• 한국생산제조학회지
• /
• 제9권1호
• /
• pp.38-44
• /
• 2000

The background of this study lies in he investigation of the formation mechanism of ductile mode(nkanometer-size) chips of brittle materials such as fine ceramics glass and silicon. As the first step to achieve this purpose this paper intends to observe the micro-deformation behavior of these materials in sub${\mu}{\textrm}{m}$ depth indentation tests using a diamond indentor. In this study it was developed Ultra-Micro Indentation. Device using the PZT actuator. Experimentally by using the Ultra-Micro Indentation device the micro fracture behavior of the silicon wafer was investigated. It was possible that ductile-brittle transition point in ultimate surface of brittle material can be detected by adding an acoustic emission sensor system to the Ultra-Micro Indentation appartus.

• 대한기계학회논문집A
• /
• 제23권11호
• /
• pp.2078-2086
• /
• 1999

Fracture behaviors of an interface crack in a ductile layer sandwiched by rigid substrates are analyzed by finite element method. Several fracture mechanisms and the corresponding criteria are examined. And the crack growth behavior and fracture toughness are predicted. As the results, various crack growth procedures such as the crack jump to the other interface on the opposite side, the creation of a new crack far from the initial crack front, and the asymmetric relation of fracture toughness vs. mode mixity ($J_c$-$\Phi$) can be successfully explained.

• 한국생산제조학회지
• /
• 제21권1호
• /
• pp.85-89
• /
• 2012

Conventional grinding of BK7 glass will normally result in brittle fracture at the surface, generating severe sub-surface damage and poor surface finish. The precision grinding of BK7 glass in parallel grinding modes has been investigated. Grinding process, maximum chip thickness, ductile/brittle regime, surface roughness and sub-surface damage have been addressed. Special attention has been given to the condition for generating a ductile mode response on the ground surface. Experiments reveal that the level of surface roughness and depth of sub-surface damage vary differently for different condition. This study gives an indication of the strategy to follow to achieve high quality ground surfaces on brittle materials.

• 한국구조물진단유지관리공학회 논문집
• /
• 제14권6호
• /
• pp.142-152
• /
• 2010

본 연구는 표준실험체인 전단보강근이 없는 철근콘크리트 보(SSS)와 전단보강근이 있는 철근콘크리트 보(BSS), 성능개선실험체로는 전단보강근이 없는 철근콘크리트 보에 고로슬래그미분말을 혼입한 고인성섬유 복합모르타르를 타설한 실험체(SHF시리즈, SHFSC시리즈)로 총 11개의 실험체를 축소 제작하여 실험을 수행하였다. 실험을 통하여 얻어진 결과를 비교 분석하여 하중-변위, 파괴형태, 최대내력, 전단응력 등을 규명함으로써 구조성능의 개선정도를 평가하였다. 고로슬래그미분말을 혼입한 고인성섬유 복합모르타르를 이용한 철근콘크리트 보 실험체(SHF시리즈, SHFSC시리즈)의 경우 전단보강근이 없는 표준실험체(SSS)보다 전단응력은 각각 26%, 28%, 연성능력은 각각 5.27, 5.75배 증가하는 결과를 나타내었다. 또한, 충분한 연성적인 거동과 안정적인 휨인장 파괴를 나타내었다.

• 한국해양공학회지
• /
• 제31권4호
• /
• pp.288-298
• /
• 2017

A study of the damage evolution laws for ductile materials was carried out to predict the ductile fracture behavior of a marine structural steel (EH36). We conducted proportional and non-proportional stress tests in the experiments. The existing 3-D fracture strain surface was newly calibrated using two fracture parameters: the average stress triaxiality and average normalized load angle taken from the proportional tests. Linear and non-linear damage evolution models were taken into account in this study. A damage exponent of 3.0 for the non-linear damage model was determined based on a simple optimization technique, for which proportional and non-proportional stress tests were simultaneously used. We verified the validity of the three fracture models: the newly calibrated fracture strain model, linear damage evolution model, and non-linear damage evolution model for the tensile tests of the asymmetric notch specimens. Because the stress evolution pattern for the verification tests remained at mode I in terms of the linear elastic fracture mechanics, the three models did not show significant differences in their fracture initiation predictions.

