The present article is concerned with the application of an electrochemical noise (EN) monitoring technique to analyze the initiation and propagation of Pb-assisted stress corrosion cracking (SCC) of an Alloy 600 material in a simulated environment of a steam generator (SG) sludge pile at high temperatures. A typical increase of electrochemical current noise (ECN) and electrochemical potential noise (EPN) was frequently recorded from the EN measurement in a caustic solution with such impurities as PbO and CuO, indicating that there are localized corrosion events occurring. With the aid of microscopic and spectral analyses, the EN data involving information on such stochastic processes as uniform corrosion and the initiation and propagation of SCC, were analyzed based on a stochastic theory.

• Corrosion Science and Technology
• /
• v.8 no.5
• /
• pp.203-207
• /
• 2009

Electrochemical methods have been widely used to study the performances and mechanisms for the degradation of organic and inorganic coatings. In this study, EN(Electrochemical noise) measurement was applied to the protective properties and review the parameters analyzed noise signals in the time and in the frequency domain for epoxy resin based coated steels during exposure to hot sea water($40^{\circ}C$) and salt spray for 200 days. It was also found that $R_n$(Noise resistance), $R_{sn}$($f_{min}$)(Spectral noise resistance) and 2H(Hurst exponent) represented the performance of epoxy coated steels. $R_n$ can be determined as the ratio of the standard deviations of potential and current noise signals and is decreased to exposure time. Data qualities can be easily checked by PSD(Power Spectral Density) plot and $V_{psd}$, $I_{psd}$ and $R_{sn}$($f_{min}$) is useful to research the protective performances and mechanisms of coated steels. Hurst exponent represents the degradation of coated steels. But, it is difficult to directly apply the protective criterion to the evaluation of epoxy coated steels used the shipbuilding processes.

• Corrosion Science and Technology
• /
• v.12 no.2
• /
• pp.93-101
• /
• 2013

The object of this work is to establish an electrochemical noise(EN) measurement technique combined with a direct current potential drop(DCPD) method for monitoring of localized corrosion cracking of nickel-based alloy, and to analyze its mechanism. The electrochemical current and potential noises were measured under various conditions of applied stress to a compact tension specimen in a simulated primary water chemistry of a pressurized water reactor. The amplitude and frequency of the EN signals were evaluated in both time and frequency domains based on a shot noise theory, and then quantitatively analyzed using statistical Weibull distribution function. From the spectral analysis, the effect of the current application in DCPD was found to be effectively excluded from the EN signals generated from the localized corrosion cracking. With the aid of a microstructural analysis, the relationship between EN signals and the localized corrosion cracking mechanism was investigated by comparing the shape parameter of Weibull distribution of a mean time-to-failure.

• Corrosion Science and Technology
• /
• v.16 no.4
• /
• pp.194-200
• /
• 2017

Stress-corrosion cracking (SCC) of alloy 600 and alloy 800 in 0.5 mol/L thiosulfate solution during constant strain was investigated using electrochemical noise (EN) combined with 3-D microscope techniques. The in-situ morphology observation and EN results indicate that the SCC process could be divided into three stages: (1) passive film stabilization and growth, (2) crack initiation, (3) and crack growth. Power Spectral Density (PSD) and the probability distribution obtained from EN were used as the "fingerprint" to distinguish the different processes. During passive film stabilization and growth, the current noise signals resembled "white noise": when the crack initiated, many transient peaks could be seen in the current noise and the wavelet energy at low frequency as well as the noise resistance decreased. After crack propagation, the noise amplitudes increased, particularly the white noises at low and high frequencies ($W_L$ and $W_H$) in the PSDs. Finally, the detection of metal structure corrosion in a simulated sea splash zone and pipeline corrosion in the atmosphere are established.

• KEPCO Journal on Electric Power and Energy
• /
• v.2 no.4
• /
• pp.615-618
• /
• 2016

Electrochemical noise(EN) has been used to analyze the deterioration of coating films of offshore wind substructures. In this study, prototype sensors using EN have been developed to detect the corrosion rate. To verify the reliability of sensors, experiments were conducted both in the laboratory and offshore using probe and standard samples. New analysis and data processing techniques show that the sensor can provide useful information about the corrosion rate.

• Journal of Electrochemical Science and Technology
• /
• v.8 no.2
• /
• pp.115-123
• /
• 2017

Electrochemical noise signals in many cases exhibit a DC drift that should be removed prior to further data analysis. Polynomial fitting and moving average removal method have been used to remove trends of electrochemical noise (EN) in time domain. The corrosion inhibition of synthesized schiff base N,N'-bis(3,5-dihydroxyacetophenone)-2,2-dimethylpropandiimine on API-5L-X70 steel in hydrochloric acid solutions were used to study the effects of drifts removal methods on noise resistance calculation. Also, electrochemical impedance spectroscopy (EIS) was used to study the corrosion inhibition property of the inhibitor. The results showed that for the calculation of $R_n$, both methods were effective in trend removal and the polynomial with m=4 and MAR with p=40 were in agreement.