0.84 eV and 0.94 eV, respectively. The solder bumps with ENIG surface finish showed longer electromigration lifetime than OSP surface finish. Shear strengths between ENIG and OSP were similar, and the shear energies decreased with increasing shear speed. Failure analysis showed that electrical and mechanical reliabilities were very closely related to the interfacial IMC stabilities.

• Journal of the Microelectronics and Packaging Society
• /
• v.16 no.1
• /
• pp.7-11
• /
• 2009

In this study, solder joints were made with Sn-3.5Ag (wt%) solder ball. Electroless nickel / immersion gold (ENIG) printed circuit board (PCB) substrates were employed in this work. The mechanical and electrical properties were measured as a function of the number of reflow. Die shear strength was measured with increasing reflow number. Until the forth or fifth reflow, shear force increased and after the fifth reflow the shear force of die decreased. The electrical resistivity of solder joint linearly increased with increasing reflow number.

• Journal of the Microelectronics and Packaging Society
• /
• v.28 no.2
• /
• pp.95-103
• /
• 2021

Sn-58Bi-xRu composite solders were prepared by adding Ru nanoparticles to Sn-58Bi, a typical low-temperature solder, and the interfacial reaction and solder joint reliability were analyzed by reacting with Cu/OSP and ENIG surface treated PCB boards. The Cu₆Sn₅ IMC formed by the reaction with Cu/OSP had little change in thickness depending on the Ru content, and ductile fracture occurred inside the solder during the high-speed shear test without any significant change even after 100 hr aging. In reaction with ENIG, the Ni₃Sn₄ IMC thickness tended to decrease as the Ru content increased, and ENIG-specific brittle fracture was found in some specimens. Since Ru element is not found near the interface, it is judged not to be significantly involved in the interfacial reaction, and it is analyzed that it mainly exists together with the Bi phase.

• Korean Journal of Metals and Materials
• /
• v.46 no.2
• /
• pp.80-87
• /
• 2008

Many researches related to the reliability of Pb-free solder joints with PCB (printed circuit board) surface finish under thermal or vibration stresses are in progress, because the electronics is operating in hash environment. Therefore, it is necessary to assess Pb-free solder joints life with PCB surface finish under thermal and mechanical stresses. We have investigated 4-points bending fatigue lifetime of Pb-free solder joints with OSP (organic solderability preservative) and ENIG (electroless nickel and immersion gold) surface finish. To predict the bending fatigue life of Sn-3.0Ag-0.5Cu solder joints, we use the test coupons mounted 192 BGA (ball grid array) package to be added the thermal stress by conducting thermal shock test, 500, 1,000, 1,500 and 2,000 cycles, respectively. An 4-point bending test is performed in force controlling mode. It is considered that as a failure when the resistance of daisy-chain circuit of test coupons reaches more than $1,000{\Omega}$. Finally, we obtained the solder joints fatigue life with OSP and ENIG surface finish using by Weibull probability distribution.

• Proceedings of the KWS Conference
• /
• 2006.05a
• /
• pp.230-232
• /
• 2006

Eutectic Au-20Sn solder has been widely used for optoelectronic packages because of fluxless soldering process and thus are particularly valuable for many applications such as biomedical, photonic, and MEMS devices that can not use any flux. Also when good joint strength, superior resistance to corrosion, whisker-free, and good thermal conductivity are demanded, eutectic Au-20Sn solder can be satisfied with above-mentions best. In this study, we tried to know the interfacial reactions between Au-20Sn solder and Cu substrate with or without ENIG plating layer In the results, Au-Cu-Sn ternary phases were formed at the Au-20Sn/Cu substrate, and Au-Ni-Sn, Au-Ni-Cu-Sn phases were formed at the Au-20Sn/ENIG substrate.

• Journal of the Microelectronics and Packaging Society
• /
• v.14 no.4
• /
• pp.27-36
• /
• 2007

In this study, we investigated the interfacial reactions between various Sn-Ag-Cu(SAC) solder alloys and ENIG(Electroless Ni Immersion Gold) and Cu-OSP(Organic Solderability Preservative) pad finish. In the case of the interfacial reaction between Sb added SAC solder and ENlf thinner P-rich Ni layer was formed at the interface. In the case of the interfacial reaction between Ni added SAC solder and Cu-OSP, the uniform $Cu_6Sn_5$, intermetallic compounds(IMCs) were formed and $Cu_6Sn_5$ grain did not grow after multiple reflows. Thinner $Cu_3Sn$ IMCs were farmed at the interface between $Cu_6Sn_5$ and Cu-OSP after $150^{\circ}C$ thermal aging.