• 한국재료학회지
• /
• 제31권9호
• /
• pp.519-524
• /
• 2021

The impact properties of two austenitic Fe-23Mn-0.4C steels with different Al contents for cryogenic applications are investigated in this study. The 4Al steel consists mostly of austenite single-phase microstructure, while the 5Al steel exhibits a two-phase microstructure of austenite and delta-ferrite with coarse and elongated grains. Charpy impact test results reveal that the 5Al steel with duplex phases of austenite and delta-ferrite exhibits a ductile-to-brittle transition behavior, while the 4Al steel with only single-phase austenite has higher absorbed energy over 100 J at -196 ℃. The SEM fractographs of Charpy impact specimens show that the 4Al steel has a ductile dimple fracture regardless of test temperature, whereas the 5Al steel fractured at -100 ℃ and -196 ℃ exhibits a mixed fracture mode of both ductile and brittle fractures. Additionally, quasi-cleavage fracture caused by crack propagation of delta-ferrite phase is found in some regions of the brittle fracture surface of the 5Al steel. Based on these results, the delta-ferrite phase hardly has a significant effect on absorbed energy at room-temperature, but it significantly deteriorates low-temperature toughness by acting as the main site of the propagation of brittle cracks at cryogenic-temperatures.

• Computers and Concrete
• /
• 제27권5호
• /
• pp.457-472
• /
• 2021

Reinforced concrete (RC) buildings in Taiwan have suffered failure from strong earthquakes, which was magnified by the non-ductile detailing frames. Inadequate reinforcement as a consequence of the design philosophy prior to the introduction of current standards resulted in severe damage in the column and beam-column joint (BCJ). This study establishes a finite element analysis (FEA) of the non-ductile detailing RC column, BCJ, and three-story building that was previously tested through a tri-axial shaking table test. The results were then validated to laboratory specimens having the exact same dimensions and properties. FEA simulation integrates the concrete damage plasticity model and the elastic-perfectly plastic model for steel. The load-displacement responses of the column and BCJ specimens obtained from FEA were in a reasonable agreement with the experimental curves. The resulting initial stiffness and maximum base shear were found to be a close approximation to the experimental results. Also, the findings of a dynamic analysis of the three-story building showed that the time-history data of acceleration and displacement correlated well with the shaking table test results. This indicates the FEA implementation can be effectively used to predict the RC frame performance and failure mode under seismic loads.

• 한국해양공학회지
• /
• 제29권6호
• /
• pp.445-453
• /
• 2015

The stress triaxiality and lode angle are known to be most dominant fracture parameters in ductile materials. This paper proposes a three-dimensional failure strain surface for a ductile steel, called a low-temperature high-tensile steel (EH36), using average stress triaxiality and average normalized lode parameter, along with briefly introducing their theoretical background. It is an extension of previous works by Choung et al. (2011; 2012; 2014a; 2014b) and Choung and Nam (2013), in which a two-dimensional failure strain locus was presented. A series of tests for specially designed specimens that were expected to fail in the shear mode, shear-tension mode, and compression mode was conducted to develop a three-dimensional fracture surface covering wide ranges for the two parameters. This paper discusses the test procedures for three different tests in detail. The tensile force versus stroke data are presented as the results of these tests and will be used for the verification of numerical simulations and fracture identifications in Part II.

• 대한기계학회논문집A
• /
• 제33권6호
• /
• pp.552-559
• /
• 2009

The effect of porosity on the crack propagation is studied by using the cohesive zone model. Standard mode I fracture test were done by using compact tension specimens with various porosities. Load-load line displacement curves and ${\delta}_5$-crack resistance curves for various porosities were obtained from experiments. The cohesive zone model proposed by Xu and Needleman was employed to describe the crack propagation in porous media, and the Gurson model is used for constitutive relation of porous materials. These models were implemented into user subroutines of a finite element program ABAQUS. The fracture mode changes from ductile fracture to brittle fracture as the porosity increases. Numerical calculations agree well with experimental results.

• 한국주조공학회지
• /
• 제10권6호
• /
• pp.503-508
• /
• 1990

The effect of interlamellar spacing on tensile behavior and fracture mode at high temperatures has been studied for unidirectionally solidified $Al-CuAl_2$ eutectic composite. The tensile properties at room temperature in $Al-CuAl_2$ eutectic composite improved as the interlamellar spacing decreased due to the constraint effects of closely spaced lamellae, while the opposite behavior was observed at high temperatures due to the annihilation of the constraint effects by phase boundary sliding. The $Al-CuAl_2$ eutectic composite exhibited brittle fracture mode below the temperature at which the reinforcing phase softened but ductile fracture mode above the temperature.